Influence of Raw Materials Ratio and Sintering Temperature on the Properties of the Refractory Mullite-Corundum Ceramics

The alumosilicate ceramics with mullite crystalline phase are used in various branches of science and technique. The mullite refractory ceramics with high porosity serve as a heat insulator and as a constructional materials [1], [2]. The purpose of the work was to sinter high porosity ceramic and to increase the quantity of mullite phase in this mullite, mullite-corundum ceramics. Two types of compositions were prepared at during the experiment. The first type is compositions with commercial alumina and silica oxides. The second type is from mixing these oxides with 10, 20 and 30 wt.%. of kaolin. In all samples the Al2O3 and SiO2 were in 2.57:1 ratio, because that was conformed to mullite stechiometric compositions (3Al2O3.2SiO2). The types of alumina oxides were α-Al2O3 (d50=4µm) and γ-Al2O3 (d50=80µm). Ratios of α-: γ-Al2O3 were (1:1) or (1:3). The porous materials were prepared by slip casting of suspension of raw materials. The aluminium paste (0.18 wt.%) was used as a pore former. Water content in the suspensions was 26-47 wt.%. Pore formation occurred as a result of hydrogen formation in chemical reaction between aluminium paste and water [2]. The samples were sintered at the temperature of 1650°C and 1750°C for one hour. The increasing amount of kaolin, α-: γ-Al2O3 at the ratio (1:3) and sintering at the highest temperature raised the quantity of mullite phase. The mullite phase began to dominate over the corundum phase.

Authors:

• L. Mahnicka

Keywords:

• Alumina
• Kaolin
• Mullite-corundum
• Porous refractory ceramics

References:

[1] K. Okada. "Activation energy of mullitization from various starting
materials." J. Eur. Ceram. Soc., vol. 28, pp. 377-382, 2008.
[2] R. Svinka, V. Svinka, G. Bula, T. Juettner, E. Palcevskis. "Influence of
suspensions rheology on the properties of light weight high temperature
materials." Adv. Sci. Technol., vol. 45, pp. 2266-2271, 2006.
[3] T. Juettner, H. Moertel, V. Svinka, R. Svinka. "Structure of kaoline-
alumina based foam ceramics for high temperature applications." J. Eur.
Ceram. Soc., vol. 27, pp. 1435-1441, 2007.
[4] H. J. Kleebe, F. Siegelin, T. Straubinger, G. Ziegler. "Conversion of
Al2O3-SiO2 powder mixtures to 3:2 mullite following the stable or
metastable phase diagram." J. Eur. Ceram. Soc., vol. 21, pp. 2521-2533,
2001.
[5] A. Aras. "The change of phase composition in kaolinite- and illite-rich
clay-based ceramic bodies." Appl. Clay Sci., vol. 24, pp. 257-269, 2004.
[6] H. Schneider, S. Komarneni. "Mullite." WILEY-VCH Verlag GmbH &
Co.KGaA, pp. 180-190, 2005.
[7] Encyclopædia Britannica Online, s.v. "aluminosilicate: phase diagram of
the alumina-silica system", accessed October 27, 2011.
[8] H. Schneider, E. Eberhard. "Thermal expansion of mullite". J. Am.
Ceram. Soc., vol. 73, pp. 2073-2076, 1990.
[9] B. Nait-Ali, K. Haberko, H. Vesteghem, J. Absi, D. S. Smith.
"Preparation and thermal conductivity characterisation of highly porous
ceramics: Comparison between experimental results, analytical
calculations and numerical simulations." J. Am. Ceram. Soc., vol. 27, pp.
1345-1350, 2007.
[10] A. Esharghawi, C. Penot, F. Nardou. "Contribution to porous mullite
synthesis from clays by adding Al and Mg powders." J. Eur. Ceram.
Soc., vol. 29, pp. 31-38, 2009.