Abstract: CuO thin films were deposited by spray ultrasonic
pyrolysis with different precursor solution. Two staring solution slats
were used namely: copper acetate and copper chloride. The influence
of these solutions on CuO thin films proprieties of is instigated. The
X rays diffraction (XDR) analysis indicated that the films deposed
with copper acetate are amorphous however the films elaborated with
copper chloride have monoclinic structure. UV- Visible transmission
spectra showed a strong absorbance of the deposited CuO thin films
in the visible region. Electrical characterization has shown that CuO
thin films prepared with copper acetate have a higher electrical
conductivity.
Abstract: The present study deals with the characterization of
CrSiN coatings obtained by PVD magnetron sputtering systems.
CrSiN films were deposited with different Si contents, in order to
check the effect of at.% variation on the different properties of the
Cr–N system. Coatings were characterized by scanning electron
microscopy (SEM) for thickness measurements, X-ray diffraction.
Surface morphology and the roughness characteristics were explored
using AFM, Mechanicals properties, elastic and plastic deformation
resistance of thin films were investigated using nanoindentation test. We observed that the Si addition improved the hardness and the
Young’s modulus of the Cr–N system. Indeed, the hardness value is
18,56 GPa for CrSiN coatings. Besides, the Young’s modulus value
is 224,22 GPa for CrSiN coatings for Si content of 1.2 at.%.
Abstract: Si-Ge solid solutions (bulk poly- and mono-crystalline
samples, thin films) are characterized by high perspectives for
application in semiconductor devices, in particular, optoelectronics
and microelectronics. From this point of view, complex studying of
structural state of the defects and structural-sensitive physical
properties of Si-Ge solid solutions depending on the contents of Si
and Ge components is very important. Present work deals with the
investigations of microstructure, microhardness, internal friction and
shear modulus of Si1-xGex(x≤0,02) bulk monocrystals conducted at
room temperature. Si-Ge bulk crystals were obtained by Czochralski
method in [111] crystallographic direction. Investigated
monocrystalline Si-Ge samples are characterized by p-type
conductivity and carriers’ concentration 5.1014-1.1015cm-3.
Microhardness was studied on Dynamic Ultra Micro hardness Tester
DUH-201S with Berkovich indenter. Investigate samples are characterized with 0,5x0,5x(10-15)mm3
sizes, oriented along [111] direction at torsion oscillations ≈1Hz,
multistage changing of internal friction and shear modulus has been
revealed in an interval of strain amplitude of 10-5-5.10-3. Critical
values of strain amplitude have been determined at which hysteretic
changes of inelastic characteristics and microplasticity are observed. The critical strain amplitude and elasticity limit values are also
determined. Dynamic mechanical characteristics decreasing trend is
shown with increasing Ge content in Si-Ge solid solutions. Observed
changes are discussed from the point of view of interaction of various
dislocations with point defects and their complexes in a real structure
of Si-Ge solid solutions.
Abstract: This paper deals with the problem of management of
information resources in libraries of the public institution Sultan
Moulay Slimane University (SMSU) in order to analyze the
satisfaction of the readers, and allow university leaders to make better
strategic and instant decisions. For this, the integration of an
integrated management decision library system is a priority program
of higher education, as part of the Digital Morocco, which has a
proactive policy to develop the use of new technologies information
and communication in higher institutions. This operational
information system can provide better services to the students and for
the leaders. Our approach is to integrate the tools of business
intelligence (BI) in the library management by using power BI.
Abstract: A novel chromium-free protective coating films based
on a zeolite coating was growing onto a FeCrAlloy metal using in –
situ hydrothermal method. The zeolite film was obtained using in-situ
crystallization process that is capable of coating large surfaces with
complex shape and in confined spaces has been developed. The
zeolite coating offers an advantage of a high mechanical stability and
thermal stability. The physicochemical properties were investigated
using X-ray diffraction (XRD), Electron Microscopy (SEM), Energy
Dispersive X–ray Analysis (EDX) and Thermogravimetric Analysis
(TGA). The transition from oxide-on-alloy wires to hydrothermally
synthesised uniformly zeolite coated surfaces was followed using
SEM and XRD. In addition, the robustness of the prepared coating
was confirmed by subjecting these to thermal cycling (ambient to
550oC).
