Abstract: This research aimed to modify pineapple leaf paper
(PALP) for using as wet media in the evaporation cooling system by
improving wet mechanical property (tensile strength) without
compromising water absorption property. Polyamideamineepichorohydrin
resin (PAE) and carboxymethylcellulose (CMC)
were used to strengthen the paper, and the PAE and CMC ratio of
80:20 showed the optimum wet and dry tensile index values, which
were higher than those of the commercial cooling pad (CCP).
Compared with CCP, PALP itself and all the PAE/CMC modified
PALP possessed better water absorption. The PAE/CMC modified
PALP had potential to become a new type of wet media.
Abstract: Permeability reduction induced by asphaltene
precipitation during gas injection is one of the serious problems in
the oil industry. This problem can lead to formation damage and
decrease the oil production rate. In this work, Malaysian light oil
sample has been used to investigate the effect CO2 injection and
Water Alternating Gas (WAG) injection on permeability reduction.
In this work, dynamic core flooding experiments were conducted to
study the effect of CO2 and WAG injection on the amount of
asphaltene precipitated. Core properties after displacement were
inspected for any permeability reduction to study the effect of
asphaltene precipitation on rock properties.
The results showed that WAG injection gave less asphaltene
precipitation and formation damage compared to CO2 injection. The
study suggested that WAG injection can be one of the important
factors of managing asphaltene precipitation.
Abstract: Bentonitic material from South Aswan, Egypt was evaluated in terms of mineral-ogy and chemical composition as bleaching clay in refining of transformer oil before and after acid activation and thermal treatment followed by acid leaching using HCl and H2SO4 for different contact times. Structural modification and refining power of bento-nite were investigated during modification by means of X-ray diffraction and infrared spectroscopy. The results revealed that the activated bentonite could be used for refining of transformer oil. The oil parameters such as; dielectric strength, viscosity and flash point had been improved. The dielectric breakdown strength of used oil increased from 29 kV for used oil treated with unactivated bentonite to 74 kV after treatment with activated bentonite. Kinematic Viscosity changed from 19 to 11 mm2 /s after treatment with activated bentonite. However, flash point achieved 149 ºC.
Abstract: The copper flotation tailings from Konkola Copper
mine in Nchanga, Zambia were used in the study. The purpose of this
study was to determine the leaching characteristics of the tailings
material prior and after the physical beneficiation process is
employed. The Knelson gravity concentrator (KC-MD3) was used for
the beneficiation process. The copper leaching efficiencies and
impurity co-extraction percentages in both the upgraded and the raw
feed material were determined at different pH levels and temperature.
It was observed that the copper extraction increased with an increase
in temperature and a decrease in pH levels. In comparison to the raw
feed sample, the upgraded sample reported a maximum copper
extraction of 69% which was 9%, higher than raw feed % extractions.
The impurity carry over was reduced from 18% to 4 % on the
upgraded sample. The reduction in impurity co-extraction was as a
result of the removal of the reactive gangue elements during the
upgrading process, this minimized the number of side reaction
occurring during leaching.
Abstract: The gel-supported precipitation (GSP) process can be
used to make spherical particles (spherules) of nuclear fuel,
particularly for very high temperature reactors (VHTR) and even for
implementing the process called SPHEREPAC. In these different
cases, the main characteristics are the sphericity of the particles to be
manufactured and the control over their grain size. Nonetheless,
depending on the specifications defined for these spherical particles,
the GSP process has intrinsic limits, particularly when fabricating
very small particles. This paper describes the use of secondary
fragmentation (water, water/PVA and uranyl nitrate) on solid
surfaces under varying temperature and vibration conditions to assess
the relevance of using this new technique to manufacture very small
spherical particles by means of a modified GSP process. The
fragmentation mechanisms are monitored and analysed, before the
trends for its subsequent optimised application are described.
Abstract: Titanium dioxide coatings were deposited by utilizing
atmospheric plasma spraying (APS) system. The agglomerated nanopowder
and different spraying parameters were used to determine
their influences on the microstructure surface feature and photoabsorption
of the coatings. The microstructure of as-sprayed TiO2
coatings were characterized by scanning electron microscope (SEM).
