Abstract: Food is widely packaged with plastic materials to
prevent microbial contamination and spoilage. Ionizing radiation is
widely used to sterilize the food-packaging materials. Sterilization by
γ-radiation causes degradation such as embrittlement, stiffening,
softening, discoloration, odour generation, and decrease in molecular
weight. Many antioxidants can prevent γ-degradation but most of
them are toxic. The migration of antioxidants to its environment
gives rise to major concerns in case of food packaging plastics. In
this attempt, we have aimed to utilize synergistic mixtures of
stabilizers which are approved for food-contact applications.
Ethylene-propylene-diene terpolymer has been melt-mixed with
hindered amine stabilizers (HAS), phenolic antioxidants and organophosphites
(hydroperoxide decomposer). Results were discussed by
comparing the stabilizing efficiency of mixtures with and without
phenol system. Among phenol containing systems where we mostly
observed discoloration due to the oxidation of hindered phenol, the
combination of secondary HAS, tertiary HAS, organo-phosphite and
hindered phenol exhibited improved stabilization efficiency than
single or binary additive systems. The mixture of secondary HAS and
tertiary HAS, has shown antagonistic effect of stabilization.
However, the combination of organo-phosphite with secondary HAS,
tertiary HAS and phenol antioxidants have been found to give
synergistic even at higher doses of Gamma-irradiation. The effects
have been explained through the interaction between the stabilizers.
After γ-irradiation, the consumption of oligomeric stabilizer
significantly depends on the components of stabilization mixture. The
effect of the organo-phosphite antioxidant on the overall stability has
been discussed.
Abstract: This paper reveals the interaction between hydrogen
and surface stress in austenitic stainless steel by X-ray diffraction
stress measurement and thermal desorption analysis before and after
being charged with hydrogen. The surface residual stress was varied
by surface finishing using several disc polishing agents. The obtained
results show that the residual stress near surface had a significant
effect on hydrogen absorption behavior, that is, tensile residual stress
promoted the hydrogen absorption and compressive one did opposite.
Also, hydrogen induced equi-biaxial stress and this stress has a linear
correlation with hydrogen content.
Abstract: Concerns on corrosion and effective coating
protection of double hull tankers and bulk carriers in service have
been raised especially in water ballast tanks (WBTs). Test
protocols/methodologies specifically that which is incorporated in the
International Maritime Organisation (IMO), Performance Standard
for Protective Coatings for Dedicated Sea Water ballast tanks (PSPC)
are being used to assess and evaluate the performance of the coatings
for type approval prior to their application in WBTs. However, some
of the type approved coatings may be applied as very thick films to
less than ideally prepared steel substrates in the WBT. As such films
experience hygrothermal cycling from operating and environmental
conditions, they become embrittled which may ultimately result in
cracking. This embrittlement of the coatings is identified as an
undesirable feature in the PSPC but is not mentioned in the test
protocols within it. There is therefore renewed industrial research
aimed at understanding this issue in order to eliminate cracking and
achieve the intended coating lifespan of 15 years in good condition.
This paper will critically review test protocols currently used for
assessing and evaluating coating performance, particularly the IMO
PSPC.
Abstract: We investigated the effects of the additions of Zr and other alloying elements on the mechanical properties and microstructure in Cr-Mo plastic mold steels. The addition of alloying elements changed the microstructure of the normalized samples from the upper bainite to lower bainite due to the increased hardenability. The tempering temperature influenced the strength and hardness values, especially the phenomenon of 350oC embrittlement was observed. The alloy additions of Cr, Mo, and V improved the resistance to the temper embrittlement. The addition of Zr improved the tensile strength and yield strength, but the impact energy was sharply decreased. It may be caused by the formation of Zr-MnS inclusion and rectangular-shaped Zr inclusion due to the Zr addition.
Abstract: Hydrogen diffusion is the main problem for corrosion fatigue in corrosive environment. In order to analyze the phenomenon, it is needed to understand their behaviors specially the hydrogen behavior during the diffusion. So, Hydrogen embrittlement and prediction its behavior as a main corrosive part of the fractions, needed to solve combinations of different equations mathematically. The main point to obtain the equation, having knowledge about the source of causing diffusion and running the atoms into materials, called driving force. This is produced by either gradient of electrical or chemical potential. In this work, we consider the gradient of chemical potential to obtain the property equation. In diffusion of atoms, some of them may be trapped but, it could be ignorable in some conditions. According to the phenomenon of hydrogen embrittlement, the thermodynamic and chemical properties of hydrogen are considered to justify and relate them to fracture mechanics. It is very important to get a stress intensity factor by using fugacity as a property of hydrogen or other gases. Although, the diffusive behavior and embrittlement event are common and the same for other gases but, for making it more clear, we describe it for hydrogen. This considering on the definite gas and describing it helps us to understand better the importance of this relation.
Abstract: In this study, the hydrogen transport phenomenon was
numerically evaluated by using hydrogen-enhanced localized
plasticity (HELP) mechanisms. Two dominant governing equations,
namely, the hydrogen transport model and the elasto-plastic model,
were introduced. In addition, the implicitly formulated equations of
the governing equations were implemented into ABAQUS UMAT
user-defined subroutines. The simulation results were compared to
published results to validate the proposed method.
Abstract: In pressure vessels contain hydrogen, the role of
hydrogen will be important because of hydrogen cracking problem. It
is difficult to predict what is happened in metallurgical field spite of a
lot of studies have been searched. The main role in controlling the
mass diffusion as driving force is related to stress. In this study, finite
element analysis is implemented to estimate material-s behavior
associated with hydrogen embrittlement. For this purpose, one model
of a pressure vessel is introduced that it has definite boundary and
initial conditions. In fact, finite element is employed to solve the
sequentially coupled mass diffusion with stress near a crack front in a
pressure vessel. Modeling simulation intergrarnular fracture of AISI
4135 steel due to hydrogen is investigated. So, distribution of
hydrogen and stress are obtained and they indicate that their
maximum amounts occur near the crack front. This phenomenon is
happened exactly the region between elastic and plastic field.
Therefore, hydrogen is highly mobile and can diffuse through crystal
lattice so that this zone is potential to trap high volume of hydrogen.
Consequently, crack growth and fast fracture will be happened.
Abstract: Environment-assisted cracking (EAC) is one of the most serious causes of structural failure over a broad range of industrial applications including offshore structures. In EAC condition there is not a definite relation such as Paris equation in Linear Elastic Fracture Mechanics (LEFM). According to studying and searching a lot what the researchers said either a material has contact with hydrogen or any other corrosive environment, phenomenon of electrical and chemical reactions of material with its environment will be happened. In the literature, there are many different works to consider fatigue crack growing and solve it but they are experimental works. Thus, in this paper, authors have an aim to evaluate mathematically the pervious works in LEFM. Obviously, if an environment is more sour and corrosive, the changes of stress intensity factor is more and the calculation of stress intensity factor is difficult. A mathematical relation to deal with the stress intensity factor during the diffusion of sour environment especially hydrogen in a marine pipeline is presented. By using this relation having and some experimental relation an analytical formulation will be presented which enables the fatigue crack growth and critical crack length under cyclic loading to be predicted. In addition, we can calculate KSCC and stress intensity factor in the pipeline caused by EAC.