Abstract: This article experimentally investigates various physical properties of special fire retardant sewing threads under different sewing speeds. The aramid threads are common for sewing the fire-fighter clothing due to high strength and high melting temperature. 3 types of aramid threads with different linear densities are used for sewing at different speed of 2000 to 4000 r/min. The needle temperature is measured at different speeds of sewing and tensile properties of threads are measured before and after the sewing process respectively. The results shows that the friction and abrasion during the sewing process causes a significant loss to the tensile properties of the threads and needle temperature rises to nearly 300oC at 4000 r/min of machine speed. The Scanning electron microscope images are taken before and after the sewing process and shows no melting spots but significant damage to the yarn. It is also found that machine speed of 2000r/min is ideal for sewing firefighter clothing for higher tensile properties and production.
Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.
Abstract: The main cause of Alzheimer disease (AD) was
believed to be mainly due to the accumulation of free radicals owing
to oxidative stress (OS) in brain tissue. The mechanism of the
neurotoxicity of Aluminum chloride (AlCl3) induced AD in
hippocampus Albino wister rat brain tissue, the curative & the
protective effects of Lipidium sativum group (LS) water extract were
assessed after 8 weeks by attenuated total reflection spectroscopy
ATR-IR and histologically by light microscope. ATR-IR results
revealed that the membrane phospholipid undergo free radical
attacks, mediated by AlCl3, primary affects the polyunsaturated fatty
acids indicated by the increased of the olefinic -C=CH sub-band area
around 3012 cm-1 from the curve fitting analysis. The narrowing in
the half band width (HBW) of the sνCH2 sub-band around 2852 cm-1
due to Al intoxication indicates the presence of trans form fatty acids
rather than gauch rotomer. The degradation of hydrocarbon chain to
shorter chain length, increasing in membrane fluidity, disorder, and
decreasing in lipid polarity in AlCl3 group indicated by the detected
changes in certain calculated area ratios compared to the control.
Administration of LS was greatly improved these parameters
compared to the AlCl3 group. Al influences the Aβ aggregation and
plaque formation, which in turn interferes to and disrupts the
membrane structure. The results also showed a marked increase in
the β-parallel and antiparallel structure, that characterize the Aβ
formation in Al-induced AD hippocampal brain tissue, indicated by
the detected increase in both amide I sub-bands around 1674, 1692
cm-1. This drastic increase in Aβ formation was greatly reduced in the
curative and protective groups compared to the AlCl3 group and
approached nearly the control values. These results supported too by
the light microscope. AlCl3 group showed significant marked
degenerative changes in hippocampal neurons. Most cells appeared
small, shrieked and deformed. Interestingly, the administration of LS
in curative and protective groups markedly decreases the amount of
degenerated cells compared to the non-treated group. In addition, the
intensity of congo red stained cells was decreased. Hippocampal
neurons looked more/or less similar to those of control. This study showed a promising therapeutic effect of Lipidium
sativum group (LS) on AD rat model that seriously overcome the
signs of oxidative stress on membrane lipid and restore the protein
misfolding.
Abstract: Ceramic obtained on the base of aluminum oxide has
wide application range, because it has unique properties, for example,
wear-resistance, dielectric characteristics, and exploitation ability at
high temperatures and in corrosive atmosphere. Low temperature
synthesis of α-Al2O3 is energo-economical process and it is topical
for developing technologies of corundum ceramics fabrication. In the present work possibilities of low temperature transformation
of oxyhydroxides in α-Al2O3, during the presence of small amount of
rare–earth elements compounds (also Th, Re), have been discussed.
