Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: ZnO nanostructure were synthesized via microwave
method using zinc acetate as starting material, guanidinium as
structure directing agents, and water as solvent.. This work
investigates the photodegradation of azo dyes using the ZnO Flowerlike
in aqueous solutions. As synthesized ZnO samples were
characterized using X-Ray powder diffraction (XRD), scanning
electron microscopy (SEM), and FTIR spectroscopy.In this work
photodecolorization of congored azo dye under UV irradiation by
nano ZnO was studied.
Abstract: Ultrafast doped zinc oxide crystal promised us a good
opportunity to build new instruments for ICF fusion neutron
measurement. Two pulsed neutron detectors based on ZnO crystal
wafer have been conceptually designed, the superfast ZnO timing
detector and the scintillation recoil proton neutron detection system.
The structure of these detectors was presented, and some characters
were studied as well. The new detectors could be much faster than
existing systems, and would be more competent for ICF neutron
diagnostics.
Abstract: Zinc oxide thin films with various microstructures
were grown on substrates by using HCOOH-sols. The reaction
mechanism of the sol system was investigated by performing an XPS
analysis of as-synthesized films, due to the products of hydrolysis
and condensation in the sol system contributing to the chemical state
of the as-synthesized films. The chemical structures of the assynthesized
films related to the microstructures of the final annealed
films were also studied. The results of the Zn 2p3/2, C 1s and O1s
XPS patterns indicate that the hydrolysis reaction in the sol system is
strongly influenced by the HCOOH agent. The results of XRD and
FE-SEM demonstrated the microstructures of the annealed films are
related to the content of hydrolyzed zinc hydrate (Zn-OH) species
present, and that content of the Zn-OH species in the sol system
increases the HCOOH adding, and these Zn-OH species existing in
the sol phase are responsible for large ZnO crystallites in the final
annealed films.
Abstract: We investigate the ZnO role in the inherent protection
of old manuscripts to protect them against environmental damaging
effect of ultraviolet radiation, pollutant gasses, mold and bacteria. In
this study a cellulosic nanocomposite of ZnO were used as protective
coating on the surface of paper fibers. This layered nanocomposite
can act as a consolidate materials too. Furthermore, to determine how
well paper works screen objects from the damaging effects, two
accelerated aging mechanisms due to light and heat are discussed.
Results show good stability of papers with nanocomposite coating.
Also, a good light stability was shown in the colored paper that
treated with this nanocomposite. Furthermore, to demonstrate the
degree of antifungal and antibacterial properties of coated papers,
papers was treated with four common molds and bacteria and the
good preventive effects of coated paper against molds and bacteria
are described.
Abstract: We have fabricated a-IGZO TFT and investigated the
stability under positive DC and AC bias stress. The threshold voltage
of a-IGZO TFT shifts positively under those biases, and that reduces
on-current. For this reason, conventional shift-register circuit
employing TFTs which stressed by positive bias will be unstable, may
do not work properly. We have designed a new 6-transistor
shift-register, which has less transistors than prior circuits. The TFTs
of the proposed shift-register are not suffering from positive DC or AC
stress, mainly kept unbiased. Despite the compact design, the stable
output signal was verified through the SPICE simulation even under
RC delay of clock signal.
Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.
Abstract: ZnO nanocrystals with mean diameter size 14 nm
have been prepared by precipitation method, and examined as
photocatalyst for the UV-induced degradation of insecticide diazinon
as deputy of organic pollutant in aqueous solution. The effects of
various parameters, such as illumination time, the amount of
photocatalyst, initial pH values and initial concentration of
insecticide on the photocatalytic degradation diazinon were
investigated to find desired conditions. In this case, the desired
parameters were also tested for the treatment of real water containing
the insecticide. Photodegradation efficiency of diazinon was
compared between commercial and prepared ZnO nanocrystals. The
results indicated that UV/ZnO process applying prepared
nanocrystalline ZnO offered electrical energy efficiency and
quantum yield better than commercial ZnO. The present study, on the
base of Langmuir-Hinshelwood mechanism, illustrated a pseudo
first-order kinetic model with rate constant of surface reaction equal
to 0.209 mg l-1 min-1 and adsorption equilibrium constant of 0.124 l
mg-1.
