Abstract: Magnesium containing boron compounds with hexagonal structure have been drawn much attention due to their superconductive nature. The main target of this work is new modified microwave oven by on our own has an ability about passing through a gas in the oven medium for attainment of oxygen-free compounds such as c-BN. Mg containing boride was synthesized by modified-microwave method under nitrogen atmosphere using amorphous boron and magnesium source in appropriate molar ratio. Microwave oven with oxygen free environment has been modified to aimed to obtain magnesium boride without oxygen. Characterizations were done by powder X-ray diffraction (XRD), and Fourier transform infrared (FTIR) spectroscopy. Mg containing boride, generally named magnesium boride, with amorphous character without oxygen is obtained via designed microwave oven system.
Abstract: Cesium molybdates with general formula
CsMIII(MoO4)2, where MIII = Bi, Dy, Pr, Er, exhibit rich
polymorphism, and crystallize in a layered structure. These properties
cause intensive studies on cesium molybdates. CsBi(MoO4)2 was synthesized by microwave method by using
cerium sulphate, bismuth oxide and molybdenum (VI) oxide in an
appropriate molar ratio. Characterizations were done by x-ray
diffraction (XRD), fourier transform infrared (FTIR) spectroscopy,
scanning electron microscopy/energy dispersive analyze (SEM/EDS),
thermo gravimetric/differantial thermal analysis (TG/DTA).
Abstract: The first laboratory synthesis of hard materials such as
diamond proceeded to attack of developing materials with high
hardness to compete diamond. Boron rich solids are good candidates
owing to their short interatomic bond lengths and strong covalent
character. Boron containing hard material was synthesized by modifiedmicrowave
method under nitrogen atmosphere by using a fuel
(glycine or urea), amorphous boron and/or boric acid in appropriate
molar ratio. Characterizations were done by x-ray diffraction (XRD),
Fourier transform infrared (FTIR) spectroscopy, scanning electron
microscopy/energy dispersive analyze (SEM/EDS), thermo
gravimetric/differential thermal analysis (TG/DTA).
Abstract: In this research, it is aimed not only microwave synthesis of magnesium borates but also evaluation of magnesium wastes. Synthesis process can be described with the reaction of Mg wastes and boric acid using microwave energy. X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) were applied to synthesized minerals. According to XRD results, magnesium borate hydrate mixtures were obtained as mcallisterite (pdf# = 01-070-1902, Mg2(B6O7(OH)6)2.9(H2O)) at higher crystallinity properties was achieved at the mole ratio raw material 1:1. Also, other kinds of magnesium borate hydrates were obtained at lower crystallinity such as admontite (pdf # = 01-076-0540, MgO(B2O3)3.7(H2O)), inderite (pdf # = 01-072-2308, 2MgO.3B2O3.15(H2O)) and magnesium borate hydrates (pdf # = 01-076-0539, MgO(B2O3)3.6(H2O)). FT-IR spectrums indicated that minor changes were seen at the band values of characteristic stretching in each experiment. At the end of experiments it is seen that using microwave energy may contribute positive effects to design of synthesis process such as reducing reaction time and products at higher crystallinity.
Abstract: Due to their strong mechanical and thermal properties magnesium borates have a wide usage area such as ceramic industry, detergent production, friction reducing additive and grease production. In this study, microwave synthesis of magnesium borates from MgCl2.6H2O (Magnesium chloride hexahydrate), MgO (Magnesium oxide) and H3BO3 (Boric acid) for different reaction times is researched. X-ray Diffraction (XRD) and Fourier Transform Infrared (FT-IR) Spectroscopy are used to find out how the reaction time sways on the products. The superficial properties are investigated with Scanning Electron Microscopy (SEM). According to XRD analysis, the synthesized compounds are 00-041-1407 pdf coded Shabinite (Mg5(BO3)4Cl2(OH)5.4(H2O)) and 01-073-2158 pdf coded Karlite (Mg7(BO3)3(OH,Cl)5).