Abstract: Two different superhydrophobic surfaces were
elaborated and their oil repellency behavior was evaluated using
several liquid with different surface tension. A silicone rubber/SiO2
nanocomposite coated (A) on aluminum substrate by “spin-coating"
and the sample B was an anodized aluminum surface covered by
Teflon-like coating. A high static contact angle about ∼162° was
measured for two prepared surfaces on which the water droplet rolloff.
Scanning electron microscopy (SEM) showed the presence of
micro/nanostructures for both sample A and B similar to that of lotus
leaf.
However the sample A presented significantly different behaviour
of wettability against the low surface tension liquid. Sample A has
been wetted totally by oil (dodecan) droplet while sample B showed
oleophobic behaviour. Oleophobic property of Teflon like coating
can be contributed to the presence of CF2 and CF3 functional group
which was shown by XPS analysis.
Abstract: In the present work homogeneous silica film on
silicon was fabricated by colloidal silica sol. The silica sol precursor
with uniformly granular particle was derived by the alkaline
hydrolysis of tetraethoxyorthosilicate (TEOS) in presence of glycerol
template. The film was prepared by dip coating process. The
templated hetero-structured silica film was annealed at elevated
temperatures to generate nano- and meso porosity in the film. The
film was subsequently annealed at different temperatures to make it
defect free and abrasion resistant. The sol and the film were
characterized by the measurement of particle size distribution,
scanning electron microscopy, XRD, FTIR spectroscopy,
transmission electron microscopy, atomic force microscopy,
measurement of the refractive index, thermal conductivity and
abrasion resistance. The porosity of the films decreased whereas
refractive index and dielectric constant of it `increased with the
increase in the annealing temperature. The thermal conductivity of
the films increased with the increase in the film thickness. The
developed porous silica film holds strong potential for use in
different areas.
Abstract: Wetting characteristics of reactive (Sn–0.7Cu solder)
and non– reactive (castor oil) wetting of liquids on Cu and Ag plated
Al substrates have been investigated. Solder spreading exhibited
capillary, gravity and viscous regimes. Oils did not exhibit noticeable
spreading regimes. Solder alloy showed better wettability on Ag
coated Al substrate compared to Cu plating. In the case of castor oil,
Cu coated Al substrate exhibited good wettability as compared to Ag
coated Al substrates. The difference in wettability during reactive
wetting of solder and non–reactive wetting of oils is attributed to the
change in the surface energies of Al substrates brought about by the
formation of intermetallic compounds (IMCs).
Abstract: Gold coated silica core nanoparticles have an optical
response dictated by the plasmon resonance. The wavelength at
which the resonance occurs depends on the core and shell sizes,
allowing nanoshells to be tailored for particular applications. The
purposes of this study was to synthesize and use different
concentration of gold nanoshells as exogenous material for skin
tissue soldering and also to examine the effect of laser soldering
parameters on the properties of repaired skin. Two mixtures of
albumin solder and different concentration of gold nanoshells were
prepared. A full thickness incision of 2×20 mm2 was made on the
surface and after addition of mixtures it was irradiated by an 810nm
diode laser at different power densities. The changes of tensile
strength σt due to temperature rise, number of scan (Ns), and scan
velocity (Vs) were investigated. The results showed at constant laser
power density (I), σt of repaired incisions increases by increasing the
concentration of gold nanoshells, Ns and decreasing Vs. It is therefore
important to consider the trade off between the scan velocity and the
surface temperature for achieving an optimum operating condition. In
our case this corresponds to σt =1610 gr/cm2 at I~ 60 Wcm-2, T ~
65ºC, Ns =10 and Vs=0.2mms-1.
Abstract: Most simple nonlinear thresholding rules for
wavelet- based denoising assume that the wavelet coefficients are independent. However, wavelet coefficients of natural images have significant dependencies. This paper attempts to give a recipe for selecting one of the popular image-denoising algorithms based
on VisuShrink, SureShrink, OracleShrink, BayesShrink and BiShrink and also this paper compares different Bivariate models used for image denoising applications. The first part of the paper
compares different Shrinkage functions used for image-denoising.
The second part of the paper compares different bivariate models
and the third part of this paper uses the Bivariate model with modified marginal variance which is based on Laplacian assumption. This paper gives an experimental comparison on six 512x512 commonly used images, Lenna, Barbara, Goldhill,
Clown, Boat and Stonehenge. The following noise powers 25dB,26dB, 27dB, 28dB and 29dB are added to the six standard images and the corresponding Peak Signal to Noise Ratio (PSNR) values
are calculated for each noise level.
Abstract: The paper relates to a catalyst, comprising copperchromium
spinel, coated on carrier γ-Al2O3. The effect of preparation
conditions on the active component composition and activity
behavior of the catalysts is discussed. It was found that the activity of
carbon monoxide, DME, formaldehyde and methanol oxidation
reaches a maximum at an active component content of 20 – 30 wt. %.
