Abstract: This paper reports the viability of developing Zn-27Al
alloy matrix hybrid composites reinforced with alumina, graphite and
fly ash (solid waste bye product of coal in thermal power plants).
This research work was aimed at developing low cost-high
performance Zn-27Al matrix composite with low density. Alumina
particulates (Al2O3), graphite added with 0, 2, 3, 4 and 5 wt% fly ash
were utilized to prepare 10wt% reinforcing phase with Zn-27Al alloy
as matrix using two-step stir casting method. Density measurement,
estimated percentage porosity, tensile testing, micro hardness
measurement and optical microscopy were used to assess the
performance of the composites produced. The results show that the
hardness, ultimate tensile strength, and percent elongation of the
hybrid composites decrease with increase in fly ash content. The
maximum decrease in hardness and ultimate tensile strength of
13.72% and 15.25% respectively were observed for composite grade
containing 5wt% fly ash. The percentage elongation of composite
sample without fly ash is 8.9% which is comparable with that of the
sample containing 2wt% fly ash with percentage elongation of 8.8%.
The fracture toughness of the fly ash containing composites was
however superior to those of composites without fly ash with 5wt%
fly ash containing composite exhibiting the highest fracture
toughness. The results show that fly ash can be utilized as
complementary reinforcement in ZA-27 alloy matrix composite to
reduce cost.