Abstract: In the present work, fly ash geopolymer based
composites including polyester (PES) waste were studied. Specimens
of three compositions were prepared: (a) fly ash geopolymer with 5%
PES waste; (b) fly ash geopolymer mortar with 5% PES waste; (c) fly
ash geopolymer mortar with 6.25% PES waste. Compressive and
bending strength measurements, water absorption test and
determination of thermal conductivity coefficient were performed.
The results showed that the addition of sand in a mixture of
geopolymer with 5% PES content led to higher compressive strength,
while it increased water absorption and reduced thermal conductivity
coefficient. The increase of PES addition in geopolymer mortars
resulted in a more dense structure, indicated by the increase of
strength and thermal conductivity and the decrease of water
absorption.
Abstract: Thin-walled elements with a matrix set on a base of
high-valuable Portland cement with dispersed reinforcement from
alkali-resistant glass fibres are used in a range of applications as
claddings of buildings and infrastructure constructions as well as
various architectural elements of residential buildings.
Even though their elementary thickness and therefore total weight
is quite low, architects and building companies demand on even
further decreasing of the bulk density of these fibre-cement elements
for the reason of loading elimination of connected superstructures
and easier assembling in demand conditions.
By the means of various kinds of light-weight aggregates it is
possible to achieve light-weighing of these composite elements.
From the range of possible fillers with different material properties
granulated expanded glass worked the best.
By the means of laboratory testing an effect of two fillers based on
expanded glass on the fibre reinforced cement composite was
verified.
Practical applicability was tested in the production of commonly
manufactured glass fibre reinforced concrete elements, such as
channels for electrical cable deposition, products for urban equipment
and especially various cladding elements.
Even though these are not structural elements, it is necessary to
evaluate also strength characteristics and resistance to environment
for their durability in certain applications.
Abstract: In this work, we report, a systematic study on the
structural and optical properties of Pr-doped ZnO nanostructures and
PVA:Zn98Pr2O polymer matrix nanocomposites free standing films.
These particles are synthesized through simple wet chemical route
and solution casting technique at room temperature, respectively.
Structural studies carried out by X-ray diffraction method confirm
that the prepared pure ZnO and Pr doped ZnO nanostructures are in
hexagonal wurtzite structure and the microstrain is increased upon
doping. TEM analysis reveals that the prepared materials are in sheet
like nature. Absorption spectra show free excitonic absorption band
at 370 nm and red shift for the Pr doped ZnO nanostructures. The
PVA:Zn98Pr2O composite film exhibits both free excitonic and PVA
absorption bands at 282 nm. Fourier transform infrared spectral
studies confirm the presence of A1 (TO) and E1 (TO) modes of Zn-O
bond vibration and the formation of polymer composite materials.
Abstract: Poly vinyl acetate (PVA)-based titania (TiO2)–carbon
nanotube composite nanofibers (PVA-TCCNs) with various
PVA-to-solvent ratios and PVA-based TiO2 composite nanofibers
(PVA-TN) were synthesized using an electrospinning process,
followed by thermal treatment. The photocatalytic activities of these
nanofibers in the degradation of airborne monocyclic aromatics under
visible-light irradiation were examined. This study focuses on the
application of these photocatalysts to the degradation of the target
compounds at sub-part-per-million indoor air concentrations. The
characteristics of the photocatalysts were examined using scanning
electron microscopy, X-ray diffraction, ultraviolet-visible
spectroscopy, and Fourier-transform infrared spectroscopy. For all the
target compounds, the PVA-TCCNs showed photocatalytic
degradation efficiencies superior to those of the reference PVA-TN.
Specifically, the average photocatalytic degradation efficiencies for
benzene, toluene, ethyl benzene, and o-xylene (BTEX) obtained using
the PVA-TCCNs with a PVA-to-solvent ratio of 0.3 (PVA-TCCN-0.3)
were 11%, 59%, 89%, and 92%, respectively, whereas those observed
using PVA-TNs were 5%, 9%, 28%, and 32%, respectively.
PVA-TCCN-0.3 displayed the highest photocatalytic degradation
efficiency for BTEX, suggesting the presence of an optimal
PVA-to-solvent ratio for the synthesis of PVA-TCCNs. The average
photocatalytic efficiencies for BTEX decreased from 11% to 4%, 59%
to 18%, 89% to 37%, and 92% to 53%, respectively, when the flow
rate was increased from 1.0 to 4.0 L min1. In addition, the average
photocatalytic efficiencies for BTEX increased 11% to ~0%, 59% to
3%, 89% to 7%, and 92% to 13%, respectively, when the input
concentration increased from 0.1 to 1.0 ppm. The prepared
PVA-TCCNs were effective for the purification of airborne aromatics
at indoor concentration levels, particularly when the operating
conditions were optimized.
