Abstract: Calcium phosphate cement (CPC) is one of the most
attractive bioceramics due to its moldable and shape ability to fill
complicated bony cavities or small dental defect positions. In this
study, CPC was produced by using mixture of tetracalcium phosphate
(TTCP, Ca4O(PO4)2) and dicalcium phosphate anhydrous (DCPA,
CaHPO4) in equimolar ratio (1/1) with aqueous solutions of acetic
acid (C2H4O2) and disodium hydrogen phosphate dehydrate
(Na2HPO4.2H2O) in combination with sodium alginate in order to
improve theirs moldable characteristic. The concentration of the
aqueous solutions and sodium alginate were varied to investigate the
effect of different aqueous solutions and alginate on properties of the
cements. The cement paste was prepared by mixing cement powder
(P) with aqueous solution (L) in a P/L ratio of 1.0g/0.35ml. X-ray
diffraction (XRD) was used to analyses phase formation of the
cements. Setting time and compressive strength of the set CPCs were
measured using the Gilmore apparatus and Universal testing
machine, respectively.
The results showed that CPCs could be produced by using both
basic (Na2HPO4.2H2O) and acidic (C2H4O2) solutions. XRD results
show the precipitation of hydroxyapatite in all cement samples. No
change in phase formation among cements using difference
concentrations of Na2HPO4.2H2O solutions. With increasing
concentration of acidic solutions, samples obtained less
hydroxyapatite with a high dicalcium phosphate dehydrate leaded to
a shorter setting time. Samples with sodium alginate exhibited higher
crystallization of hydroxyapatite than that of without alginate as a
result of shorten setting time in a basic solution but a longer setting
time in an acidic solution. The stronger cement was attained from
samples using the acidic solution with sodium alginate; however the
strength was lower than that of using the basic solution.
Abstract: This article presents summary on preparation and
characterization of zinc, copper, cadmium and cobalt chromite
nanocrystals, embedded in an amorphous silica matrix. The
ZnCr2O4/SiO2, CuCr2O4/SiO2, CdCr2O4/SiO2 and CoCr2O4/SiO2
nanocomposites were prepared by a conventional sol-gel method
under acid catalysis. Final heat treatment of the samples was carried
out at temperatures in the range of 900−1200 ◦C to adjust the
phase composition and the crystallite size, respectively. The resulting
samples were characterized by Powder X-ray diffraction (PXRD),
High Resolution Transmission Electron Microscopy (HRTEM),
Raman/FTIR spectroscopy and magnetic measurements. Formation
of the spinel phase was confirmed in all samples. The average size of
the nanocrystals was determined from the PXRD data and by direct
particle size observation on HRTEM; both results were correlated.
The mean particle size (reviewed by HRTEM) was in the range from
∼4 to 46 nm. The results showed that the sol-gel method can be
effectively used for preparation of the spinel chromite nanoparticles
embedded in the silica matrix and the particle size is driven by the
type of the cation A2+ in the spinel structure and the temperature
of the final heat treatment. Magnetic properties of the nanocrystals
were found to be just moderately modified in comparison to the bulk
phases.
Abstract: Metal-enhanced Luminescence of silicon nanocrystals
(SiNCs) was determined using two different particle sizes of silver
nanoparticles (AgNPs). SiNCs have been characterized by scanning
electron microscopy (SEM), high resolution transmission electron
microscopy (HRTEM), Fourier transform infrared spectroscopy
(FTIR) and X-ray photoelectron spectroscopy (XPS). It is found that
the SiNCs are crystalline with an average diameter of 65 nm and FCC
lattice. AgNPs were synthesized using photochemical reduction of
AgNO3 with sodium dodecyl sulphate (SDS). The enhanced
luminescence of SiNCs by AgNPs was evaluated by confocal Raman
microspectroscopy. Enhancement up to x9 and x3 times were
observed for SiNCs that mixed with AgNPs which have an average
particle size of 100 nm and 30 nm, respectively. Silver NPs-enhanced
luminescence of SiNCs occurs as a result of the coupling between the
excitation laser light and the plasmon bands of AgNPs; thus this
intense field at AgNPs surface couples strongly to SiNCs.
Abstract: Calcium phosphate coating (CaP) has been employed
for protein delivery, but the typical direct protein adsorption on the
coating led to low incorporation content and fast release of the
protein from the coating. By using bovine serum albumin (BSA) as a
model protein, rapid biomimetic co-precipitation between calcium
phosphate and BSA was employed to control the distribution of BSA
within calcium phosphate coating during biomimetic formation on
titanium surface for only 6 h at 50oC in an accelerated calcium
phosphate solution. As a result, the amount of BSA incorporation and
release duration could be increased by using a rapid biomimetic coprecipitation
technique. Up to 43 fold increases in the BSA
incorporation content and the increase from 6 h to more than 360 h in
release duration compared to typical direct adsorption technique were
observed depending on the initial BSA concentration used during coprecipitation
(1, 10 and 100 μg.ml-1). From x-ray diffraction and
Fourier transform infrared spectroscopy studies, the coating
composition was not altered with the incorporation of BSA by this
rapid biomimetic co-precipitation and mainly comprised octacalcium
phosphate and hydroxyapatite. However, the microstructure of
calcium phosphate crystals changed from straight, plate-like units to
curved, plate-like units with increasing BSA content.
