Abstract: Sisal leaves were subjected to enzymatic retting
method to extract the sisal fibre. A portion of the fibre was pretreated
with alkali (NaOH), and further treated with benzoyl chloride
and silane treatment reagents. Both the treated and untreated Sisal
fibre composites were used to fabricate the composite by hand lay-up
technique using unsaturated polyester resin. Tensile, flexural, water
absorption, density, thickness swelling and chemical resistant tests
were conducted and evaluated on the composites. Results obtained
for all the parameters showed an increase in the treated fibre
compared to untreated fibre. FT-IR spectra results ascertained the
inclusion of benzoyl and silane groups on the fibre surface. Scanning
electron microscopy (SEM) result obtained showed variation in the
morphology of the treated and untreated fibre. Chemical modification
was found to improve adhesion of the fibre to the matrix, as well as
physico-mechanical properties of the composites.
Abstract: The layered structure LiNi1/3Co1/3Mn1/3-xAlxO2 (x = 0 ~
0.04) series cathode materials were synthesized by a carbonate
co-precipitation method, followed by a high temperature calcination
process. The influence of Al substitution on the microstructure and
electrochemical performances of the prepared materials was
investigated by X-Ray diffraction (XRD), scanning electron
microscopy (SEM), and galvanostatic charge/discharge test. The
results show that the LiNi1/3Co1/3Mn1/3-xAlxO2 has a well-ordered
hexagonal α-NaFeO2 structure. Although the discharge capacity of
Al-doped samples decreases as x increases,
LiNi1/3Co1/3Mn1/3-0.02Al0.02O2 exhibits superior capacity retention at
high voltage (4.6 V). Therefore, LiNi1/3Co1/3Mn1/3-0.02Al0.02O2 is a
promising material for “green” vehicles.
Abstract: This paper investigates the application of metallic
coatings on high fiber volume fraction carbon/epoxy polymer matrix
composites. For the grip of the metallic layer, a method of modifying
the surface of the composite by introducing a mixture of copper and
steel powder (filler powders) which can reduce the impact of thermal
spray particles. The powder was introduced to the surface at the time
of the forming. Arc spray was used to project the zinc coating layer.
The substrate was grit blasted to avoid poor adherence. The porosity, microstructure, and morphology of layers are
characterized by optical microscopy, SEM and image analysis. The
samples were studied also in terms of hardness and erosion resistance.
This investigation did not reveal any visible evidence damage to the
substrates. The hardness of zinc layer was about 25.94 MPa and the
porosity was around (∼6.70%). The erosion test showed that the zinc
coating improves the resistance to erosion. Based on the results
obtained, we can conclude that thermal spraying allows the production
of protective coating on PMC. Zinc coating has been identified as a
compatible material with the substrate. The filler powders layer
protects the substrate from the impact of hot particles and allows
avoiding the rupture of brittle carbon fibers.
Abstract: Some of the main causes for degradation of polymeric materials are thermal aging, hydrolysis, oxidation or chemical degradation by acids, alkalis or water. The first part of this paper provides a brief summary of advances in technology, methods and specification of composite materials for relining as a rehabilitation technique for sewage systems. The second part summarizes an investigation on frequently used composite materials for relining in Sweden, the rubber filled epoxy composite and reinforced polyester composite when they were immersed in deionized water or in dry conditions, and elevated temperatures up to 80°C in the laboratory. The tests were conducted by visual inspection, microscopy, Dynamic Mechanical Analysis (DMA), Differential Scanning Calorimetry (DSC) as well as mechanical testing, three point bending and tensile testing.