Temperature calcination at 500oC seems to be optimal for the γ–
alumina supported CuO-Cr2O3 catalysts for CO, DME, formaldehyde
and methanol oxidation. A three months industrial experiment was
carried out to elucidate the changes in the catalyst composition
during industrial exploitation of the catalyst and the main reasons for
catalyst deactivation.
It was concluded that the CuO–Cr2O3/γ–alumina supported
catalysts have enhanced activity toward CO, DME, formaldehyde
and methanol oxidation and that these catalysts are suitable for
industrial application. The main reason for catalyst deactivation
seems to be the deposition of iron and molybdenum, coming from the
main reactor, on the active component surface.
Abstract: In this study, a nickel film with nano-crystalline grains,
high hardness and smooth surface was electrodeposited using a post
supercritical carbon dioxide (CO2) mixed Watts electrolyte. Although
the hardness was not as high as its Sc-CO2 counterpart, the thin coating
contained significantly less number of nano-sized pinholes. By
measuring the escape concentration of the dissolved CO2 in post
Sc-CO2 mixed electrolyte with the elapsed time, it was believed that
the residue of dissolved CO2 bubbles should closely relate to the
improvement in hardness and surface roughness over its conventional
plating counterpart. Therefore, shortening the duration of
electroplating with the raise of current density up to 0.5 A/cm2 could
effectively retain more post Sc-CO2 mixing effect. This study not only
confirms the roles of dissolved CO2 bubbles in electrolyte but also
provides a potential process to overcome most issues associated with
the cost in building high-pressure chamber for large size products and
continuous plating using supercritical method.
Abstract: Plastics occupy wide place in the applications of
automotive, electronics and house goods. Especially reinforced
plastics become popular because of their high strength besides their
advantages of low weight and easy manufacturability. In this study,
mechanical and morphological properties of polypropylene (PP) and
high density polyethylene (HDPE) matrix composites reinforced with
surface modified nano titan dioxide (TiO2) particles were
investigated. Surface modification was made by coating the nano
powders with maleic anhydride grafted styrene ethylene butylene
styrene (SEBS-g-MA) and silane, respectively. After surface
modification, PP/TiO2 and HDPE/TiO2 composites were obtained by
using twin screw extruder at titan dioxide loading of 1 wt.%, 3 wt.%
and 5 wt.%. Effects of surface modification were determined by
thermal and morphological analysis. SEBS-g-MA provided bridging
effect between TiO2 particles and polymer matrix while silane was
effective as a dispersant. Depending on that, homogenous structures
without agglomeration were obtained. Mechanical tests were
performed on the injection moldings of the composites for obtaining
the impact strength, tensile strength, stress at break, elongation and
elastic modulus. Reinforced HDPE and PP moldings gave higher
tensile strength and elastic modulus due to the rigid structure of TiO2.
Slight increment was seen in stress at break. Elongation and impact
strength decreased due to the stiffness of the nano titan dioxide.
Abstract: The steam cracking reactions are always accompanied with the formation of coke which deposits on the walls of the tubular reactors. The investigation has attempted to control catalytic coking by the applying aluminum, zinc and ceramic coating like aluminum-magnesium by thermal spray and pack cementation method. Rate of coke formation during steam cracking of naphtha has been investigated both for uncoated stainless steel (with different alloys) and metal coating constructed with thermal Spray and pack cementation method with metal powders of Aluminum, Aluminum-Magnesium, zinc, silicon, nickel and chromium. The results of the study show that passivating the surface of SS321 with a coating of Aluminum and Aluminum-Magnesium can significantly reduce the rate of coke deposition during naphtha pyrolysis. SEM and EDAX techniques (Philips XL Series) were used to examine the coke deposits formed by the metal-hydrocarbon reactions. Our objective was to separate the different stages by identifying the characteristic morphologies.
Abstract: In the following text, we show that by introducing
universal kinetic scheme, the origin of rate retardation and inhibition
period which observed in dithiobenzoate-mediated RAFT
polymerization can be described properly. We develop our model by
utilizing the method of moments, then we apply our model to
different monomer/RAFT agent systems, both homo- and
copolymerization. The modeling results are in an excellent
agreement with experiments and imply the validity of universal
kinetic scheme, not only for dithiobenzoate-mediated systems, but
also for different types of monomer/RAFT agent ones.
Abstract: In the Lost Foam Casting process, melting point
temperature of metal, as well as volume and rate of the foam
degradation have significant effect on the mold filling pattern.
