Abstract: Concrete is found to undergo degradation when
subjected to elevated temperatures and loose substantial amount of its
strength. The loss of strength in concrete is mainly attributed to
decomposition of C-S-H and release of physically and chemically
bound water, which begins when the exposure temperature exceeds
100°C. When such a concrete comes in contact with moisture, the
cement paste is found rehydrate and considerable amount of strength
lost is found to recover. This paper presents results of an
experimental program carried out to investigate the effect of recuring
on strength gain of OPC concrete specimens subjected to elevated
temperatures from 200°C to 800°C, which were subjected to
retention time of two hours and four hours at the designated
temperature. Strength recoveries for concrete subjected to 7
designated elevated temperatures are compared. It is found that the
efficacy of recuring as a measure of strength recovery reduces with
increase in exposure temperature.
Abstract: The operation of nuclear power plants involves
continuous monitoring of the environment in their area. This
monitoring is performed using a complex data acquisition system,
which collects status information about the system itself and values
of many important physical variables e.g. temperature, humidity,
dose rate etc. This paper describes a proposal and optimization of
communication that takes place in teledosimetric system between the
central control server responsible for the data processing and storing
and the decentralized measuring stations, which are measuring the
physical variables. Analyzes of ongoing communication were
performed and consequently the optimization of the system
architecture and communication was done.
Abstract: In our paper we describe the security capabilities of
data collection. Data are collected with probes located in the near and
distant surroundings of the company. Considering the numerous
obstacles e.g. forests, hills, urban areas, the data collection is realized
in several ways. The collection of data uses connection via wireless
communication, LAN network, GSM network and in certain areas
data are collected by using vehicles. In order to ensure the connection
to the server most of the probes have ability to communicate in
several ways. Collected data are archived and subsequently used in
supervisory applications.
To ensure the collection of the required data, it is necessary to
propose algorithms that will allow the probes to select suitable
communication channel.
Abstract: In this experiment Polystyrene/Zinc-oxide (PS/ZnO) nanocomposite fibers were produced by electrospinning technique using limonene as a green solvent. First, the morphology of electrospun pure polystyrene (PS) and PS/ZnO nanocomposite fibers investigated by SEM. Results showed the PS fiber diameter decreased by increasing concentration of Zinc Oxide nanoparticles (ZnO NPs). Thermo Gravimetric Analysis (TGA) results showed thermal stability of nanocomposites increased by increasing ZnO NPs in PS electrospun fibers. Considering Differential Scanning Calorimeter (DSC) thermograms for electrospun PS fibers indicated that introduction of ZnO NPs into fibers affects the glass transition temperature (Tg) by reducing it. Also, UV protection properties of nanocomposite fibers were increased by increasing ZnO concentration. Evaluating the effect of metal oxide NPs amount on mechanical properties of electrospun layer showed that tensile strength and elasticity modulus of the electrospun layer of PS increased by addition of ZnO NPs. X-ray diffraction (XRD) pattern of nanopcomposite fibers confirmed the presence of NPs in the samples.
Abstract: In today’s business environment, companies should
make strategic decisions to gain sustainable competitive advantage.
Order selection is a crucial issue among these decisions especially for
steel production industry. When the companies allocate a high
proportion of their design and production capacities to their ongoing
projects, determining which customer order should be chosen among
the potential orders without exceeding the remaining capacity is the
major critical problem. In this study, it is aimed to identify and
prioritize the evaluation factors for the customer order selection
problem. Conjoint Analysis is used to examine the importance level
of each factor which is determined as the potential profit rate per unit
of time, the compatibility of potential order with available capacity,
the level of potential future order with higher profit, customer credit
of future business opportunity, and the negotiability level of
production schedule for the order.
Abstract: Occurrence of popcorn in IC packages while assembling them onto the PCB is a well known moisture sensitive reliability issues, especially for surface mount packages. Commonly reflow soldering simulation process is conducted to assess the impact of assembling IC package onto PCB. A strain gauge-based instrumentation is developed to investigate the popcorn effect in surface mount packages during reflow soldering process. The instrument is capable of providing real-time quantitative information of the occurrence popcorn phenomenon in IC packages. It is found that the popcorn occur temperatures between 218 to 241°C depending on moisture soak condition, but not at the peak temperature of the reflow process. The presence of popcorn and delamination are further confirmed by scanning acoustic tomography as a failure analysis.