Surface characteristics were investigated by Fourier Transform
Infrared (FT-IR). The photo absorption was determined by UV-VIS
spectrophotometer. It is found that the spray parameters have an
influence on the microstructure, surface feature and photo-absorption
of the TiO2 coatings.
Abstract: In the forming of ceramic materials the plasticity
concept is commonly used. This term is related to a particular
mechanical behavior when clay is mixed with water. A plastic
ceramic material shows a permanent strain without rupture
when a compressive load produces a shear stress that exceeds
the material-s yield strength. For a plastic ceramic body it
observes a measurable elastic behavior before the yield
strength and when the applied load is removed. In this work, a
mathematical model was developed from applied concepts of
the plasticity theory by using the stress/strain diagram under
compression.
Abstract: Ti-6Al-4V alloy has demonstrated a high strength to
weight ratio as well as good properties at high temperature. The
successful application of the alloy in some important areas depends
on suitable joining techniques. Friction welding has many
advantageous features to be chosen for joining Titanium alloys. The
present work investigates the feasibility of producing similar metal
joints of this Titanium alloy by rotary friction welding method. The
joints are produced at three different speeds and the performances of
the welded joints are evaluated by conducting microstructure studies,
Vickers Hardness and tensile tests at the joints. It is found that the
weld joints produced are sound and the ductile fractures in the tensile
weld specimens occur at locations away from the welded joints. It is
also found that a rotational speed of 1500 RPM can produce a very
good weld, with other parameters kept constant.
Abstract: (Bi0.5Na0.5)TiO3 doped with 8 mol % BaTiO3 powder
(BNT-BT0.08), prepared by sol-gel method was compacted and
sintered by Spark Plasma Sintering (SPS) process. The influence of
SPS temperature on the densification of BNT-BT0.08 ceramic was
investigated. Starting from sol-gel nanopowder of BNT-BT
containing 8 mol % BaTiO3 with an average particles size of about
30 nm, were obtained ceramics with density around 98 % of the
theoretical density value when the SPS temperature used was about
850 °C. The average grain size of the resulting ceramics was 80 nm.
The BNT-BT0.08 ceramic sample obtained by SPS method has shown
good electric properties at various frequencies.
Abstract: Platinum oxide nanoparticles were prepared by a
simple hydrothermal route and chemical reduction using
carbohydrates (Fructose and sucrose) as the reducing and
stabilizing agents. The crystallite size of these nanoparticles was
evaluated from X-ray diffraction (XRD), atomic force microscopy
(AFM) and transmission electron microscopy (TEM) and was
found to be 10 nm as shown in figure 1, which is the
demonstration of EM bright field and transmission electron
microscopy. The effect of carbohydrates on the morphology of the
nanoparticles was studied using TEM (Figure 1). The
nanoparticles (100 μg/ml) were administered to the Pseudomonas
Stutzeri and Lactobacillus cultures and the incubation was done at
35 oC for 24 hours. The nanocomposites exhibited interesting
inhibitory as well as bactericidal activity against P. Stutzeri and
and Lactobacillus species. Incorporation of nanoparticles also
increased the thermal stability of the carbohydrates.
Abstract: Chemical vapor deposition method was used to
produce carbon nanotubes on an iron based catalyst from acetylene.
Gas-phase samples collected from the different positions of the tubular reactor were analyzed by GC/MS. A variety of species ranging from hydrogen to naphthalene were observed and changes in their concentrations were plotted against the reactor position. Briefly benzene, toluene, styrene, indene and naphthalene were the main
higher molecular weight species and vinylacetylene and diacetylene were the important intermediates. Nanotube characterization was performed by scanning electron microscopy and transmission electron microscopy.
Abstract: Lightweight ceramic materials in the form of bricks
and blocks are widely used in modern construction. They may be
obtained by adding of rice husk, rye straw, etc, as porous forming
materials. Rice husk is a major by-product of the rice milling
industry. Its utilization as a valuable product has always been a
problem. Various technologies for utilization of rice husk through
biological and thermochemical conversion are being developed.