Aluminum unstable oxyhydroxides have been obtained by hydrolysis
of aluminium isopropoxide, nitrates, sulphate, and chloride in
alkaline environment at 80-90ºC temperatures. β-Al(OH)3 has been
received from aluminum powder by ultrasonic development. Drying
of oxyhydroxide sol has been conducted with presence of various
types seeds, which amount reaches 0,1-0,2% (mas). Neodymium,
holmium, thorium, lanthanum, cerium, gadolinium, disprosium
nitrates and rhenium carbonyls have been used as seeds and they
have been added to the sol specimens in amount of 0.1-0.2% (mas)
calculated on metals. Annealing of obtained gels is carried out at 70–
1100ºC for 2 hrs. The same specimen transforms in α-Al2O3 at
1100ºC. At this temperature in case of presence of lanthanum and
gadolinium transformation takes place by 70-85%. In case of
presence of thorium stabilization of γ-and θ-phases takes place. It is
established, that thorium causes inhibition of α-phase generation at
1100ºC, and at the time when in all other doped specimens α-phase is
generated at lower temperatures (1000-1050ºC). Synthesis of various
type compounds and simultaneous consolidation has developed in the
furnace of OXY-GON. Composite materials containing oxide and
non-oxide components close to theoretical data have been obtained in
this furnace respectively. During the work the following devices have
been used: X-ray diffractometer DRON-3M (Cu-Kα, Ni filter,
2º/min), High temperature vacuum furnace OXY-GON, electronic
scanning microscopes Nikon ECLIPSE LV 150, NMM-800TRF,
planetary mill Pulverisette 7 premium line, SHIMADZU Dynamic
Ultra Micro Hardness Tester, DUH-211S, Analysette 12 Dyna sizer.
Abstract: Erosion and abrasion are wear mechanisms reducing
the lifetime of machine elements like valves, pump and pipe systems.
Both wear mechanisms are acting at the same time, causing a
“Synergy” effect, which leads to a rapid damage of the surface.
Different parameters are effective on erosive abrasive wear rate. In
this study effect of particle impact angle on wear rate and wear
mechanism of ductile and brittle materials was investigated. A new
slurry pot was designed for experimental investigation. As abrasive
particle, silica sand was used. Particle size was ranking between 200-
500 μm. All tests were carried out in a sand-water mixture of 20%
concentration for four hours. Impact velocities of the particles were
4.76 m/s. As ductile material steel St 37 with Vickers Hardness
Number (VHN) of 245 and quenched St 37 with 510 VHN was used
as brittle material. After wear tests, morphology of the eroded
surfaces were investigated for better understanding of the wear
mechanisms acting at different impact angles by using Scanning
Electron Microscope. The results indicated that wear rate of ductile
material was higher than brittle material. Maximum wear rate was
observed by ductile material at a particle impact angle of 300 and
decreased further by an increase in attack angle. Maximum wear rate
by brittle materials was by impact angle of 450 and decreased further
up to 900. Ploughing was the dominant wear mechanism by ductile
material. Microcracks on the surface were detected by ductile
materials, which are nucleation centers for crater formation. Number
of craters decreased and depth of craters increased by ductile
materials by attack angle higher than 300. Deformation wear
mechanism was observed by brittle materials. Number and depth of
pits decreased by brittle materials by impact angles higher than 450.
At the end it is concluded that wear rate could not be directly related
to impact angle of particles due to the different reaction of ductile and
brittle materials.
Abstract: This paper presents thermal annealing de-wetting
technique for the preparation of porous metal membrane for Thin
Film Encapsulation (TFE) application. Thermal annealing de-wetting
experimental results reveal that pore size formation in porous metal
membrane depend upon i.e. 1. The substrate at which metal is
deposited, 2. Melting point of metal used for porous metal cap layer
membrane formation, 3. Thickness of metal used for cap layer, 4.
Temperature used for formation of porous metal membrane. In order
to demonstrate this technique, Silver (Ag) was used as a metal for
preparation of porous metal membrane on amorphous silicon (a-Si)
and silicon oxide. The annealing of the silver thin film of various
thicknesses was performed at different temperature. Pores in porous
silver film were analyzed using Scanning Electron Microscope
(SEM). In order to check the usefulness of porous metal film for TFE
application, the porous silver film prepared on amorphous silicon (a-
Si) and silicon oxide was released using XeF2 and VHF, respectively.
Finally, guide line and structures are suggested to use this porous
membrane for robust TFE application.