Abstract: Cross-linked konjac glucomannan and kappa
carrageenan film were prepared by chemical crosslinking using
glutaraldehyde (GA) as the crosslinking agent. The effect
crosslinking on the swelling degree was investigated. Konjac
glucomannan and its mixture with kappa carrageenan film was
immersed in GA solution and then thermally cured. The obtained
cross-linked film was washed and soaked in the ethanol to remove
the unreacted GA. The obtained film was air dried at room
temperature to a constant weight. The infrared spectra and the value
of swelling degree of obtained crosslinked film showed that
glucomannan and kappa carrageenan was able to be cross-linked
using glutaraldehyde by film immersion and curing method without
catalyst. The cross-linked films were found to be pH sensitive,
indicating a potential to be used in drug delivery polymer system.
Abstract: RF magnetron sputtering is used on the ceramic targets,
each of which contains zinc oxide (ZnO), zinc oxide doped with
aluminum (AZO) and zinc oxide doped with gallium (GZO). The XRD
analysis showed a preferred orientation along the (002) plane for ZnO,
AZO, and GZO films. The AZO film had the best electrical properties;
it had the lowest resistivity of 6.6 × 10-4 cm, the best sheet resistance of
2.2 × 10-1 Ω/square, and the highest carrier concentration of 4.3 × 1020
cm-3, as compared to the ZnO and GZO films.
Abstract: These Monolayer and multilayer coatings of CrN and
AlCrN deposited on 100Cr6 (AISI 52100) substrate by PVD
magnetron sputtering system. The microstructures of the coatings
were characterized using atomic force microscopy (AFM). The AFM
analysis revealed the presence of domes and craters that are
uniformly distributed over all surfaces of the various layers.
Nanoindentation measurement of CrN coating showed maximum
hardness (H) and modulus (E) of 14 GPa and 190 GPa, respectively.
The measured H and E values of AlCrN coatings were found to be 30
GPa and 382 GPa, respectively. The improved hardness in both the
coatings was attributed mainly to a reduction in crystallite size and
decrease in surface roughness. The incorporation of Al into the CrN
coatings has improved both hardness and Young’s modulus.
Abstract: The purpose of the paper is to address the strategic
risk issues surrounding Hindi film distribution in Mumbai for a film
distributor, who acts as an entrepreneur when launching a product
(movie) in the market (film territory).The paper undertakes a
fundamental review of films and risk in the Hindi film industry and
applies Grounded Theory technique to understand the complex
phenomena of risk taking behavior of the film distributors (both
independent and studios) in Mumbai. Rich in-depth interviews with
distributors are coded to develop core categories through constant
comparison leading to conceptualization of the phenomena of
interest. This paper is a first-of-its-kind-attempt to understand risk
behavior of a distributor, which is akin to entrepreneurial risk
behavior under conditions of uncertainty.
Abstract: In this study, to clarify the effectiveness of an
aluminum/chromium/tungsten-based-coated tool for cutting sintered
steel, tool wear was experimentally investigated. The sintered steel
was turned with the (Al60,Cr25,W15)N-, (Al60,Cr25,W15)(C,N)- and
(Al64,Cr28,W8)(C,N)-coated cemented carbide tools according to the
physical vapor deposition (PVD) method. Moreover, the tool wear of
the aluminum/chromium/tungsten-based-coated item was compared
with that of the (Al,Cr)N coated tool. Furthermore, to clarify the tool
wear mechanism of the aluminum/chromium/tungsten-coating film for
cutting sintered steel, Scanning Electron Microscope observation and
Energy Dispersive x-ray Spectroscopy mapping analysis were
conducted on the abraded surface. The following results were
obtained: (1) The wear progress of the (Al64,Cr28,W8)(C,N)-coated
tool was the slowest among that of the five coated tools. (2) Adding
carbon (C) to the aluminum/chromium/tungsten-based-coating film
was effective for improving the wear-resistance. (3) The main wear
mechanism of the (Al60,Cr25,W15)N-, the (Al60,Cr25,W15)(C,N)-
and the (Al64,Cr28,W8)(C,N)-coating films was abrasive wear.