Abstract: Today, the pollution due to non-degradable material
such as plastics, has led to studies about the development of
environmental-friendly material. Because of biodegradability
obtained from natural sources, polylactid acid (PLA) and ijuk fiber
are interesting to modify into a composite. This material is also
expected to reduce the impact of environmental pollution. Surface
modification of ijuk fiber through alkalinization with 0.25 M NaOH
solution for 30 minutes was aimed to enhance its compatibility to
PLA, in order to improve properties of the composite such as the
mechanical properties. Alkalinization of the ijuk fibers annihilates
some surface components such as lignin, wax and hemicelloluse, so
the pore on the surface clearly appeared, decreasing of the density
and diameter of the ijuk fibers. The change of the ijuk fiber properties
leads to increase the mechanical properties of PLA composites
reinforced the ijuk fibers through strengthening of the mechanical
interlocking with the PLA matrix. An addition to enhance the
distribution of the fibers in the PLA matrix, the stirring during DCM
solvent evaporation from the mixture of the ijuk fibers and the
dissolved-PLA can reduce amount of the trapped-voids and fibers
pull-out phenomena, which can decrease the mechanical properties of
the composite.
Abstract: The composite pavement system considered in this
paper is composed of a functional surface layer, a fiber reinforced
asphalt middle layer and a fiber reinforced lean concrete base layer.
The mix design of the fiber reinforced lean concrete corresponds to the
mix composition of conventional lean concrete but reinforced by
fibers. The quasi-absence of research on the durability or long-term
performances (fatigue, creep, etc.) of such mix design stresses the
necessity to evaluate experimentally the long-term characteristics of
this layer composition. This study tests the creep characteristics as one
of the long-term characteristics of the fiber reinforced lean concrete
layer for composite pavement using a new creep device. The test
results reveal that the lean concrete mixed with fiber reinforcement
and fly ash develops smaller creep than the conventional lean
concrete. The results of the application of the CEB-FIP prediction
equation indicate that a modified creep prediction equation should be
developed to fit with the new mix design of the layer.
Abstract: This paper presents Finite Element Method (FEM) for
analyzing the internal responses generated in thin rectangular plates
with various edge conditions and rigidity conditions. Comparison has
been made between the FEM (ANSYS software) results for
displacement, stresses and moments generated with and without the
consideration of hole in plate and different aspect ratios. In the end
comparison for responses in plain and composite square plates has
been studied.
Abstract: In this paper 3D FEM analysis was carried out on
double lap bonded joint with composite adherents subjected to
dynamic shear. The adherents are made of Carbon/Epoxy while the
adhesive is epoxy Araldite 2031. The maximum average shear stress
and the stress homogeneity in the adhesive layer were examined.
Three fibers textures were considered: UD; 2.5D and 3D with same
volume fiber then a parametric study based on changing the thickness
and the type of fibers texture in 2.5D was accomplished. Moreover,
adherents’ dissimilarity was also investigated. It was found that the
main parameter influencing the behavior is the longitudinal stiffness
of the adherents. An increase in the adherents’ longitudinal stiffness
induces an increase in the maximum average shear stress in the
adhesive layer and an improvement in the shear stress homogeneity
within the joint. No remarkable improvement was observed for
dissimilar adherents.
Abstract: Sustainability and eco-friendly requirement of
engineering materials are sort for in recent times, thus giving rise to
the development of bio-composites. However, the natural fibres to
matrix interface interactions remain a key issue in getting the desired
mechanical properties from such composites. Treatment of natural
fibres is essential in improving matrix to filler adhesion, hence
improving its mechanical properties. In this study, investigations
were carried out to determine the effect of sodium hydroxide
treatment on the tensile, flexural, impact and hardness properties of
crushed and uncrushed Luffa cylindrica fibre reinforced recycled low
density polyethylene composites. The LC (Luffa cylindrica) fibres
were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium
hydroxide (NaOH) concentrations for a period of 24 hours under
room temperature conditions. A formulation ratio of 80/20 g (matrix
to reinforcement) was maintained for all developed samples. Analysis
of the results showed that the uncrushed luffa fibre samples gave
better mechanical properties compared with the crushed luffa fibre
samples. The uncrushed luffa fibre composites had a maximum
tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively
corresponding to a young modulus and flexural modulus of 21.08
MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration
respectively. Results obtained in the research showed that NaOH
treatment with the 8% NaOH concentration improved the mechanical
properties of the LC fibre reinforced composites when compared with
other NaOH treatment concentration values.