Abstract: We have aimed to produce a self-cleaning transparent
polymer coating with polyurethane (PU) matrix as the latter is highly
solvent, chemical and weather resistant having good mechanical
properties. Nano-silica modified by 1H, 1H, 2H, 2Hperflurooctyltriethoxysilane
was incorporated into the PU matrix for
attaining self-cleaning ability through hydrophobicity. The
modification was confirmed by particle size analysis and scanning
electron microscopy (SEM). Thermo-gravimetric (TGA) studies were
carried to ascertain the grafting of silane onto the silica. Several
coating formulations were prepared by varying the silica loading
content and compared to a commercial equivalent. The effect of
dispersion and the morphology of the coated films were assessed by
SEM analysis. All coating standardized tests like solvent resistance,
adhesion, flexibility, acid, alkali, gloss etc. have been performed as
per ASTM standards. Water contact angle studies were conducted to
analyze the hydrophobic character of the coating. In addition, the
coatings were also subjected to salt spray and accelerated weather
testing to analyze the durability of the coating.
Abstract: This work aims to investigate the structure–property
relationship in ternary nanocomposites consisting of polypropylene
as the matrix, polyamide 66 as the minor phase and treated nanoclay
DELLITE 67G as the reinforcement. All PP/PA66/Nanoclay systems
with polypropylene grafted maleic anhydride PP-g-MAH as a
compatibilizer were prepared via melt compounding and
characterized in terms of nanoclay content. Morphological structure
was investigated by scanning electron microscopy. The rheological
behavior of the nanocomposites was determined by various methods,
viz melt flow index (MFI) and parallel plate rheological
measurements. The PP/PP-g-MAH/PA66 nanocomposites showed a homogeneous
morphology supporting the compatibility improvement between PP,
PA66, and nanoclay. SEM results revealed the formation of
nanocomposites as the nanoclay was intercalated and exfoliated. In
the ternary nanocomposites, the rheological behavior showed that, the
complex viscosity is increased with increasing the nanoclay. The results showed that the use of nanoclay affects the variations
of storage modulus (G′), loss modulus (G″) and the melt elasticity.
Abstract: Cadmium oxide (CdO) nanoparticles have been
prepared by chemical coprecipitation method. The synthesized
nanoparticles were characterized by X-ray diffraction analysis
(XRD), scanning electron microscopy (SEM), transmission electron
microscopy (TEM), UV analysis, and dielectric studies. The
crystalline nature and particle size of the CdO nanoparticles were
characterized by Powder X-ray diffraction analysis (XRD). The
morphology of prepared CdO nanoparticles was studied by scanning
electron microscopy. The particle size was studied using the
transmission electron microscopy (TEM).The optical properties were
obtained from UV-Vis absorption spectrum. The dielectric properties
of CdO nanoparticles were studied in the frequency range of 50 Hz–5
MHz at different temperatures. The frequency dependence of the
dielectric constant and dielectric loss is found to decrease with an
increase in the frequency at different temperatures. The ac
conductivity of CdO nanoparticle has been studied.
Abstract: Durian skin is a newly explores natural fibre
potentially reinforced polyolefin for diverse applications. In this
work, investigation on the effect of coupling agent, maleic anhydride
polypropylene (MAPP) on the mechanical, morphological, and
thermal properties of polypropylene (PP) reinforced with durian skin
fibre (DSF) was conducted. The presence of 30 wt% DSF
significantly reduced the tensile strength of PP-DSF composite.
Interestingly, even though the same trend goes to PP-DSF with the
presence of MAPP, the reduction is only about 4% relative to
unreinforced PP and 18% higher than PP-DSF without MAPP
(untreated composite or UTC). The used of MAPP in treated
composite (TC) also increased the tensile modulus, flexural
properties and degradation temperature. The enhanced mechanical
properties are consistent with good interfacial interaction as
evidenced under scanning electron microscopy.