Abstract: Nanophotocatalysts such as titanium (TiO2), zinc (ZnO), and iron (Fe2O3) oxides can be used in organic pollutants oxidation, and in many other applications. But among the challenges for technological application (scale-up) of the nanotechnology scientific developments two aspects are still little explored: research on environmental risk of the nanomaterials preparation methods, and the study of nanomaterials properties and/or performance variability. The environmental analysis was performed for six different methods of ZnO nanoparticles synthesis, and showed that it is possible to identify the more environmentally compatible process even at laboratory scale research. The obtained ZnO nanoparticles were tested as photocatalysts, and increased the degradation rate of the Rhodamine B dye up to 30 times.
Abstract: In this paper, Zinc Oxide (ZnO) thin films are deposited on glass substrate by sol-gel method. The ZnO thin films with well defined orientation were acquired by spin coating of zinc acetate dehydrate monoethanolamine (MEA), de-ionized water and isopropanol alcohol. These films were pre-heated at 275°C for 10 min and then annealed at 350°C, 450°C and 550°C for 80 min. The effect of annealing temperature and different thickness on structure and surface morphology of the thin films were verified by Atomic Force Microscopy (AFM). It was found that there was a significant effect of annealing temperature on the structural parameters of the films such as roughness exponent, fractal dimension and interface width. Thin films also were characterizied by X-ray Diffractometery (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure and show the c-axis grain orientation. Increasing annealing temperature increased the crystallite size and the c-axis orientation of the film after 450°C. Also In this study, ZnO thin films in different thickness have been prepared by sol-gel method on the glass substrate at room temperature. The thicknesses of films are 100, 150 and 250 nm. Using fractal analysis, morphological characteristics of surface films thickness in amorphous state were investigated. The results show that with increasing thickness, surface roughness (RMS) and lateral correlation length (ξ) are decreased. Also, the roughness exponent (α) and growth exponent (β) were determined to be 0.74±0.02 and 0.11±0.02, respectively.
Abstract: Post growth annealing of solution grown ZnO
nanowire array is performed under controlled oxygen ambience. The
role of annealing over surface defects and their consequence on
dark/photo-conductivity and photosensitivity of nanowire array is
investigated. Surface defect properties are explored using various
measurement tools such as contact angle, photoluminescence, Raman
spectroscopy and XPS measurements. The contact angle of the NW
films reduces due to oxygen annealing and nanowire film surface
changes from hydrophobic (96°) to hydrophilic (16°). Raman and
XPS spectroscopy reveal that oxygen annealing improves the crystal
quality of the nanowire films. The defect band emission intensity
(relative to band edge emission, ID/IUV) reduces from 1.3 to 0.2 after
annealing at 600 °C at 10 SCCM flow of oxygen. An order
enhancement in dark conductivity is observed in O2 annealed
samples, while photoconductivity is found to be slightly reduced due
to lower concentration of surface related oxygen defects.
Abstract: In this paper, we proposed the effects of Mo thickness
on the properties of AZO/Mo/AZO multilayer thin films for
opto-electronics applications. The structural, optical and electrical
properties of AZO/Mo/AZO thin films were investigated.
Optimization of the thin films coatings resulted with low resistivity of
9.98 × 10-5 )-cm, mobility of 12.75 cm2/V-s, carrier concentration of
1.05 × 1022 cm-3, maximum transmittance of 79.13% over visible
spectrum of 380 – 780 nm and Haacke figure of merit (FOM) are 5.95
× 10-2 )-1 under Mo layer thickness of 15 nm. These results indicate an
alternative candidate for use as a transparent electrode in solar cells
and various displays applications.