Abstract: The structures obtained with the use of sandwich
technologies combine low weight with high energy absorbing
capacity and load carrying capacity. Hence, there is a growing and
markedly interest in the use of sandwiches with aluminum foam core
because of very good properties such as flexural rigidity and energy
absorption capability. In the current investigation, the static threepoint
bending tests were carried out on the sandwiches with
aluminum foam core and glass fiber reinforced polymer (GFRP)
skins at different values of support span distances aiming the analyses
of their flexural performance. The influence of the core thickness and
the GFRP skin type was reported in terms of peak load and energy
absorption capacity. For this purpose, the skins with two different
types of fabrics which have same thickness value and the aluminum
foam core with two different thicknesses were bonded with a
commercial polyurethane based flexible adhesive in order to combine
the composite sandwich panels. The main results of the bending tests
are: force-displacement curves, peak force values, absorbed energy,
collapse mechanisms and the effect of the support span length and
core thickness. The results of the experimental study showed that the
sandwich with the skins made of S-Glass Woven fabrics and with the
thicker foam core presented higher mechanical values such as load
carrying and energy absorption capacities. The increment of the
support span distance generated the decrease of the mechanical
values for each type of panels, as expected, because of the inverse
proportion between the force and span length. The most common
failure types of the sandwiches are debonding of the lower skin and
the core shear. The obtained results have particular importance for
applications that require lightweight structures with a high capacity
of energy dissipation, such as the transport industry (automotive,
aerospace, shipbuilding and marine industry), where the problems of
collision and crash have increased in the last years.
Abstract: An experimental and analytical research on shear
buckling of a comparably large polymer composite I-section is
presented. It is known that shear buckling load of a large span
composite beam is difficult to determine experimentally. In order to
sensitively detect shear buckling of the tested I-section, twenty strain
rosettes and eight displacement sensors were applied and attached on
the web and flange surfaces. The tested specimen was a pultruded
composite beam made of vinylester resin, E-glass, carbon fibers and
micro-fillers. Various coupon tests were performed before the shear
buckling test to obtain fundamental material properties of the Isection.
An asymmetric four-point bending loading scheme was
utilized for the shear test. The loading scheme resulted in a high shear
and almost zero moment condition at the center of the web panel. The
shear buckling load was successfully determined after analyzing the
obtained test data from strain rosettes and displacement sensors. An
analytical approach was also performed to verify the experimental
results and to support the discussed experimental program.
Abstract: This study presented to reduce earthquake damage and
emergency rehabilitation of critical structures such as schools, hightech
factories, and hospitals due to strong ground motions associated
with climate changes. Regarding recent trend, a strong earthquake
causes serious damage to critical structures and then the critical
structure might be influenced by sequence aftershocks (or tsunami)
due to fault plane adjustments. Therefore, in order to improve seismic
performance of critical structures, retrofitted or strengthening study
of the structures under aftershocks sequence after emergency
rehabilitation of the structures subjected to strong earthquakes is
widely carried out. Consequently, this study used composite material
for emergency rehabilitation of the structure rather than concrete and
steel materials because of high strength and stiffness, lightweight,
rapid manufacturing, and dynamic performance. Also, this study was
to develop or improve the seismic performance or seismic retrofit of
critical structures subjected to strong ground motions and earthquake
aftershocks, by utilizing GFRP-Corrugated Infill Panels (GCIP).
Abstract: ABC classification is widely used by managers for
inventory control. The classical ABC classification is based on Pareto
principle and according to the criterion of the annual use value only.
Single criterion classification is often insufficient for a closely
inventory control. Multi-criteria inventory classification models have
been proposed by researchers in order to consider other important
criteria. From these models, we will consider a specific model in
order to make a sensitive analysis on the composite score calculated
for each item. In fact, this score, based on a normalized average
between a good and a bad optimized index, can affect the ABC-item
classification. We will focus on items differently assigned to classes
and then propose a classification compromise.
