Abstract: This paper presents a spectroscopic study on doping
of Vanadyl pathalocyanine (VOPc) by [6,6]-phenyl C61 butyric acid
methyl ester (PCBM). The films are characterized by UV/Vis/NIR
spectroscopy. A drastic increase in the absorption coefficient has
been observed with increasing dopant concentration. Optical
properties of VOPc:PCBM films deposited by spin coating technique
were studied in detail. Optical band gap decreased with the PCBM
incorporation in the VOPc film. Optical band gap calculated from the
absorption spectra decreased from 3.32 eV to 3.26 eV with a
variation of 0–75 % of PCBM concentration in the VOPC films.
Abstract: Two different superhydrophobic surfaces were
elaborated and their oil repellency behavior was evaluated using
several liquid with different surface tension. A silicone rubber/SiO2
nanocomposite coated (A) on aluminum substrate by “spin-coating"
and the sample B was an anodized aluminum surface covered by
Teflon-like coating. A high static contact angle about ∼162° was
measured for two prepared surfaces on which the water droplet rolloff.
Scanning electron microscopy (SEM) showed the presence of
micro/nanostructures for both sample A and B similar to that of lotus
leaf.
However the sample A presented significantly different behaviour
of wettability against the low surface tension liquid. Sample A has
been wetted totally by oil (dodecan) droplet while sample B showed
oleophobic behaviour. Oleophobic property of Teflon like coating
can be contributed to the presence of CF2 and CF3 functional group
which was shown by XPS analysis.
Abstract: In recent times there has been a growing interest in the
development of quasi-two-dimensional niobium pentoxide (Nb2O5)
as a semiconductor for the potential electronic applications such as
capacitors, filtration, dye-sensitised solar cells and gas sensing
platforms. Therefore once the purpose is established, Nb2O5 can be
prepared in a number of nano- and sub-micron-structural
morphologies that include rods, wires, belts and tubes. In this study
films of Nb2O5 were prepared on gold plated silicon substrate using
spin-coating technique and subsequently by mechanical exfoliation.
The reason this method was employed was to achieve layers of less
than 15nm in thickness. The sintering temperature of the specimen
was 800oC. The morphology and structural characteristics of the
films were analyzed by Atomic Force Microscopy (AFM), Raman
Spectroscopy, X-ray Photoelectron Spectroscopy (XPS).