Abstract: This paper presents the findings of an
experimental investigation to study the effect of alkali content
in geopolymer mortar specimens exposed to sulphuric acid.
Geopolymer mortar specimens were manufactured from Class F fly
ash by activation with a mixture of sodium hydroxide and sodium
silicate solution containing 5% to 8% Na2O. Durability of specimens
were assessed by immersing them in 10% sulphuric acid solution and
periodically monitoring surface deterioration and depth of
dealkalization, changes in weight and residual compressive strength
over a period of 24 weeks. Microstructural changes in the specimens
were studied with Scanning electron microscopy (SEM) and EDAX.
Alkali content in the activator solution significantly affects the
durability of fly ash based geopolymer mortars in sulphuric acid.
Specimens manufactured with higher alkali content performed better
than those manufactured with lower alkali content. After 24 weeks in
sulphuric acid, specimen with 8% alkali still recorded a residual
strength as high as 55%.
Abstract: A simple and dexterous in situ method was introduced to load CdS nanocrystals into organofunctionalized mesoporous, which used an ion-exchange method. The products were extensively characterized by combined spectroscopic methods. X- ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) demonstrated both the maintenance of pore symmetry (space group p6mm) of SBA-15 and the presence of CdS nanocrystals with uniform sizes of about 6 - 8 nm inside the functionalized SBA-15 channels. These mesoporous silica-supported CdS composites showed room temperature photoluminescence properties with a blue shift, indicating the quantum size effect of nanocrystalline CdS.
Abstract: Topical photodynamic therapy (PDT) with
5-aminolevulinic acid (ALA) is an alternative therapy for treating
superficial cancer, especially for skin or oral cancer. ALA, a precursor
of the photosensitizer protoporphyrin IX (PpIX), is present as
zwitterions and hydrophilic property which make the low permeability
through the cell membrane. Collagen is a traditional carrier; its
molecular composed various amino acids which bear positive charge
and negative charge. In order to utilize the ion-pairs with ALA and
collagen, the study employed various pH values adjusting the net
charge. The aim of this study was to compare a series collagen form,
including solution, gel and sponge to investigate the topical delivery
behavior of ALA. The in vivo confocal laser scanning microscopy
(CLSM) study demonstrated that PpIX generation ability was different
pattern after apply for 6 h. Gel type could generate high PpIX, and
archived more deep of skin depth.
Abstract: Herein, we report the different types of surface morphology due to the interaction between the pure protein Insulin (INS) and catanionic surfactant mixture of Sodium Dodecyl Sulfate (SDS) and Cetyl Trimethyl Ammonium Bromide (CTAB) at air/water interface obtained by the Langmuir-Blodgett (LB) technique. We characterized the aggregations by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM) and Fourier transform infrared spectroscopy (FTIR) in LB films. We found that the INS adsorption increased in presence of catanionic surfactant at air/water interface. The presence of small amount of surfactant induces two-stage growth kinetics due to the pure protein absorption and protein-catanionic surface micelle interaction. The protein remains in native state in presence of small amount of surfactant mixture. Smaller amount of surfactant mixture with INS is producing surface micelle type structure. This may be considered for drug delivery system. On the other hand, INS becomes unfolded and fibrillated in presence of higher amount of surfactant mixture. In both the cases, the protein was successfully immobilized on a glass substrate by the LB technique. These results may find applications in the fundamental science of the physical chemistry of surfactant systems, as well as in the preparation of drug-delivery system.
Abstract: Carbon nanotubes (CNTs) with their high mechanical,
electrical, thermal and chemical properties are regarded as promising
materials for many different potential applications. Having unique
properties they can be used in a wide range of fields such as
electronic devices, electrodes, drug delivery systems, hydrogen
storage, textile etc. Catalytic chemical vapor deposition (CCVD) is a
common method for CNT production especially for mass production.
