Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.
Abstract: Wet chemistry methods are used to prepare the
SiO2/Au nanoshells. The purpose of this research was to synthesize
gold coated SiO2 nanoshells for biomedical applications. Tunable
nanoshells were prepared by using different colloidal concentrations.
The nanoshells are characterized by FTIR, XRD, UV-Vis
spectroscopy and atomic force microscopy (AFM). The FTIR results
confirmed the functionalization of the surfaces of silica nanoparticles
with NH2 terminal groups. A tunable absorption was observed
between 470-600 nm with a maximum range of 530-560 nm. Based
on the XRD results three main peaks of Au (111), (200) and (220)
were identified. Also AFM results showed that the silica core
diameter was about 100 nm and the thickness of gold shell about 10
nm.
Abstract: Reinforced Concrete (RC) structures strengthened
with fiber reinforced polymer (FRP) lack in thermal resistance under
elevated temperatures in the event of fire. This phenomenon led to
the lining of strengthened concrete with thin high performance
cementitious composites (THPCC) to protect the substrate against
elevated temperature. Elevated temperature effects on THPCC, based
on different cementitious materials have been studied in the past but
high-alumina cement (HAC)-based THPCC have not been well
characterized. This research study will focus on the THPCC based on
HAC replaced by 60%, 70%, 80% and 85% of ground granulated
blast furnace slag (GGBS). Samples were evaluated by the
measurement of their mechanical strength (28 & 56 days of curing)
after exposed to 400°C, 600°C and 28°C of room temperature for
comparison and corroborated by their microstructure study. Results
showed that among all mixtures, the mix containing only HAC
showed the highest compressive strength after exposed to 600°C as
compared to other mixtures. However, the tensile strength of THPCC
made of HAC and 60% GGBS content was comparable to the
THPCC with HAC only after exposed to 600°C. Field emission
scanning electron microscopy (FESEM) images of THPCC
accompanying Energy Dispersive X-ray (EDX) microanalysis
revealed that the microstructure deteriorated considerably after
exposure to elevated temperatures which led to the decrease in
mechanical strength.
Abstract: Nanostructured materials have attracted many
researchers due to their outstanding mechanical and physical
properties. For example, carbon nanotubes (CNTs) or carbon
nanofibres (CNFs) are considered to be attractive reinforcement
materials for light weight and high strength metal matrix composites.
These composites are being projected for use in structural
applications for their high specific strength as well as functional
materials for their exciting thermal and electrical characteristics. The
critical issues of CNT-reinforced MMCs include processing
techniques, nanotube dispersion, interface, strengthening mechanisms
and mechanical properties. One of the major obstacles to the effective
use of carbon nanotubes as reinforcements in metal matrix
composites is their agglomeration and poor distribution/dispersion
within the metallic matrix. In order to tap into the advantages of the
properties of CNTs (or CNFs) in composites, the high dispersion of
CNTs (or CNFs) and strong interfacial bonding are the key issues
which are still challenging. Processing techniques used for synthesis
of the composites have been studied with an objective to achieve
homogeneous distribution of carbon nanotubes in the matrix.
Modified mechanical alloying (ball milling) techniques have emerged
as promising routes for the fabrication of carbon nanotube (CNT)
reinforced metal matrix composites. In order to obtain a
homogeneous product, good control of the milling process, in
particular control of the ball movement, is essential. The control of
the ball motion during the milling leads to a reduction in grinding
energy and a more homogeneous product. Also, the critical inner
diameter of the milling container at a particular rotational speed can
be calculated. In the present work, we use conventional and modified
mechanical alloying to generate a homogenous distribution of 2 wt.
% CNT within Al powders. 99% purity Aluminium powder (Acros,
200mesh) was used along with two different types of multiwall
carbon nanotube (MWCNTs) having different aspect ratios to
produce Al-CNT composites. The composite powders were processed
into bulk material by compaction, and sintering using a cylindrical
compaction and tube furnace. Field Emission Scanning electron
microscopy (FESEM), X-Ray diffraction (XRD), Raman
spectroscopy and Vickers macro hardness tester were used to
evaluate CNT dispersion, powder morphology, CNT damage, phase
analysis, mechanical properties and crystal size determination.
