Abstract: Cobalt-gadolinium catalyst for Fischer-Tropsch synthesis was prepared by impregnation method with commercial silica gel, and its texture properties were characterized by BET, XRD, and TPR. The catalytic performance of the catalyst was tested in a fixed bed reactor. The results showed that the addition of gadolinium to the cobalt catalyst might decrease the size of cobalt particles, and increased the dispersion of catalytic active cobalt phases. The carbon number distributions for the catalysts was calculated by ASF equation.
Abstract: In this paper, MCM-41 mesoporous material nanofibers were synthesized by an electrospinning technique. The nanofibers were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), x-ray diffraction (XRD), and nitrogen adsorption–desorption measurement. Tetraethyl orthosilicate (TEOS) and polyvinyl alcohol (PVA) were used as a silica source and fiber forming source, respectively. TEM and SEM images showed synthesis of MCM-41 nanofibers with a diameter of 200 nm. The pore diameter and surface area of calcined MCM-41 nanofibers was 2.2 nm and 970 m2/g, respectively. The morphology of the MCM-41 nanofibers depended on spinning voltages.
Abstract: The paper examines the mechanism of pozzolan-soil reactions, using a recent study on the chemical stabilization of a Class A-2-7 (3) lateritic soil, with corn cob ash (CCA) as case study. The objectives are to establish a nexus between cation exchange capacity of the soil, the alkaline forming compounds in CCA and percentage CCA addition to soil beyond which no more improvement in strength properties can be achieved; and to propose feasible chemical reactions to explain the chemical stabilization of the lateritic soil with CCA alone. The lateritic soil, as well as CCA of pozzolanic quality Class C were separately analysed for their metallic oxide composition using the X-Ray Fluorescence technique. The cation exchange capacity (CEC) of the soil and the CCA were computed theoretically using the percentage composition of the base cations Ca2+, Mg2+ K+ and Na2+ as 1.48 meq/100 g and 61.67 meq/100 g respectively, thus indicating a ratio of 0.024 or 2.4%. This figure, taken as the theoretical amount required to just fill up the exchangeable sites of the clay molecules, compares well with the laboratory observation of 1.5% for the optimum level of CCA addition to lateritic soil. The paper went on to present chemical reaction equations between the alkaline earth metals in the CCA and the silica in the lateritic soil to form silicates, thereby proposing an extension of the theory of mechanism of soil stabilization to cover chemical stabilization with pozzolanic ash only. The paper concluded by recommending further research on the molecular structure of soils stabilized with pozzolanic waste ash alone, with a view to confirming the chemical equations advanced in the study.
Abstract: The present work describes the preparation and characterization of nanosized SiO2@PbS core-shell particles by using a simple wet chemical route. This method utilizes silica spheres formation followed by successive ionic layer adsorption and reaction method assisted lead sulphide shell layer formation. The final product was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV–vis spectroscopic, infrared spectroscopy (IR) and transmission electron microscopy (TEM) experiments. The morphological studies revealed the uniformity in size distribution with core size of 250 nm and shell thickness of 18 nm. The electron microscopic images also indicate the irregular morphology of lead sulphide shell layer. The structural studies indicate the face-centered cubic system of PbS shell with no other trace for impurities in the crystal structure.
Abstract: The aim of this article is to access the optimal mix design of self-compacting light weight concrete. The effects of magnetic water, superplasticizer based on polycarboxylic-ether, and silica fume on characteristics of this type of concrete are studied. The workability of fresh concrete and the compressive strength of hardened concrete are considered here. For this purpose, nine mix designs were studied. The percentages of superplasticizer were 0.5, 1, and 2% of the weight of cement, and the percentages of silica fume were 0, 6, and 10% of the weight of cement. The water to cementitious ratios were 0.28, 0.32, and 0.36. The workability of concrete samples was analyzed by the devices such as slump flow, V-funnel, L box, U box, and Urimet with J ring. Then, the compressive strengths of the mixes at the ages of 3, 7, 28, and 90 days were obtained. The results show that by using magnetic water, the compressive strengths are improved at all the ages. In the concrete samples with ordinary water, more superplasticizer dosages were needed. Moreover, the combination of superplasticizer and magnetic water had positive effects on the mixes containing silica fume and they could flow easily.
Abstract: This study was initiated to evaluate and optimize the conversion of animal fat from tannery wastes into methyl ester. In the pre-treatment stage, animal fats feedstock was hydrolysed and esterified through solid state fermentation (SSF) using Microbacterium species immobilized onto sand silica matrix. After 72 hours of fermentation, predominant esters in the animal fats were found to be with 83.9% conversion rate. Later, esterified animal fats were transesterified at 3 hour reaction time with 1% NaOH (w/v %), 6% methanol to oil ratio (w/v %) to produce 89% conversion rate. C13 NMR revealed long carbon chain in fatty acid methyl esters at 22.2817-31.9727 ppm. Methyl esters of palmitic, stearic, oleic represented the major components in biodiesel.