Therefore, gas generation capacity and gas gap length are two
important parameters for modeling of mold filling time of the lost
foam casting processes. In this paper, the gas gap length at the liquidfoam
interface for a low melting point (aluminum) alloy and a high
melting point (Carbon-steel) alloy are investigated by the
photography technique. Results of the photography technique
indicated, that the gas gap length and the mold filling time are
increased with increased coating thickness and density of the foam.
The Gas gap lengths measured in aluminum and Carbon-steel,
depend on the foam density, and were approximately 4-5 and 25-60
mm, respectively. By using a new system, the gas generation
capacity for the aluminum and steel was measured. The gas
generation capacity measurements indicated that gas generation in
the Aluminum and Carbon-steel lost foam casting was about 50 CC/g
and 3200 CC/g polystyrene, respectively.
Abstract: Adhesion strength of exterior or interior coating of
steel pipes is too important. Increasing of coating adhesion on
surfaces can increase the life time of coating, safety factor of
transmitting line pipe and decreasing the rate of corrosion and costs.
Preparation of steel pipe surfaces before doing the coating process is
done by shot and grit blasting. This is a mechanical way to do it.
Some effective parameters on that process, are particle size of
abrasives, distance to surface, rate of abrasive flow, abrasive physical
properties, shapes, selection of abrasive, kind of machine and its
power, standard of surface cleanness degree, roughness, time of
blasting and weather humidity. This search intended to find some
better conditions which improve the surface preparation, adhesion
strength and corrosion resistance of coating. So, this paper has
studied the effect of varying abrasive flow rate, changing the
abrasive particle size, time of surface blasting on steel surface
roughness and over blasting on it by using the centrifugal blasting
machine. After preparation of numbers of steel samples (according to
API 5L X52) and applying epoxy powder coating on them, to
compare strength adhesion of coating by Pull-Off test. The results
have shown that, increasing the abrasive particles size and flow rate,
can increase the steel surface roughness and coating adhesion
strength but increasing the blasting time can do surface over blasting
and increasing surface temperature and hardness too, change,
decreasing steel surface roughness and coating adhesion strength.
Abstract: In this paper, Zinc Oxide (ZnO) thin films are deposited on glass substrate by sol-gel method. The ZnO thin films with well defined orientation were acquired by spin coating of zinc acetate dehydrate monoethanolamine (MEA), de-ionized water and isopropanol alcohol. These films were pre-heated at 275°C for 10 min and then annealed at 350°C, 450°C and 550°C for 80 min. The effect of annealing temperature and different thickness on structure and surface morphology of the thin films were verified by Atomic Force Microscopy (AFM). It was found that there was a significant effect of annealing temperature on the structural parameters of the films such as roughness exponent, fractal dimension and interface width. Thin films also were characterizied by X-ray Diffractometery (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure and show the c-axis grain orientation. Increasing annealing temperature increased the crystallite size and the c-axis orientation of the film after 450°C. Also In this study, ZnO thin films in different thickness have been prepared by sol-gel method on the glass substrate at room temperature. The thicknesses of films are 100, 150 and 250 nm. Using fractal analysis, morphological characteristics of surface films thickness in amorphous state were investigated. The results show that with increasing thickness, surface roughness (RMS) and lateral correlation length (ξ) are decreased. Also, the roughness exponent (α) and growth exponent (β) were determined to be 0.74±0.02 and 0.11±0.02, respectively.
Abstract: The purpose is to study the model and characteristic of
participation of the suitable community to lead to develop permanent
water marketing in Bang Noi Floating Market, Bangkonti District,
Samutsongkhram Province. A total of 342 survey questionnaire was
administered to potential respondents. The researchers interviewed
the leader of the community. Appreciation Influence Control (AIC)
was used to talk with 20 villagers on arena. The findings revealed
that overall, most people had the middle level of the participation in
developing the durable Bang Noi Floating Market, Bangkonti,
Samutsongkhram Province and in aspects of gaining benefits from
developing it with atmosphere and a beautiful view for tourism. For
example, the landscape is beautiful with public utilities. The
participation in preserving and developing Bang Noi Floating Market
remains in the former way of life. The basic factor of person affects
to the participation of people such as age, level of education, career,
and income per month. Most participants are the original hosts that
have houses and shops located in the marketing and neighbor. These
people involve with the benefits and have the power to make a water
marketing strategy, the major role to set the information database. It
also found that the leader and the villagers play the important role in
setting a five-physical database. Data include level of information
such as position of village, territory of village, road, river, and
premises. Information of culture consists of a two-level of
information, interesting point, and Itinerary. The information occurs
from presenting and practicing by the leader and villagers in the
community.All of phases are presented for listening and investigating
database together in both the leader and villagers in the process of
participation.
Abstract: In this study, we propose a tongue diagnosis method
which detects the tongue from face image and divides the tongue area into six areas, and finally generates tongue coating ratio of each area.