Despite the success of ball milling in dispersing CNTs in Al powder,
it is often accompanied with considerable strain hardening of the Al
powder, which may have implications on the final properties of the
composite. The results show that particle size and morphology vary
with milling time. Also, by using the mixing process and sonication
before mechanical alloying and modified ball mill, dispersion of the
CNTs in Al matrix improves.
Abstract: The localized corrosion behavior of laser surface
melted 304L austenitic stainless steel was studied by
potentiodynamic polarization test. The extent of improvement in
corrosion resistance was governed by the preferred orientation and
the percentage of delta ferrite present on the surface of the laser
melted sample. It was established by orientation imaging microscopy
that the highest pitting potential value was obtained when grains were
oriented in the most close- packed [101] direction compared to the
random distribution of the base metal and other laser surface melted
samples oriented in [001] direction. The sample with lower
percentage of ferrite had good pitting resistance.
Abstract: The characterization of κ-carrageenan could provide a
better understanding of its functions in biological, medical and
industrial applications. Chemical and physical analyses of
carrageenan from seaweeds, Euchema cottonii L., were done to offer
information on its properties and the effects of Co-60 γ-irradiation on
its thermochemical characteristics. The structural and morphological
characteristics of κ-carrageenan were determined using scanning
electron microscopy (SEM) while the composition, molecular weight
and thermal properties were determined using attenuated total
reflectance Fourier transform infrared spectroscopy (ATR-FTIR), gel
permeation chromatography (GPC), thermal gravimetric analysis
(TGA) and differential scanning calorimetry (DSC). Further chemical
analysis was done using hydrogen-1 nuclear magnetic resonance (1H
NMR) and functional characteristics in terms of biocompatibility
were evaluated using cytotoxicity test.
Abstract: In this paper, the residual stress of thermal spray
coatings in gas turbine component by curvature method has been
studied. The samples and shaft were coated by hard WC-12Co
cermets using high velocity oxy fuel (HVOF) after preparation in
same conditions. The curvature of coated samples was measured by
using of coordinate measurement machine (CMM). The metallurgical
and Tribological studies has been made on the coated shaft using
optical microscopy and scanning electron microscopy (SEM)
Abstract: We study the problem of reconstructing a three dimensional binary matrices whose interiors are only accessible through few projections. Such question is prominently motivated by the demand in material science for developing tool for reconstruction of crystalline structures from their images obtained by high-resolution transmission electron microscopy. Various approaches have been suggested to reconstruct 3D-object (crystalline structure) by reconstructing slice of the 3D-object. To handle the ill-posedness of the problem, a priori information such as convexity, connectivity and periodicity are used to limit the number of possible solutions. Formally, 3Dobject (crystalline structure) having a priory information is modeled by a class of 3D-binary matrices satisfying a priori information. We consider 3D-binary matrices with periodicity constraints, and we propose a polynomial time algorithm to reconstruct 3D-binary matrices with periodicity constraints from two orthogonal projections.
Abstract: Bacterial cellulose, a biopolysaccharide, is produced by the bacterium, Gluconacetobacter xylinus. Static batch fermentation for bacterial cellulose production was studied in sucrose and date syrup solutions (Bx. 10%) at 28 °C using G. xylinus (PTCC, 1734). Results showed that the maximum yields of bacterial cellulose (BC) were 4.35 and 1.69 g/l00 ml for date syrup and sucrose medium after 336 hours fermentation period, respectively. Comparison of FTIR spectrum of cellulose with BC indicated appropriate coincidence which proved that the component produced by G. xylinus was cellulose. Determination of the area under X-ray diffractometry patterns demonstrated that the crystallinity amount of cellulose (83.61%) was more than that for the BC (60.73%). The scanning electron microscopy imaging of BC and cellulose were carried out in two magnifications of 1 and 6K. Results showed that the diameter ratio of BC to cellulose was approximately 1/30 which indicated more delicacy of BC fibers relative to cellulose.
