Abstract: Several review papers exist in literature related to the concrete containing mineral admixtures; however this paper reviews the durability characteristics of the concrete containing fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBS), metakaolin (MK) and rice husk ash (RHA). Durability related properties reviewed include permeability, resistance to sulfate attack, alkali-silica reaction (ASR), carbonation, chloride ion penetration, freezing and thawing, abrasion, fire, acid and efflorescence. From review of existing literature, it is found that permeability of concrete depends upon the content of alumina in mineral admixtures, i.e. higher the alumina content, lesser the permeability which results higher resistance to sulfate and chloride ion penetration. Highly reactive mineral admixtures prevent more ASR and reduce efflorescence. The carbonation increases with the mineral admixtures because higher water binder ratio and lesser content of portlandite in concrete due to pozzolanic reaction. Mineral admixtures require air entrainment except MK and RHA for better resistance to freezing and thawing.
Abstract: Implementing significant advantages in the supply of self-compacting concrete (SCC) is necessary because of the, negative features of SCC. Examples of these features are the ductility problem along with the very high cost of its constituted materials. Silica fume with steel fiber can fix this matter by improving the ductility and decreasing the total cost of SCC by varying the cement ingredients. Many different researchers have found that there have not been enough research carried out on the steel fiber-reinforced self-compacting concrete (SFRSCC) produced with silica fume. This paper inspects both the fresh and the mechanical properties of SFRSCC with silica fume, the fresh qualities where slump flow, slump T50 and V- funnel. While, the mechanical characteristics were the compressive strength, ultrasound pulse velocity (UPV) and elastic modulus of the concrete samples. The experimental results have proven that steel fiber can enhance the mechanical features. In addition, the silica fume within the entire hybrid mix may possibly adapt the fiber dispersion and strengthen deficits due to the fibers. It could also improve the strength plus the bond between the fiber and the matrix with a dense calcium silicate-hydrate gel in SFRSCC. The concluded result was predicted using linear mathematical models and was found to be in great agreement with the experimental results.
Abstract: This paper presents the experimental results of the
investigation of various properties related to the durability and longterm
performance of mortars made of Fly Ash blended cement, FA
and Ordinary Portland cement, OPC. The properties that were
investigated in an experimental program include; equilibration of
specimen in different relative humidity, determination of total
porosity, compressive strength, chloride permeability index, and
electrical resistivity. Fly Ash blended cement mortar specimens
exhibited 10% to 15% lower porosity when measured at equilibrium
conditions in different relative humidities as compared to the
specimens made of OPC mortar, which resulted in 6% to 8% higher
compressive strength of FA blended cement mortar specimens. The
effects of ambient relative humidity during sample equilibration on
porosity and strength development were also studied. For specimens
equilibrated in higher relative humidity conditions, such as 75%, the
total porosity of different mortar specimens was between 35% to 50%
less than the porosity of samples equilibrated in 12% relative
humidity, consequently leading to higher compressive strengths of
these specimens.A valid statistical correlation between values of
compressive strength, porosity and the degree of saturation was
obtained. Measured values of chloride permeability index of fly ash
blended cement mortar were obtained as one fourth to one sixth of
those measured for OPC mortar specimens, which indicates high
resistance against chloride ion penetration in FA blended cement
specimens, hence resulting in a highly durable mortar.