Catalysts impregnated on a suitable substrate are important for
production with chemical vapor deposition (CVD) method. Iron
catalyst and MgO substrate is one of most common catalyst-substrate
combination used for CNT. In this study, CNTs were produced by
CCVD of acetylene (C2H2) on magnesium oxide (MgO) powder
substrate impregnated by iron nitrate (Fe(NO3)3•9H2O) solution. The
CNT synthesis conditions were as follows: at synthesis temperatures
of 500 and 800°C multiwall and single wall CNTs were produced
respectively. Iron (Fe) catalysts were prepared by with Fe:MgO ratio
of 1:100, 5:100 and 10:100. The duration of syntheses were 30 and
60 minutes for all temperatures and catalyst percentages. The
synthesized materials were characterized by thermal gravimetric
analysis (TGA), transmission electron microscopy (TEM) and Raman
spectroscopy.
Abstract: Magnesium is used implant material potentially for
non-toxicity to the human body. Due to the excellent
bio-compatibility, Mg alloys is applied to implants avoiding removal
second surgery. However, it is found commercial magnesium alloys
including aluminum has low corrosion resistance, resulting
subcutaneous gas bubbles and consequently the approach as
permanent bio-materials. Generally, Aluminum is known to pollution
substance, and it raises toxicity to nervous system. Therefore
especially Mg-35Zn-3Ca alloy is prepared for new biodegradable
materials in this study. And the pulsed power is used in
constant-current mode of DC power kinds of anodization. Based on
the aforementioned study, it examines corrosion resistance and
biocompatibility by effect of current and frequency variation. The
surface properties and thickness were compared using scanning
electronic microscopy. Corrosion resistance was assessed via
potentiodynamic polarization and the effect of oxide layer on the body
was assessed cell viability. Anodized Mg-35Zn-3Ca alloy has good
biocompatibility in vitro by current and frequency variation.
Abstract: A novel thermo-sensitive superabsorbent hydrogel
with salt- and pH-responsiveness properties was obtained by grafting
of mixtures of acrylic acid (AA) and N-isopropylacrylamide
(NIPAM) monomers onto kappa-carrageenan, kC, using ammonium
persulfate (APS) as a free radical initiator in the presence of
methylene bisacrylamide (MBA) as a crosslinker. Infrared
spectroscopy was carried out to confirm the chemical structure of the
hydrogel. Moreover, morphology of the samples was examined by
scanning electron microscopy (SEM). The effect of MBA
concentration and AA/NIPAM weight ratio on the water absorbency
capacity has been investigated. The swelling variations of hydrogels
were explained according to swelling theory based on the hydrogel
chemical structure. The hydrogels exhibited salt-sensitivity and
cation exchange properties. The temperature- and pH-reversibility
properties of the hydrogels make the intelligent polymers as good
candidates for considering as potential carriers for bioactive agents,
e.g. drugs.
Abstract: Superplastic deformation and high temperature load
relaxation behavior of coarse-grained iron aluminides with the
composition of Fe-28 at.% Al have been investigated. A series of load
relaxation and tensile tests were conducted at temperatures ranging
from 600 to 850oC. The flow curves obtained from load relaxation
tests were found to have a sigmoidal shape and to exhibit stress vs.
strain rate data in a very wide strain rate range from 10-7/s to 10-2/s.
Tensile tests have been conducted at various initial strain rates ranging
from 3×10-5/s to 1×10-2/s. Maximum elongation of ~500 % was
obtained at the initial strain rate of 3×10-5/s and the maximum strain
rate sensitivity was found to be 0.68 at 850oC in binary Fe-28Al alloy.
Microstructure observation through the optical microscopy (OM) and
the electron back-scattered diffraction (EBSD) technique has been
carried out on the deformed specimens and it has revealed the
evidences for grain boundary migration and grain refinement to occur
during superplastic deformation, suggesting the dynamic
recrystallization mechanism. The addition of Cr by the amount of 5
at.% appeared to deteriorate the superplasticity of the binary iron
aluminide. By applying the internal variable theory of structural
superplasticity, the addition of Cr has been revealed to lower the
contribution of the frictional resistance to dislocation glide during high
temperature deformation of the Fe3Al alloy.