Abstract: Chemical and physical functionalization of multiwalled
carbon nanotubes (MWCNT) has been commonly practiced to
achieve better dispersion of carbon nanotubes (CNTs) in polymer
matrix. This work describes various functionalization methods (acidtreatment,
non-ionic surfactant treatment with TritonX-100),
fabrication of MWCNT/PP nanocomposites via melt blending and
characterization of mechanical properties. Microscopy analysis
(FESEM, TEM, XPS) showed effective purification of MWCNTs
under acid treatment, and better dispersion under both chemical and
physical functionalization techniques combined, in their respective
order. Tensile tests showed increase in tensile strength for the
nanocomposites that contain MWCNTs up to 2 wt%. A decrease in
tensile strength was seen in samples that contain 4 wt% of MWCNTs
for both raw and Triton X-100 functionalized, signifying MWCNT
degradation/rebundling at composition with higher content of
MWCNTs. For the acid-treated MWCNTs, however, the tensile
results showed slight improvement even at 4wt%, indicating effective
dispersion of MWCNTs.
Abstract: In this study, Li4SiO4 powder was successfully
synthesized via sol gel method followed by drying at 150oC. Lithium
oxide, Li2O and silicon oxide, SiO2 were used as the starting
materials with citric acid as the chelating agent. The obtained powder
was then sintered at various temperatures. Crystallographic phase
analysis, morphology and ionic conductivity were investigated
systematically employing X-ray diffraction, Fourier Transform
Infrared, Scanning Electron Microscopy and AC impedance
spectroscopy. XRD result showed the formation of pure monoclinic
Li4SiO4 crystal structure with lattice parameters a = 5.140 Å, b =
6.094 Å, c = 5.293 Å, β = 90o in the sample sintered at 750oC. This
observation was confirmed by FTIR analysis. The bulk conductivity
of this sample at room temperature was 3.35 × 10-6 S cm-1 and the
highest bulk conductivity of 1.16 × 10-4 S cm-1 was obtained at
100°C. The results indicated that, the Li4SiO4 compound has
potential to be used as host for LISICON structured solid electrolyte
for low temperature application.
Abstract: Electro Chemical Discharge Machining (ECDM) is an
emerging hybrid machining process used in precision machining of hard and brittle non-conducting materials. The present paper gives a
critical review on materials machined by ECDM under the prevailing machining conditions; capability indicators of the process are
reported. Some results obtained while performing experiments in micro-channeling on soda lime glass using ECDM are also presented. In these experiments, Tool Wear (TW) and Material Removal (MR)
were studied using design of experiments and L–4 orthogonal array. Experimental results showed that the applied voltage was the most influencing parameter in both MR and TW studies. Field
emission scanning electron microscopy (FESEM) results obtained on the microchannels confirmed the presence of micro-cracks, primarily responsible for MR. Chemical etching was also seen along the edges.
The Energy dispersive spectroscopy (EDS) results were used to detect the elements present in the debris and specimens.
Abstract: In this study, synthesis of biomemitic patterned nano
hydroxyapatite-starch biocomposites using different concentration of
starch to evaluate effect of polymer alteration on biocomposites
structural properties has been reported. Formation of hydroxyapatite
nano particles was confirmed by X-ray diffraction (XRD) and Fourier
transform infrared spectroscopy (FT-IR). Size and morphology of the
samples were characterized using scanning and transmission electron
microscopy (SEM and TEM). It seems that by increasing starch
content, the more active site of polymer (oxygen atoms) can be
provided for interaction with Ca2+ followed by phosphate and
hydroxyl group.
Abstract: Electrochemical-oxidation of Reactive Black-5 (RB- 5) was conducted for degradation using DSA type Ti/RuO2-SnO2- Sb2O5 electrode. In the study, for electro-oxidation, electrode was indigenously fabricated in laboratory using titanium as substrate. This substrate was coated using different metal oxides RuO2, Sb2O5 and SnO2 by thermal decomposition method. Laboratory scale batch reactor was used for degradation and decolorization studies at pH 2, 7 and 11. Current density (50mA/cm2) and distance between electrodes (8mm) were kept constant for all experiments. Under identical conditions, removal of color, COD and TOC at initial pH 2 was 99.40%, 55% and 37% respectively for initial concentration of 100 mg/L RB-5. Surface morphology and composition of the fabricated electrode coatings were characterized using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) respectively. Coating microstructure was analyzed by X-ray diffraction (XRD). Results of this study further revealed that almost 90% of oxidation occurred within 5-10 minutes.