Abstract: Composite material based on Fe3Si micro-particles
and Mn-Zn nano-ferrite was prepared using powder metallurgy
technology. The sol-gel followed by autocombustion process was
used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically
milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano
powder system was homogenized by the Resonant Acoustic Mixing
using ResodynLabRAM Mixer. This non-invasive homogenization
technique was used to preserve spherical morphology of Fe3Si
powder particles. Uniaxial cold pressing in the closed die at pressure
600 MPa was applied to obtain a compact sample. Microwave
sintering of green compact was realized at 800°C, 20 minutes, in air.
Density of the powders and composite was measured by
Hepycnometry. Impulse excitation method was used to measure
elastic properties of sintered composite. Mechanical properties were
evaluated by measurement of transverse rupture strength (TRS) and
Vickers hardness (HV). Resistivity was measured by 4 point probe
method. Ferrite phase distribution in volume of the composite was
documented by metallographic analysis.
It has been found that nano-ferrite particle distributed among
micro- particles of Fe3Si powder alloy led to high relative density
(~93%) and suitable mechanical properties (TRS >100 MPa, HV
~1GPa, E-modulus ~140 GPa) of the composite. High electric
resistivity (R~6.7 ohm.cm) of prepared composite indicate their
potential application as soft magnetic material at medium and high
frequencies.
Abstract: This study was developed to compare the behavior
and the ability of polymer foam composites towards sound absorption
test of Shorea leprosula wood (SL) of acid hydrolysis treatment with
particle size
Abstract: The development of Drugs Delivery System (DDS)
has been widely investigated in the last decades. In this paper, first a
general overview of traditional and modern wound dressing is
presented. This is followed by a review of what scientists have done
in the medical environment, focusing on the possibility to develop a
new alternative for DDS through transdermal pathway, aiming to
treat melanoma skin cancer.
Abstract: In rapid industrial development, the demand for
high-strength and lightweight materials have been increased. Thus,
various CFRP (Carbon Fiber Reinforced Plastics) with composite
materials are being used. The design variables of CFRP are its
lamination direction, order and thickness. Thus, the hardness and
strength of CFRP depends much on their design variables. In this
paper, the lamination direction of CFRP was used to produce a
symmetrical ply [0°/0°, -15°/+15°, -30°/+30°, -45°/+45°, -60°/+60°,
-75°/+75° and 90°/90°] and an asymmetrical ply [0°/15°, 0°/30°,
0°/45°, 0°/60° 0°/75° and 0°/90°]. The bending flexure stress of the
CFRP specimen was evaluated through a bending test. Its thermal
property was measured using an infrared camera. The symmetrical
specimen and the asymmetrical specimen were analyzed. The results
showed that the asymmetrical specimen increased the bending loads
according to the increase in the orientation angle; and from 0°, the
symmetrical specimen showed a tendency opposite the asymmetrical
tendency because the tensile force of fiber differs at the vertical
direction of its load. Also, the infrared camera showed that the thermal
property had a trend similar to that of the mechanical properties.
Abstract: This study examines analytically the effect of tsunami loads on reinforced concrete (RC) frame buildings. The impact of tsunami wave loads and waterborne objects are analyzed using a typical substandard full-scale two-story RC frame building tested as part of the EU-funded Ecoleader project. The building was subjected to shake table tests in bare condition, and subsequently strengthened using Carbon Fiber Reinforced Polymers (CFRP) composites and retested. Numerical models of the building in both bare and CFRP-strengthened conditions are calibrated in DRAIN-3DX software to match the test results. To investigate the response of wave loads and impact forces, the numerical models are subjected to nonlinear dynamic analyses using force time-history input records. The analytical results are compared in terms of displacements at the floors and at the “impact point” of a boat. The results show that the roof displacement of the CFRP-strengthened building reduced by 63% when compared to the bare building. The results also indicate that strengthening only the mid-height of the impact column using CFRP is more effective at reducing damage when compared to strengthening other parts of the column. Alternative solutions to mitigate damage due to tsunami loads are suggested.
Abstract: Biofuels production has come forth as a future
technology to combat the problem of depleting fossil fuels. Bio-based
ethanol production from enzymatic lignocellulosic biomass
degradation serves an efficient method and catching the eye of
scientific community. High cost of the enzyme is the major obstacle
in preventing the commercialization of this process. Thus main
objective of the present study was to optimize composition of
medium components for enhancing cellulase production by newly
isolated strain of Bacillus tequilensis. Nineteen factors were taken
into account using statistical Plackett-Burman Design. The significant
variables influencing the cellulose production were further employed
in statistical Response Surface Methodology using Central
Composite Design for maximizing cellulase production. The
optimum medium composition for cellulase production was: peptone
(4.94 g/L), ammonium chloride (4.99 g/L), yeast extract (2.00 g/L),
Tween-20 (0.53 g/L), calcium chloride (0.20 g/L) and cobalt chloride
(0.60 g/L) with pH 7, agitation speed 150 rpm and 72 h incubation at
37oC. Analysis of variance (ANOVA) revealed high coefficient of
determination (R2) of 0.99. Maximum cellulase productivity of 11.5
IU/ml was observed against the model predicted value of 13 IU/ml.
