Abstract: This paper aims to scale up Dye-sensitized Solar Cell
(DSSC) production using a commonly available industrial material –
stainless steel - and industrial plasma equipment. A working DSSC
electrode formed by (1) coating titania nanotube (TiO2 NT) film on
304 stainless steel substrate using a plasma spray technique; then, (2)
filling the nano-pores of the TiO2 NT film using a TiF4 sol-gel method.
A DSSC device consists of an anode absorbed photosensitive dye
(N3), a transparent conductive cathode with platinum (Pt)
nano-catalytic particles adhered to its surface, and an electrolytic
solution sealed between the anode and the transparent conductive
cathode. The photo-current conversion efficiency of the DSSC sample
was tested under an AM 1.5 Solar Simulator. The sample has a short
current (Isc) of 0.83 mA cm-2, open voltage (Voc) of 0.81V, filling
factor (FF) of 0.52, and conversion efficiency (η) of 2.18% on a 0.16
cm2 DSSC work-piece.
Abstract: This paper aims to fabricated high quality anodic
aluminum oxide (AAO) film by anodization method. AAO pore size,
pore density, and film thickness can be controlled in 10~500 nm,
108~1011 pore.cm-2, and 1~100 μm. AAO volume and surface area can
be computed based on structural parameters such as thickness, pore
size, pore density, and sample size. Base on the thetorical calculation,
AAO has 100 μm thickness with 15 nm, 60 nm, and 500 nm pore
diameters AAO surface areas are 1225.2 cm2, 3204.4 cm2, and 549.7
cm2, respectively. The large unit surface area which is useful for
adsorption application. When AAO adsorbed pH indictor of
bromphenol blue presented a sensitive pH detection of solution
change. This testing method can further be used for the precise
measurement of biotechnology, convenience measurement of
industrial engineering.