TBC for Protection of Al Alloy Aerospace Component

The use of a conventional air plasma-sprayed thermal barrier coating (TBC) and a porous, functionally graded TBC as a thermal insulator for Al7075 alloy was explored. A quench test at 1200°C employing fast heating and cooling rates was setup to represent a dynamic thermal condition of an aerospace component. During the test, coated samples were subjected the ambient temperature of 1200°C for a very short time. This was followed by a rapid drop in temperature resulting in cracking of the coatings. For the conventional TBC, it was found that the temperature of the Al7075 substrate decreases with the increase in the ZrO2 topcoat thickness. However, at the topcoat thickness of 1100 µm, large horizontal cracks can be observed in the topcoat and at the topcoat thickness of 1600 µm, the topcoat delaminate during cooling after the quench test. The porous, functionally graded TBC with 600 µm thick topcoat, on the other hand, was found to be as effective at reducing the substrate temperature as the conventional TBC with 1100 µm thick topcoat. The maximum substrate temperature is about 213°C for the former and 208°C for the latter when a heating rate of 38°C/s was used. When the quench tests were conducted with a faster heating rate of 128°C/s, the Al7075 substrate heat up faster with a reduction in the maximum substrate temperatures. The substrate temperatures dropped from 297 to 212°C for the conventional TBC and from 213 to 155°C for the porous TBC, both with 600 µm thick topcoat. Segmentation cracks were observed in both coating after the quench test.





References:
[1] P. E. Magnusen, R. J. Bucci, A. J. Hinkle, J. R. Brockenbrough and H. J.
Konish, “Analysis and prediction of microstructural effects on long-term
fatigue performance of an aluminum aerospace alloy”, Int. J. Fatigue
Vol. 19, (1997) S275–S283.
[2] M. S. Kenevisi, S. M. Mousavi Khoie, “An investigation on
microstructure and mechanical properties of Al7075 to Ti–6Al–4V
Transient Liquid Phase (TLP) bonded joint”, Materials and Design 38
(2012) 19–25.
[3] J. Ren, Y. Li and T. Feng, “Microstructure characteristics in the interface
zone of Ti/Al diffusion bonding”, Materials Letters, Volume 56, Issue 5,
(2002) 647-652.
[4] K. Dehghani, A. Nekahi, M. Ali and M. Mirzaie, “Optimizing the bake
hardening behavior of Al7075 using response surface methodology”,
Materials and Design 31 (2010) 1768–1775.
[5] R. McPherson, “A review of microstructure and properties of plasma
sprayed ceramic coatings”, Surface and Coatings Technology, Volumes
39–40, Part 1, (1989) 173-181.
[6] P. G. Klemens, M. Gell, “Thermal conductivity of thermal barrier
coatings”, Materials Science and Engineering A245 (1998) 143–149.
[7] F. Cernuschi, S. Ahmaniemi, P. Vuoristo, T. Mäntylä, “Modelling of
thermal conductivity of porous materials: application to thick thermal
barrier coatings”, Journal of the European Ceramic Society, Volume 24,
Issue 9, (2004) 2657-2667.
[8] H. Zhao, F. Yu, T.D. Bennett and H. N. G. Wadley, “Morphology and
thermal conductivity of yttria-stabilized zirconia coatings”, Acta
Materialia, Volume 54, Issue 19, (2006) 5195-5207.
[9] J. Zhang, V. Desai, “Determining thermal conductivity of plasma
sprayed TBC by electrochemical impedance spectroscopy”, Surface and
Coatings Technology, Volume 190, Issue 1, ( 2005) 90-97
[10] E. F. Rejda, D. F. Socie and T. Itoh, “Deformation behavior of plasmasprayed
thick thermal barrier coatings”, Surface and Coatings
Technology 113 (1999) 218–226.
[11] S. Ahmaniemi, P. Vuoristo, T. Mantyla, C. Gualco, A. Bonadei, R. Di
Maggio, “Thermal cycling resistance of modified thick thermal barrier
coatings”, Surface & Coatings Technology 190 (2005) 378– 387.
[12] F. Cernuschi, S. Ahmaniemi, P. Vuoristo, T. Mantyla, “Modelling of
thermal conductivity of porous materials: application to thick thermal
barrier coatings”, Journal of the European Ceramic Society 24 (2004)
2657–2667.
[13] A. Kulkarni, A. Vaidya, A. Goland, S. Sampath, H. Herman,
“Processing effects on porosity-property correlations in plasma sprayed
yttria-stabilized zirconia coatings”, Materials and Engineering A359
(2003) 100-111.
[14] S. Ahmaniemi, P. Vuoristo, T. Mantyla, F. Cernuschi, L. Lorenzoni,
“Modified thick thermal barrier coatings: Thermophysical
characterization”, Journal of the European Ceramic Society 24 (2004)
2669–2679.
[15] A. M. Khoddami, A. Sabour, S. M. M. Hadavi, “Microstructure
formation in thermally-sprayed duplex and functionally graded
NiCrAlY/Yttria-Stabilized Zirconia coatings”, Surface & Coatings
Technology 201 (2007) 6019–6024.
[16] Z. L. Dong, K. A. Khor, Y. W. Gu, “Microstructure formation in
plasma-sprayed functionally graded NiCoCrAlY/yttria-stabilized
zirconia coatings”, Surface and Coatings Technology 114 (1999) 181–
186.
[17] N. R. Shankar, C. C. Berndt and H. Herman, "Failure And Acoustic
Emission Response Of Plasma Sprayed ZrO2-8wt.%Y2O3",
Ceram.Eng.Sci.Proc., 3(9-10) (1982) 772-792.
[18] K. A. Khor, Z. L. Dong and Y. W. Gu, “Influence of oxide mixtures on
mechanical properties of plasma sprayed functionally graded coating”,
Thin Solid Films, Volume 368, Issue 1, ( 2000) 86-92.
[19] W. Shen, F. C. Wang, Q. B. Fan, Z. Ma, X. W. Yang, “Finite element
simulation of tensile bond strength of atmospheric plasma spraying
thermal barrier coatings”, Surface and Coatings Technology, Volume
205, Issues 8–9 ( 2011) 2964–2969.
[20] O. Bleeck, D. Munz, W. Schaller and Y. Y Yang, “Effect of a graded
interlayer on the stress intensity factor of cracks in a joint under thermal
loading”, Engineering Fracture Mechanics, Volume 60, Issues 5–6,
(1998) 615-623.
[21] B. Ercan, K. J. Bowman, R. W. Trice, H. Wang and W. Porter, “Effect
of initial powder morphology on thermal and mechanical properties of
stand-alone plasma-sprayed 7 wt.% Y2O3–ZrO2 coatings”, Materials
Science and Engineering A 435–436 (2006) 212–220.