Abstract: Within this paper, latest results on processing of energetic nanomaterials by means of the Spray Flash Evaporation technique are presented. This technology constitutes a highly effective and continuous way to prepare fascinating materials on the nano- and micro-scale. Within the process, a solution is set under high pressure and sprayed into an evacuated atomization chamber. Subsequent ultrafast evaporation of the solvent leads to an aerosol stream, which is separated by cyclones or filters. No drying gas is required, so the present technique should not be confused with spray dying. Resulting nanothermites, insensitive explosives or propellants and compositions are foreseen to replace toxic (according to REACH) and very sensitive matter in military and civil applications. Diverse examples are given in detail: nano-RDX (n-Cyclotrimethylentrinitramin) and nano-aluminum based systems, mixtures (n-RDX/n-TNT - trinitrotoluene) or even cocrystalline matter like n-CL-20/HMX (Hexanitrohexaazaisowurtzitane/ Cyclotetra-methylentetranitramin). These nanomaterials show reduced sensitivity by trend without losing effectiveness and performance. An analytical study for material characterization was performed by using Atomic Force Microscopy, X-Ray Diffraction, and combined techniques as well as spectroscopic methods. As a matter of course, sensitivity tests regarding electrostatic discharge, impact, and friction are provided.
Abstract: NiFe2O4 (nickel ferrite), ZnFe2O4 (zinc ferrite) and
Ni0.5Zn0.5Fe2O4 (nickel-zinc ferrite) were prepared by
mechanochemical route in a planetary ball mill starting from mixture
of the appropriate quantities of the Ni(OH)2/Fe(OH)3,
Zn(OH)2/Fe(OH)3 and Ni(OH)2/Zn(OH)2/Fe(OH)3 hydroxide
powders. In order to monitor the progress of chemical reaction and
confirm phase formation, powder samples obtained after 25 h, 18 h
and 10 h of milling were characterized by X-ray diffraction (XRD),
transmission electron microscopy (TEM), IR, Raman and Mössbauer
spectroscopy. It is shown that the soft mechanochemical method, i.e.
mechanochemical activation of hydroxides, produces high quality
single phase ferrite samples in much more efficient way. From the IR
spectroscopy of single phase samples it is obvious that energy of
modes depends on the ratio of cations. It is obvious that all samples
have more than 5 Raman active modes predicted by group theory in
the normal spinel structure. Deconvolution of measured spectra
allows one to conclude that all complex bands in the spectra are made
of individual peaks with the intensities that vary from spectrum to
spectrum. The deconvolution of Raman spectra allows to separate
contributions of different cations to a particular type of vibration and
to estimate the degree of inversion.
Abstract: Introduction: The process to build a better safety
culture, methods of error analysis, and preventive measures, starts
with an understanding of the effects when human factors engineering
refer to remote microscopic diagnosis in surgery and specially in
organ transplantation for the remote evaluation of the grafts. It has
been estimated that even in well-organized transplant systems an
average of 8% to 14% of the grafts (G) that arrive at the recipient
hospitals may be considered as diseased, injured, damaged or
improper for transplantation. Digital microscopy adds information on
a microscopic level about the grafts in Organ Transplant (OT), and
may lead to a change in their management. Such a method will
reduce the possibility that a diseased G, will arrive at the recipient
hospital for implantation. Aim: Ergonomics of Digital Microscopy
(DM) based on virtual slides, on Telemedicine Systems (TS) for
Tele-Pathological (TPE) evaluation of the grafts (G) in organ
transplantation (OT). Material and Methods: By experimental
simulation, the ergonomics of DM for microscopic TPE of Renal
Graft (RG), Liver Graft (LG) and Pancreatic Graft (PG) tissues is
analyzed. In fact, this corresponded to the ergonomics of digital
microscopy for TPE in OT by applying Virtual Slide (VS) system for
graft tissue image capture, for remote diagnoses of possible
microscopic inflammatory and/or neoplastic lesions. Experimentation
included: a. Development of an OTE-TS similar Experimental
Telemedicine System (Exp.-TS), b. Simulation of the integration of
TS with the VS based microscopic TPE of RG, LG and PG applying
DM. Simulation of the DM based TPE was performed by 2
specialists on a total of 238 human Renal Graft (RG), 172 Liver Graft
(LG) and 108 Pancreatic Graft (PG) tissues digital microscopic
images for inflammatory and neoplastic lesions on four electronic
spaces of the four used TS. Results: Statistical analysis of specialist‘s
answers about the ability to diagnose accurately the diseased RG, LG
and PG tissues on the electronic space among four TS (A,B,C,D)
showed that DM on TS for TPE in OT is elaborated perfectly on the
ES of a Desktop, followed by the ES of the applied Exp.-TS. Tablet
and Mobile-Phone ES seem significantly risky for the application of
DM in OT (p
Abstract: Cesium molybdates with general formula
CsMIII(MoO4)2, where MIII = Bi, Dy, Pr, Er, exhibit rich
polymorphism, and crystallize in a layered structure. These properties
cause intensive studies on cesium molybdates. CsBi(MoO4)2 was synthesized by microwave method by using
cerium sulphate, bismuth oxide and molybdenum (VI) oxide in an
appropriate molar ratio. Characterizations were done by x-ray
diffraction (XRD), fourier transform infrared (FTIR) spectroscopy,
scanning electron microscopy/energy dispersive analyze (SEM/EDS),
thermo gravimetric/differantial thermal analysis (TG/DTA).