Abstract: Image mosaicing is a technique that permits to enlarge the field of view of a camera. For instance, it is employed to achieve panoramas with common cameras or even in scientific applications, to achieve the image of a whole culture in microscopical imaging. Usually, a mosaic of cell cultures is achieved through using automated microscopes. However, this is often performed in batch, through CPU intensive minimization algorithms. In addition, live stem cells are studied in phase contrast, showing a low contrast that cannot be improved further. We present a method to study the flat field from live stem cells images even in case of 100% confluence, this permitting to build accurate mosaics on-line using high performance algorithms.
Abstract: This paper present some preliminary work on the
preparation and physicochemical caracterization of nanocomposite
MFI-alumina structures based on alumina hollow fibres. The fibers
are manufactured by a wet spinning process. α-alumina particles were
dispersed in a solution of polysulfone in NMP. The resulting slurry is
pressed through the annular gap of a spinneret into a precipitation
bath. The resulting green fibres are sintered. The mechanical strength
of the alumina hollow fibres is determined by a three-point-bending
test while the pore size is characterized by bubble-point testing. The
bending strength is in the range of 110 MPa while the average pore
size is 450 nm for an internal diameter of 1 mm and external diameter
of 1.7 mm. To characterize the MFI membranes various techniques
were used for physicochemical characterization of MFI–ceramic
hollow fibres membranes: The nitrogen adsorption, X-ray
diffractometry, scanning electron microscopy combined with X
emission microanalysis. Scanning Electron Microscopy (SEM) and
Energy Dispersive Microanalysis by the X-ray were used to observe
the morphology of the hollow fibre membranes (thickness,
infiltration into the carrier, defects, homogeneity). No surface film,
has been obtained, as observed by SEM and EDX analysis and
confirmed by high temperature variation of N2 and CO2 gas
permeances before cation exchange. Local analysis and characterise
(SEM and EDX) and overall (by ICP elemental analysis) were
conducted on two samples exchanged to determine the quantity and
distribution of the cation of cesium on the cross section fibre of the
zeolite between the cavities.
Abstract: ZnO-SnO2 i.e. Zinc-Tin-Oxide (ZTO) thin films were
deposited on glass substrate with varying concentrations (ZnO:SnO2
- 100:0, 90:10, 70:30 and 50:50 wt.%) at room temperature by flash
evaporation technique. These deposited ZTO film were annealed at
450 0C in vacuum. These films were characterized to study the effect
of annealing on the structural, electrical, and optical properties.
Atomic force microscopy (AFM) and Scanning electron microscopy
(SEM) images manifest the surface morphology of these ZTO thin
films. The apparent growth of surface features revealed the formation
of nanostructure ZTO thin films. The small value of surface
roughness (root mean square RRMS) ensures the usefulness in
optical coatings. The sheet resistance was also found to be decreased
for both types of films with increasing concentration of SnO2. The
optical transmittance found to be decreased however blue shift has
been observed after annealing.
Abstract: Two different superhydrophobic surfaces were
elaborated and their oil repellency behavior was evaluated using
several liquid with different surface tension. A silicone rubber/SiO2
nanocomposite coated (A) on aluminum substrate by “spin-coating"
and the sample B was an anodized aluminum surface covered by
Teflon-like coating. A high static contact angle about ∼162° was
measured for two prepared surfaces on which the water droplet rolloff.
Scanning electron microscopy (SEM) showed the presence of
micro/nanostructures for both sample A and B similar to that of lotus
leaf.
However the sample A presented significantly different behaviour
of wettability against the low surface tension liquid. Sample A has
been wetted totally by oil (dodecan) droplet while sample B showed
oleophobic behaviour. Oleophobic property of Teflon like coating
can be contributed to the presence of CF2 and CF3 functional group
which was shown by XPS analysis.