Abstract: The aim of this work is to present a theoretical analysis of a 2D ultrasound transducer comprised of crossed arrays of metal strips placed on both sides of thin piezoelectric layer (a). Such a structure is capable of electronic beam-steering of generated wavebeam both in elevation and azimuth. In this paper a semi-analytical model of the considered transducer is developed. It is based on generalization of the well-known BIS-expansion method. Specifically, applying the electrostatic approximation, the electric field components on the surface of the layer are expanded into fast converging series of double periodic spatial harmonics with corresponding amplitudes represented by the properly chosen Legendre polynomials. The problem is reduced to numerical solving of certain system of linear equations for unknown expansion coefficients.
Abstract: In this paper, strontium ferrite (SrO.6Fe2O3) was
synthesized by the sol-gel auto-combustion process. The thermal
behavior of powder obtained from self-propagating combustion of
initial gel was evaluated by simultaneous differential thermal analysis
(DTA) and thermo gravimetric (TG), from room temperature to
1200°C. The as-burnt powder was calcined at various temperatures
from 700-900°C to achieve the single-phase Sr-ferrite. Phase
composition, morphology and magnetic properties were investigated
using X-ray diffraction (XRD), transmission electron microscopy
(TEM) and vibrating sample magnetometry (VSM) techniques.
Results showed that the single-phase and nano-sized hexagonal
strontium ferrite particles were formed at calcination temperature of
800°C with crystallite size of 27 nm and coercivity of 6238 Oe.
Abstract: Boron-gypsum is a waste which occurs in the boric
acid production process. In this study, the boron content of this waste
is evaluated for the use in synthesis of magnesium borates and such
evaluation of this kind of waste is useful more than storage or
disposal. Magnesium borates, which are a sub-class of boron
minerals, are useful additive materials for the industries due to their
remarkable thermal and mechanical properties. Magnesium borates
were obtained hydrothermally at different temperatures. Novelty of
this study is the search of the solution density effects to magnesium
borate synthesis process for the increasing the possibility of borongypsum
usage as a raw material. After the synthesis process, products
are subjected to XRD and FT-IR to identify and characterize their
crystal structure, respectively.
Abstract: The effect of various humidities on process yields and
degrees of crystallinity for spray-dried powders from spray drying of
lactose with humid air in a straight-through system have been
studied. It has been suggested by Williams–Landel–Ferry kinetics
(WLF) that a higher particle temperature and lower glass-transition
temperature would increase the crystallization rate of the particles
during the spray-drying process. Freshly humidified air produced by
a Buchi-B290 spray dryer as a humidifier attached to the main spray
dryer decreased the particle glass-transition temperature (Tg), while
allowing the particle temperature (Tp) to reach higher values by using
an insulated drying chamber. Differential scanning calorimetry
(DSC) and moisture sorption analysis were used to measure the
degree of crystallinity for the spray-dried lactose powders. The
results showed that higher Tp-Tg, as a result of applying humid air,
improved the process yield from 21 ± 4 to 26 ± 2% and crystallinity
of the particles by decreasing the latent heat of crystallization from
43 ± 1 to 30 ± 11 J/g and the sorption peak height from 7.3 ± 0.7% to
6 ± 0.7%.
Abstract: This paper presents the design and analysis of Liquid
Crystal (LC) based tunable reflectarray antenna with different design
configurations within X-band frequency range. The effect of LC
volume used for unit cell element on frequency tunability and
reflection loss performance has been investigated. Moreover different
slot embedded patch element configurations have been proposed for
LC based tunable reflectarray antenna design with enhanced
performance. The detailed fabrication and measurement procedure
for different LC based unit cells has been presented. The waveguide
scattering parameter measured results demonstrated that by using the
circular slot embedded patch elements, the frequency tunability and
dynamic phase range can be increased from 180MHz to 200MHz and
120° to 124° respectively. Furthermore the circular slot embedded
patch element can be designed at 10GHz resonant frequency with a
patch volume of 2.71mm3 as compared to 3.47mm3 required for
rectangular patch without slot.
Abstract: Biological conversion of biomass to methane has
received increasing attention in recent years. Grasses have been
explored for their potential anaerobic digestion to methane. In this
review, extensive literature data have been tabulated and classified.