Abstract: An Australian manufacturer has fabricated an
innovative GFRP sandwich panel made from E-glass fiber skin and a
modified phenolic core for structural applications. Debonding, which
refers to separation of skin from the core material in composite
sandwiches, is one of the most common types of damage in
composites. The presence of debonding is of great concern because it
not only severely affects the stiffness but also modifies the dynamic
behaviour of the structure. Generally it is seen that the majority of
research carried out has been concerned about the delamination of
laminated structures whereas skin-core debonding has received
relatively minor attention. Furthermore it is observed that research
done on composite slabs having multiple skin-core debonding is very
limited. To address this gap, a comprehensive research investigating
dynamic behaviour of composite panels with single and multiple
debonding is presented. The study uses finite-element modelling and
analyses for investigating the influence of debonding on free
vibration behaviour of single and multilayer composite sandwich
panels. A broad parametric investigation has been carried out by
varying debonding locations, debonding sizes and support conditions
of the panels in view of both single and multiple debonding.
Numerical models were developed with Strand7 finite element
package by innovatively selecting the suitable elements to diligently
represent their actual behavior. Three-dimensional finite element
models were employed to simulate the physically real situation as
close as possible, with the use of an experimentally and numerically
validated finite element model. Comparative results and conclusions
based on the analyses are presented. For similar extents and locations
of debonding, the effect of debonding on natural frequencies appears
greatly dependent on the end conditions of the panel, giving greater
decrease in natural frequency when the panels are more restrained.
Some modes are more sensitive to debonding and this sensitivity
seems to be related to their vibration mode shapes. The fundamental
mode seems generally the least sensitive mode to debonding with
respect to the variation in free vibration characteristics. The results
indicate the effectiveness of the developed three dimensional finite
element models in assessing debonding damage in composite
sandwich panels.
Abstract: The main objective of incorporating natural fibers such as Henequen microfibers (NF) into the High Density Polyethylene (HDPE) polymer matrix is to reduce the cost and to enhance the mechanical as well as other properties. The Henequen microfibers were chopped manually to 5-7mm in length and added into the polymer matrix at the optimized concentration of 8 wt %. In order to facilitate the link between Henequen microfibers (NF) and HDPE matrix, coupling agent such as Glycidoxy (Epoxy) Functional Methoxy Silane (GPTS) at various concentrations from 0.1%, 0.3%, 0.5%, 0.7%, 0.9% and 1% by weight to the total fibers were added. The tensile strength of the composite increased marginally while % elongation at break of the composites decreased with increase in silane loading by wt %. Tensile modulus and stiffness observed increased at 0.9 wt % GPTS loading. Flexural as well as impact strength of the composite decreased with increase in GPTS loading by weight %. Dielectric strength of the composite also found increased marginally up to 0.5wt % silane loading and thereafter remained constant.
Abstract: Chrome tannery wastewater causes serious environmental hazard due to its high pollution potential. As a result, rigorous treatment is necessary for abatement of pollution from this type of wastewater. There are many research studies on chrome tannery wastewater treatment in the field of physical, chemical, and biological methods. In general, biological treatment process is found ineffective for direct application because of adverse effects by toxic chromium, sulphide, chloride etc. However, biological methods were employed mainly for a few sub processes generating significant amount of organic matter and without chromium, chlorides etc. In this context the present paper reviews the characteristics feature and pollution potential of wastewater generated from chrome tannery units and treatment of the same. The different biological processes used earlier and their chronological development for treatment of the chrome tannery wastewater are thoroughly reviewed in this paper. In this regard, the scope of hybrid bioreactor - an advanced technology option has also been explored, as this kind of treatment is well suited for the wastewater having inhibitory substances.
Abstract: A chromium-loaded ash originating from incineration of tannery sludge under anoxic conditions was mixed with low grade soda-lime glass powder coming from commercial glass bottles. The relative weight proportions of ash over glass powder tested were 30/70, 40/60 and 50/50. The solid mixtures, formed in green state compacts, were sintered at the temperature range of 800o C up to 1200o C. The resulting products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDXS) and micro-indentation. The above methods were employed to characterize the various phases, microstructure and hardness of the produced materials. Thermal treatment at 800o C and 1000o C produced opaque ceramic products composed of a variety of chromium-containing and chromium-free crystalline phases. Thermal treatment at 1200o C gave rise to composite products, where only chromium-containing crystalline phases were detected. Hardness results suggest that specific products are serious candidates for structural applications.
Abstract: An innovative flooring underlayment was produced
and tested. The composite system is made of common OSB boards
and a layer of eco-friendly non-cement gypsum based material
(GeoGypTM). It was found that the shear bond between the two
materials is sufficient to secure the composite interaction between the
two. The very high compressive strength and relatively high tensile
strength of the non-cement based component together with its high
modulus of elasticity provides enough strength and stiffness for the
composite product to cover wider spacing between the joists. The
initial findings of this study indicate that with joist spacing as wide as
800 mm, the flooring system provides enough strength without
compromising the serviceability requirements of the building codes.