Abstract: In the present work homogeneous silica film on
silicon was fabricated by colloidal silica sol. The silica sol precursor
with uniformly granular particle was derived by the alkaline
hydrolysis of tetraethoxyorthosilicate (TEOS) in presence of glycerol
template. The film was prepared by dip coating process. The
templated hetero-structured silica film was annealed at elevated
temperatures to generate nano- and meso porosity in the film. The
film was subsequently annealed at different temperatures to make it
defect free and abrasion resistant. The sol and the film were
characterized by the measurement of particle size distribution,
scanning electron microscopy, XRD, FTIR spectroscopy,
transmission electron microscopy, atomic force microscopy,
measurement of the refractive index, thermal conductivity and
abrasion resistance. The porosity of the films decreased whereas
refractive index and dielectric constant of it `increased with the
increase in the annealing temperature. The thermal conductivity of
the films increased with the increase in the film thickness. The
developed porous silica film holds strong potential for use in
different areas.
Abstract: An ecofriendly Citrus paradisipeel extract mediated synthesis of TiO2 nanoparticles is reported under sonication. U.V.-vis, Transmission electron microscopy, Dynamic light scattering, and X-ray analyses are performed to characterize the formation of TiO2 nanoparticles. It is almost spherical in shape, having a size of 60–140 nm and the XRD peaks at 2θ = 25.363° confirm the characteristic facets for anatase form. The synthesized nanocatalyst is highly active in the decomposition of methyl orange (64 mg/L) in sunlight (~73%) for 2.5h.
Abstract: Microparticles carrier systems made from naturally occurring polymers based on chitosan/casein system appears to be a promising carrier for the sustained release of orally and parenteral administered drugs. In the current study we followed a microencapsulation technique based aqueous coacervation method to prepare chitosan/casein microparticles of compositions 1:1, 1:2 and 1:5 incorporated with chloramphenicol. Glutaraldehyde was used as a chemical cross-linking agent. The microparticles were prepared by aerosol method and studied by optical microscopy, infrared spectroscopy, thermo gravimetric analysis, swelling studies and drug release studies at various pH. The percentage swelling of the polymers are found to be in the order pH 4 > pH 10 > pH 7 and the increase in casein composition decrease the swelling percentage. The drug release studies also follow the above order.
Abstract: This paper reports on the influence of surface-treated coarse recycled concrete aggregate (RCA) on developing the compressive strength of concrete. The coarse RCA was initially treated by separately impregnating it in calcium metasilicate (CM) or wollastonite and nanosilica (NS) prepared at various concentrations. The effects of both treatment materials on concrete properties (e.g., slump, density and compressive strength) were evaluated. Scanning electron microscopy (SEM) analysis was performed to examine the microstructure of the resulting concrete. Results show that the effective use of treated coarse RCA significantly enhances the compressive strength of concrete. This result is supported by the SEM analysis, which indicates the formation of a dense interface between the treated coarse RCA and the cement matrix. Coarse RCA impregnated in CM solution results in better concrete strength than NS, and the optimum concentration of CM solution recommended for treated coarse RCA is 10%.
Abstract: Delamination between layers in composite materials is a major structural failure. The delamination resistance is quantified by the critical strain energy release rate (SERR). The present investigation deals with the strain energy release rate of two woven fabric composites. Materials used are made of two types of glass fiber (360 gsm and 600 gsm) of plain weave and epoxy as matrix. The fracture behavior is studied using the mode I, double cantilever beam test and the mode II, end notched flexure test, in order to determine the energy required for the initiation and growth of an artificial crack. The delamination energy of these two materials is compared in order to study the effect of weave and reinforcement on mechanical properties. The fracture mechanism is also analyzed by means of scanning electron microscopy (SEM). It is observed that the plain weave fabric composite with lesser strand width has higher inter laminar fracture properties compared to the plain weave fabric composite with more strand width.