Abstract: The use of a conventional air plasma-sprayed thermal barrier coating (TBC) and a porous, functionally graded TBC as a thermal insulator for Al7075 alloy was explored. A quench test at 1200°C employing fast heating and cooling rates was setup to represent a dynamic thermal condition of an aerospace component. During the test, coated samples were subjected the ambient temperature of 1200°C for a very short time. This was followed by a rapid drop in temperature resulting in cracking of the coatings. For the conventional TBC, it was found that the temperature of the Al7075 substrate decreases with the increase in the ZrO2 topcoat thickness. However, at the topcoat thickness of 1100 µm, large horizontal cracks can be observed in the topcoat and at the topcoat thickness of 1600 µm, the topcoat delaminate during cooling after the quench test. The porous, functionally graded TBC with 600 µm thick topcoat, on the other hand, was found to be as effective at reducing the substrate temperature as the conventional TBC with 1100 µm thick topcoat. The maximum substrate temperature is about 213°C for the former and 208°C for the latter when a heating rate of 38°C/s was used. When the quench tests were conducted with a faster heating rate of 128°C/s, the Al7075 substrate heat up faster with a reduction in the maximum substrate temperatures. The substrate temperatures dropped from 297 to 212°C for the conventional TBC and from 213 to 155°C for the porous TBC, both with 600 µm thick topcoat. Segmentation cracks were observed in both coating after the quench test.
Abstract: Combustion of fuels in industrial and transport sector has lead to an alarming release of polluting gases to the atmosphere. Carbon monoxide is one such pollutant, which is formed as a result of incomplete oxidation of the fuel. In order to analyze the effect of catalyst on the reduction of CO emissions to the atmosphere, two catalysts Mn2O3 and Hopcalite are considered. A model was formed based on mass and energy balance equations. Results show that Hopcalite catalyst as compared to Mn2O3 catalyst helped in faster conversion of the polluting gas as the operating temperature of the hopcalite catalyst is much lower as compared to the operating temperature of Mn2O3 catalyst.
Abstract: In this paper, the periodic surveillance scheme has
been proposed for any convex region using mobile wireless sensor
nodes. A sensor network typically consists of fixed number of
sensor nodes which report the measurements of sensed data such as
temperature, pressure, humidity, etc., of its immediate proximity
(the area within its sensing range). For the purpose of sensing an
area of interest, there are adequate number of fixed sensor
nodes required to cover the entire region of interest. It implies
that the number of fixed sensor nodes required to cover a given
area will depend on the sensing range of the sensor as well as
deployment strategies employed. It is assumed that the sensors to
be mobile within the region of surveillance, can be mounted on
moving bodies like robots or vehicle. Therefore, in our
scheme, the surveillance time period determines the number of
sensor nodes required to be deployed in the region of interest.
The proposed scheme comprises of three algorithms namely:
Hexagonalization, Clustering, and Scheduling, The first algorithm
partitions the coverage area into fixed sized hexagons that
approximate the sensing range (cell) of individual sensor node.
The clustering algorithm groups the cells into clusters, each of
which will be covered by a single sensor node. The later
determines a schedule for each sensor to serve its respective cluster.
Each sensor node traverses all the cells belonging to the cluster
assigned to it by oscillating between the first and the last cell for
the duration of its life time. Simulation results show that our
scheme provides full coverage within a given period of time using
few sensors with minimum movement, less power consumption,
and relatively less infrastructure cost.
Abstract: Thermally insulating ceramic coatings also known as
thermal barrier coatings (TBCs) have been essential technologies to
improve the performance and efficiency of advanced gas turbines in
service at extremely high temperatures. The damage mechanisms of
air-plasma sprayed YSZ thermal barrier coatings (TBC) with various
microstructures were studied by microscopic techniques after thermal
cycling. The typical degradation of plasma TBCs that occurs during
cyclic furnace testing of an YSZ and alumina coating on a Titanium
alloy are analyzed. During the present investigation the effects of
topcoat thickness, bond coat oxidation, thermal cycle lengths and test
temperature are investigated using thermal cycling. These results
were correlated with stresses measured by a spectroscopic technique
in order to understand specific damage mechanism. The failure
mechanism of former bond coats was found to involve fracture
initiation at the thermally grown oxide (TGO) interface and at the
TGO bond coat interface. The failure mechanism of the YZ was
found to involve combination of fracture along the interface between
TGO and bond coat.