To detect the tongue area from face image, we use ASM as one of the active shape models. Detected tongue area is divided into six areas
widely used in the Korean traditional medicine and the distribution of tongue coating of the six areas is examined by SVM(Support Vector
Machine). For SVM, we use a 3-dimensional vector calculated by PCA(Principal Component Analysis) from a 12-dimentional vector
consisting of RGB, HIS, Lab, and Luv. As a result, we detected the tongue area stably using ASM and found that PCA and SVM helped
raise the ratio of tongue coating detection.
Abstract: Titanium alloys like the modern alloy Ti 6Al 2Sn 4Zr 6Mo (Ti-6246) combine excellent specific mechanical properties and corrosion resistance. On the other hand,due to their material characteristics, machining of these alloys is difficult to perform. The aim of the current study is the analyses of wear mechanisms of coated cemented carbide tools applied in orthogonal cutting experiments of Ti-6246 alloy. Round bars were machined with standard coated tools in dry conditions on a CNC latheusing a wide range of cutting speeds and cutting depths. Tool wear mechanisms were afterwards investigated by means of stereo microscopy, optical microscopy, confocal microscopy and scanning electron microscopy. Wear mechanisms included fracture of the tool tip (total failure) and abrasion. Specific wear features like crater wear, micro cracks and built-up edgeformation appeared depending of the mechanical and thermal conditions generated in the workpiece surface by the cutting action.
Abstract: In an effort to understand the preliminary effects of aerodynamic stress on alveolar epithelial cells, we developed a multifluidic cell culture platform capable of supporting alveolar cultures at an air-liquid interface under constant air flow and exposure to varying pressure stimuli on the apical side while providing nourishment on the basolateral plane. Our current study involved utilizing the platform to study the effect of basement membrane coating and addition of dexamethasone on cellular response to pressure in A549 and H441 alveolar epithelial cells.
Abstract: Double heterogeneity of randomly located pebbles in
the core and Coated Fuel Particles (CFPs) in the pebbles are specific
features in pebble bed reactors and usually, because of difficulty to
model with MCNP code capabilities, are neglected. In this study,
characteristics of HTR-10, Tsinghua University research reactor, are
used and not only double heterogeneous but also truncated CFPs and
Pebbles are considered.Firstly, 8335 CFPs are distributed randomly
in a pebble and then the core of reactor is filled with those pebbles
and graphite pebbles as moderator such that 57:43 ratio of fuel and
moderator pebbles is established.Finally, four different core
configurations are modeled. They are Simple Cubic (SC) structure
with truncated pebbles,SC structure without truncated pebble, and
Simple Hexagonal(SH) structure without truncated pebbles and SH
structure with truncated pebbles. Results like effective multiplication
factor (Keff), critical height,etc. are compared with available data.
Abstract: Various assisted reproductive techniques have been
developed and refined to obtain a large number of offspring from
genetically superior animals or obtain offspring from infertile (or
subfertile) animals. The embryo transfer is one assisted reproductive
technique developed well, aimed at increased productivity of selected
females, disease control, importation and exportation of livestock,
rapid screening of AI sires for genetically recessive characteristics,
treatment or circumvention of certain types of infertility. Embryo
transfer also is a useful research tool for evaluating fetal and maternal
interactions. This technique has been applied to nearly every species
of domestic animal and many species of wildlife and exotic animals,
including humans and non-human primates. The successful of
embryo transfers have been limited to within-animal, homologous
replacement of the embryos. There are several examples of
interspecific and intergeneric embryo transfers in which embryos
implanted but did not develop to term: sheep and goat, mouse and rat.
An immunological rejections and placental incompatibility between
the embryo and the surrogate mother appear to restrict interspecific
embryo transfer/interspecific pregnancy. Recently, preimplantation
embryo manipulation procedures have been applied, such as
technique of inner cell mass transfer. This technique will possible to
overcome the reproductive barrier interspecific embryo
transfer/interspecific pregnancy, if there is a protective mechanism
which prevents recognition of the foreign fetus by the mother of the
other species
Abstract: Genetic Folding (GF) a new class of EA named as is
introduced for the first time. It is based on chromosomes composed
of floating genes structurally organized in a parent form and
separated by dots. Although, the genotype/phenotype system of GF
generates a kernel expression, which is the objective function of
superior classifier. In this work the question of the satisfying
mapping-s rules in evolving populations is addressed by analyzing
populations undergoing either Mercer-s or none Mercer-s rule. The
results presented here show that populations undergoing Mercer-s
rules improve practically models selection of Support Vector
Machine (SVM). The experiment is trained multi-classification
problem and tested on nonlinear Ionosphere dataset. The target of this
paper is to answer the question of evolving Mercer-s rule in SVM
addressed using either genetic folding satisfied kernel-s rules or not
applied to complicated domains and problems.