The influences of several parameters on the potential of these
feedstocks to produce methane are presented. Lignocellulosic
biomass represents a mostly unused source for biogas and ethanol
production. Many factors, including lignin content, crystallinity of
cellulose, and particle size, limit the digestibility of the hemicellulose
and cellulose present in the lignocellulosic biomass. Pretreatments
have used to improve the digestibility of the lignocellulosic biomass.
Each pretreatment has its own effects on cellulose, hemicellulose and
lignin, the three main components of lignocellulosic biomass. Solidstate
anaerobic digestion (SS-AD) generally occurs at solid
concentrations higher than 15%. In contrast, liquid anaerobic
digestion (AD) handles feedstocks with solid concentrations between
0.5% and 15%. Animal manure, sewage sludge, and food waste are
generally treated by liquid AD, while organic fractions of municipal
solid waste (OFMSW) and lignocellulosic biomass such as crop
residues and energy crops can be processed through SS-AD. An
increase in operating temperature can improve both the biogas yield
and the production efficiency, other practices such as using AD
digestate or leachate as an inoculant or decreasing the solid content
may increase biogas yield but have negative impact on production
efficiency. Focus is placed on substrate pretreatment in anaerobic
digestion (AD) as a means of increasing biogas yields using today’s
diversified substrate sources.
Abstract: This paper presents the design and analysis of Liquid
Crystal (LC) based tunable reflectarray antenna with different design
configurations within X-band frequency range. The effect of LC
volume used for unit cell element on frequency tunability and
reflection loss performance has been investigated. Moreover different
slot embedded patch element configurations have been proposed for
LC based tunable reflectarray antenna design with enhanced
performance. The detailed fabrication and measurement procedure
for different LC based unit cells has been presented. The waveguide
scattering parameter measured results demonstrated that by using the
circular slot embedded patch elements, the frequency tunability and
dynamic phase range can be increased from 180MHz to 200MHz and
120° to 124° respectively. Furthermore the circular slot embedded
patch element can be designed at 10GHz resonant frequency with a
patch volume of 2.71mm3 as compared to 3.47mm3 required for
rectangular patch without slot.
Abstract: A simple multi-wavelength passively Q-switched
Erbium-doped fiber laser (EDFL) is demonstrated using low cost
multi-walled carbon nanotubes (MWCNTs) based saturable absorber
(SA), which is prepared using polyvinyl alcohol (PVA) as a host
polymer. The multi-wavelength operation is achieved based on
nonlinear polarization rotation (NPR) effect by incorporating 50 m
long photonic crystal fiber (PCF) in the ring cavity. The EDFL
produces a stable multi-wavelength comb spectrum for more than 14
lines with a fixed spacing of 0.48 nm. The laser also demonstrates a
stable pulse train with the repetition rate increases from 14.9 kHz to
25.4 kHz as the pump power increases from the threshold power of
69.0 mW to the maximum pump power of 133.8 mW. The minimum
pulse width of 4.4 μs was obtained at the maximum pump power of
133.8 mW while the highest energy of 0.74 nJ was obtained at pump
power of 69.0 mW.
Abstract: Partial shadowing is one of the problems that are always faced in terrestrial applications of solar photovoltaic (PV). The effects of partial shadow on the energy yield of conventional mono-crystalline and multi-crystalline PV modules have been researched for a long time. With deployment of new thin-film solar PV modules in the market, it is important to understand the performance of new PV modules operating under the partial shadow in the tropical zone. This paper addresses the impacts of different partial shadowing on the operating characteristics of four different types of solar PV modules that include multi-crystalline, amorphous thin-film, CdTe thin-film and CIGS thin-film PV modules.
Abstract: With growth of PV market in tropical region, it is necessary to investigate the performance of different types of PV technology under the tropical weather conditions. Singapore Polytechnic was funded by Economic Development Board (EDB) to set up a solar PV test-bed for the research on performance of different types of PV modules in the country. The PV test-bed installed the nine different types of PV systems that are integrated to power utility grid for monitoring and analyzing their operating performances. This paper presents the 12 months operational data of nine different PV systems and analyses on performances of installed PV systems using energy yield and performance ratio. The nine types of PV systems under test have shown their energy yields ranging from 2.67 to 3.36 kWh/kWp and their performance ratios (PRs) ranging from 70% to 88%.
Abstract: Microwave dielectric ceramic materials of
(Mg1-xNix)2(Ti0.95Sn0.05)O4 for x = 0.01, 0.03, 0.05, 0.07 and 0.09 were
prepared and sintered at 1250–1400 ºC. The microstructure and
microwave dielectric properties of the ceramic materials were
examined and measured. The observations shows that the content of
Ni2+ ions has little effect on the crystal structure, dielectric constant,
temperature coefficient of resonant frequency (τf) and sintering
temperatures of the ceramics. However, the quality values (Q×f) are
greatly improved due to the addition of Ni2+ ions. The present study
showed that the ceramic material prepared for x = 0.05 and sintered at
1325ºC had the best Q×f value of 392,000 GHz, about 23%
improvement compared with that of Mg2(Ti0.95Sn0.05)O4.
