Abstract: Effect of 2wt% Cu addition on tensile properties and
fracture behavior of Al-6Si-0.5Mg-2Ni alloy at various strain rates
were studied. The solution treated Al-6Si-0.5Mg-2Ni (-2Cu) alloys,
were aged isochronally for 1 hour at temperatures up to 300oC. The
uniaxial tension test was carried out at strain rate ranging from 10-4s-1
to 10-2s-1 in order to investigate the strain rate dependence of tensile
properties. Tensile strengths were found to increase with ageing
temperature and the maximum being attained ageing for 1 hr at
225oC (peak aged condition). Addition of 2wt% Cu resulted in an
increase in tensile properties at all strain rates. Evaluation of tensile
properties at three different strain rates (10-4, 10-3 and 10-2 s-1)
showed that strain rates affected the tensile properties significantly.
At higher strain rates the strength was better but ductility was poor.
Microstructures of broken specimens showed that both the void
coalescence and the interface debonding affect the fracture behavior
of the alloys
Abstract: High strength Fe-36Ni-base Invar alloys containing Al contents up to 0.3 weight percent were cast into ingots and thermodynamic equilibrium during solidification has been investigated in this study. From the thermodynamic simulation using Thermo-CalcĀ®, it has been revealed that equilibrium phases which can be formed are two kinds of MC-type precipitates, MoC, and M2C carbides. The mu phase was also expected to form by addition of aluminum. Microstructure observation revealed the coarse precipitates in the as-cast ingots, which was non-equilibrium phase and could be resolved by the successive heat treatment. With increasing Al contents up to 0.3 wt.%, tensile strength of Invar alloy increased as 1400MPa after cold rolling and thermal expansion coefficient increased significantly. Cold rolling appeared to dramatically decrease thermal expansion coefficient.
Abstract: An industrial epoxy adhesive used in Carbon Fiber Reinforced Polymer (CFRP) strengthening systems was modified by dispersing multi-walled carbon nanotubes (MWCNTs). Nanocomposites were fabricated using the solvent-assisted dispersion method and ultrasonic mixing. Thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and tensile tests were conducted to study the effect of nanotubes dispersion on the thermal and mechanical properties of the epoxy composite. Experimental results showed a substantial enhancement in the decomposition temperature and tensile properties of epoxy composite, while, the glass transition temperature (Tg) was slightly reduced due to the solvent effect. The morphology of the epoxy nanocomposites was investigated by SEM. It was proved that using solvent improves the nanotubes dispersion. However, at contents higher than 2 wt. %, nanotubes started to re-bundle in the epoxy matrix which negatively affected the final properties of epoxy composite.
Abstract: Natural fibres have emerged as the potential reinforcement material for composites and thus gain attraction by many researchers. This is mainly due to their applicable benefits as they offer low density, low cost, renewable, biodegradability and environmentally harmless and also comparable mechanical properties with synthetic fibre composites. The properties of hybrid composites highly depends on several factors, including the interaction of fillers with the polymeric matrix, shape and size (aspect ratio), and orientation of fillers [1]. In this study, natural fibre kenaf composites and kenaf/fibreglass hybrid composites were fabricated by a combination of hand lay-up method and cold-press method. The effect of different fibre types (powder, short and long) on the tensile properties of composites is investigated. The kenaf composites with and without the addition of fibreglass were then characterized by tensile testing and scanning electron microscopy. A significant improvement in tensile strength and modulus were indicated by the introduction of long kenaf/woven fibreglass hybrid composite. However, the opposite trends are observed in kenaf powder composite. Fractographic observation shows that fibre/matrix debonding causes the fibres pull out. This phenomenon results in the fibre and matrix fracture.
Abstract: This study demonstrates the feasibility of joining the commercial pure copper plates by friction stir welding (FSW). Microstructure, microhardness and tensile properties in terms of the joint efficiency were found 94.03 % compare to as receive base material (BM). The average hardness at the top was higher than bottom. Hardness of weld zone was higher than the base material. Different microstructure zones were revealed by optical microscopy and scanning electron microscopy. The stirred zone (SZ) exhibited primary two phases namely, recrystallized grains and fine precipitates in matrix of copper.