Abstract: Chloride induced corrosion of steel reinforcement is
the main cause of deterioration of reinforced concrete marine
structures. This paper investigates the relative performance of
alternative repair options with respect to the deterioration of
reinforced concrete bridge elements in marine environments. Focus is
placed on the initiation phase of reinforcement corrosion. A
laboratory study is described which involved exposing concrete
samples to accelerated chloride-ion ingress. The study examined the
relative efficiencies of two repair methods, namely Ordinary Portland
Cement (OPC) concrete and a concrete which utilised Ground
Granulated Blastfurnace Cement (GGBS) as a partial cement
replacement. The mix designs and materials utilised were identical to
those implemented in the repair of a marine bridge on the South East
coast of Ireland in 2007. The results of this testing regime serve to
inform input variables employed in probabilistic modelling of
deterioration for subsequent reliability based analysis to compare the
relative performance of the studied repair options.
Abstract: This paper presents the experimental results of the
investigation of various properties related to the durability and longterm
performance of mortars made of Fly Ash blended cement, FA
and Ordinary Portland cement, OPC. The properties that were
investigated in an experimental program include; equilibration of
specimen in different relative humidity, determination of total
porosity, compressive strength, chloride permeability index, and
electrical resistivity. Fly Ash blended cement mortar specimens
exhibited 10% to 15% lower porosity when measured at equilibrium
conditions in different relative humidities as compared to the
specimens made of OPC mortar, which resulted in 6% to 8% higher
compressive strength of FA blended cement mortar specimens. The
effects of ambient relative humidity during sample equilibration on
porosity and strength development were also studied. For specimens
equilibrated in higher relative humidity conditions, such as 75%, the
total porosity of different mortar specimens was between 35% to 50%
less than the porosity of samples equilibrated in 12% relative
humidity, consequently leading to higher compressive strengths of
these specimens.A valid statistical correlation between values of
compressive strength, porosity and the degree of saturation was
obtained. Measured values of chloride permeability index of fly ash
blended cement mortar were obtained as one fourth to one sixth of
those measured for OPC mortar specimens, which indicates high
resistance against chloride ion penetration in FA blended cement
specimens, hence resulting in a highly durable mortar.
Abstract: This paper represents the results of long term strength of mortar incorporating Rice Husk Ash (RHA). For these work mortar samples were made according to ASTM standard C 109/C. OPC cement was partially replaced by RHA at 0, 10, 15, 20, 25 and 30 percent replacement level. After casting all samples were kept in controlled environment and curing was done up to 90 days. Test of mortar was performed on 3, 7, 28, 90, 365 and 700 days. It is noticed that OPC mortar shows better strength at early age than mortar having RHA but at 90 days and onward the picture is different. At 700 days it is observed that mortar containing 20% RHA shows better result than any other samples.
Abstract: In the modern construction practices, industrial wastes
or by-products are largely used as raw materials in cement and
concrete. These impart many benefits to the environment and bringabout
an economic impact because the cost of waste disposal is
constantly increasing due to strict environmental regulations. It was
reported in literature that the leakage of oil onto concrete element in
older cement grinding unit resulted in concrete with greater resistance
to freezing and thawing. This effect was thought to be similar to
adding an air-entraining chemical admixture to concrete. This paper
presents an investigation on the load deflection behaviour and crack
patterns of reinforced concrete (RC) beams subjected to four point
loading. Ten 120x260x1900 mm beams were cast with 100%
ordinary Portland cement (OPC) concrete, 20% fly ash (FA) and 20%
rice husk ash (RHA) blended cement concrete. 0.15% dosage of
admixtures (used engine oil, new engine oil, and superplasticizer)
was used throughout the experiment. Results show that OPC and
OPC/RHA RC beams containing used engine oil and superplasticizer
exhibit higher capacity, 18-26% than their corresponding control
mix.
Abstract: The Philosophy of Sufficiency Economy, bestowed
by His Majesty the King Bhumibol Adulyadej to the people of
Thailand, highlights a balanced way of living. Three principles of
moderation reasonableness, and immunity, along with the conditions
for morality and knowledge, can be applied to any level of the
society–from an individual to the nation. The Philosophy of
Sufficiency Economy helps address the current development
challenges, which are issues on institutions, environmental
sustainability, human well-being, and the role of the government.