Abstract: This study was conducted to determine sex
differentiation of laboratory reared Elm nymphalid (Nymphalis
polychloros Linnaeus, 1758) by examining the morphological
structure of pupal stage. Laboratory colony of elm nymphalid, reared
on pear leaves, was used to set up experiments. It was performed
with 5 replications having 8 pupae for each replication. Dorsal,
ventral and lateral parts of external morphological structures of pupae
were examined by Olympus SZX9 stereozoom microscope and
photographed. When fully grown, mature larvae wander the highest
part of the rearing cage and pupae were formed hanging by
cremaster. After completing prepupa stage about 1.5±0.3 days, they
all pupated. Pupal stage was completed at 24±1°C about 4.38±1.20
days. Pupal weights were 0.483±0.05 g in females and 0.392±0.08 g
(n=40) in males respectively. Pupal emergence rate was 95%, with
22 females and 16 males. Examinations of ventral parts of 8th, 9th,
and 10th abdominal segments revealed that anal opening were found
at 10th abdominal segment in both sexes, 3 lumps were determined at
9th abdominal segments then the specific opening structure at 8th
segment was only found on female pupae.
Abstract: In this study, to clarify the effectiveness of an
aluminum/chromium/tungsten-based-coated tool for cutting sintered
steel, tool wear was experimentally investigated. The sintered steel
was turned with the (Al60,Cr25,W15)N-, (Al60,Cr25,W15)(C,N)- and
(Al64,Cr28,W8)(C,N)-coated cemented carbide tools according to the
physical vapor deposition (PVD) method. Moreover, the tool wear of
the aluminum/chromium/tungsten-based-coated item was compared
with that of the (Al,Cr)N coated tool. Furthermore, to clarify the tool
wear mechanism of the aluminum/chromium/tungsten-coating film for
cutting sintered steel, Scanning Electron Microscope observation and
Energy Dispersive x-ray Spectroscopy mapping analysis were
conducted on the abraded surface. The following results were
obtained: (1) The wear progress of the (Al64,Cr28,W8)(C,N)-coated
tool was the slowest among that of the five coated tools. (2) Adding
carbon (C) to the aluminum/chromium/tungsten-based-coating film
was effective for improving the wear-resistance. (3) The main wear
mechanism of the (Al60,Cr25,W15)N-, the (Al60,Cr25,W15)(C,N)-
and the (Al64,Cr28,W8)(C,N)-coating films was abrasive wear.
Abstract: Superabsorbent polymers received much attention and
are used in many fields because of their superior characters to
traditional absorbents, e.g., sponge and cotton. So, it is very
important but challenging to prepare highly and fast-swelling
superabsorbents. A reliable, efficient and low-cost technique for
removing heavy metal ions from wastewater is the adsorption using
bio-adsorbents obtained from biological materials, such as
polysaccharides-based hydrogels superabsorbents. In this study, novel multi-functional superabsorbent composites
type semi-interpenetrating polymer networks (Semi-IPNs) were
prepared via graft polymerization of acrylamide onto chitosan
backbone in presence of gelatin, CTS-g-PAAm/Ge, using potassium
persulfate and N,N’-methylene bisacrylamide as initiator and
crosslinker, respectively. These hydrogels were also partially
hydrolyzed to achieve superabsorbents with ampholytic properties
and uppermost swelling capacity. The formation of the grafted
network was evidenced by Fourier Transform Infrared Spectroscopy
(ATR-FTIR) and Thermogravimetric Analysis (TGA). The porous
structures were observed by Scanning Electron Microscope (SEM).
From TGA analysis, it was concluded that the incorporation of the Ge
in the CTS-g-PAAm network has marginally affected its thermal
stability. The effect of gelatin content on the swelling capacities of
these superabsorbent composites was examined in various media
(distilled water, saline and pH-solutions). The water absorbency was
enhanced by adding Ge in the network, where the optimum value was
reached at 2 wt. % of Ge. Their hydrolysis has not only greatly
optimized their absorption capacity but also improved the swelling
kinetic.These materials have also showed reswelling ability. We
believe that these super-absorbing materials would be very effective
for the adsorption of harmful metal ions from wastewater.