Abstract: In this paper, the wear of high speed steel hobs during
hobbing has been studied. The wear mechanisms are strongly
influenced by the choice of cutting speed. At moderate and high
cutting speeds three major wear mechanisms were identified:
abrasion, mild adhesive and severe adhesive. The microstructure and
wear behavior of two high speed steel grades (M2 and ASP30) has
been compared. In contrast, a variation in chemical composition or
microstructure of HSS tool material generally did not change the
dominant wear mechanism. However, the tool material properties
determine the resistance against the operating wear mechanism and
consequently the tool life. The metallographic analysis and wear
measurement at the tip of hob teeth included scanning electron
microscopy and stereoscope microscopy. Roughness profilometery is
used for measuring the gear surface roughness.
Abstract: The use of magnetic and magnetic/gold core/shell
nanoparticles in biotechnology or medicine has shown good promise
due to their hybrid nature which possesses superior magnetic and
optical properties. Some of these potential applications include
hyperthermia treatment, bio-separations, diagnostics, drug delivery
and toxin removal. Synthesis refinement to control geometric and
magnetic/optical properties, and finding functional surfactants for
biomolecular attachment, are requirements to meet application
specifics.
Various high-temperature preparative methods were used for the
synthesis of iron oxide and gold-coated iron oxide nanoparticles.
Different surface functionalities, such as 11-aminoundecanoic and
11-mercaptoundecanoic acid, were introduced on the surface of the
particles to facilitate further attachment of biomolecular functionality
and drug-like molecules. Nanoparticle thermal stability, composition,
state of aggregation, size and morphology were investigated and the
results from techniques such as Fourier Transform-Infra Red
spectroscopy (FT-IR), Ultraviolet visible spectroscopy (UV-vis),
Transmission Electron Microscopy (TEM) and thermal analysis are
discussed.
Abstract: This study investigates a voltage-controllable liquid crystals lens with a Fresnel zone electrode. When applying a proper voltage on the liquid crystal cell, a Fresnel-zone-distributed electric field is induced to direct liquid crystals aligned in a concentric structure. Owing to the concentrically aligned liquid crystals, a Fresnel lens is formed. We probe the Fresnel liquid crystal lens using a polarized incident beam with a wavelength of 632.8 nm, finding that the diffraction efficiency depends on the applying voltage. A remarkable diffraction efficiency of ~39.5 % is measured at the voltage of 0.9V. Additionally, a dual focus lens is fabricated by attaching a plane-convex lens to the Fresnel liquid crystals cell. The Fresnel LC lens and the dual focus lens may be applied for DVD/CD pick-up head, confocal microscopy system, or electrically-controlling optical systems.
Abstract: The objective of the present investigation was to
evaluate the morphology of Escherchia coli bacteria in interaction
with SiO2 nanoparticles.
This study was made by atomic force microscopy and quartz
crystal microbalance using SiO2 nanoparticles with 10nm, 50nm and
100nm diameter and bacteria immobilized on polyelectrolyte
multilayer films obtained by spin coating or by “layer by layer”
(LbL) method.
Abstract: Transcription factor p53 has a powerful tumor
suppressing function that is associated with many cancers. However,
p53 of the molecular weight was higher make the limitation across to
skin or cell membrane. Thymidine dinucleotide (pTT), an
oligonucleotide, can activate the p53 transcription factor. pTT is a
hydrophilic and negative charge oligonucleotide, which delivery in to
cell membrane need an appropriate carrier. The aim of this study was
to improve the bioavailability of the nucleotide fragment, thymidine
dinucleotide (pTT), using elasic liposome carriers to deliver the drug
into the skin. The study demonstrate that dioleoylphosphocholine
(DOPC) incorporated with sodium cholate at molar ratio 1:1 can
archived the particle size about 220 nm. This elastic liposome could
penetration through skin from stratum corneum to whole epidermis by
confocal laser scanning microscopy (CLSM). Moreover, we observed
the the slight increase in generation of p53 by western blot.
Abstract: The mechanical and tribological properties in WC-Co
coatings are strongly affected by hardness and elasticity
specifications. The results revealed the effect of spraying distance on
microhardness and elasticity modulus of coatings. The metallurgical
studies have been made on coated samples using optical microscopy,
scanning electron microscopy (SEM).