Abstract: This paper aims to scale up Dye-sensitized Solar Cell
(DSSC) production using a commonly available industrial material –
stainless steel - and industrial plasma equipment. A working DSSC
electrode formed by (1) coating titania nanotube (TiO2 NT) film on
304 stainless steel substrate using a plasma spray technique; then, (2)
filling the nano-pores of the TiO2 NT film using a TiF4 sol-gel method.
A DSSC device consists of an anode absorbed photosensitive dye
(N3), a transparent conductive cathode with platinum (Pt)
nano-catalytic particles adhered to its surface, and an electrolytic
solution sealed between the anode and the transparent conductive
cathode. The photo-current conversion efficiency of the DSSC sample
was tested under an AM 1.5 Solar Simulator. The sample has a short
current (Isc) of 0.83 mA cm-2, open voltage (Voc) of 0.81V, filling
factor (FF) of 0.52, and conversion efficiency (η) of 2.18% on a 0.16
cm2 DSSC work-piece.
Abstract: TiO2/Ag composite films were prepared by
incorporating Ag in the pores of mesoporous TiO2 films using a
photoreduction method. The Ag nanoparticle sizes were in a range of
3.66-38.56 nm. The TiO2/Ag composite films were characterized by
X-ray diffraction (XRD), scanning electron microscopy (SEM) and
transmission electron microscropy (TEM). The TiO2 films and
TiO2/Ag composite films were immersed in a 0.3 mM N719 dye
solution and characterized by UV-Vis spectrophotometer. The
TiO2/Ag/N719 composite film showed that an optimal size of Ag
nanoparticles was 19.12 nm and, hence, gave the maximum optical
absorption spectra. The improved absorption was due to surface
plasmon resonance induced by the Ag nanoparticles to enhance the
absorption coefficient of the dye.
Abstract: The hard clam (meretrix lusoria) cultivated industry
has been developed vigorously for recent years in Taiwan, and
seawater quality determines the cultivated environment. The pH
concentration variation affects survival rate of meretrix lusoria
immediately. In order to monitor seawater quality, solid-state sensing
electrode of ruthenium-doped titanium dioxide (TiO2:Ru) is developed
to measure hydrogen ion concentration in different cultivated
solutions. Because the TiO2:Ru sensing electrode has high chemical
stability and superior sensing characteristics, thus it is applied as a pH
sensor. Response voltages of TiO2:Ru sensing electrode are readout by
instrument amplifier in different sample solutions. Mean sensitivity
and linearity of TiO2:Ru sensing electrode are 55.20 mV/pH and 0.999
from pH1 to pH13, respectively. We expect that the TiO2:Ru sensing
electrode can be applied to real environment measurement, therefore
we collect two sample solutions by different meretrix lusoria
cultivated ponds in the Yunlin, Taiwan. The two sample solutions are
both measured for 200 seconds after calibration of standard pH buffer
solutions (pH7, pH8 and pH 9). Mean response voltages of sample 1
and sample 2 are -178.758 mV (Standard deviation=0.427 mV) and
-180.206 mV (Standard deviation =0.399 mV), respectively. Response
voltages of the two sample solutions are between pH 8 and pH 9 which
conform to weak alkali range and suitable meretrix lusoria growth. For
long-term monitoring, drift of cultivated solutions (sample 1 and
sample 2) are 1.16 mV/hour and 1.03 mV/hour, respectively.
Abstract: The steady mixed convection boundary layer flow from
a vertical cone in a porous medium filled with a nanofluid is
numerically investigated using different types of nanoparticles as Cu
(copper), Al2O3 (alumina) and TiO2 (titania). The boundary value
problem is solved by using the shooting technique by reducing it
into an ordinary differential equation. Results of interest for the local
Nusselt number with various values of the constant mixed convection
parameter and nanoparticle volume fraction parameter are evaluated.
It is found that dual solutions exist for a certain range of mixed
convection parameter.
Abstract: Noble metal participation in nanostructured
semiconductor catalysts has drawn much interest because of their
improved properties. Recently, it has been discussed by many
researchers that Ag participation in TiO2, CuO, ZnO semiconductors
showed improved photocatalytic and optical properties. In this
research, Ag/ZnO nanocomposite particles were prepared by
Ultrasonic Spray Pyrolysis(USP) Method. 0.1M silver and zinc
nitrate aqueous solutions were used as precursor solutions. The
Ag:Zn atomic ratio of the solution was selected 1:1. Experiments
were taken place under constant air flow of 400 mL/min at 800°C
furnace temperature. Particles were characterized by X-Ray
Diffraction (XRD), Scanning Electron Microscope (SEM) and
Energy Dispersive Spectroscopy (EDS). The crystallite sizes of Ag
and ZnO in composite particles are 24.6 nm, 19.7 nm respectively.