Abstract: Intermetallic materials are among advanced
technology materials that have outstanding mechanical and physical
properties for high temperature applications. Especially creep
resistance, low density and high hardness properties stand out in such
intermetallics. The microstructure, mechanical properties of %88Ni-
%10Cr and %2Mn powders were investigated using specimens
produced by tube furnace sintering at 900-1300°C temperature. A
composite consisting of ternary additions, a metallic phase, Fe, Cr
and Mn have been prepared under Ar shroud and then tube furnace
sintered. XRD, SEM (Scanning Electron Microscope), were
investigated to characterize the properties of the specimens.
Experimental results carried out for composition %88Ni-%10Cr and
%2Mn at 1300°C suggest that the best properties as 138,80HV and
6,269/cm3 density were obtained at 1300°C.
Abstract: In this study, ultrasonic assisted machining (UAM) technique is applied in side-surface milling experiment for glass-ceramic workpiece material. The tungsten carbide cutting-tool with diamond coating is used in conjunction with two kinds of cooling/lubrication mediums such as water-soluble (WS) cutting fluid and minimum quantity lubricant (MQL). Full factorial process parameter combinations on the milling experiments are planned to investigate the effect of process parameters on cutting performance. From the experimental results, it tries to search for the better process parameter combination which the edge-indentation and the surface roughness are acceptable. In the machining experiments, ultrasonic oscillator was used to excite a cutting-tool along the radial direction producing a very small amplitude of vibration frequency of 20KHz to assist the machining process. After processing, toolmaker microscope was used to detect the side-surface morphology, edge-indentation and cutting tool wear under different combination of cutting parameters, and analysis and discussion were also conducted for experimental results. The results show that the main leading parameters to edge-indentation of glass ceramic are cutting depth and feed rate. In order to reduce edge-indentation, it needs to use lower cutting depth and feed rate. Water-soluble cutting fluid provides a better cooling effect in the primary cutting area; it may effectively reduce the edge-indentation and improve the surface morphology of the glass ceramic. The use of ultrasonic assisted technique can effectively enhance the surface finish cleanness and reduce cutting tool wear and edge-indentation.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: Morphological interaction of porcine cumulus-oocyte
complexes (pCOCs) was investigated on in vitro condition using
electron microscope (SEM and TEM). The totals of 1,923 oocytes
were round in shape, surrounded by Zona pellucida with layer of
cumulus cells ranging between 59.29-202.14 μm in size. They were
classified into intact-, multi-, partial cumulus cell layer oocyte, and
completely denuded oocyte, at the percentage composition of 22.80%
32.70%, 18.60%, and 25.90 % respectively. The pCOCs classified as
intact- and multi cumulus cell layer oocytes were further culturing at
37°C with 5% CO2, 95% air atmosphere and high humidity for 44 h
in M199 with Earle’s salts supplemented with 10% HTFCS, 2.2
mg/mL NaHCO3, 1 M Hepes, 0.25 mM pyruvate, 15 μg/mL porcine
follicle-stimulating hormone, 1 μg/mL LH, 1μg/mL estradiol with
ethanol, and 50 μg/mL gentamycin sulfate. On electron microscope
study, cumulus cells were found to stick their processes to secrete
substance from the sac-shape end into Zona pellucida of the oocyte
and also communicated with the neighboring cells through their
microvilli on the beginning of incubation period. It is believed that
the cumulus cells communicate with the oocyte by inserting the
microvilli through this gap and embedded in the oocyte cytoplasm
before secreting substance, through the sac-shape end of the
microvilli, to inhibit primary oocyte development at the prophase I.
