Hydrogen Generation by Accelerating Aluminum Corrosion in Water with Alumina

For relatively small particles of aluminum (<60 μm), a measurable percentage of the aluminum (>5%) is observed to corrode before passivation occurs at moderate temperatures (>50oC) in de-ionized water within one hour. Physical contact with alumina powder results in a significant increase in both the rate of corrosion and the extent of corrosion before passivation. Whereas the resulting release of hydrogen gas could be of commercial interest for portable hydrogen supply systems, the fundamental aspects of Al corrosion acceleration in presence of dispersed alumina particles are equally important. This paper investigates the effects of various amounts of alumina on the corrosion rate of aluminum powders in water and the effect of multiple additions of aluminum into a single reactor.

Authors:

• J. Skrovan
• A. Alfantazi
• T. Troczynski

Keywords:

• Alumina
• Aluminum
• Corrosion
• Hydrogen

References:

[1] J. Larminie, J. Lowry, Electric Vehicle Technology Explained. John
Wiley & Sons, Ltd, (2003).
[2] J. M. Ogden, Prospects for building a hydrogen energy infrastructure,
Annu. Rev. Energy Environ 24 (1999) 227-279.
[3] J. Graetz, New approaches to hydrogen storage, Chemical Society
Reviews, 38(1) (2009) 73-82.
[4] A. Zuttel, Materials for hydrogen storage, Materials Today, Sept.
(2003) 24-33.
[5] C. Vargel, Corrosion of aluminium, Elsevier, (2004).
[6] A. V. Parmuzina O. V. Kravchenko, Activation of aluminum metal to
evolve hydrogen from water, Int. J. Hydrogen Energy, 33 (2008) 3073-
3076.
[7] R.S. Alwitt, The aluminium - water system, In: Dekker M (ed), Oxides
and Oxide Films, Diggle J W, New York (1976) pp. 171-254
[8] T. Hiraki, M. Takeuchi, M. Hisa, Hydrogen production from waste
aluminum at different temperatures with LCA, Mater Trans., 46 5 (2005)
1052-1057.
[9] H. Z. Wang, et al, A review on hydrogen production using aluminum
and aluminum alloys, Renew Sustain Energy Rev. 10, (2008) 1016.
[10] D. Belitskus, Reaction of Aluminum with Sodium Hydroxide Solution as
a Source of Hydrogen, J. Electrochem Soc., 117 (8), (1970) 1097-1099.
[11] E. R. Andersen, E. J. Andersen, Method for Producing Hydrogen, WO
patent WO 2004/052775 A1 (2004).
[12] Z. Y. Deng, J. M. Ferreira, Y. Sakka, Hydrogen-Generation Materials for
Portable Applications, J. Am. Ceram. Soc., 91 12 (2008) 3825-3834.
[13] M. Q. Fan et al, Hydrolysis of ball milling Al-Bi-hydride and Al-Bi-salt
mixture for hydrogen generation, J. Alloys and Compounds, 460 (2008)
125-129.
[14] A. C. D. Chaklader, Hydrogen generation from water split reaction, US
patent 6,440,385 B1 (2002).
[15] E. Czech, T. Troczynski, Hydrogen generation through massive
corrosion of deformed aluminum in water, International Journal of
Hydrogen Energy, 35 3 (2010) 1029-1037.
[16] J. Skrovan, A. Alfantazi, T. Troczynski, Enhancing aluminum corrosion
in water, J. Applied Electrochemistry, 39 10 (2009) 1695-1702.
[17] B. C. Bunker, G. C. Nelson, K. R. Zavadil, et al., Hydration of passive
oxide films on aluminum, J. Phys. Chem., 106 (2002) 4705-4713.
[18] J. Skrovan, A. Alfantazi, T. Troczynski, The Role of Alumina in
Aluminum Corrosion and Passivation, ECS Transactions, 28 (24) 157-
169 (2010).