Abstract: Silver nanoparticles were prepared by chemical reduction method. Silver nitrate was taken as the metal precursor and hydrazine hydrate as a reducing agent. The formation of the silver nanoparticles was monitored using UV-Vis absorption spectroscopy. The UV-Vis spectroscopy revealed the formation of silver nanopart├¡cles by exhibing the typical surface plasmon absorption maxima at 418-420 nm from the UV–Vis spectrum. Comparison of theoretical (Mie light scattering theory) and experimental results showed that diameter of silver nanoparticles in colloidal solution is about 60 nm. We have used energy-dispersive spectroscopy (EDX), X-ray diffraction (XRD), transmission electron microscopy (TEM) and, UV–Vis spectroscopy to characterize the nanoparticles obtained. The energy-dispersive spectroscopy (EDX) of the nanoparticles dispersion confirmed the presence of elemental silver signal no peaks of other impurity were detected. The average size and morphology of silver nanoparticles were determined by transmission electron microscopy (TEM). TEM photographs indicate that the nanopowders consist of well dispersed agglomerates of grains with a narrow size distribution (40 and 60 nm), whereas the radius of the individual particles are between 10 and 20 nm. The synthesized nanoparticles have been structurally characterized by X-ray diffraction and transmission high-energy electron diffraction (HEED). The peaks in the XRD pattern are in good agreement with the standard values of the face-centered-cubic form of metallic silver (ICCD-JCPDS card no. 4-0787) and no peaks of other impurity crystalline phases were detected. Additionally, the antibacterial activity of the nanopart├¡culas dispersion was measured by Kirby-Bauer method. The nanoparticles of silver showed high antimicrobial and bactericidal activity against gram positive bacteria such as Escherichia Coli, Pseudimonas aureginosa and staphylococcus aureus which is a highly methicillin resistant strain.
Abstract: Adsorption of methanol and ethanol over mesoporous
siliceous material are studied in the current paper. The pure
mesoporous silica is prepared using tetraethylorthosilicate (TEOS) as
silica source and dodecylamine as template at low pH. The prepared
material was characterized using nitrogen adsorption,nX-ray
diffraction (XRD) and scanning electron microscopy (SEM). The
adsorption kinetics of methanol and ethanol from aqueous solution
were studied over the prepared mesoporous silica material. The
percent removal of alcohol was calculated per unit mass of adsorbent
used. The 1st order model is found to be in agreement with both
adsorbates while the 2nd order model fit the adsorption of methanol
only.
Abstract: In this paper, Zinc Oxide (ZnO) thin films are deposited on glass substrate by sol-gel method. The ZnO thin films with well defined orientation were acquired by spin coating of zinc acetate dehydrate monoethanolamine (MEA), de-ionized water and isopropanol alcohol. These films were pre-heated at 275°C for 10 min and then annealed at 350°C, 450°C and 550°C for 80 min. The effect of annealing temperature and different thickness on structure and surface morphology of the thin films were verified by Atomic Force Microscopy (AFM). It was found that there was a significant effect of annealing temperature on the structural parameters of the films such as roughness exponent, fractal dimension and interface width. Thin films also were characterizied by X-ray Diffractometery (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure and show the c-axis grain orientation. Increasing annealing temperature increased the crystallite size and the c-axis orientation of the film after 450°C. Also In this study, ZnO thin films in different thickness have been prepared by sol-gel method on the glass substrate at room temperature. The thicknesses of films are 100, 150 and 250 nm. Using fractal analysis, morphological characteristics of surface films thickness in amorphous state were investigated. The results show that with increasing thickness, surface roughness (RMS) and lateral correlation length (ξ) are decreased. Also, the roughness exponent (α) and growth exponent (β) were determined to be 0.74±0.02 and 0.11±0.02, respectively.