Abstract: The present study deals with the characterization of
CrSiN coatings obtained by PVD magnetron sputtering systems.
CrSiN films were deposited with different Si contents, in order to
check the effect of at.% variation on the different properties of the
Cr–N system. Coatings were characterized by scanning electron
microscopy (SEM) for thickness measurements, X-ray diffraction.
Surface morphology and the roughness characteristics were explored
using AFM, Mechanicals properties, elastic and plastic deformation
resistance of thin films were investigated using nanoindentation test. We observed that the Si addition improved the hardness and the
Young’s modulus of the Cr–N system. Indeed, the hardness value is
18,56 GPa for CrSiN coatings. Besides, the Young’s modulus value
is 224,22 GPa for CrSiN coatings for Si content of 1.2 at.%.
Abstract: Friction stir welding and tungsten inert gas welding
techniques were employed to weld armor grade aluminum alloy to
investigate the effect of welding processes on tensile behavior of
weld joints. Tensile tests, Vicker microhardness tests and optical
microscopy were performed on developed weld joints and base metal.
Welding process influenced tensile behavior and microstructure of
weld joints. Friction stir welded joints showed tensile behavior better
than tungsten inert gas weld joints.
Abstract: This paper reports the viability of developing Zn-27Al
alloy matrix hybrid composites reinforced with alumina, graphite and
fly ash (solid waste bye product of coal in thermal power plants).
This research work was aimed at developing low cost-high
performance Zn-27Al matrix composite with low density. Alumina
particulates (Al2O3), graphite added with 0, 2, 3, 4 and 5 wt% fly ash
were utilized to prepare 10wt% reinforcing phase with Zn-27Al alloy
as matrix using two-step stir casting method. Density measurement,
estimated percentage porosity, tensile testing, micro hardness
measurement and optical microscopy were used to assess the
performance of the composites produced. The results show that the
hardness, ultimate tensile strength, and percent elongation of the
hybrid composites decrease with increase in fly ash content. The
maximum decrease in hardness and ultimate tensile strength of
13.72% and 15.25% respectively were observed for composite grade
containing 5wt% fly ash. The percentage elongation of composite
sample without fly ash is 8.9% which is comparable with that of the
sample containing 2wt% fly ash with percentage elongation of 8.8%.
The fracture toughness of the fly ash containing composites was
however superior to those of composites without fly ash with 5wt%
fly ash containing composite exhibiting the highest fracture
toughness. The results show that fly ash can be utilized as
complementary reinforcement in ZA-27 alloy matrix composite to
reduce cost.
