Abstract: Metal hydride water pumping system uses hydrogen as working fluid to pump water for low head and high discharge. The principal operation of this pump is based on the desorption of hydrogen at high pressure and its absorption at low pressure by a metal hydride. This work is devoted to study a concept of the dynamic behavior of a metal hydride pump using unsteady model and LaNi5 as hydriding alloy. This study shows that with MHP, it is possible to pump 340l/kg-cycle of water in 15 000s using 1 Kg of LaNi5 at a desorption temperature of 360 K, a pumping head equal to 5 m and a desorption gear ratio equal to 33. This study reveals also that the error given by the steady model, using LaNi5 is about 2%.A dimensional mathematical model and the governing equations of the pump were presented to predict the coupled heat and mass transfer within the MHP. Then, a numerical simulation is carried out to present the time evolution of the specific water discharge and to test the effect of different parameters (desorption temperature, absorption temperature, desorption gear ratio) on the performance of the water pumping system (specific water discharge, pumping efficiency and pumping time). In addition, a comparison between results obtained with steady and unsteady model is performed with different hydride mass. Finally, a geometric configuration of the reactor is simulated to optimize the pumping time.
Abstract: In this work, effects of catalysts (TiO2, and Nb2O5) were investigated on the hydrogen desorption of Mg(BH4)2. LiBH4 and MgCl2 with 2:1 molar ratio were mixed by using ball milling to prepare Mg(BH4)2. The desorption behaviors were measured by thermo-volumetric apparatus. The hydrogen desorption capacity of the mixed sample milled for 2 h was 4.78 wt% with a 2-step released. The first step occurred at 214 °C and the second step appeared at 374 °C. The addition of 16 wt% Nb2O5 decreased the desorption temperature in the second step about 66 °C and increased the hydrogen desorption capacity to 4.86 wt% hydrogen. The addition of TiO2 also improved the desorption temperature in the second step and the hydrogen desorption capacity. It decreased the desorption temperature about 71°C and showed a high amount of hydrogen, 5.27 wt%, released from the mixed sample. The hydrogen absorption after desorption of Mg(BH4)2 was also studied under 9.5 MPa and 350 °C for 12 h.