Abstract: This paper presents an experimental study on
structural performance of an innovative noise barrier consisting of
poly-block, light polyurethane foam (LPF) and polyurea. This wall
system (flexi-wall) is intended to be employed as a vertical extension
to existing sound barriers in an accelerated construction method. To
aid in the wall design, several mechanical tests were conducted on
LPF specimens and two full-scale walls were then fabricated
employing the same LPF material. The full-scale walls were
subjected to lateral loading in order to establish their lateral
resistance. A cyclic fatigue test was also performed on a full-scale
flexi-wall in order to evaluate the performance of the wall under a
repetitive loading condition. The result of the experiments indicated
the suitability of flexi-wall in accelerated construction and confirmed
that the structural performance of the wall system under lateral
loading is satisfactory for the sound barrier application. The
experimental results were discussed and a preliminary design
procedure for application of flexi-wall in sound barrier applications
was also developed.
Abstract: When printing a plate (or dish) by an FDM 3D printer,
the process normally requires support material, which causes several
problems. This paper proposes a method for forming thin plates
without using wasteful support material. This method requires several
extraordinary parameter values when slicing plates. The experiments
show that the plates can, for the most part, be successfully formed
using a conventional slicer and a 3D printer; however, seams between
layers spoil them and the quality of printed objects strongly depends
on the slicer.
Abstract: In this paper, we investigated the athermal pressure
behavior of the structural and elastic properties of scheelite BaWO4
phase up to 7 GPa using the ab initio pseudo-potential method. The
calculated lattice parameters pressure relation have been compared
with the experimental values and found to be in good agreement with
these results. Moreover, we present for the first time the investigation
of the elastic properties of this compound using the density functional
perturbation theory (DFPT). It is shown that this phase is
mechanically stable up to 7 GPa after analyzing the calculated elastic
constants. Other relevant quantities such as bulk modulus, pressure
derivative of bulk modulus, shear modulus; Young’s modulus,
Poisson’s ratio, anisotropy factors, Debye temperature and sound
velocity have been calculated. The obtained results, which are
reported for the first time to the best of the author’s knowledge, can
facilitate assessment of possible applications of the title material.
Abstract: The crude methanol extracts of five indigenous vegetables namely, Amarathus tricolor, Basella rubra L., Chochurus olitorius L., Ipomea batatas, and Momordica chuchinensis L., were examined for their phytochemical profile and antioxidant activity using 1,1-diphenyl-2-picrylhydrazyl (DPPH) free radical. The values for DPPH radical scavenging activity ranged from 7.6-89.53% with B. rubra and I. batatas having the lowest and highest values, respectively. The total flavonoid content of all five indigenous vegetables ranged from 74.65-277.3 mg quercetin equivalent per gram of dried vegetable material while the total phenolic content ranged from 1.93-6.15 mg gallic acid equivalent per gram dried material. Phytochemical screening revealed the presence of steroids, flavonoids, saponins, tannins, carbohydrates and reducing sugars, which may also be associated with the antioxidant activity shown by these indigenous vegetables.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: The substantial development of the construction
industry has forced the cement industry, its major support, to focus
on achieving maximum productivity to meet the growing demand for
this material. This means that the reliability of a cement production
system needs to be at the highest level that can be achieved by good
maintenance. This paper studies the extent to which the
implementation of RCM is needed as a strategy for increasing the
reliability of the production systems component can be increased,
thus ensuring continuous productivity. In a case study of four Libyan
cement factories, 80 employees were surveyed and 12 top and middle
managers interviewed. It is evident that these factories usually
breakdown more often than once per month which has led to a
decline in productivity. In many times they cannot achieve the
minimum level of production amount. This has resulted from the
poor reliability of their production systems as a result of poor or
insufficient maintenance. It has been found that most of the factories’
employees misunderstand maintenance and its importance. The main
cause of this problem is the lack of qualified and trained staff, but in
addition it has been found that most employees are not found to be
motivated as a result of a lack of management support and interest. In
response to these findings, it has been suggested that the RCM
strategy should be implemented in the four factories. The results
show the importance of the development of maintenance strategies
through the implementation of RCM in these factories. The purpose
of it would be to overcome the problems that could secure the
reliability of the production systems. This study could be a useful
source of information for academic researchers and the industrial
organizations which are still experiencing problems in maintenance
practices.
Abstract: The aim of this study is to investigate formability of
Al based closed cell metallic foams at high temperature. The foam
specimens with rectangular section were produced from
AlMg1Si0.6TiH20.8 alloy preform material. Bending and free
bending tests based on gravity effect were applied to foam specimens
at high temperatures. During the tests, the time-angular deformation
relationships with various temperatures were determined.