Abstract: In the immunologic sense, clinical infection is a state
of failure of the immune system to combat the pathogenic weapon of
the bacteria invading the host. A motile gram negative vibroid
organism associated with marked mono and poly nuclear cell
responses was traced during the examination of a clinical material
from an infected common carp Cyprinus carpio. On primary plate
culture, growth was shown to be pure, dense population of an
Aeromonas-like colony morphotype. The pure isolate was found to
be; Aerobic, facultatively anaerobic, non-halophilic, grew at 0C, and
37C, oxidase positive utilizes glucose through fermentative pathway,
resist 0/129 and novobiocin, produces alanine and lysine
decarboxylases but non-producing ornithine dehydrolases. Tests for
the in vitro determinants of pathogenicity has shown to be; Betahaemolytic
onto blood agar, gelatinase, casienase and amylase
producer. Three in vivo determinants of pathogenicity were tested as,
the lethal dose fifty, the pathogenesis and pathogenicity. It was
evident that 0.1 milliliter of the causal bacterial cell suspension of a
density 1 x 107 CFU/ml injected intramuscularly into an average of
100gms fish toke five days incubation period, then at the day six
morbidity and mortality were initiated. LD50 was recorded at the day
12 post-infection. Use of an LD50 doses to study the pathogenicity,
reveals mononuclear and polynuclear cell responses, on examining
the stained direct films of the clinical materials from the
experimentally infected fish. Re-isolation tests confirm that the reisolant
is same. The course of the infection in natural case was shown
manifestation of; skin ulceration, haemorrhage and descaling. On
evisceration, the internal organs were shown; congestion in the
intestines, spleen and, air sacs. The induced infection showed a
milder form of these manifestations. The grading of the virulence of
this organism was virulent causing chronic course of infections as
indicated from the pathogenesis and pathogenicity studies. Thus the
infectious bacteria were consistent with Aeromonas hydrophila, and
the infection was chronic.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.
Abstract: Poly bag and mulch films for agricultural field caused
pose environmental problem due to the non-degradable plastics
wastes upon disposal. Thus, a degradable poly bag was designed with
hybrid sago starch (SS) and polyvinyl alcohol (PVA). Two Different
blended compositions of SS and PVA hybrid have been compounded.
Then, the hybrids blended are mixed with linear line density
polyethylene (LLDPE) resin to fabricate poly bag film through
conventional film blowing process. Samples of LLDPE, SS and PVA
hybrid film were exposed to UV light and soil burial. The weight
losses were determined during degradation process. Hybrid film by
degradation of starch was found to hydrolyze and hydroxyl groups
decrease on esterification upon exposure to soil burial and uv
radiation. It was found out that, the hybrid film for 60% of SS
composition showed greatest degradation in soil and UV radiation.
Abstract: The introduction of degradable plastic materials into
agricultural sectors has represented a promising alternative to
promote green agriculture and environmental friendly of modern
farming practices. Major challenges of developing degradable
agricultural films are to identify the most feasible types of
degradation mechanisms, composition of degradable polymers and
related processing techniques. The incorrect choice of degradable
mechanisms to be applied during the degradation process will cause
premature losses of mechanical performance and strength. In order to
achieve controlled process of agricultural film degradation, the
compositions of degradable agricultural film also important in order
to stimulate degradation reaction at required interval of time and to
achieve sustainability of the modern agricultural practices. A set of
photodegradable polyethylene based agricultural film was developed
and produced, following the selective optimization of processing
parameters of the agricultural film manufacturing system. Example of
agricultural films application for oil palm seedlings cultivation is
presented.