This was found to be optimally active at 60oC and pH 5.5.
Abstract: Waste silicon carbide (waste SiC) filled high-density
polyethylene (HDPE) with and without surface modifiers were
studied. Two types of surface modifiers namely; high-density
polyethylene-grafted-maleic anhydride (HDPE-g-MA) and 3-aminopropyltriethoxysilane have been used in this study. The
composites were produced using a two roll mill, extruder and shaped
in a hydraulic compression molding machine. The mechanical
properties of polymer composites such as flexural strength and
modulus, impact strength, tensile strength, stiffness and hardness
were investigated over a range of compositions. It was found that,
flexural strength and modulus, tensile modulus and hardness
increased, whereas impact strength and tensile strength decreased
with the increasing in filler contents, compared to the neat HDPE. At
similar filler content, the effect of both surface modifiers increased
flexural modulus, impact strength, tensile strength and stiffness but
reduced the flexural strength. Morphological investigation using
SEM revealed that the improvement in mechanical properties was
due to enhancement of the interfacial adhesion between waste SiC
and HDPE.
Abstract: Sandwich structure composites produced by epoxy
core and aluminium skin were developed as potential building
materials. Interface bonding between core and skin was controlled by
varying kenaf content. Five different weight percentage of kenaf
loading ranging from 10 wt% to 50 wt% were employed in the core
manufacturing in order to study the mechanical properties of the
sandwich composite. Properties of skin aluminium with epoxy were
found to be affected by drying time of the adhesive. Mechanical
behavior of manufactured sandwich composites in relation with
properties of constituent materials was studied. It was found that 30
wt% of kenaf loading contributed to increase the flexural strength and
flexural modulus up to 102 MPa and 32 GPa, respectively. Analysis
were done on the flatwise and edgewise compression test. For
flatwise test, it was found that 30 wt% of fiber loading could
withstand maximum force until 250 kN, with compressive strength
results at 96.94 MPa. However, at edgewise compression test, the
sandwich composite with same fiber loading only can withstand 31
kN of the maximum load with 62 MPa of compressive strength
results.
Abstract: Fiber Bragg optic sensor is embedded in composite
material to detect and monitor the damage that occurs in composite
structures. In this paper, we deal with the mode-Ι delamination to
determine the material strength to crack propagation, using the
coupling mode theory and T-matrix method to simulate the FBGs
spectrum for both uniform and non-uniform strain distribution. The
double cantilever beam test is modeled in FEM to determine the
longitudinal strain. Two models are implemented, the first is the
global half model, and the second is the sub-model to represent the
FBGs with higher refined mesh. This method can simulate damage in
composite structures and converting strain to a wavelength shifting in
the FBG spectrum.
Abstract: The industrial process adds to engineering wood
products features absent in solid wood, with homogeneous structure
and reduced defects, improved physical and mechanical properties,
bio-deterioration, resistance and better dimensional stability,
improving quality and increasing the reliability of structures wood.
These features combined with using fast-growing trees, make them
environmentally ecological products, ensuring a strong consumer
market. The wood I-joists are manufactured by the industrial profiles
bonding flange and web, an important aspect of the production of
wooden I-beams is the adhesive joint that bonds the web to the
flange. Adhesives can effectively transfer and distribute stresses,
thereby increasing the strength and stiffness of the composite. The
objective of this study is to evaluate different resins in a shear strain
specimens with the aim of analyzing the most efficient resin and
possibility of using national products, reducing the manufacturing
cost. First was conducted a literature review, where established the
geometry and materials generally used, then established and analyzed
8 national resins and produced six specimens for each.
Abstract: In this research the effects of adding silica and
alumina nanoparticles on flow ability and compressive strength of
cementitious composites based on Portland cement were investigated.
In the first stage, the rheological behavior of different samples
containing nanosilica, nanoalumina and polypropylene, polyvinyl
alcohol and polyethylene fibers were evaluated. With increasing of
nanoparticles in fresh samples, the slump flow diameter reduced.
Fibers reduced the flow ability of the samples and viscosity
increased. With increasing of the micro silica particles to cement
ratio from 2/1 to 2/2, the slump flow diameter increased. By adding
silica and alumina nanoparticles up to 3% and 2% respectively, the
compressive strength increased and after decreased. Samples
containing silica nanoparticles and fibers had the highest compressive
strength.