Abstract: The present work was conducted for the synthesis of
nano size zerovalent iron (nZVI) and hexavalent chromium (Cr(VI))
removal as a highly toxic pollutant by using this nanoparticles. Batch
experiments were performed to investigate the effects of Cr(VI),
nZVI concentration, pH of solution and contact time variation on
the removal efficiency of Cr(VI). nZVI was synthesized by
reduction of ferric chloride using sodium borohydrid. SEM and
XRD examinations applied for determination of particle size and
characterization of produced nanoparticles. The results showed that
the removal efficiency decreased with Cr(VI) concentration and pH
of solution and increased with adsorbent dosage and contact time.
The Langmuir and Freundlich isotherm models were used for the
adsorption equilibrium data and the Langmuir isotherm model was
well fitted. Nanoparticle ZVI presented an outstanding ability to
remove Cr(VI) due to high surface area, low particle size and high
inherent activity.
Abstract: This study evaluates the performance of horizontal
subsurface flow constructed wetland (HSSF-CW) for the removal of
chlorinated resin and fatty acids (RFAs) from pulp and paper mill
wastewater. The dimensions of the treatment system were 3.5 m x 1.5
m x 0.28 m with surface area of 5.25 m2, filled with fine sand and
gravel. The cell was planted with an ornamental plant species Canna
indica. The removal efficiency of chlorinated RFAs was in the range
of 92-96% at the hydraulic retention time (HRT) of 5.9 days. Plant
biomass and soil (sand and gravel) were analyzed for chlorinated
RFAs content. No chlorinated RFAs were detected in plant biomass
but detected in soil samples. Mass balance studies of chlorinated
RFAs in HSSF-CW were also carried out.
Abstract: High purity hydrogen and the valuable by-product of carbon nanotubes (CNTs) can be produced by the methane catalytic decomposition. The methane conversion and the performance of CNTs were determined by the choices of catalysts and the condition of decomposition reaction. In this paper, Ni/MgO and Ni/O-D (oxidized diamond) catalysts were prepared by wetness impregnation method. The effects of reaction temperature and space velocity of methane on the methane conversion were investigated in a fixed-bed. The surface area, structure and micrography were characterized with BET, XPS, SEM, EDS technology. The results showed that the conversion of methane was above 8% within 150 min (T=500) for 33Ni/O-D catalyst and higher than 25% within 120 min (T=650) for 41Ni/MgO catalyst. The initial conversion increased with the increasing temperature of the decomposition reaction, but their catalytic activities decreased rapidly while at too higher temperature. To decrease the space velocity of methane was propitious to promote the methane conversion, but not favor of the hydrogen yields. The appearance of carbon resulted from the methane decomposition lied on the support type and the condition of catalytic reaction. It presented as fiber shape on the surface of Ni/O-D at the relatively lower temperature such as 500 and 550, but as grain shape stacked on and overlayed on the surface of the metal nickel while at 650. The carbon fiber can form on the Ni/MgO surface at 650 and the diameter of the carbon fiber increased with the decreasing space velocity.
Abstract: This paper aims to fabricated high quality anodic
aluminum oxide (AAO) film by anodization method. AAO pore size,
pore density, and film thickness can be controlled in 10~500 nm,
108~1011 pore.cm-2, and 1~100 μm. AAO volume and surface area can
be computed based on structural parameters such as thickness, pore
size, pore density, and sample size. Base on the thetorical calculation,
AAO has 100 μm thickness with 15 nm, 60 nm, and 500 nm pore
diameters AAO surface areas are 1225.2 cm2, 3204.4 cm2, and 549.7
cm2, respectively. The large unit surface area which is useful for
adsorption application. When AAO adsorbed pH indictor of
bromphenol blue presented a sensitive pH detection of solution
change. This testing method can further be used for the precise
measurement of biotechnology, convenience measurement of
industrial engineering.
Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.
