Abstract: Roller-compacted concrete pavement (RCCP), an environmental friendly pavement of which load carry capacity benefitted from both hydration and aggregate interlock from roller compacting, demonstrated a superb structural performance for a relatively small amount of water and cement content. Even though an excellent structural performance can be secured, it is required to investigate roller-compacted concrete (RCC) under environmental loading and its long-term durability under critical conditions. In order to secure long-term durability, an appropriate internal air-void structure is required for this concrete. In this study, a method for improving the long-term durability of RCCP is suggested by analyzing the internal air-void structure and corresponding durability of RCC. The method of improving the long-term durability involves measurements of air content, air voids, and air-spacing factors in RCC that experiences changes in terms of type of air-entraining agent and its usage amount. This test is conducted according to the testing criteria in ASTM C 457, 672, and KS F 2456. It was found that the freezing-thawing and scaling resistances of RCC without any chemical admixture was quite low. Interestingly, an improvement of freezing-thawing and scaling resistances was observed for RCC with appropriate the air entraining (AE) agent content; Relative dynamic elastic modulus was found to be more than 80% for those mixtures. In RCC with AE agent mixtures, large amount of air was distributed within a range of 2% to 3%, and an air void spacing factor ranging between 200 and 300 μm (close to 250 μm, recommended by PCA) was secured. The long-term durability of RCC has a direct relationship with air-void spacing factor, and thus it can only be secured by ensuring the air void spacing factor through the inclusion of the AE in the mixture.
Abstract: Oxidative stress associated with semen cryopreservation may result in lipid peroxidation (LPO), DNA damage and apoptosis, leading to decreased sperm motility and fertilization ability. Curcumin (CUR), a natural phenol isolated from Curcuma longa Linn. has been presented as a possible supplement for a more effective semen cryopreservation because of its antioxidant properties. This study focused to evaluate the effects of CUR on selected oxidative stress parameters in cryopreserved bovine semen. 20 bovine ejaculates were split into two aliquots and diluted with a commercial semen extender containing CUR (50 μmol/L) or no supplement (control), cooled to 4 °C, frozen and kept in liquid nitrogen. Frozen straws were thawed in a water bath for subsequent experiments. Computer assisted semen analysis was used to evaluate spermatozoa motility, and reactive oxygen species (ROS) generation was quantified by using luminometry. Superoxide generation was evaluated with the NBT test, and LPO was assessed via the TBARS assay. CUR supplementation significantly (P
Abstract: Freezing and thawing are considered to be one of the major causes of concrete deterioration in the cold regions. This study aimed at assessing the freezing and thawing of concrete within the cover zone by monitoring the formation of ice and melting at different temperatures using electrical measurement technique. A multi-electrode array system was used to obtain the resistivity of ice formation and melting at discrete depths within the cover zone of the concrete. A total number of four concrete specimens (250 mm x 250 mm x 150 mm) made of ordinary Portland cement concrete and ordinary Portland cement replaced by 65% ground granulated blast furnace slag (GGBS) is investigated. Water/binder ratios of 0.35 and 0.65 were produced and ponded with water to ensure full saturation and then subjected to freezing and thawing process in a refrigerator within a temperature range of -30 0C and 20 0C over a period of time 24 hours. The data were collected and analysed. The obtained results show that the addition of GGBS changed the pore structure of the concrete which resulted in the decrease in conductance. It was recommended among others that, the surface of the concrete structure should be protected as this will help to prevent the instantaneous propagation of ice trough the rebar and to avoid corrosion and subsequent damage.
Abstract: The using of waste materials in the construction
industry can reduce the dependence on the natural aggregates which
are going at the end to deplete. The glass waste is generated in a huge
amount which can make one of its disposals in concrete industry
effective not only as a green solution but also as an advantage to
enhance the performance of mechanical properties and durability of
concrete. This article reports the performance of concrete specimens
containing different percentages of milled glass waste as a partial
replacement of cement (Powder), when they are subject to cycles of
freezing and thawing. The tests were conducted on 75-mm cubes and
75 x 75 x 300-mm prisms. Compressive strength based on laboratory
testing and non-destructive ultrasonic pulse velocity test were
performed during the action of freezing-thawing cycles (F/T). The
results revealed that the incorporation of glass waste in concrete
mixtures is not only feasible but also showed generally better strength
and durability performance than control concrete mixture. It may be
said that the recycling of waste glass in concrete mixes is not only a
disposal way, but also it can be an exploitation in concrete industry.