Morphological changes of the complexes were observed after
culturing for 24-44 h. One hundred percentages of the cumulus layers
were expanded and cumulus cells were peeling off from the oocyte
surface. In addition, the round-shape cumulus cells transformed
themselves into either an elongate shape or a columnar shape, and no
communication between cumulus neighboring cells. After 44 h of
incubation time, diameter of oocytes surrounded by cumulus cells
was larger than 0 h incubation. The effect of hormones in culture
medium is exerted by their receptors present in porcine oocyte. It is
likely that all morphological changes of the complexes after hormone
treatment were to allow maturation of the oocyte. This study
demonstrated that the association of hormones in M199 could
promote porcine follicle activation in 44 h in vitro condition. This
culture system should be useful for studying the regulation of early
follicular growth and development, especially because these follicles represent a large source of oocytes that could be used in vitro for cell
technology.
Abstract: Considering palm oil as non-drying oil owing to its
low iodine value, an attempt was taken to increase the unsaturation in
the fatty acid chains of palm oil for the preparation of alkyds. To
increase the unsaturation in the palm oil, sulphuric acid (SA) and
para-toluene sulphonic acid (PTSA) was used prior to alcoholysis for
the dehydration process. The iodine number of the oil samples was
checked for the unsaturation measurement by Wijs method. Alkyd
resin was prepared using the dehydrated palm oil by following
alcoholysis and esterification reaction. To improve the film properties
0.5wt.% multi-wall carbon nano tubes (MWCNTs) were used to
manufacture polymeric film. The properties of the resins were
characterized by various physico-chemical properties such as density,
viscosity, iodine value, saponification value, etc. Structural
elucidation was confirmed by Fourier transform of infrared
spectroscopy and proton nuclear magnetic resonance; surfaces of the
films were examined by field-emission scanning electron microscope.
In addition, pencil hardness and chemical resistivity was also
measured by using standard methods. The effect of enhancement of
the unsaturation in the fatty acid chain found significant and
motivational. The resin prepared with dehydrated palm oil showed
improved properties regarding hardness and chemical resistivity
testing. The incorporation of MWCNTs enhanced the thermal
stability and hardness of the films as well.
Abstract: In recent years, the hair building fiber has become
popular, in other words, it is an effective method which helps people
who suffer hair loss or sparse hair since the hair building fiber is
capable to create a natural look of simulated hair rapidly. In the
markets, there are a lot of hair fiber brands that have been designed to
formulate an intense bond with hair strands and make the hair appear
more voluminous instantly. However, those products have their own
set of properties. Thus, in this report, some measurement techniques
are proposed to identify those products. Up to five different brands of
hair fiber are tested. The electrostatic and dielectric properties of the
hair fibers are macroscopically tested using design DC and high
frequency microwave techniques. Besides, the hair fibers are
microscopically analysis by magnifying the structures of the fiber
using scanning electron microscope (SEM). From the SEM photos,
the comparison of the uniformly shaped and broken rate of the hair
fibers in the different bulk samples can be observed respectively.
Abstract: Microbial fuel cells (MFCs) represent a promising
technology for simultaneous bioelectricity generation and wastewater
treatment. Catalysts are significant portions of the cost of microbial
fuel cell cathodes. Many materials have been tested as aqueous
cathodes, but air-cathodes are needed to avoid energy demands for
water aeration. The sluggish oxygen reduction reaction (ORR) rate at
air cathode necessitates efficient electrocatalyst such as carbon
supported platinum catalyst (Pt/C) which is very costly. Manganese
oxide (MnO2) was a representative metal oxide which has been
studied as a promising alternative electrocatalyst for ORR and has
been tested in air-cathode MFCs. However the single MnO2 has poor
electric conductivity and low stability. In the present work, the MnO2
catalyst has been modified by doping Pt nanoparticle. The goal of the
work was to improve the performance of the MFC with minimum Pt
loading. MnO2 and Pt nanoparticles were prepared by hydrothermal
and sol gel methods, respectively. Wet impregnation method was
used to synthesize Pt/MnO2 catalyst. The catalysts were further used
as cathode catalysts in air-cathode cubic MFCs, in which anaerobic
sludge was inoculated as biocatalysts and palm oil mill effluent
(POME) was used as the substrate in the anode chamber. The asprepared
Pt/MnO2 was characterized comprehensively through field
emission scanning electron microscope (FESEM), X-Ray diffraction
(XRD), X-ray photoelectron spectroscopy (XPS), and cyclic
voltammetry (CV) where its surface morphology, crystallinity,
oxidation state and electrochemical activity were examined,
respectively. XPS revealed Mn (IV) oxidation state and Pt (0)
nanoparticle metal, indicating the presence of MnO2 and Pt.