Deformation types formed in cell walls were investigated by means
of Scanning Electron Microscopy (SEM) and optical microscopy.
Bending deformation about 90° was achieved without any defect at
high temperatures. The importance of a critical temperature and
deformation rate was emphasized in maintaining the deformation.
Significant slip lines on surface of cell walls at tensile zones of
bending specimen were observed. At high strain rates, the microcrack
formation in boundaries of elongated grains was determined.
Abstract: One of the main challenges in using the Discrete
Element Method (DEM) is to specify the correct input parameter
values. In general, the models are sensitive to the input parameter
values and accurate results can only be achieved if the correct values
are specified. For the linear contact model, micro-parameters such as
the particle density, stiffness, coefficient of friction, as well as the
particle size and shape distributions are required. There is a need for
a procedure to accurately calibrate these parameters before any
attempt can be made to accurately model a complete bulk materials
handling system. Since DEM is often used to model applications in
the mining and quarrying industries, a calibration procedure was
developed for materials that consist of relatively large (up to 40 mm
in size) particles. A coarse crushed aggregate was used as the test
material. Using a specially designed large shear box with a diameter
of 590 mm, the confined Young’s modulus (bulk stiffness) and
internal friction angle of the material were measured by means of the
confined compression test and the direct shear test respectively. DEM
models of the experimental setup were developed and the input
parameter values were varied iteratively until a close correlation
between the experimental and numerical results was achieved. The
calibration process was validated by modelling the pull-out of an
anchor from a bed of material. The model results compared well with
experimental measurement.
Abstract: Fly ash (FA) thanks to the significant presence of SiO2
and Al2O3 as the main components is a potential raw material for
geopolymers production. Mechanical activation is a method for
improving FA reactivity and also the porosity of final mixture; those
parameters can be analysed through sorption properties. They have
direct impact on the durability of fly ash based geopolymer mortars.
In the paper, effect of FA fineness on sorption properties of
geopolymers based on sodium silicate, as well as relationship
between fly ash fineness and apparent density, compressive and
flexural strength of geopolymers are presented. The best results in the
evaluated area reached the sample H1, which contents the highest
portion of particle under 20μm (100% of GFA). The interdependence
of individual tested properties was confirmed for geopolymer
mixtures corresponding to those in the cement based mixtures: higher
is portion of fine particles < 20μm, higher is strength, density and
lower are sorption properties. The compressive strength as well as
sorption parameters of the geopolymer can be reasonably controlled
by grinding process and also ensured by the higher share of fine
particle (to 20μm) in total mass of the material.
Abstract: In this study, ultrasonic assisted machining (UAM) technique is applied in side-surface milling experiment for glass-ceramic workpiece material. The tungsten carbide cutting-tool with diamond coating is used in conjunction with two kinds of cooling/lubrication mediums such as water-soluble (WS) cutting fluid and minimum quantity lubricant (MQL). Full factorial process parameter combinations on the milling experiments are planned to investigate the effect of process parameters on cutting performance. From the experimental results, it tries to search for the better process parameter combination which the edge-indentation and the surface roughness are acceptable. In the machining experiments, ultrasonic oscillator was used to excite a cutting-tool along the radial direction producing a very small amplitude of vibration frequency of 20KHz to assist the machining process. After processing, toolmaker microscope was used to detect the side-surface morphology, edge-indentation and cutting tool wear under different combination of cutting parameters, and analysis and discussion were also conducted for experimental results. The results show that the main leading parameters to edge-indentation of glass ceramic are cutting depth and feed rate. In order to reduce edge-indentation, it needs to use lower cutting depth and feed rate. Water-soluble cutting fluid provides a better cooling effect in the primary cutting area; it may effectively reduce the edge-indentation and improve the surface morphology of the glass ceramic. The use of ultrasonic assisted technique can effectively enhance the surface finish cleanness and reduce cutting tool wear and edge-indentation.
Abstract: Activated carbon is an amorphous carbon chain which
has extremely extended surface area. High surface area of activated
carbon is due to the porous structure. Activated carbon, using a
variety of materials such as coal and cellulosic materials; can be
obtained by both physical and chemical methods. The prepared
activated carbon can be used for decolorize, deodorize and also can
be used for removal of organic and non-organic pollution. In this
study, pomegranate peel was subjected to 800W microwave power
for 1 to 4 minutes. Also fresh pomegranate peel was used for the
reference material. Then ZnCl2 was used for the chemical activation
purpose. After the activation process, activated pomegranate peels
were used for the adsorption of Zn metal (40 ppm) in the waste water.