Although, spherical nanocomposite particles are in a range of 300-
800 nm, these particles are formed by the aggregation of primary
particles which are in a range of 20-60 nm.
Abstract: In this study, we sought to investigate the mercury
removal efficiency of manganese oxides from natural gas. The
fundamental studies on mercury removal with manganese oxides
sorbents were carried out in a laboratory scale fixed bed reactor at 30
°C with a mixture of methane (20%) and nitrogen gas laden with 4.8
ppb of elemental mercury. Manganese oxides with varying surface
area and crystalline phase were prepared by conventional precipitation
method in this study. The effects of surface area, crystallinity and
other metal oxides on mercury removal efficiency were investigated.
Effect of Ag impregnation on mercury removal efficiency was also
investigated. Ag supported on metal oxide such titania and zirconia as
reference materials were also used in this study for comparison. The
characteristics of mercury removal reaction with manganese oxide
was investigated using a temperature programmed desorption (TPD)
technique.
Manganese oxides showed very high Hg removal activity (about
73-93% Hg removal) for first time use. Surface area of the manganese
oxide samples decreased after heat-treatment and resulted in complete
loss of Hg removal ability for repeated use after Hg desorption in the
case of amorphous MnO2, and 75% loss of the initial Hg removal
activity for the crystalline MnO2. Mercury desorption efficiency of
crystalline MnO2 was very low (37%) for first time use and high (98%)
after second time use. Residual potassium content in MnO2 may have
some effect on the thermal stability of the adsorbed Hg species.
Desorption of Hg from manganese oxides occurs at much higher
temperatures (with a peak at 400 °C) than Ag/TiO2 or Ag/ZrO2.
Mercury may be captured on manganese oxides in the form of mercury
manganese oxide.
Abstract: Thermal conductivity is an important characteristic of
a nanofluid in laminar flow heat transfer. This paper presents an
improved model for the prediction of the effective thermal
conductivity of nanofluids based on dimensionless groups. The
model expresses the thermal conductivity of a nanofluid as a function
of the thermal conductivity of the solid and liquid, their volume
fractions and particle size. The proposed model includes a parameter
which accounts for the interfacial shell, brownian motion, and
aggregation of particle. The validation of the model is verified by
applying the results obtained by the experiments of Tio2-water and
Al2o3-water nanofluids.
Abstract: Nano-MgO was successfully deposited on titania using deposition-precipitation method. The catalyst produced was characterised using FTIR, XRD, BET and XRF and its activity was tested on the transesterification reaction of soybean oil to biodiesel. The catalyst activity improved when the reaction temperature was increasedfrom 150 and 225 OC. It was also observed that increasing the reaction time above 1h had no significant benefit on conversion. The stability fixed MgO on TiO2 was investigated using XRF and ICP-OES. It was observed that MgO loss during the reaction was between 0.5-2.3 percent and that there was no correlation between the reaction temperature and the MgO loss.
Abstract: In this work, effects of catalysts (TiO2, and Nb2O5) were investigated on the hydrogen desorption of Mg(BH4)2. LiBH4 and MgCl2 with 2:1 molar ratio were mixed by using ball milling to prepare Mg(BH4)2. The desorption behaviors were measured by thermo-volumetric apparatus. The hydrogen desorption capacity of the mixed sample milled for 2 h was 4.78 wt% with a 2-step released. The first step occurred at 214 °C and the second step appeared at 374 °C. The addition of 16 wt% Nb2O5 decreased the desorption temperature in the second step about 66 °C and increased the hydrogen desorption capacity to 4.86 wt% hydrogen. The addition of TiO2 also improved the desorption temperature in the second step and the hydrogen desorption capacity. It decreased the desorption temperature about 71°C and showed a high amount of hydrogen, 5.27 wt%, released from the mixed sample. The hydrogen absorption after desorption of Mg(BH4)2 was also studied under 9.5 MPa and 350 °C for 12 h.