Abstract: Cashew nut shells were converted into activated carbon powders using KOH activation plus CO2 gasification at 1027 K. The increase both of impregnation ratio and activation time, there was swiftly the development of mesoporous structure with increasing of mesopore volume ratio from 20-28% and 27-45% for activated carbon with ratio of KOH per char equal to 1 and 4, respectively. Activated carbon derived from KOH/char ratio equal to 1 and CO2 gasification time from 20 to 150 minutes were exhibited the BET surface area increasing from 222 to 627 m2.g-1. And those were derived from KOH/char ratio of 4 with activation time from 20 to 150 minutes exhibited high BET surface area from 682 to 1026 m2.g-1. The adsorption of Lead(II) and Cadmium(II) ion was investigated. This adsorbent exhibited excellent adsorption for Lead(II) and Cadmium(II) ion. Maximum adsorption presented at 99.61% at pH 6.5 and 98.87% at optimum conditions. The experimental data was calculated from Freundlich isotherm and Langmuir isotherm model. The maximum capacity of Pb2+ and Cd2+ ions was found to be 28.90 m2.g-1 and 14.29 m2.g-1, respectively.
Abstract: A new SUZ-4 zeolite membrane with
tetraethlyammonium hydroxide as the template was fabricated on
mullite tube via hydrothermal sol-gel synthesis in a rotating
autoclave reactor. The suitable synthesis condition was SiO2:Al2O3
ratio of 21.2 for 4 days at 155 °C crystallization under autogenous
pressure. The obtained SUZ-4 possessed a high BET surface area of
396.4 m2/g, total pore volume at 2.611 cm3/g, and narrow pore size
distribution with 97 nm mean diameter and 760 nm long of needle
crystal shape. The SUZ-4 layer obtained from seeding crystallization
was thicker than that of without seeds or in situ crystallization.
Abstract: This study focuses on an evaluation of Hokkaido which
is the northernmost and largest prefecture by surface area in Japan and
particularly on two points: the rivalry between all kinds of land use
such as urban land and agricultural and forestry land in various cities
and their surrounding areas and the possibilities for forestry biomass in
areas other than those mentioned above and grasps which areas require
examination of the nature of land use control and guidance through
conducting land use analysis at the district level using GIS
(Geographic Information Systems). The results of analysis in this
study demonstrated that it is essential to divide the whole of Hokkaido
into two areas: those within delineated city planning areas and those
outside of delineated city planning areas and to conduct an evaluation
of each land use control.
In delineated urban areas, particularly urban areas, it is essential to
re-examine land use from the point of view of compact cities or smart
cities along with conducting an evaluation of land use control that
focuses on issues of rivalry between all kinds of land use such as urban
land and agricultural and forestry land. In areas outside of delineated
urban areas, it is desirable to aim to build a specific community
recycling range based on forest biomass utilization by conducting an
evaluation of land use control concerning the possibilities for forest
biomass focusing particularly on forests within and outside of city
planning areas.
Abstract: In this research, CaO-ZnO catalysts (with various
Ca:Zn atomic ratios of 1:5, 1:3, 1:1, and 3:1) prepared by incipientwetness
impregnation (IWI) and co-precipitation (CP) methods were
used as a catalyst in the transesterification of palm oil with methanol
for biodiesel production. The catalysts were characterized by several
techniques, including BET method, CO2-TPD, and Hemmett
Indicator. The effects of precursor concentration, and calcination
temperature on the catalytic performance were studied under reaction
conditions of a 15:1 methanol to oil molar ratio, 6 wt% catalyst,
reaction temperature of 60°C, and reaction time of 8 h. At Ca:Zn
atomic ratio of 1:3 gave the highest FAME value owing to a basic
properties and surface area of the prepared catalyst.
Abstract: In this study, some physical and mechanical properties
of jujube fruits, were measured and compared at constant moisture
content of 15.5% w.b. The results showed that the mean length, width
and thickness of jujube fruits were 18.88, 16.79 and 15.9 mm,
respectively. The mean projected areas of jujube perpendicular to
length, width, and thickness were 147.01, 224.08 and 274.60 mm2,
respectively. The mean mass and volume were 1.51 g and 2672.80
mm3, respectively. The arithmetic mean diameter, geometric mean
diameter and equivalent diameter varied from 14.53 to 20 mm, 14.5
to 19.94 mm, and 14.52 to 19.97 mm, respectively. The sphericity,
aspect ratio and surface area of jujube fruits were 0.91, 0.89 and
926.28 mm2, respectively. Whole fruit density, bulk density and
porosity of jujube fruits were measured and found to be 1.52 g/cm3,
0.3 g/cm3 and 79.3%, respectively. The angle of repose of jujube fruit
was 14.66° (±0.58°). The static coefficient of friction on galvanized
iron steel was higher than that on plywood and lower than that on
glass surface. The values of rupture force, deformation, hardness and
energy absorbed were found to be between 11.13-19.91N, 2.53-
4.82mm, 3.06-5.81N mm and 20.13-39.08 N/mm, respectively.