Abstract: Forward Osmosis (FO) polyamide thin-film composite
membranes have been prepared by interfacial polymerization using
commercial UF polyethersulfoneas membrane support. Different
interfacial polymerization times (10s, 30s and 60s) in the organic
solution containing trimesoyl chloride (TMC) at constant m-phenylenediamine
(MPD) concentration (2% w/v) were studied. The
synthesized polyamide membranes then tested for treatment of
natural organic matter (NOM) and compared to commercial Cellulose
TriAcetate (CTA) membrane. It was found that membrane prepared
with higher reaction time (30s and 60s) exhibited better membrane
performance (flux and humic acid removal) over commercial CTA
membrane.
Abstract: Verification of vented wooden façade system with
bonded joints is presented in this paper. The potential of bonded
joints is studied and described in more detail. The paper presents the results of an experimental and theoretical research about the effects of freeze cycling on the bonded joint. For the purpose of tests spruce
timber profiles were chosen for the load bearing substructure. Planks from wooden plastic composite and Siberian larch are representing facade cladding. Two types of industrial polyurethane adhesives intended for structural bonding were selected. The article is focused on the preparation as well as on the subsequent curing and conditioning of test samples. All test samples were subjected to 15 cycles that represents sudden temperature changes, i.e. immersion in a water bath at (293.15 ± 3) K for 6 hours and subsequent freezing to (253.15 ± 2) K for 18 hours. Furthermore, the retention of bond strength between substructure and cladding wastested and strength in shear was determined under tensile stress.Research data indicate that little, if any, damage to the bond results from freezingcycles. Additionally, the suitability of selected group of adhesives in combination with timber substructure was confirmed.
Abstract: Dental porcelain composites reinforced and toughened
by 20 wt.% tetragonal zirconia (3Y-TZP) were processed by hot
pressing at 1000°C. Two types of particles were tested: yttriastabilized
zirconia (ZrO2–3%Y2O3) agglomerates and pre-sintered
yttria-stabilized zirconia (ZrO2–3%Y2O3) particles. The composites
as well as the reinforcing particles were analyzed by the means of
optical and Scanning Electron Microscopy (SEM), Energy Dispersion
Spectroscopy (EDS) and X-Ray Diffraction (XRD). The mechanical
properties were obtained by the transverse rupture strength test. Wear
tests were also performed on the composites and monolithic
porcelain. The best mechanical results were displayed by the
porcelain reinforced with the pre-sintered ZrO2–3%Y2O3
agglomerates.
Abstract: Nanofibers of PVA /nickel nitrate/silica/alumina
izopropoxide/boric acid composite were prepared by using sol-gel
processing and electrospinning technique. By high temperature
calcinations of the above precursor fibers, nanofibers of
NiO/Al2O3/B2O3/SiO2 composite with diameters about 500 nm
could be successfully obtained. The fibers were characterized by
XRD and SEM analyses.
Abstract: Problems insulation of building structures is often
closely connected with the problem of moisture remediation. In the
case of historic buildings or if only part of the redevelopment of
envelope of structures, it is not possible to apply the classical external
thermal insulation composite systems. This application is mostly
effective thermal insulation plasters with high porosity and controlled
capillary properties which assures improvement of thermal properties
construction, its diffusion openness towards the external environment
and suitable treatment capillary properties of preventing the
penetration of liquid moisture and salts thereof toward the outer
surface of the structure.
With respect to the current trend of reducing the energy
consumption of building structures and reduce the production of CO2
is necessary to develop capillary-active materials characterized by
their low density, low thermal conductivity while maintaining good
mechanical properties. The aim of researchers at the Faculty of Civil
Engineering, Brno University of Technology is the development and
study of hygrothermal behaviour of optimal materials for thermal
insulation and rehabilitation of building structures with the possible
use of alternative, less energy demanding binders in comparison with
conventional, frequently used binder, which represents cement.
The paper describes the evaluation of research activities aimed at
the development of thermal insulation and repair materials using
lightweight aggregate and alternative binders such as metakaolin and
finely ground fly ash.