The purpose of this work is to develop lightweight ceramic
materials with clay matrix and filler of rice husk and examine their
main physicomechanical properties. The results obtained allow to
suppose that the materials synthesized on the basis of waste materials
can be used as lightweight materials for construction purpose.
Abstract: Emphasis on the advancement of new materials and technology has been there for the past few decades. The global development towards using cheap and durable materials from renewable resources contributes to sustainable development. An experimental investigation of mechanical behaviour of sisal fibre-reinforced concrete is reported for making a suitable building material in terms of reinforcement. Fibre reinforced Composite is one such material, which has reformed the concept of high strength. Sisal fibres are abundantly available in the hot areas. Sisal fibre has emerged as a reinforcing material for concretes, used in civil structures. In this work, properties such as hardness and tensile strength of sisal fibre reinforced cement composites with 6, 12, 18 and 24% by weight of sisal fibres were assessed. Sisal fibre reinforced cement composite slabs with long sisal fibres were manufactured using a cast hand lay up technique. Mechanical response was measured under tension. The high energy absorption capacity of the developed composite system was reflected in high toughness values under tension respectively.
Abstract: Heavy metals have bad effects on environment and
soils and it can uptake by natural HAP .natural Hap is an inexpensive
material that uptake large amounts of various heavy metals like Zn
(II) .Natural HAP (N-HAP), extracted from bovine cortical bone ash,
is a good choice for substitution of commercial HAP. Several
experiments were done to investigate the sorption capacity of Zn (II)
to N-HAP in various particles sizes, temperatures, initial
concentrations, pH and reaction times. In this study, the sorption of
Zinc ions from a Zn solution onto HAP particles with sizes of 1537.6
nm and 47.6 nm at three initial pH values of 4.50, 6.00 and 7.50 was
studied. The results showed that better performance was obtained
through a 47.6 nm particle size and higher pH values. The
experimental data were analyzed using Langmuir, Freundlich, and
Arrhenius equations for equilibrium, kinetic and thermodynamic
studies. The analysis showed a maximum adsorption capacity of NHAP
as being 1.562 mmol/g at a pH of 7.5 and small particle size.
Kinetically, the prepared N-HAP is a feasible sorbent that retains Zn
(II) ions through a favorable and spontaneous sorption process.
Abstract: novel and simple method is introduced for rapid and
highly efficient water treatment by reverse osmosis (RO) method using
multi-walled carbon nanotubes (MWCNTs) / polyacrylonitrile (PAN)
polymer as a flexible, highly efficient, reusable and semi-permeable
mixed matrix membrane (MMM). For this purpose, MWCNTs were
directly synthesized and on-line purified by chemical vapor deposition
(CVD) process, followed by directing the MWCNT bundles towards an
ultrasonic bath, in which PAN polymer was simultaneously suspended
inside a solid porous silica support in water at temperature to ~70 οC.
Fabrication process of MMM was finally completed by hot isostatic
pressing (HIP) process. In accordance with the analytical figures of
merit, the efficiency of fabricated MMM was ~97%. The rate of water
treatment process was also evaluated to 6.35 L min-1. The results reveal
that, the CNT-based MMM is suitable for rapid treatment of different
forms of industrial, sea, drinking and well water samples.
Abstract: We report here, the results of molecular dynamics
simulation of p-doped (Ga-face)GaN over n-doped (Siface)(
0001)4H-SiC hetero-epitaxial material system with one-layer
each of Ga-flux and (Al-face)AlN, as the interface materials, in the
form of, the total Density of States (DOS). It is found that the total
DOS at the Fermi-level for the heavily p-doped (Ga-face)GaN and ndoped
(Si-face)4H-SiC hetero-epitaxial system, with one layer of
(Al-face)AlN as the interface material, is comparatively higher than
that of the various cases studied, indicating that there could be good
vertical conduction across the (Ga-face)GaN over (Si-face)(0001)4HSiC
hetero-epitaxial material system.