Abstract: The purpose of this study is to investigate the
efficiency of a double-layer roof in collecting solar energy as an
application to the areas such as raising high-end temperature of
organic Rankine cycle (ORC). The by-product of the solar roof is to
reduce building air-conditioning loads. The experimental apparatus
are arranged to evaluate the effects of the solar roof in absorbing solar
energy. The flow channel is basically formed by an aluminum plate on
top of a plywood plate. The geometric configurations in which the
effects of absorbing energy is analyzed include: a bare uncovered
aluminum plate, a glass-covered aluminum plate, a
glass-covered/black-painted aluminum plate, a plate with variable
lengths, a flow channel with stuffed material (in an attempt on
enhancement of heat conduction), and a flow channel with variable
slanted angles. The experimental results show that the efficiency of
energy collection varies from 0.6 % to 11 % for the geometric
configurations mentioned above. An additional study is carried out
using CFD simulation to investigate the effects of fins on the
aluminum plate. It shows that due to vastly enhanced heat conduction,
the efficiency can reach ~23 % if 50 fins are installed on the aluminum
plate. The study shows that a double-layer roof can efficiently absorb
solar energy and substantially reduce building air-conditioning
loads. On the high end of an organic Rankine cycle, a solar pond is
used to replace the warm surface water of the sea as OTEC (ocean
thermal energy conversion) is the driving energy for the ORC. The
energy collected from the double-layered solar roof can be pumped
into the pond and raise the pond temperature as the pond surface area is
equivalently increased by nearly one-fourth of the total area of the
double-layer solar roof. The effect of raising solar pond temperature is
especially prominent if the double-layer solar roofs are installed in a
community area.
Abstract: The pressure drag from a cam shaped tube in cross flows have been investigated experimentally using pressure distribution measurement. The range of angle of attack and Reynolds number based on an equivalent circular tube are within 0≤α≤360° and 2×104< Reeq < 3.4 ×104, respectively. It is found that the pressure drag coefficient is at its highest at α=90° and 270° over the whole range of Reynolds number. Results show that the pressure drag coefficient of the cam shaped tube is lower than that of circular tube with the same surface area for more of the angles of attack. Furthermore, effects of the diameter ratio and finite length of the cam shaped tube upon the pressure drag coefficient are discussed.
Abstract: In this paper, the effects of thermodynamic,
hydrodynamic and geometric of an air cooled condenser on COP of
vapor compression cycle are investigated for a fixed condenser facing
surface area. The system is utilized with a scroll compressor,
modeled based on thermodynamic and heat transfer equations
employing Matlab software. The working refrigerant is R134a whose
thermodynamic properties are called from Engineering Equation
Software. This simulation shows that vapor compression cycle can
be designed by different configurations and COPs, economical and
optimum working condition can be obtained via considering these
parameters.
Abstract: Batch adsorption of recalcitrant melanoidin using the abundantly available coal fly ash was carried out. It had low specific surface area (SBET) of 1.7287 m2/g and pore volume of 0.002245 cm3/g while qualitative evaluation of the predominant phases in it was done by XRD analysis. Colour removal efficiency was found to be dependent on various factors studied. Maximum colour removal was achieved around pH 6, whereas increasing sorbent mass from 10g/L to 200 g/L enhanced colour reduction from 25% to 86% at 298 K. Spontaneity of the process was suggested by negative Gibbs free energy while positive values for enthalpy change showed endothermic nature of the process. Non-linear optimization of error functions resulted in Freundlich and Redlich-Peterson isotherms describing sorption equilibrium data best. The coal fly ash had maximum sorption capacity of 53 mg/g and could thus be used as a low cost adsorbent in melanoidin removal.
Abstract: The objective of this paper was to designing a
ventilation system to enhance the performance of roof solar collector
(RSC) for reducing heat accumulation inside the house. The RSC has
1.8 m2 surface area made of CPAC monier roof tiles on the upper part
and gypsum board on the lower part. The space between CPAC
monier and gypsum board was fixed at 14 cm.
Ventilation system of modified roof solar collector (modified
RSC) consists of 9 tubes of 0.15m diameter and installed in the
lower part of RSC. Experimental result showed that the temperature
of the room, and attic temperature. The average temperature
reduction of room of house used modified RSC is about 2oC. and the
percentage of room temperature reduction varied between 0 to 10%.