Abstract: The problem of toughening in brittle materials
reinforced by fibers is complex, involving all of the mechanical
properties of fibers, matrix and the fiber/matrix interface, as well as
the geometry of the fiber. Development of new numerical methods
appropriate to toughening simulation and analysis is necessary. In
this work, we have performed simulations and analysis of toughening
in brittle matrix reinforced by randomly distributed fibers by means
of the discrete elements method. At first, we put forward a
mechanical model of toughening contributed by random fibers. Then
with a numerical program, we investigated the stress, damage and
bridging force in the composite material when a crack appeared in the
brittle matrix. From the results obtained, we conclude that: (i) fibers
of high strength and low elasticity modulus are beneficial to
toughening; (ii) fibers of relatively high elastic modulus compared to
the matrix may result in substantial matrix damage due to spalling
effect; (iii) employment of high-strength synthetic fibers is a good
option for toughening. We expect that the combination of the discrete
element method (DEM) with the finite element method (FEM) can
increase the versatility and efficiency of the software developed. The
present work can guide the design of ceramic composites of high
performance through the optimization of the parameters.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: Machining of hard materials is a recent technology for
direct production of work-pieces. The primary challenge in
machining these materials is selection of cutting tool inserts which
facilitates an extended tool life and high-precision machining of the
component. These materials are widely for making precision parts for
the aerospace industry. Nickel-based alloys are typically used in
extreme environment applications where a combination of strength,
corrosion resistance and oxidation resistance material characteristics
are required. The present paper reports the theoretical and
experimental investigations carried out to understand the influence of
machining parameters on the response parameters. Considering the
basic machining parameters (speed, feed and depth of cut) a study has
been conducted to observe their influence on material removal rate,
surface roughness, cutting forces and corresponding tool wear.
Experiments are designed and conducted with the help of Central
Composite Rotatable Design technique. The results reveals that for a
given range of process parameters, material removal rate is favorable
for higher depths of cut and low feed rate for cutting forces. Low feed
rates and high values of rotational speeds are suitable for better finish
and higher tool life.
Abstract: In the present work, the dielectric properties of
Epoxy/MWCNT-muscovite HYBRID and MIXED composites based
on a ratio 30:70 were studied. The multi-wall carbon nanotubes
(MWCNT) were prepared using two methods: (a) MWCNTmuscovite
hybrids were synthesised by chemical vapour deposition
(CVD) and (b) physically mixing muscovite with MWCNT. The
effects of different preparation of the composites and filler loading
were evaluated. It was revealed that the dielectric constants of
HYBRID epoxy composites are slightly higher than MIXED epoxy
composites. It was also indicated that the dielectric constant increased
by increasing the MWCNT filler loading.
Abstract: An experimental study was performed to investigate
the behavior and strength of proposed technique to connect
reinforced concrete (RC) beam to steel or composite columns. This
approach can practically be used in several types of building
construction. In this technique, the main beam of the frame consists
of a transfer part (part of beam; Tr.P) and a common reinforcement
concrete beam. The transfer part of the beam is connected to the
column, whereas the rest of the beam is connected to the transfer part
from each side. Four full-scale beam-column connections were tested
under static loading. The test parameters were the length of the
transfer part and the column properties. The test results show that
using of the transfer part technique leads to modify the deformation
capabilities for the RC beam and hence it increases its resistance
against failure. Increase in length of the transfer part did not
necessarily indicate an enhanced behavior. The test results contribute
to the characterization of the connection behavior between RC beam -
steel column and can be used to calibrate numerical models for the
simulation of this type of connection.
Abstract: Chemical vapor deposition (CVD) diamond coated
cutting tool has excellent cutting performance, it is the most ideal tool
for the processing of nonferrous metals and alloys, composites,
nonmetallic materials and other difficult-to-machine materials
efficiently and accurately. Depositing CVD diamond coating on the
cemented carbide with high cobalt content can improve its toughness
and strength, therefore, it is very important to research on the
preparation technology and cutting properties of CVD diamond coated
cemented carbide cutting tool with high cobalt content. The
preparation technology of boron-doped diamond (BDD) coating has
been studied and the coated drills were prepared. BDD coating were
deposited on the drills by using the optimized parameters and the SEM
results show that there are no cracks or collapses in the coating.
Cutting tests with the prepared drills against the silumin and aluminum
base printed circuit board (PCB) have been studied. The results show
that the wear amount of the coated drill is small and the machined
surface has a better precision. The coating does not come off during
the test, which shows good adhesion and cutting performance of the
drill.