Abstract: Sodium borosilicate glasses doped with different
content of NdF3 mol % have been prepared by rapid quenching
method. Ultrasonic velocities (both longitudinal and shear)
measurements have been carried out at room temperature and at
ultrasonic frequency of 4 MHz. Elastic moduli, Debye temperature,
softening temperature and Poisson's ratio have been obtained as a
function of NdF3 modifier content. Results showed that the elastic
moduli, Debye temperature, softening temperature and Poisson's ratio
have very slight change with the change of NdF3 mol % content.
Based on FTIR spectroscopy and theoretical (Bond compression)
model, quantitative analysis has been carried out in order to obtain
more information about the structure of these glasses. The study
indicated that the structure of these glasses is mainly composed of
SiO4 units with four bridging oxygens (Q4), and with three bridging
and one nonbridging oxygens (Q3).
Abstract: In this paper, sodium borosilicates glasses were prepared by melting in air. These heat-resistant transparent glasses have subjected subsequently isothermal treatments at different times, which have transformed them at opaque glass (milky white color). Such changes indicate that these glasses showed clearly phase separation (immiscibility). The immiscibility region in a sodium borosilicate ternary system was investigated in this work, i.e. to determine the regions from which some compositions can show phase separation. For this we went through the conditions of thermodynamic equilibrium, which were translated later by mathematical equations to find an approximate solution. The latter has been translated in a simulation which was established thereafter to find the immiscibility regions in this type of special glasses.