Abstract: This study investigated the improvement in concrete properties with addition of cellulose, steel, carbon and PET fibers. Each fiber was added at four percentages to the fresh concrete, which was moist-cured for 28-days and then tested for compressive, flexural and tensile strengths. Changes in strength and increases in cost were analyzed. Results showed that addition of cellulose caused a decrease between 9.8% and 16.4% in compressive strength. This range may be acceptable as cellulose fibers can significantly increase the concrete resistance to fire, and freezing and thawing cycles. Addition of steel fibers to concreteincreased the compressive strength by up to 20%. Increases 121.5% and 80.7% were reported in tensile and flexural strengths respectively. Carbon fibers increased flexural and tensile strengths by up to 11% and 45%, respectively. Concrete strength properties decreased after the addition of PET fibers. Results showed that improvement in strength after addition of steel and carbon fibers may justify the extra cost of fibers.
Abstract: Several review papers exist in literature related to the concrete containing mineral admixtures; however this paper reviews the durability characteristics of the concrete containing fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBS), metakaolin (MK) and rice husk ash (RHA). Durability related properties reviewed include permeability, resistance to sulfate attack, alkali-silica reaction (ASR), carbonation, chloride ion penetration, freezing and thawing, abrasion, fire, acid and efflorescence. From review of existing literature, it is found that permeability of concrete depends upon the content of alumina in mineral admixtures, i.e. higher the alumina content, lesser the permeability which results higher resistance to sulfate and chloride ion penetration. Highly reactive mineral admixtures prevent more ASR and reduce efflorescence. The carbonation increases with the mineral admixtures because higher water binder ratio and lesser content of portlandite in concrete due to pozzolanic reaction. Mineral admixtures require air entrainment except MK and RHA for better resistance to freezing and thawing.
Abstract: In the modern construction practices, industrial wastes
or by-products are largely used as raw materials in cement and
concrete. These impart many benefits to the environment and bringabout
an economic impact because the cost of waste disposal is
constantly increasing due to strict environmental regulations. It was
reported in literature that the leakage of oil onto concrete element in
older cement grinding unit resulted in concrete with greater resistance
to freezing and thawing. This effect was thought to be similar to
adding an air-entraining chemical admixture to concrete. This paper
presents an investigation on the load deflection behaviour and crack
patterns of reinforced concrete (RC) beams subjected to four point
loading. Ten 120x260x1900 mm beams were cast with 100%
ordinary Portland cement (OPC) concrete, 20% fly ash (FA) and 20%
rice husk ash (RHA) blended cement concrete. 0.15% dosage of
admixtures (used engine oil, new engine oil, and superplasticizer)
was used throughout the experiment. Results show that OPC and
OPC/RHA RC beams containing used engine oil and superplasticizer
exhibit higher capacity, 18-26% than their corresponding control
mix.
Abstract: The first and basic cause of the failure of concrete is repeated freezing (thawing) of moisture contained in the pores, microcracks, and cavities of the concrete. On transition to ice, water existing in the free state in cracks increases in volume, expanding the recess in which freezing occurs. A reduction in strength below the initial value is to be expected and further cycle of freezing and thawing have a further marked effect. By using some experimental parameters like nuclear magnetic resonance variation (NMR), enthalpy-temperature (or heat capacity) variation, we can resolve between the various water states and their effect on concrete properties during cooling through the freezing transition temperature range. The main objective of this paper is to describe the principal type of water responsible for the reduction in strength and structural damage (frost damage) of concrete following repeated freeze –thaw cycles. Some experimental work was carried out at the institute of cryogenics to determine what happens to water in concrete during the freezing transition.
Abstract: Prickly pear juice has received renewed attention with regard to the effects of processing and preservation on its sensory qualities (colour, taste, flavour, aroma, astringency, visual browning and overall acceptability). Juice was prepared by homogenizing fruit and treating the pulp with pectinase (Aspergillus niger). Juice treatments applied were sugar addition, acidification, heat-treatment, refrigeration, and freezing and thawing. Prickly pear pulp and juice had unique properties (low pH 3.88, soluble solids 3.68 oBrix and high titratable acidity 0.47). Sensory profiling and descriptive analyses revealed that non-treated juice had a bitter taste with high astringency whereas treated prickly pear was significantly sweeter. All treated juices had a good sensory acceptance with values approximating or exceeding 7. Regression analysis of the consumer sensory attributes for non-treated prickly pear juice indicated an overwhelming rejection, while treated prickly pear juice received overall acceptability. Thus, educed favourable sensory responses and may have positive implications for consumer acceptability.