Abstract: Fly ash-slag based Geopolymer Cement (GPC) is presenting mechanical properties and environmental advantages that make it the predominant “green” alternative to Portland Cement (PC). Although numerous life-cycle analyses praising its environmental advantages, disposal after the end of its life remains as an issue that has been barely explored. The present study is investigating the recyclability of fly ash-slag GPC as aggregate in mortars. The purpose of the study was to evaluate the effect of GPC fine Recycled Aggregates (RA), at replacement levels of 25% and 50%, on the main mechanical properties of PC and GPC mortar mixes. The results were compared with those obtained by corresponding mixes incorporating natural and PC-RA. The main physical properties of GPC-RA were examined and proven to be comparable to those of PC-RA and slightly inferior to those of natural sand. A negligible effect was observed at 28-day compressive and flexural strength of PC mortars with GPC aggregates having a milder effect than PC. As far as GPC mortars are concerned, the influence of GPC aggregates was enhancing for the investigated mechanical properties. Additionally, a screening test showed that recycled geopolymer aggregates are not prone of inducing alkali silica reaction.
Abstract: This paper reports the strength and durability properties of high strength high performance concrete incorporating rice husk ash (RHA) having high silica, low carbon content and appropriate fineness. In this study concrete containing 10%, 15% and 20% RHA as cement replacement and water to binder ratio of 0.25 were investigated. The results show that increasing amount of RHA increases the dosage of superplasticizer to maintain similar workability. Partial replacement of cement with RHA did not increase the early age compressive strength of concrete. However, concrete containing RHA showed higher compressive strength at later ages. The results showed that compressive strength of concrete in the 90-115 MPa range can be obtained at 28 curing days and the durability properties of RHA concrete performed better than that of control concrete. The water absorption of concrete incorporating 15% RHA exhibited the lowest value. The porosity of concrete is consistent with water absorption whereby higher replacement of RHA decreased the porosity of concrete. There is a positive correlation between reducing porosity and increasing compressive strength of high strength high performance concrete. The results also indicate that up to 20% of RHA incorporation could be advantageously blended with cement without adversely affecting the strength and durability properties of concrete.
Abstract: Cytotoxic platinum compounds play a major role in the chemotherapy of a large number of human cancers. However, due to the severe side effects for the patient and other problems associated with their use, there is a need for the development of more efficient drugs and new methods for their selective delivery to the tumours. One way to achieve the latter could be in the use of nanoparticular substrates that can adsorb or chemically bind the drug. In the cell, the drug is supposed to be slowly released, either by physical desorption or by dissolution of the particle framework. Ideally, the cytotoxic properties of the platinum drug unfold only then, in the cancer cell and over a longer period of time due to the gradual release. In this paper, we report on our first steps in this direction. The binding properties of a series of cytotoxic Pt(II) oxadiazoline compounds to mesoporous silica particles has been studied by NMR and UV/vis spectroscopy. High loadings were achieved when the Pt(II) compound was relatively polar, and has been dissolved in a relatively nonpolar solvent before the silica was added. Typically, 6-10 hours were required for complete equilibration, suggesting the adsorption did not only occur to the outer surface but also to the interior of the pores. The untreated and Pt(II) loaded particles were characterised by C, H, N combustion analysis, BET/BJH nitrogen sorption, electron microscopy (REM and TEM) and EDX. With the latter methods we were able to demonstrate the homogenous distribution of the Pt(II) compound on and in the silica particles, and no Pt(II) bulk precipitate had formed. The in vitro cytotoxicity in a human cancer cell line (HeLa) has been determined for one of the new platinum compounds adsorbed to mesoporous silica particles of different size, and compared with the corresponding compound in solution. The IC50 data are similar in all cases, suggesting that the release of the Pt(II) compound was relatively fast and possibly occurred before the particles reached the cells. Overall, the platinum drug is chemically stable on silica and retained its activity upon prolonged storage.
Abstract: Nanocomposites of isotactic polypropylene (iPP) and
date wood fiber were prepared after modification of the host matrix
by reactive extrusion grafting of maleic anhydride. Chemical and
mechanical treatment of date wood flour (WF) was conducted to
obtain nanocrystalline cellulose. Layered silicates (clay) were
partially intercalated with date wood fiber, and the modified layered
silicate was used as filler in the PP matrix via a melt-blending
process. The tensile strength of composites prepared from wood fiber
modified clay was greater than that of the iPP-clay and iPP-WF
composites at a 6% filler concentration, whereas deterioration of
mechanical properties was observed when clay and WF were used
alone for reinforcement. The dispersion of the filler in the matrix
significantly decreased after clay modification with cellulose at
higher concentrations, as shown by X-ray diffraction (XRD) data.