Morphology of Pt/MnO2 observed from FESEM shows that the
doping of Pt did not cause change in needle-like shape of MnO2
which provides large contacting surface area. The electrochemical
active area of the Pt/MnO2 catalysts has been increased from 276 to
617 m2/g with the increase in Pt loading from 0.2 to 0.8 wt%. The
CV results in O2 saturated neutral Na2SO4 solution showed that
MnO2 and Pt/MnO2 catalysts could catalyze ORR with different
catalytic activities. MFC with Pt/MnO2 (0.4 wt% Pt) as air cathode
catalyst generates a maximum power density of 165 mW/m3, which
is higher than that of MFC with MnO2 catalyst (95 mW/m3). The
open circuit voltage (OCV) of the MFC operated with MnO2 cathode
gradually decreased during 14 days of operation, whereas the MFC
with Pt/MnO2 cathode remained almost constant throughout the
operation suggesting the higher stability of the Pt/MnO2 catalyst.
Therefore, Pt/MnO2 with 0.4 wt% Pt successfully demonstrated as an
efficient and low cost electrocatalyst for ORR in air cathode MFC with higher electrochemical activity, stability and hence enhanced
performance.
Abstract: The wear measuring and wear modelling are
fundamental issues in the industrial field, mainly correlated to the
economy and safety. Therefore, there is a need to study the wear
measurements and wear estimation. Pin-on-disc test is the most
common test which is used to study the wear behaviour. In this paper,
the pin-on-disc (AEROTECH UNIDEX 11) is used for the
investigation of the effects of normal load and hardness of material on
the wear under dry and sliding conditions. In the pin-on-disc rig, two
specimens were used; one, a pin is made of steel with a tip, positioned
perpendicular to the disc, where the disc is made of aluminium. The
pin wear and disc wear were measured by using the following
instruments: The Talysurf instrument, a digital microscope, and the
alicona instrument. The Talysurf profilometer was used to measure
the pin/disc wear scar depth, digital microscope was used to measure
the diameter and width of wear scar, and the alicona was used to
measure the pin wear and disc wear. After that, the Archard model,
American Society for Testing and Materials model (ASTM), and
neural network model were used for pin/disc wear modelling.
Simulation results were implemented by using the Matlab program.
This paper focuses on how the alicona can be used for wear
measurements and how the neural network can be used for wear
estimation.
Abstract: In the scope of application of technical textiles, Non-
Crimp Fabrics are increasingly used. In general, NCF exhibit
excellent load bearing properties, but caused by the manufacturing
process, there are some remaining disadvantages which have to be
reduced. Regarding to this, a novel technique of processing NCF was
developed substituting the binding-thread by an adhesive. This stitchfree
method requires new manufacturing concept as well as new basic
methods to prove adhesion of glue at fibres and textiles. To improve
adhesion properties and the wettability of carbon-fibres by the
adhesive, oxy-fluorination was used. The modification of carbonfibres
by oxy-fluorination was investigated via scanning electron
microscope, X-ray photoelectron spectroscopy and single fibre
tensiometry. Special tensile tests were developed to determine the
maximum force required for detachment.
Abstract: To develop AZ91D magnesium alloys with improved
properties, we have applied TiN and VN/TiN multilayer coatings
using DC magnetron sputter technique. Coating structure, surface
morphology, chemical bonding and corrosion resistance of coatings
were analyzed by x-ray diffraction (XRD), scanning electron
microscope (SEM), x-ray photoelectron spectroscopy (XPS), and
tafel extrapolation method, respectively. XPS analysis reveal that VN
overlayer reacts with oxygen at the VN/TiN interface and forms more
stable TiN layer. Morphological investigations and the corrosion
results show that VN/TiN multilayer thin film coatings are quite
effective to optimize the corrosion resistance of Mg alloys.