Abstract: Co metal supported on SiO2 and Al2O3 catalysts with
a metal loading varied from 30 of 70 wt.% were evaluated for
decomposition of methane to COx free hydrogen and carbon
nanomaterials. The catalytic runs were carried out from 550-800oC
under atmospheric pressure using fixed bed vertical flow reactor. The
fresh and spent catalysts were characterized by BET surface area
analyzer, XRD, SEM, TEM and TG analysis. The data showed that
50% Co/Al2O3 catalyst exhibited remarkable higher activity at 800oC
with respect to H2 production compared to rest of the catalysts.
However, the catalytic activity and durability was greatly declined at
higher temperature. The main reason for the catalytic inhibition of Co
containing SiO2 catalysts is the higher reduction temperature of
Co2SiO4. TEM images illustrate that the carbon materials with
various morphologies, carbon nanofibers (CNFs), helical-shaped
CNFs and branched CNFs depending on the catalyst composition and
reaction temperature were obtained.
Abstract: High purity hydrogen and the valuable by-product of carbon nanotubes (CNTs) can be produced by the methane catalytic decomposition. The methane conversion and the performance of CNTs were determined by the choices of catalysts and the condition of decomposition reaction. In this paper, Ni/MgO and Ni/O-D (oxidized diamond) catalysts were prepared by wetness impregnation method. The effects of reaction temperature and space velocity of methane on the methane conversion were investigated in a fixed-bed. The surface area, structure and micrography were characterized with BET, XPS, SEM, EDS technology. The results showed that the conversion of methane was above 8% within 150 min (T=500) for 33Ni/O-D catalyst and higher than 25% within 120 min (T=650) for 41Ni/MgO catalyst. The initial conversion increased with the increasing temperature of the decomposition reaction, but their catalytic activities decreased rapidly while at too higher temperature. To decrease the space velocity of methane was propitious to promote the methane conversion, but not favor of the hydrogen yields. The appearance of carbon resulted from the methane decomposition lied on the support type and the condition of catalytic reaction. It presented as fiber shape on the surface of Ni/O-D at the relatively lower temperature such as 500 and 550, but as grain shape stacked on and overlayed on the surface of the metal nickel while at 650. The carbon fiber can form on the Ni/MgO surface at 650 and the diameter of the carbon fiber increased with the decreasing space velocity.
Abstract: Potassium monopersulfate has been decomposed in aqueous solution in the presence of Co(II). The process has been simulated by means of a mechanism based on elementary reactions. Rate constants have been taken from literature reports or, alternatively, assimilated to analogous reactions occurring in Fenton's chemistry. Several operating conditions have been successfully applied.
Abstract: Potassium monopersulfate has been decomposed in
aqueous solution in the presence of Co(II). The effect of the main
operating variables has been assessed. Minimum variations in pH
exert a considerable influence on the process kinetics. Thus, when no
pH adjustment is considered, the actual effect of variables like initial
monopersulfate and/or catalyst concentration may be hindered. As
expected, temperature enhances the monopersulfate decomposition
rate by following the Arrhenius law. The activation energy in the
proximity of 85 kJ/mol has been obtained. Amongst the different
solids tested in the monopersulfate decomposition, only the
perovskite LaTi0.15Cu0.85O3 has shown a significant catalytic activity.