Abstract: Biological processes based on oxidation of sulfur
compounds by chemolithotrophic microorganisms are emerging as an
efficient and eco-friendly technique for removal of sulfur from the
coal. In the present article, study was carried out to investigate the
potential of biodesulfurization process in removing the sulfur from
lignite coal sample collected from a Mongolian coal mine. The batch
biodesulfurization experiments were conducted in 2.5 L borosilicate
baffle type reactors at 35 ºC using Acidithiobacillus ferrooxidans.
The effect of pulp density on efficiency of biodesulfurization was
investigated at different solids concentration (1-10%) of coal. The
results of the present study suggested that the rate of desulfurization
was retarded at higher coal pulp density. The optimum pulp density
found 5% at which about 48% of the total sulfur was removed from
the coal.
Abstract: Geopolymer (cement-free) concrete is the most promising green alternative to ordinary Portland cement concrete and other cementitious materials. While a range of different geopolymer concretes have been produced, a common feature of these concretes is heat curing treatment which is essential in order to provide sufficient mechanical properties in the early age. However, there are several practical issues with the application of heat curing in large-scale structures. The purpose of this study is to develop cement-free concrete without heat curing treatment. Experimental investigations were carried out in two phases. In the first phase (Phase A), the optimum content of water, polycarboxylate based superplasticizer contents and potassium silicate activator in the mix was determined. In the second stage (Phase B), the effect of ground granulated blast furnace slag (GGBFS) incorporation on the compressive strength of fly ash (FA) and Slag based geopolymer mixtures was evaluated. Setting time and workability were also conducted alongside with compressive tests. The results showed that as the slag content was increased the setting time was reduced while the compressive strength was improved. The obtained compressive strength was in the range of 40-50 MPa for 50% slag replacement mixtures. Furthermore, the results indicated that increment of water and superplasticizer content resulted to retarding of the setting time and slight reduction of the compressive strength. The compressive strength of the examined mixes was considerably increased as potassium silicate content was increased.
Abstract: Effective treatment of ground instability is essential when managing the impacts associated with historic mining. A field trial was undertaken by the Coal Authority to investigate the geotechnical performance and potential use of composite materials comprising resin and fill or stone to safely treat surface collapses, such as crown-holes, associated with shallow mining. Test pits were loosely filled with various granular fill materials. The fill material was injected with commercially available silicate and polyurethane resin foam products. In situ and laboratory testing was undertaken to assess the geotechnical properties of the resultant composite materials. The test pits were subsequently excavated to assess resin permeation. Drilling and resin injection was easiest through clean limestone fill materials. Recycled building waste fill material proved difficult to inject with resin; this material is thus considered unsuitable for use in resin composites. Incomplete resin permeation in several of the test pits created irregular ‘blocks’ of composite. Injected resin foams significantly improve the stiffness and resistance (strength) of the un-compacted fill material. The stiffness of the treated fill material appears to be a function of the stone particle size, its associated compaction characteristics (under loose tipping) and the proportion of resin foam matrix. The type of fill material is more critical than the type of resin to the geotechnical properties of the composite materials. Resin composites can effectively support typical design imposed loads. Compared to other traditional treatment options, such as cement grouting, the use of resin composites is potentially less disruptive, particularly for sites with limited access, and thus likely to achieve significant reinstatement cost savings. The use of resin composites is considered a suitable option for the future treatment of shallow mining collapses.
Abstract: Sodium borosilicate glasses doped with different
content of NdF3 mol % have been prepared by rapid quenching
method. Ultrasonic velocities (both longitudinal and shear)
measurements have been carried out at room temperature and at
ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature,
softening temperature and Poisson's ratio have been obtained as a
function of NdF3 modifier content. Results showed that the elastic
moduli, Debye temperature, softening temperature and Poisson's ratio
have very slight change with the change of NdF3 mol % content.
Based on FTIR spectroscopy and theoretical (Bond compression)
model, quantitative analysis has been carried out in order to obtain
more information about the structure of these glasses. The study
indicated that the structure of these glasses is mainly composed of
SiO4 units with four bridging oxygens (Q4), and with three bridging
and one nonbridging oxygens (Q3).
Abstract: The objective of this research is to mitigate and prevent
the alkali silica reactivity (ASR) in highway construction projects.