Abstract: Titanium dioxide coatings were deposited by utilizing
atmospheric plasma spraying (APS) system. The agglomerated nanopowder
and different spraying parameters were used to determine
their influences on the microstructure surface feature and photoabsorption
of the coatings. The microstructure of as-sprayed TiO2
coatings were characterized by scanning electron microscope (SEM).
Surface characteristics were investigated by Fourier Transform
Infrared (FT-IR). The photo absorption was determined by UV-VIS
spectrophotometer. It is found that the spray parameters have an
influence on the microstructure, surface feature and photo-absorption
of the TiO2 coatings.
Abstract: In this paper, four carbazole-based D-D-π-A organic
dyes code as CCT2A, CCT3A, CCT1PA and CCT2PA were reported.
A series of these organic dyes containing identical donor and
acceptor group but different π-system. The effect of replacing of
thiophene by phenyl thiophene as π-system on the physical
properties has been focused. The structural, energetic properties and
absorption spectra were theoretically investigated by means of
Density Functional Theory (DFT) and Time-Dependent Density
Functional Theory (TD-DFT). The results show that nonplanar
conformation due to steric hindrance in donor part (cabazolecarbazole
unit) of dye molecule can prevent unfavorable dye
aggregation. By means of the TD-DFT method, the absorption
spectra were calculated by B3LYP and BHandHLYP to study the
affect of hybrid functional on the excitation energy (Eg). The results
revealed the increasing of thiophene units not only resulted in
decreasing of Eg, but also found the shifting of absorption spectra to
higher wavelength. TD-DFT/BHandHLYP calculated results are
more strongly agreed with the experimental data than B3LYP
functions. Furthermore, the adsorptions of CCT2A and CCT3A on the
TiO2 anatase (101) surface were carried out by mean of the chemical
periodic calculation. The result exhibit the strong adsorption energy.
The calculated results provide our new organic dyes can be
effectively used as dye for Dye Sensitized Solar Cell (DSC).
Abstract: Semiconductor nanomaterials like TiO2 nanoparticles
(TiO2-NPs) approximately less than 100 nm in diameter have become
a new generation of advanced materials due to their novel and
interesting optical, dielectric, and photo-catalytic properties. With the
increasing use of NPs in commerce, to date few studies have
investigated the toxicological and environmental effects of NPs.
Motivated by the importance of TiO2-NPs that may contribute to the
cancer research field especially from the treatment prospective
together with the fractal analysis technique, we have investigated the
effect of TiO2-NPs on colony morphology in the dark condition
using fractal dimension as a key morphological characterization
parameter. The aim of this work is mainly to investigate the cytotoxic
effects of TiO2-NPs in the dark on the growth of human cervical
carcinoma (HeLa) cell colonies from morphological aspect. The in
vitro studies were carried out together with the image processing
technique and fractal analysis. It was found that, these colonies were
abnormal in shape and size. Moreover, the size of the control
colonies appeared to be larger than those of the treated group. The
mean Df +/- SEM of the colonies in untreated cultures was
1.085±0.019, N= 25, while that of the cultures treated with TiO2-NPs
was 1.287±0.045. It was found that the circularity of the control
group (0.401±0.071) is higher than that of the treated group
(0.103±0.042). The same tendency was found in the diameter
parameters which are 1161.30±219.56 μm and 852.28±206.50 μm
for the control and treated group respectively. Possible explanation of
the results was discussed, though more works need to be done in
terms of the for mechanism aspects. Finally, our results indicate that
fractal dimension can serve as a useful feature, by itself or in
conjunction with other shape features, in the classification of cancer
colonies.
Abstract: The effect of calcination temperature and MgO crystallite sizes on the structure and catalytic performance of TiO2 supported nano-MgO catalyst for the trans-esterification of soybean oil has been studied. The catalyst has been prepared by deposition precipitation method, characterised by XRD and FTIR and tested in an autoclave at 225oC. The soybean oil conversion after 15 minutes of the trans-esterification reaction increased when the calcination temperature was increased from 500 to 600oC and decreased with further increase in calcination temperature. Some glycerolysis activity was also detected on catalysts calcined at 600 and 700oC after 45 minutes of reaction. The trans-esterification reaction rate increased with the decrease in MgO crystallite size for the first 30 min.