Abstract: Considering palm oil as non-drying oil owing to its
low iodine value, an attempt was taken to increase the unsaturation in
the fatty acid chains of palm oil for the preparation of alkyds. To
increase the unsaturation in the palm oil, sulphuric acid (SA) and
para-toluene sulphonic acid (PTSA) was used prior to alcoholysis for
the dehydration process. The iodine number of the oil samples was
checked for the unsaturation measurement by Wijs method. Alkyd
resin was prepared using the dehydrated palm oil by following
alcoholysis and esterification reaction. To improve the film properties
0.5wt.% multi-wall carbon nano tubes (MWCNTs) were used to
manufacture polymeric film. The properties of the resins were
characterized by various physico-chemical properties such as density,
viscosity, iodine value, saponification value, etc. Structural
elucidation was confirmed by Fourier transform of infrared
spectroscopy and proton nuclear magnetic resonance; surfaces of the
films were examined by field-emission scanning electron microscope.
In addition, pencil hardness and chemical resistivity was also
measured by using standard methods. The effect of enhancement of
the unsaturation in the fatty acid chain found significant and
motivational. The resin prepared with dehydrated palm oil showed
improved properties regarding hardness and chemical resistivity
testing. The incorporation of MWCNTs enhanced the thermal
stability and hardness of the films as well.
Abstract: The Al-MoO3-P-CdTe-Al MOS sandwich structures
were fabricated by vacuum deposition method on cleaned glass
substrates. Capacitance versus voltage measurements were performed
at different frequencies and sweep rates of applied voltages for oxide
and semiconductor films of different thicknesses. In the negative
voltage region of the C-V curve a high differential capacitance of the
semiconductor was observed and at high frequencies (
Abstract: In this work, we report, a systematic study on the
structural and optical properties of Pr-doped ZnO nanostructures and
PVA:Zn98Pr2O polymer matrix nanocomposites free standing films.
These particles are synthesized through simple wet chemical route
and solution casting technique at room temperature, respectively.
Structural studies carried out by X-ray diffraction method confirm
that the prepared pure ZnO and Pr doped ZnO nanostructures are in
hexagonal wurtzite structure and the microstrain is increased upon
doping. TEM analysis reveals that the prepared materials are in sheet
like nature. Absorption spectra show free excitonic absorption band
at 370 nm and red shift for the Pr doped ZnO nanostructures. The
PVA:Zn98Pr2O composite film exhibits both free excitonic and PVA
absorption bands at 282 nm. Fourier transform infrared spectral
studies confirm the presence of A1 (TO) and E1 (TO) modes of Zn-O
bond vibration and the formation of polymer composite materials.
Abstract: Paints are the most widely used methods of protection
against atmospheric corrosion of metals. The aim of this work was to
determine the protective performance of epoxy coating against sea
water before and after damage.
Investigations are conducted using stationary and non-stationary
electrochemical tools such as electrochemical impedance
spectroscopy has allowed us to characterize the protective qualities of
these films. The application of the EIS on our damaged in-situ
painting shows the existence of several capacitive loops which is an
indicator of the failure of our tested paint. Microscopic analysis
(micrograph) helped bring essential elements in understanding the
degradation of our paint condition and immersion training corrosion
products.
Abstract: In order to detect and quantify the phenolic contents
of a wastewater with biosensors, two working electrodes based on
modified Poly(Pyrrole) films were fabricated. Enzyme horseradish
peroxidase was used as biomolecule of the prepared electrodes.
Various phenolics were tested at the biosensor. Phenol detection was
realized by electrochemical reduction of quinones produced by
enzymatic activity. Analytical parameters were calculated and the
results were compared with each other.