Abstract: In this research, carrageenan extracted from seaweed Eucheuma cottonii was mixed with polyvinyl alcohol (PVA) and then crosslinked using glutaraldehyde (GA). The obtained hydrogel films were applied to control the drug release rate of paracetamol. The aim of this research was to develop a mathematical model that can be used to describe the mass transfer rate of paracetamol from the hydrogel film into buffer solution. The effect of weight ratio carrageenan-PVA (5: 0, 1: 0.5, 1: 1, 1: 2, 0: 5) on the parameters of the mathematical model was investigated also. Based on the experimental data, the proposed mathematical model could describe the mass transfer rate of paracetamol. The weight ratio of carrageenan-PVA greatly affected the amount of paracetamol absorbed in the hydrogel film and the mass transfer rate of paracetamol.
Abstract: Hydrogel films were prepared from kappa carrageenan by crosslinking with glutaraldehyde. Carrageenan films extracted from Kappaphycus alvarezii seaweed were immersed in glutaraldehyde solution for 2 min and then cured at 110 °C for 25 min. The obtained crosslinked films were washed with ethanol to remove the unreacted glutaraldehyde and then air dried to constant weights. The aim of this research was to study the swelling degree behaviour of the hydrogel film to neutral salts solution, namely NaCl, KCl, and CaCl2. The results showed that swelling degree of crosslinked films varied non-monotonically with salinity of NaCl. Swelling degree decreased with the increasing of KCl concentration. Swelling degree of crosslinked film in CaCl2 solution was lower than that in NaCl and in KCl solutions.
Abstract: Cross-linked konjac glucomannan and kappa
carrageenan film were prepared by chemical crosslinking using
glutaraldehyde (GA) as the crosslinking agent. The effect
crosslinking on the swelling degree was investigated. Konjac
glucomannan and its mixture with kappa carrageenan film was
immersed in GA solution and then thermally cured. The obtained
cross-linked film was washed and soaked in the ethanol to remove
the unreacted GA. The obtained film was air dried at room
temperature to a constant weight. The infrared spectra and the value
of swelling degree of obtained crosslinked film showed that
glucomannan and kappa carrageenan was able to be cross-linked
using glutaraldehyde by film immersion and curing method without
catalyst. The cross-linked films were found to be pH sensitive,
indicating a potential to be used in drug delivery polymer system.