As a result of the adsorption experiments, removal of heavy metals
ranged from 89% to 85%.
Abstract: The key role in phenomenological modelling of cyclic
plasticity is good understanding of stress-strain behaviour of given
material. There are many models describing behaviour of materials
using numerous parameters and constants. Combination of individual
parameters in those material models significantly determines whether
observed and predicted results are in compliance. Parameter
identification techniques such as random gradient, genetic algorithm
and sensitivity analysis are used for identification of parameters using
numerical modelling and simulation. In this paper genetic algorithm
and sensitivity analysis are used to study effect of 4 parameters of
modified AbdelKarim-Ohno cyclic plasticity model. Results
predicted by Finite Element (FE) simulation are compared with
experimental data from biaxial ratcheting test with semi-elliptical
loading path.
Abstract: Catalytic combustion of methane is imperative due to
stability of methane at low temperature. Methane (CH4), therefore,
remains unconverted in vehicle exhausts thereby causing greenhouse
gas GHG emission problem. In this study, heterogeneous catalysts of
palladium with bio-char (2 wt% Pd/Bc) and Al2O3 (2wt% Pd/ Al2O3)
supports were prepared by incipient wetness impregnation and then
subsequently tested for catalytic combustion of CH4. Support-porous
heterogeneous catalytic combustion (HCC) material were selected
based on factors such as surface area, porosity, thermal stability,
thermal conductivity, reactivity with reactants or products, chemical
stability, catalytic activity, and catalyst life. Sustainable and
renewable support-material of bio-mass char derived from palm shell
waste material was compared with those from the conventional
support-porous materials. Kinetic rate of reaction was determined for
combustion of methane on Palladium (Pd) based catalyst with Al2O3
support and bio-char (Bc). Material characterization was done using
TGA, SEM, and BET surface area. The performance test was
accomplished using tubular quartz reactor with gas mixture ratio of
3% methane and 97% air. The methane porous-HCC conversion was
carried out using online gas analyzer connected to the reactor that
performed porous-HCC. BET surface area for prepared 2 wt% Pd/Bc
is smaller than prepared 2wt% Pd/ Al2O3 due to its low porosity
between particles. The order of catalyst activity based on kinetic rate
on reaction of catalysts in low temperature was 2wt%
Pd/Bc>calcined 2wt% Pd/ Al2O3> 2wt% Pd/ Al2O3>calcined 2wt%
Pd/Bc. Hence agro waste material can successfully be utilized as an
inexpensive catalyst support material for enhanced CH4 catalytic
combustion.
Abstract: Over the past four decades, the fatigue behavior of
nickel-based alloys has been widely studied. However, in recent
years, significant advances in the fabrication process leading to grain
size reduction have been made in order to improve fatigue properties
of aircraft turbine discs. Indeed, a change in particle size affects the
initiation mode of fatigue cracks as well as the fatigue life of the
material. The present study aims to investigate the fatigue behavior of
a newly developed nickel-based superalloy under biaxial-planar
loading. Low Cycle Fatigue (LCF) tests are performed at different
stress ratios so as to study the influence of the multiaxial stress state
on the fatigue life of the material. Full-field displacement and strain
measurements as well as crack initiation detection are obtained using
Digital Image Correlation (DIC) techniques. The aim of this
presentation is first to provide an in-depth description of both the
experimental set-up and protocol: the multiaxial testing machine, the
specific design of the cruciform specimen and performances of the
DIC code are introduced. Second, results for sixteen specimens
related to different load ratios are presented. Crack detection, strain
amplitude and number of cycles to crack initiation vs. triaxial stress
ratio for each loading case are given. Third, from fractographic
investigations by scanning electron microscopy it is found that the
mechanism of fatigue crack initiation does not depend on the triaxial
stress ratio and that most fatigue cracks initiate from subsurface
carbides.
Abstract: Activated carbons (M4P0, M4P2, and M5P2) used in
this research were produced from palm shell and polyetherether
ketone (PEEK) via carbonization, impregnation and microwave
activation. The adsorption/desorption process was carried out using
static volumetric adsorption. Regeneration is important in the overall
economy of the process and waste minimization. This work focuses
on the thermal regeneration of the CO2 exhausted microwave
activated carbons. The regeneration strategy adopted was thermal
with nitrogen purge desorption with N2 feed flow rate of 20 ml/min
for 1 h at atmospheric pressure followed by drying at 150oC.Seven
successive adsorption/regeneration processes were carried out on the
material. It was found that after seven adsorption regeneration cycles;
the regeneration efficiency (RE) for CO2 activated carbon from palm
shell only (M4P0) was more than 90% while that of hybrid palm
shell-PEEK (M4P2, M5P2) was above 95%. The cyclic adsorption
and regeneration shows the stability of the adsorbent materials.