Abstract: The tensile properties of Mg-3%Al nanocrystalline
alloys were investigated at different test environment. Bulk
nanocrystalline samples of these alloy was successfully prepared by
mechanical alloying (MA) followed by cold compaction, sintering,
and hot extrusion process. The crystal size of the consolidated milled
sample was calculated by X-Ray line profile analysis. The
deformation mechanism and microstructural characteristic at
different test condition was discussed extensively. At room
temperature, relatively lower value of activation volume (AV) and
higher value of strain rate sensitivity (SRS) suggests that new rate
controlling mechanism accommodating plastic flow in the present
nanocrystalline sample. The deformation behavior and the
microstructural character of the present samples were discussed in
details.
Abstract: Bone material is treated as heterogeneous and hierarchical in nature therefore appropriate size of bone specimen is required to analyze its tensile properties at a particular hierarchical level. Tensile properties of cortical bone are important to investigate the effect of drug treatment, disease and aging as well as for development of computational and analytical models. In the present study tensile properties of buffalo as well as goat femoral and tibiae cortical bone are analyzed using sub-size tensile specimens. Femoral cortical bone was found to be stronger in tension as compared to the tibiae cortical bone and the tensile properties obtained using sub-size specimens show close resemblance with the tensile properties of full-size cortical specimens. A two dimensional finite element (FE) modal was also applied to simulate the tensile behavior of sub-size specimens. Good agreement between experimental and FE model was obtained for sub-size tensile specimens of cortical bone.
Abstract: This current research focused on development of degradable starch based packaging film with enhanced mechanical properties. A series of low density polyethylene (LDPE)/tapioca starch compounds with various tapioca starch contents were prepared by twin screw extrusion with the addition of maleic anhydride grafted polyethylene as compatibilizer. Palm cooking oil was used as processing aid to ease the blown film process, thus, degradable film can be processed via conventional blown film machine. Studies on their characteristics, mechanical properties and biodegradation were carried out by Fourier Transform Infrared (FTIR) spectroscopy and optical properties, tensile test and exposure to fungi environment respectively. The presence of high starch contents had an adverse effect on the tensile properties of LDPE/tapioca starch blends. However, the addition of compatibilizer to the blends improved the interfacial adhesion between the two materials, hence, improved the tensile properties of the films. High content of starch amount also was found to increase the rate of biodegradability of LDPE/tapioca starch films. It can be proved by exposure of the film to fungi environment. A growth of microbes colony can be seen on the surface of LDPE/tapioca starch film indicates that the granular starch present on the surface of the polymer film is attacked by microorganisms, until most of it is assimilated as a carbon source.
Abstract: An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ~0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respectively, with a reasonably good ductility of ~9%. The liquid nitrogen rolled sample showed around 54 MPa increase in tensile strength without much reduction in the ductility as compared to the as received T6 condition alloy. The microstructural details revealed equiaxed grains in the annealed and solutionized sample and elongated grains in the rolled samples. In addition, the cryorolled samples exhibited fine grain structure compared to the room temperature rolled samples.
Abstract: This paper presents a method for determining the
uniaxial tensile properties such as Young-s modulus, yield strength
and the flow behaviour of a material in a virtually non-destructive
manner. To achieve this, a new dumb-bell shaped miniature
specimen has been designed. This helps in avoiding the removal of
large size material samples from the in-service component for the
evaluation of current material properties. The proposed miniature
specimen has an advantage in finite element modelling with respect
to computational time and memory space. Test fixtures have been
developed to enable the tension tests on the miniature specimen in a
testing machine. The studies have been conducted in a chromium
(H11) steel and an aluminum alloy (AR66). The output from the
miniature test viz. load-elongation diagram is obtained and the finite
element simulation of the test is carried out using a 2D plane stress
analysis. The results are compared with the experimental results. It is
observed that the results from the finite element simulation
corroborate well with the miniature test results. The approach seems
to have potential to predict the mechanical properties of the
materials, which could be used in remaining life estimation of the
various in-service structures.