Abstract: A simple approach is demonstrated for growing large
scale, nearly vertically aligned ZnO nanowire arrays by thermal
oxidation method. To reveal effect of temperature on growth and
physical properties of the ZnO nanowires, gold coated zinc substrates
were annealed at 300 °C and 400 °C for 4 hours duration in air. Xray
diffraction patterns of annealed samples indicated a set of well
defined diffraction peaks, indexed to the wurtzite hexagonal phase of
ZnO. The scanning electron microscopy studies show formation of
ZnO nanowires having length of several microns and average of
diameter less than 500 nm. It is found that the areal density of wires
is relatively higher, when the annealing is carried out at higher
temperature i.e. at 400°C. From the field emission studies, the values
of the turn-on and threshold field, required to draw emission current
density of 10 μA/cm2 and 100 μA/cm2 are observed to be 1.2 V/μm
and 1.7 V/μm for the samples annealed at 300 °C and 2.9 V/μm and
3.7 V/μm for that annealed at 400 °C, respectively. The field
emission current stability, investigated over duration of more than 2
hours at the preset value of 1 μA, is found to be fairly good in both
cases. The simplicity of the synthesis route coupled with the
promising field emission properties offer unprecedented advantage
for the use of ZnO field emitters for high current density
applications.
Abstract: The pyrolysis of hazelnut shell, polyethylene oxide and their blends were carried out catalytically at 500 and 650 ºC. Potassium dichromate was chosen according to its oxidative characteristics and decomposition temperature (500 ºC) where decomposition products are CrO3 and K2CrO4. As a main effect, a remarkable increase in gasification was observed using this catalyst for pure components and blends especially at 500 ºC rather than 650 ºC contrary to the main observation in the pyrolysis process. The increase in gas product quantity was compensated mainly with decrease in solid product and additionally in some cases liquid products.
Abstract: In this work, effects of catalysts (TiO2, and Nb2O5) were investigated on the hydrogen desorption of Mg(BH4)2. LiBH4 and MgCl2 with 2:1 molar ratio were mixed by using ball milling to prepare Mg(BH4)2. The desorption behaviors were measured by thermo-volumetric apparatus. The hydrogen desorption capacity of the mixed sample milled for 2 h was 4.78 wt% with a 2-step released. The first step occurred at 214 °C and the second step appeared at 374 °C. The addition of 16 wt% Nb2O5 decreased the desorption temperature in the second step about 66 °C and increased the hydrogen desorption capacity to 4.86 wt% hydrogen. The addition of TiO2 also improved the desorption temperature in the second step and the hydrogen desorption capacity. It decreased the desorption temperature about 71°C and showed a high amount of hydrogen, 5.27 wt%, released from the mixed sample. The hydrogen absorption after desorption of Mg(BH4)2 was also studied under 9.5 MPa and 350 °C for 12 h.
Abstract: The alumosilicate ceramics with mullite crystalline phase are used in various branches of science and technique. The mullite refractory ceramics with high porosity serve as a heat insulator and as a constructional materials [1], [2]. The purpose of the work was to sinter high porosity ceramic and to increase the quantity of mullite phase in this mullite, mullite-corundum ceramics. Two types of compositions were prepared at during the experiment. The first type is compositions with commercial alumina and silica oxides. The second type is from mixing these oxides with 10, 20 and 30 wt.%. of kaolin. In all samples the Al2O3 and SiO2 were in 2.57:1 ratio, because that was conformed to mullite stechiometric compositions (3Al2O3.2SiO2). The types of alumina oxides were α-Al2O3 (d50=4µm) and γ-Al2O3 (d50=80µm). Ratios of α-: γ-Al2O3 were (1:1) or (1:3). The porous materials were prepared by slip casting of suspension of raw materials. The aluminium paste (0.18 wt.%) was used as a pore former. Water content in the suspensions was 26-47 wt.%. Pore formation occurred as a result of hydrogen formation in chemical reaction between aluminium paste and water [2]. The samples were sintered at the temperature of 1650°C and 1750°C for one hour. The increasing amount of kaolin, α-: γ-Al2O3 at the ratio (1:3) and sintering at the highest temperature raised the quantity of mullite phase. The mullite phase began to dominate over the corundum phase.