Study of Reactive Wetting of Sn–0.7Cu and Sn–0.3Ag–0.7Cu Lead Free Solders during Solidification on Nickel Coated Al Substrates

Microstructure, wetting behavior and interfacial reactions between Sn–0.7Cu and Sn–0.3Ag–0.7Cu (SAC0307) solders solidified on Ni coated Al substrates were compared and investigated. Microstructure of Sn–0.7Cu alloy exhibited a eutectic matrix composed of primary β-Sn dendrites with a fine dispersion of Cu6Sn5 intermetallics whereas microstructure of SAC0307 alloy exhibited coarser Cu6Sn5 and finer Ag3Sn precipitates of IMCs with decreased tin dendrites. Contact angles ranging from 22° to 26° were obtained for Sn–0.7Cu solder solidified on substrate surface whereas for SAC0307 solder alloy contact angles were found to be in the range of 20° to 22°. Sn–0.7Cu solder/substrate interfacial region exhibited faceted (Cu, Ni)6Sn5 IMCs protruding into the solder matrix and a small amount of (Cu, Ni)3Sn4 intermetallics at the interface. SAC0307 solder/substrate interfacial region showed mainly (Cu, Ni)3Sn4 intermetallics adjacent to the coating layer and (Cu, Ni)6Sn5 IMCs in the solder matrix. The improvement in the wettability of SAC0307 solder alloy on substrate surface is attributed to the formation of cylindrical shape (Cu,Ni)6Sn5 and a layer of (Cu, Ni)3Sn4 IMCs at the interface.

Authors:

• Satyanarayana
• K.N. Prabhu

Keywords:

• Lead-free solder
• wetting
• contact angle
• intermetallics.

References:

[1] J.S. Hwang, "Implementing lead-free electronics", New York: McGraw-
Hill, 2005, pp.1-40.
[2] M.J. Rizvi, C. Bailey, Y.C. Chan, M.N. Islam, H. Lu, J., "Effect of
adding 0.3 wt% Ni into the Sn-0.7 wt% Cu solder Part II. Growth of
intermetallic layer with Cu during wetting and aging", Alloys Compd.
438 (2007) pp.122-28
[3] K. Sweatman, S. Suenaga, and T. Nishimura, "Strength of lead-free
BGA spheres in high speed loading", Proceedings Pan Pacific, 2008,
pp.127-133.
[4] G. Zeng, S. Xue, L. Zhang and L. Gao, "Recent advances on Sn-Cu
solders with alloying elements: review", J Mater Sci: Mater Electron,
22(2011) pp. 565-578.
[5] A.A. El-Daly, F. El-Tantawy, A.E. Hammad, M.S. Gaafar, E.H. El-
Mossalamy, A.A. Al-Ghamdi, "Structural and elastic properties of
eutectic Sn-Cu lead-free solder alloy containing small amount of Ag and
In", J. Alloys Compd., 509 (2011) pp.7238-7246.
[6] X. Liu, L. Wang, J. Wang and Y. Lv, "Effects of Ce Addition on
Properties of Sn-0.3Ag-0.7Cu Low-Ag Lead-free Solder",11th
International Conference on Electronic Packaging Technology & High
Density Packaging 2010, pp. 176-180.
[7] N. Mookam and K. Kanlayasiri, "Evolution of Intermetallic Compounds
between Sn-0.3Ag-0.7Cu Low-silver Lead-free Solder and Cu Substrate
during Thermal Aging", J. Mater. Sci. Technol.: 28(1)2012, pp.53-59.
[8] F. Cheng, F. Gao, J. Zhang, W. Jin and X. Xiao, "Tensile properties and
wettability of SAC0307 and SAC105 low Ag lead-free solder alloys",
J Mater Sci, 46 (2011) pp.3424-3429.
[9] S. K. Huh, K. S. Kim and Suganuma, "Effect of Ag addition on the
Microstructural and mechanical properties of Sn-Cu eutectic solder",
Materials transactions, 42(5)(2001), pp.739-744.
[10] R. Zhang, F. Guo, J. Liu, H. Shen, and F. Tai, "Morphology and Growth
of Intermetallics at the Interface of Sn-based Solders and Cu with
Different Surface Finishes", J. Electron. Mater., 38(2)(2009), pp.241-
251..
[11] C.E. Ho, R.Y. Tsai, Y.L. Lin, and C.R. Kao, "Effect of Cu
Concentration on the Reactions between Sn-Ag-Cu Solders and Ni", J.
Electron. Mater., 31(6)(2002), pp. 584-590.
[12] G. Wei, D. Luo,, L. Shi, G. He, "Influence of multiple reflows and
thermal shock on interfacial IMC of solder joints between
Sn0.3Ag0.7Cu solder/pads(HASL,OSP, electrolytic Ni/Au and ENIG
PCB finishes)", International Symposium on Advanced Packaging
Materials (APM 2011), 2011, pp. 302- 307.