Therefore, modified RSC is an interesting option in the sense that it
promotes solar energy and conserve energy.
Abstract: Biodiesel production with used frying by
transesterification reaction with methanol, using a commercial
kaolinite thermally-activated solid acid catalyst was investigated.
The surface area, the average pore diameter and pore volume of the
kaolinite catalyst were 10 m2/g, 13.0 nm and 30 mm3/g, respectively.
The optimal conditions for the transesterification reaction were
determined to be oil/methanol, in a molar ratio 1:31, temperature 160
ºC and catalyst concentration of 3% (w/w). The yield of fatty acids
methyl esters (FAME) was 92.4% after 2 h of reaction. This method
of preparation of biodiesel can be a positive alternative for utilizing
used frying corn oil for feedstock of biodiesel combined with the
inexpensive catalyst.
Abstract: Industrial surveys shows that manufacturing
companies define the qualities of thermal removing process based on
the dimension and physical appearance of the cutting material
surface. Therefore, the roughness of the surface area of the material
cut by the plasma arc cutting process and the rate of the removed
material by the manual plasma arc cutting machine was importantly
considered. Plasma arc cutter Selco Genesis 90 was used to cut
Standard AISI 1017 Steel of 200 mm x100 mm x 6 mm manually
based on the selected parameters setting. The material removal rate
(MRR) was measured by determining the weight of the specimens
before and after the cutting process. The surface roughness (SR)
analysis was conducted using Mitutoyo CS-3100 to determine the
average roughness value (Ra). Taguchi method was utilized to
achieve optimum condition for both outputs studied. The
microstructure analysis in the region of the cutting surface is
performed using SEM. The results reveal that the SR values are
inversely proportional to the MRR values. The quality of the surface
roughness depends on the dross peak that occurred after the cutting
process.
Abstract: Low silica type X (LSX) Zeolite is one of useful
material in many manufacturing due to the advantage properties
including high surface area, stability, microporous crystalline
aluminosilicates and positive ion in an extra–framework. The LSX
was used rice husk silica source which obtained by leaching with
hydrochloric acid and calcination at 500C. To improve the
synthesis method, the LSX was crystallizated in Teflon–lined
autoclave will expedite deceasing of the amorphous particles. The
mixed gel with composition of 5.5 Na2O : 1.65 K2O : Al2O3 : 2.2
SiO2 : 122 H2O was crystallized in different container
(Polypropylene bottom and Teflon–lined autoclave). The obtained
powder was characterized by X–ray diffraction (XRD), X–ray
fluorescence spectrometry, N2 adsorption-desorption analysis BET
surface area Scanning electron microscopy (SEM) and Fourier
transform infrared spectroscopy to justify the quality of zeolite. The
results showed the crystallized zeolite in Teflon lined autoclave has
102.8 nm of crystal size, 286 m2/g of surface area and fewer amounts
of round amorphous particles when compared with the crystallized
zeolite in Polypropylene.
Abstract: Electrospinning is a broadly used technology to obtain
polymeric nanofibers ranging from several micrometers down to
several hundred nanometers for a wide range of applications. It offers
unique capabilities to produce nanofibers with controllable porous
structure. With smaller pores and higher surface area than regular
fibers, electrospun fibers have been successfully applied in various
fields, such as, nanocatalysis, tissue engineering scaffolds, protective
clothing, filtration, biomedical, pharmaceutical, optical electronics,
healthcare, biotechnology, defense and security, and environmental
engineering. In this study, polyurethane nanofibers were obtained
under different electrospinning parameters. Fiber morphology and
diameter distribution were investigated in order to understand them
as a function of process parameters.
Abstract: Vertical ZnO nanowire array films were synthesized
based on aqueous method for sensing applications. ZnO nanowires
were investigated structurally using X-ray diffraction (XRD) and
scanning electron microscopy (SEM). The gas-sensing properties of
ZnO nanowires array films are studied. It is found that the ZnO
nanowires array film sensor exhibits excellent sensing properties
towards O2 and CO2 at 100 °C with the response time shorter than 5
s. High surface area / volume ratio of vertical ZnO nanowire and high
mobility accounts for the fast response and recovery. The sensor
response was measured in the range from 100 to 500 ppm O2 and CO2
in this study.