Abstract: Reinforced Concrete (RC) structures strengthened
with fiber reinforced polymer (FRP) lack in thermal resistance under
elevated temperatures in the event of fire. This phenomenon led to
the lining of strengthened concrete with thin high performance
cementitious composites (THPCC) to protect the substrate against
elevated temperature. Elevated temperature effects on THPCC, based
on different cementitious materials have been studied in the past but
high-alumina cement (HAC)-based THPCC have not been well
characterized. This research study will focus on the THPCC based on
HAC replaced by 60%, 70%, 80% and 85% of ground granulated
blast furnace slag (GGBS). Samples were evaluated by the
measurement of their mechanical strength (28 & 56 days of curing)
after exposed to 400°C, 600°C and 28°C of room temperature for
comparison and corroborated by their microstructure study. Results
showed that among all mixtures, the mix containing only HAC
showed the highest compressive strength after exposed to 600°C as
compared to other mixtures. However, the tensile strength of THPCC
made of HAC and 60% GGBS content was comparable to the
THPCC with HAC only after exposed to 600°C. Field emission
scanning electron microscopy (FESEM) images of THPCC
accompanying Energy Dispersive X-ray (EDX) microanalysis
revealed that the microstructure deteriorated considerably after
exposure to elevated temperatures which led to the decrease in
mechanical strength.