Abstract: A laboratory study on the influence of compactive
effort on expansive black cotton specimens treated with up to 8%
ordinary Portland cement (OPC) admixed with up to 8% bagasse ash
(BA) by dry weight of soil and compacted using the energies of the
standard Proctor (SP), West African Standard (WAS) or
“intermediate” and modified Proctor (MP) were undertaken. The
expansive black cotton soil was classified as A-7-6 (16) or CL using
the American Association of Highway and Transportation Officials
(AASHTO) and Unified Soil Classification System (USCS),
respectively. The 7day unconfined compressive strength (UCS)
values of the natural soil for SP, WAS and MP compactive efforts are
286, 401 and 515kN/m2 respectively, while peak values of 1019,
1328 and 1420kN/m2 recorded at 8% OPC/ 6% BA, 8% OPC/ 2% BA
and 6% OPC/ 4% BA treatments, respectively were less than the
UCS value of 1710kN/m2 conventionally used as criterion for
adequate cement stabilization. The soaked California bearing ratio
(CBR) values of the OPC/BA stabilized soil increased with higher
energy level from 2, 4 and 10% for the natural soil to Peak values of
55, 18 and 8% were recorded at 8% OPC/4% BA 8% OPC/2% BA
and 8% OPC/4% BA, treatments when SP, WAS and MP compactive
effort were used, respectively. The durability of specimens was
determined by immersion in water. Soils treatment at 8% OPC/ 4%
BA blend gave a value of 50% resistance to loss in strength value
which is acceptable because of the harsh test condition of 7 days
soaking period specimens were subjected instead of the 4 days
soaking period that specified a minimum resistance to loss in strength
of 80%. Finally An optimal blend of is 8% OPC/ 4% BA is
recommended for treatment of expansive black cotton soil for use as
a sub-base material.
Abstract: This paper presents a spectroscopic study on doping
of Vanadyl pathalocyanine (VOPc) by [6,6]-phenyl C61 butyric acid
methyl ester (PCBM). The films are characterized by UV/Vis/NIR
spectroscopy. A drastic increase in the absorption coefficient has
been observed with increasing dopant concentration. Optical
properties of VOPc:PCBM films deposited by spin coating technique
were studied in detail. Optical band gap decreased with the PCBM
incorporation in the VOPc film. Optical band gap calculated from the
absorption spectra decreased from 3.32 eV to 3.26 eV with a
variation of 0–75 % of PCBM concentration in the VOPC films.
Abstract: Transcription factor p53 has a powerful tumor
suppressing function that is associated with many cancers. However,
p53 of the molecular weight was higher make the limitation across to
skin or cell membrane. Thymidine dinucleotide (pTT), an
oligonucleotide, can activate the p53 transcription factor. pTT is a
hydrophilic and negative charge oligonucleotide, which delivery in to
cell membrane need an appropriate carrier. The aim of this study was
to improve the bioavailability of the nucleotide fragment, thymidine
dinucleotide (pTT), using elasic liposome carriers to deliver the drug
into the skin. The study demonstrate that dioleoylphosphocholine
(DOPC) incorporated with sodium cholate at molar ratio 1:1 can
archived the particle size about 220 nm. This elastic liposome could
penetration through skin from stratum corneum to whole epidermis by
confocal laser scanning microscopy (CLSM). Moreover, we observed
the the slight increase in generation of p53 by western blot.
Abstract: A lot of Scientific and Engineering problems require the solution of large systems of linear equations of the form bAx in an effective manner. LU-Decomposition offers good choices for solving this problem. Our approach is to find the lower bound of processing elements needed for this purpose. Here is used the so called Omega calculus, as a computational method for solving problems via their corresponding Diophantine relation. From the corresponding algorithm is formed a system of linear diophantine equalities using the domain of computation which is given by the set of lattice points inside the polyhedron. Then is run the Mathematica program DiophantineGF.m. This program calculates the generating function from which is possible to find the number of solutions to the system of Diophantine equalities, which in fact gives the lower bound for the number of processors needed for the corresponding algorithm. There is given a mathematical explanation of the problem as well. Keywordsgenerating function, lattice points in polyhedron, lower bound of processor elements, system of Diophantine equationsand : calculus.
Abstract: The purpose of this paper is to investigate the
durability of cement mortar in presence of Rice Husk Ash (RHA).
The strength and durability of mortar with different replacement
level (0%, 10%, 15%, 20%, 25% and 30%) of Ordinary Portland
Cement (OPC) by RHA is investigated here. RHA was
manufactured from an uncontrolled burning process. Test samples
were prepared with river sand of FM 2.73. Samples were kept in
controlled environment up to test time. The results show that
addition of RHA was shown better results for 20% replacement
level than OPC at 90 days. In durability test all samples passed for
20 cycles except 25% and 30% replacement level.