Abstract: Due to reduced stiffness, research on second
generation titanium alloys for implant applications, like the
metastable β-titanium alloy Ti-15Mo, become more and more
important in the recent years. The machinability of these alloys is
generally poor leading to problems during implant production and
comparably large production costs. Therefore, in the present study,
Ti-15Mo was alloyed with 0.8 wt.-% of the rare earth metals
lanthanum (Ti-15Mo+0.8La) and neodymium (Ti-15Mo+0.8Nd) to
improve its machinability. Their microstructure consisted of a
titanium matrix and micrometer-size particles of the rare earth metals
and two of their oxides. The particles stabilized the microstructure as
grain growth was minimized. As especially the ductility might be
affected by the precipitates, the behavior of Ti-15Mo+0.8La and Ti-
15Mo+0.8Nd was investigated during static and dynamic
deformation at elevated temperature to develop a processing route.
The resulting mechanical properties (static strength and ductility)
were similar in all investigated alloys.
Abstract: Titanium alloys like the modern alloy Ti 6Al 2Sn 4Zr 6Mo (Ti-6246) combine excellent specific mechanical properties and corrosion resistance. On the other hand,due to their material characteristics, machining of these alloys is difficult to perform. The aim of the current study is the analyses of wear mechanisms of coated cemented carbide tools applied in orthogonal cutting experiments of Ti-6246 alloy. Round bars were machined with standard coated tools in dry conditions on a CNC latheusing a wide range of cutting speeds and cutting depths. Tool wear mechanisms were afterwards investigated by means of stereo microscopy, optical microscopy, confocal microscopy and scanning electron microscopy. Wear mechanisms included fracture of the tool tip (total failure) and abrasion. Specific wear features like crater wear, micro cracks and built-up edgeformation appeared depending of the mechanical and thermal conditions generated in the workpiece surface by the cutting action.