Abstract: Today, the pollution due to non-degradable material
such as plastics, has led to studies about the development of
environmental-friendly material. Because of biodegradability
obtained from natural sources, polylactid acid (PLA) and ijuk fiber
are interesting to modify into a composite. This material is also
expected to reduce the impact of environmental pollution. Surface
modification of ijuk fiber through alkalinization with 0.25 M NaOH
solution for 30 minutes was aimed to enhance its compatibility to
PLA, in order to improve properties of the composite such as the
mechanical properties. Alkalinization of the ijuk fibers annihilates
some surface components such as lignin, wax and hemicelloluse, so
the pore on the surface clearly appeared, decreasing of the density
and diameter of the ijuk fibers. The change of the ijuk fiber properties
leads to increase the mechanical properties of PLA composites
reinforced the ijuk fibers through strengthening of the mechanical
interlocking with the PLA matrix. An addition to enhance the
distribution of the fibers in the PLA matrix, the stirring during DCM
solvent evaporation from the mixture of the ijuk fibers and the
dissolved-PLA can reduce amount of the trapped-voids and fibers
pull-out phenomena, which can decrease the mechanical properties of
the composite.
Abstract: This work introduces a simple device designed to
perform in-situ direct shear and sinkage tests on granular materials
as sand, clays, or regolith. It consists of a box nested within a larger
box. Both have open bottoms, allowing them to be lowered into the
material. Afterwards, two rotating plates on opposite sides of the
outer box will rotate outwards in order to clear regolith on either
side, providing room for the inner box to move relative to the plates
and perform a shear test without the resistance of the surrounding
soil. From this test, Coulomb parameters, including cohesion and
internal friction angle, as well as, Bekker parameters can be inferred.
This device has been designed for a laboratory setting, but with few
modifications, could be put on the underside of a rover for use in
a remote location. The goal behind this work is to ultimately create
a compact, but accurate measuring tool to put onto a rover or any
kind of exploratory vehicle to test for regolith properties of celestial
bodies.
Abstract: In this study, an experiment was executed related to
the strength of wooden materials which have been commonly used
both in the past and present against pressure and whether fire
retardant materials used against fire have any effects or not. Totally
81 samples which included 3 different wood species, 3 different
sizes, 2 different fire retardants and 2 unprocessed samples were
prepared. Compressive pressure tests were applied to the prepared
samples, their variance analyses were executed in accordance with
the obtained results and it was aimed to determine the most
convenient wooden materials and fire-retardant coating material. It
was also determined that the species of wood and the species of
coating caused the decrease and/or increase in the resistance against
pressure.
Abstract: The current study investigated the influence of milling
time and ball-to-powder (BPR) weight ratio on the microstructural
constituents and mechanical properties of bulk nanocrystalline Al;
Al-10%Cu; and Al-10%Cu-5%Ti alloys. Powder consolidation was
carried out using a high frequency induction heat sintering where the
processed metal powders were sintered into a dense and strong bulk
material. The powders and the bulk samples were characterized using
XRD and FEGSEM techniques. The mechanical properties were
evaluated at various temperatures of 25°C, 100°C, 200°C, 300°C and
400°C to study the thermal stability of the processed alloys. The
processed bulk nanocrystalline alloys displayed extremely high
hardness values even at elevated temperatures. The Al-10%Cu-5%Ti
alloy displayed the highest hardness values at room and elevated
temperatures which are related to the presence of Ti-containing
phases such as Al3Ti and AlCu2Ti. These phases are thermally stable
and retain the high hardness values at elevated temperatures up to
400ºC.
Abstract: A new method for determining the distribution of
birefringence and linear dichroism in optical polymer materials is
presented. The method is based on the use of polarizationholographic
diffraction grating that forms an orthogonal circular basis
in the process of diffraction of probing laser beam on the grating. The
intensities ratio of the orders of diffraction on this grating enables the
value of birefringence and linear dichroism in the sample to be
determined. The distribution of birefringence in the sample is
determined by scanning with a circularly polarized beam with a
wavelength far from the absorption band of the material. If the
scanning is carried out by probing beam with the wavelength near to
a maximum of the absorption band of the chromophore then the
distribution of linear dichroism can be determined. An appropriate
theoretical model of this method is presented. A laboratory setup was
created for the proposed method. An optical scheme of the laboratory
setup is presented. The results of measurement in polymer films with
two-dimensional gradient distribution of birefringence and linear
dichroism are discussed.