Abstract: This paper presents the study of strengthening R/C
beams with large circular and square opening located at flexure zone
by Carbon Fiber Reinforced Polymer (CFRP) laminates. A total of
five beams were tested to failure under four point loading to
investigate the structural behavior including crack patterns, failure
mode, ultimate load and load deflection behaviour. Test results show
that large opening at flexure reduces the beam capacity and stiffness;
and increases cracking and deflection. A strengthening configuration
was designed for each un-strengthened beams based on their
respective crack patterns. CFRP laminates remarkably restore the
beam capacity of beam with large circular opening at flexure location
while 10% re-gain of beam capacity with square opening. The use of
CFRP laminates with the designed strengthening configuration could
significantly reduce excessive cracking and deflection and increase
the ultimate capacity and stiffness of beam.
Abstract: In the modern construction practices, industrial wastes
or by-products are largely used as raw materials in cement and
concrete. These impart many benefits to the environment and bringabout
an economic impact because the cost of waste disposal is
constantly increasing due to strict environmental regulations. It was
reported in literature that the leakage of oil onto concrete element in
older cement grinding unit resulted in concrete with greater resistance
to freezing and thawing. This effect was thought to be similar to
adding an air-entraining chemical admixture to concrete. This paper
presents an investigation on the load deflection behaviour and crack
patterns of reinforced concrete (RC) beams subjected to four point
loading. Ten 120x260x1900 mm beams were cast with 100%
ordinary Portland cement (OPC) concrete, 20% fly ash (FA) and 20%
rice husk ash (RHA) blended cement concrete. 0.15% dosage of
admixtures (used engine oil, new engine oil, and superplasticizer)
was used throughout the experiment. Results show that OPC and
OPC/RHA RC beams containing used engine oil and superplasticizer
exhibit higher capacity, 18-26% than their corresponding control
mix.
Abstract: To date, theoretical studies concerning the Carbon
Fiber Reinforced Polymer (CFRP) strengthening of RC beams with
openings have been rather limited. In addition, various numerical
analyses presented so far have effectively simulated the behaviour of
solid beam strengthened by FRP material. In this paper, a two
dimensional nonlinear finite element analysis is presented to validate
against the laboratory test results of six RC beams. All beams had the
same rectangular cross-section geometry and were loaded under four
point bending. The crack pattern results of the finite element model
show good agreement with the crack pattern of the experimental
beams. The load midspan deflection curves of the finite element
models exhibited a stiffer result compared to the experimental beams.
The possible reason may be due to the perfect bond assumption used
between the concrete and steel reinforcement.