Abstract: High resolution seismic reflection has recently been carried out on Zaria batholith, with the aim of characterizing the granitic Zaria batholiths in terms of its lithology. The geology of the area has revealed that the older granite outcrops in the vicinity of Zaria are exposures of a syntectonics to late-tectonic granite batholiths which intruded a crystalline gneissic basement during the Pan-African Orogeny. During the data acquisition the geophone were placed at interval of 1 m, variable offset of 1 and 10 m was used. The common midpoint (CMP) method with 12 fold coverage was employed for the survey. Analysis of the generated 3D surface of the p wave velocities from different profiles for densities and bulk modulus revealed that the rock material is more consolidated in South East part of the batholith and less consolidated in the North Western part. This was in conformity with earlier identified geology of the area, with the South Eastern part majorly of granitic outcrop, while the North Western part is characterized with the exposure of gneisses and thick overburden cover. The difference in lithology was also confirmed by the difference in seismic sections and Arial satellite photograph. Hence two major lithologies were identified, the granitic and gneisses complex which are characterized by gradational boundaries.
Abstract: This study compared the mechanical and microstructural properties produced during friction stir welding (FSW) of S275 structural steel in air and underwater. Post weld tests assessed the tensile strength, micro-hardness, distortion, Charpy impact toughness and fatigue performance in each case. The study showed that there was no significant difference in the strength, hardness or fatigue life of the air and underwater specimens. However, Charpy impact toughness was shown to decrease for the underwater specimens and was attributed to a lower degree of recrystallization caused by the higher rate of heat loss experienced when welding underwater. Reduced angular and longitudinal distortion was observed in the underwater welded plate compared to the plate welded in air.
Abstract: Single-phase, high band gap energy Zn0.5Mg0.5O films were grown under oxygen pressure, using pulse laser deposition with a Zn0.5Mg0.5O target. Structural characterization studies revealed that the crystal structures of the ZnX-1MgXO films could be controlled via changes in the oxygen pressure. TEM analysis showed that the thickness of the deposited Zn1-xMgxO thin films was 50–75 nm. As the oxygen pressure increased, we found that one axis of the crystals did not show a very significant increase in the crystallization compared with that observed at low oxygen pressure. The X-ray diffraction peak intensity for the hexagonal-ZnMgO (002) plane increased relative to that for the cubic-ZnMgO (111) plane. The corresponding c-axis of the h-ZnMgO lattice constant increased from 5.141 to 5.148 Å, and the a-axis of the c-ZnMgO lattice constant decreased from 4.255 to 4.250 Å. EDX analysis showed that the Mg content in the mixed-phase ZnMgO films decreased significantly, from 54.25 to 46.96 at.%. As the oxygen pressure was increased from 100 to 150 mTorr, the absorption edge red-shifted from 3.96 to 3.81 eV; however, a film grown at the highest oxygen pressure tested here (200 mTorr).
Abstract: In this research, it is aimed not only microwave synthesis of magnesium borates but also evaluation of magnesium wastes. Synthesis process can be described with the reaction of Mg wastes and boric acid using microwave energy. X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) were applied to synthesized minerals. According to XRD results, magnesium borate hydrate mixtures were obtained as mcallisterite (pdf# = 01-070-1902, Mg2(B6O7(OH)6)2.9(H2O)) at higher crystallinity properties was achieved at the mole ratio raw material 1:1. Also, other kinds of magnesium borate hydrates were obtained at lower crystallinity such as admontite (pdf # = 01-076-0540, MgO(B2O3)3.7(H2O)), inderite (pdf # = 01-072-2308, 2MgO.3B2O3.15(H2O)) and magnesium borate hydrates (pdf # = 01-076-0539, MgO(B2O3)3.6(H2O)). FT-IR spectrums indicated that minor changes were seen at the band values of characteristic stretching in each experiment. At the end of experiments it is seen that using microwave energy may contribute positive effects to design of synthesis process such as reducing reaction time and products at higher crystallinity.
Abstract: Thermodynamic properties of liquids under negative pressures are interesting and important in fields of scienceand technology. Here, phase transitions of a thermotropic liquid crystal are investigatedin a range from positive to negative pressures with a metal Berthelot tube using a commercial pressure transducer.Two co-existinglines, namely crystal (Kr) –nematic (N), and isotropic liquid (I) - nematic (N) lines, weredrawn in a pressure - temperature plane. The I-N line was drawn to ca. -5 (MPa).