ASR is a deleterious reaction initiated when the silica content of the
aggregate reacts with alkali hydroxides in cement in the presence of
relatively high moisture content. The ASR results in the formation of
an expansive white colored gel-like material which forms the
destructive tensile stresses inside hardened concrete. In this research, different types of local aggregates available in the
State of Arkansas were mixed and mortar bars were poured according
to the ASTM specifications. Mortar bars expansion was measured
versus time and aggregates with potential ASR problems were
detected. Different types of supplementary cementitious materials
(SCMs) were used in remixing mortar bars with highly reactive
aggregates. Length changes for remixed bars proved that different
types of SCMs can be successfully used in reducing the expansive
effect of ASR. SCMs percentage by weight is highly dependent on
the SCM type. The result of this study will help avoiding future
losses due to ASR cracking in construction project and reduce the
maintenance, repair, and replacement budgets required for highways
network.
Abstract: We have aimed to produce a self-cleaning transparent
polymer coating with polyurethane (PU) matrix as the latter is highly
solvent, chemical and weather resistant having good mechanical
properties. Nano-silica modified by 1H, 1H, 2H, 2Hperflurooctyltriethoxysilane
was incorporated into the PU matrix for
attaining self-cleaning ability through hydrophobicity. The
modification was confirmed by particle size analysis and scanning
electron microscopy (SEM). Thermo-gravimetric (TGA) studies were
carried to ascertain the grafting of silane onto the silica. Several
coating formulations were prepared by varying the silica loading
content and compared to a commercial equivalent. The effect of
dispersion and the morphology of the coated films were assessed by
SEM analysis. All coating standardized tests like solvent resistance,
adhesion, flexibility, acid, alkali, gloss etc. have been performed as
per ASTM standards. Water contact angle studies were conducted to
analyze the hydrophobic character of the coating. In addition, the
coatings were also subjected to salt spray and accelerated weather
testing to analyze the durability of the coating.
Abstract: Concrete is an essential building material which is
widely used in construction industry all over the world due to its
compressible strength. Curing of concrete plays a vital role in
durability and other performance necessities. Improper curing can
affect the concrete performance and durability easily. When areas
like scarcity of water, structures is not accessible by humans external
curing cannot be performed, so we opt for internal curing. Internal
curing (or) self curing plays a major role in developing the concrete
pore structure and microstructure. The concept of internal curing is to
enhance the hydration process to maintain the temperature uniformly.
The evaporation of water in the concrete is reduced by self curing
agent (Super Absorbing Polymer – SAP) there by increasing the
water retention capacity of the concrete. The research work was
carried out to reduce water, which is prime material used for concrete
in the construction industry. Concrete curing plays a major role in
developing hydration process. Concept of self curing will reduce the
evaporation of water from concrete. Self curing will increase water
retention capacity as compared to the conventional concrete. Proper
self curing (or) internal curing increases the strength, durability and
performance of concrete. Super absorbing Polymer (SAP) used as
internal curing agent. In this study 0.2% to 0.4% of SAP was varied
in different grade of high strength concrete. In the experiment
replacement of cement by silica fumes with 5%, 10% and 15% are
studied. It is found that replacement of silica fumes by 10 % gives
more strength and durability when compared to others.
Abstract: Electro-osmosis in clayey soils and sediments, for
purposes of clay consolidation, dewatering, or cleanup, and electro
injection in porous media is widespread recent decades. It is
experimentally found that the chemical properties of porous media
especially PH change the characteristics of media. Electro-osmotic
conductivity is a function of soil and grout material chemistry,
altering with time. Many numerical approaches exist to simulate the
of electro kinetic flow rate considering chemical changes. This paper
presents a simplified analytical solution for constant flow rate based
on varying electro osmotic conductivity and time dependent viscosity
for injection of colloidal silica.
Abstract: This work aims to investigate the structure–property
relationship in ternary nanocomposites consisting of polypropylene
as the matrix, polyamide 66 as the minor phase and treated nanoclay
DELLITE 67G as the reinforcement. All PP/PA66/Nanoclay systems
with polypropylene grafted maleic anhydride PP-g-MAH as a
compatibilizer were prepared via melt compounding and
characterized in terms of nanoclay content. Morphological structure
was investigated by scanning electron microscopy. The rheological
behavior of the nanocomposites was determined by various methods,
viz melt flow index (MFI) and parallel plate rheological
measurements. The PP/PP-g-MAH/PA66 nanocomposites showed a homogeneous
morphology supporting the compatibility improvement between PP,
PA66, and nanoclay. SEM results revealed the formation of
nanocomposites as the nanoclay was intercalated and exfoliated. In
the ternary nanocomposites, the rheological behavior showed that, the
complex viscosity is increased with increasing the nanoclay. The results showed that the use of nanoclay affects the variations
of storage modulus (G′), loss modulus (G″) and the melt elasticity.
Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.