Abstract: Natural fibers are used in polymer composites to
improve mechanical properties to replace inorganic reinforcing
agents produced by non-renewable resources. The present study
investigates the tensile and flexural behaviors of palm fibers-high
density polyethylene (HDPE) composite as a function of volume
fraction. The surface of the fibers was treated by mercerization
treatments to improve the wetting behavior of the apolar HDPE. The
treatment characterization was obtained by scanning electron
microscopy, X-Ray diffraction and infrared spectroscopy. Results
evidences that a good adhesion interfacial between fibers-matrix
caused an increase strength and modulus flexural as well as tensile
strength in the modified fibers/HDPE composites when compared to
the pure HDPE and untreated fibers reinforced composites.
Abstract: The first laboratory synthesis of hard materials such as
diamond proceeded to attack of developing materials with high
hardness to compete diamond. Boron rich solids are good candidates
owing to their short interatomic bond lengths and strong covalent
character. Boron containing hard material was synthesized by modifiedmicrowave
method under nitrogen atmosphere by using a fuel
(glycine or urea), amorphous boron and/or boric acid in appropriate
molar ratio. Characterizations were done by x-ray diffraction (XRD),
Fourier transform infrared (FTIR) spectroscopy, scanning electron
microscopy/energy dispersive analyze (SEM/EDS), thermo
gravimetric/differential thermal analysis (TG/DTA).
Abstract: The aim of this study was to investigate the
photocatalytic activity of polycrystalline phases of bismuth tungstate
of formula Bi2WO6. Polycrystalline samples were elaborated using a
coprecipitation technique followed by a calcination process at
different temperatures (300, 400, 600 and 900°C). The obtained
polycrystalline phases have been characterized by X-ray diffraction
(XRD), scanning electron microscopy (SEM), and transmission
electron microscopy (TEM). Crystal cell parameters and cell volume
depend on elaboration temperature. High-resolution electron
microscopy images and image simulations, associated with X-ray
diffraction data, allowed confirming the lattices and space groups
Pca21. The photocatalytic activity of the as-prepared samples was
studied by irradiating aqueous solutions of Rhodamine B, associated
with Bi2WO6 additives having variable crystallite sizes. The
photocatalytic activity of such bismuth tungstates increased as the
crystallite sizes decreased. The high specific area of the
photocatalytic particles obtained at 300°C seems to condition the
degradation kinetics of RhB.
Abstract: In this paper, we study the optical nonlinearities of
Silver sulfide (Ag2S) nanostructures dispersed in the Dimethyl
sulfoxide (DMSO) under exposure to 532 nm, 15 nanosecond (ns)
pulsed laser irradiation. Ultraviolet–visible absorption spectrometry
(UV-Vis), X-ray diffraction (XRD), and transmission electron
microscopy (TEM) are used to characterize the obtained nanocrystal
samples. The band gap energy of colloid is determined by analyzing
the UV–Vis absorption spectra of the Ag2S NPs using the band
theory of semiconductors. Z-scan technique is used to characterize
the optical nonlinear properties of the Ag2S nanoparticles (NPs).
Large enhancement of two photon absorption effect is observed with
increase in concentration of the Ag2S nanoparticles using open Zscan
measurements in the ns laser regime. The values of the nonlinear
absorption coefficients are determined based on the local nonlinear
responses including two photon absorption. The observed aperture
dependence of the Ag2S NP limiting performance indicates that the
nonlinear scattering plays an important role in the limiting action of
the sample. The concentration dependence of the optical liming is
also investigated. Our results demonstrate that the optical limiting
threshold decreases with increasing the silver sulfide NPs in DMSO.
Abstract: This study intends to show the influence of the
hydrolytic degradation on the properties of the e-PTFE/NOMEX®
membranes used in fire-protective clothing. The modification of
water vapour permeability, morphology and chemical structure was
examined by MOCON Permatran, electron microscopy scanning
(SEM), and ATR-FTIR, respectively. A decrease in permeability to
water vapour of the aged samples was observed following closure of
transpiration pores. Analysis of fiber morphology indicates the
appearance of defects at the fibers surface with the presence of micro
cavities. ATR-FTIR analysis reveals the presence of a new absorption
band attributed to carboxylic acid terminal groups generated during
the amide bond hydrolysis.