Abstract: The microstructure, mechanical properties and metalgraphic characteristics of Ni plated AlN-Astaloy Cr-M powders were investigated using specimens produced by tube furnace sintering at 1000-1400 °C temperature. A uniform nickel layer on AlN powders was deposited prior to sintering using electroless plating technique. A composite consisting of ternary additions, metallic phase, Ni and ceramic phase AlN within a matrix of Astaloy Cr-M had been prepared under Ar shroud and then tube furnace sintered. The experimental results carried out by using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscope) for composition (10% AlN-Astaloy Cr-M) 10% Ni at 1400 °C suggest that the best properties as 132.45HB and permittivity were obtained at 1400 °C.
Abstract: Intermetallic materials are among advanced
technology materials that have outstanding mechanical and physical
properties for high temperature applications. Especially creep
resistance, low density and high hardness properties stand out in such
intermetallics. The microstructure, mechanical properties of %88Ni-
%10Cr and %2Mn powders were investigated using specimens
produced by tube furnace sintering at 900-1300°C temperature. A
composite consisting of ternary additions, a metallic phase, Fe, Cr
and Mn have been prepared under Ar shroud and then tube furnace
sintered. XRD, SEM (Scanning Electron Microscope), were
investigated to characterize the properties of the specimens.
Experimental results carried out for composition %88Ni-%10Cr and
%2Mn at 1300°C suggest that the best properties as 138,80HV and
6,269/cm3 density were obtained at 1300°C.