Abstract: Cu-mesoporous TiO2 is developed for removal acid
odor cooperated with ozone assistance and online- regeneration
system with/without UV irradiation (all weather) in study. The results
showed that Cu-mesoporous TiO2 present the desirable adsorption
efficiency of acid odor without UV irradiation, due to the larger
surface area, pore sizeand the additional absorption ability provided by
Cu. In the photocatalysis process, the material structure also benefits
Cu-mesoporous TiO2 to perform the more outstanding efficiency on
degrading acid odor. Cu also postponed the recombination of
electron-hole pairs excited from TiO2 to enhance photodegradation
ability. Cu-mesoporous TiO2 could gain the conspicuous increase on
photocatalysis ability from ozone assistance, but without any benefit
on adsorption. In addition, the online regeneration procedure could
process the used Cu-mesoporous TiO2 to reinstate the adsorption
ability and maintain the photodegradtion performance, depended on
scrubbing, desorping acid odor and reducing Cu to metal state.
Abstract: The control of oxygen flow rate during growth of
titanium dioxide by mass flow controller in DC plasma sputtering
growth system is studied. The impedance of TiO2 films for inductance
effect is influenced by annealing time and oxygen flow rate. As
annealing time is increased, the inductance of TiO2 film is the more.
The growth condition of optimum and maximum inductance for TiO2
film to serve as sensing device are oxygen flow rate of 15 sccm and
large annealing time. The large inductance of TiO2 film will be
adopted to fabricate the biosensor to obtain the high sensitivity of
sensing in biology.
Abstract: Laboratory experiments have been performed to investigate photocatalytic detoxification by using TiO2 photocatalyst for treating dairy effluent. Various operational parameters such as catalyst concentration, initial concentration, angle of tilt of solar flat plate reactor and flow rate were investigated. Results indicated that the photocatalytic detoxification process can efficiently treat dairy effluent. Experimental runs with dairy wastewater can be used to identify the optimum operational parameters to perform wastewater degradation on large scale for recycling purpose. Also effect of two different types of reactors on degradation process was analyzed.
Abstract: TiO2 nanoparticles were synthesized by hydrothermal
method at 180°C from TiOSO4 aqueous solution with1m/l
concentration. The obtained products were coated with silica by
means of a seeded polymerization technique for a coating time of
1440 minutes to obtain well defined TiO2@SiO2 core-shell structure.
The uncoated and coated nanoparticles were characterized by using
X-Ray diffraction technique (XRD), Fourier Transform Infrared
Spectroscopy (FT-IR) to study their physico-chemical properties.
Evidence from XRD and FTIR results show that SiO2 is
homogenously coated on the surface of titania particles. FTIR spectra
show that there exists an interaction between TiO2 and SiO2 and
results in the formation of Ti-O-Si chemical bonds at the interface of
TiO2 particles and SiO2 coating layer. The non linear optical limiting
properties of TiO2 and TiO2@SiO2 nanoparticles dispersed in
ethylene glycol were studied at 532nm using 5ns Nd:YAG laser
pulses. Three-photon absorption is responsible for optical limiting
characteristics in these nanoparticles and it is seen that the optical
nonlinearity is enhanced in core-shell structures when compared with
single counterparts. This effective three-photon type absorption at
this wavelength, is of potential application in fabricating optical
limiting devices.
Abstract: The degradation of selected pharmaceuticals in some
water matrices was studied by using several chemical treatments. The
pharmaceuticals selected were the beta-blocker metoprolol, the
nonsteroidal anti-inflammatory naproxen, the antibiotic amoxicillin,
and the analgesic phenacetin; and their degradations were conducted
by using UV radiation alone, ozone, Fenton-s reagent, Fenton-like
system, photo-Fenton system, and combinations of UV radiation and
ozone with H2O2, TiO2, Fe(II), and Fe(III). The water matrices, in
addition to ultra-pure water, were a reservoir water, a groundwater,
and two secondary effluents from two municipal WWTP. The results
reveal that the presence of any second oxidant enhanced the
oxidation rates, with the systems UV/TiO2 and O3/TiO2 providing the
highest degradation rates. It is also observed in most of the
investigated oxidation systems that the degradation rate followed the
sequence: amoxicillin > naproxen > metoprolol > phenacetin. Lower
rates were obtained with the pharmaceuticals dissolved in natural
waters and secondary effluents due to the organic matter present
which consume some amounts of the oxidant agents.
Abstract: The photocatalytic activity efficiency of TiO2 for the degradation of Toluene in photoreactor can be enhanced by nano- TiO2/LDPE composite film. Since the amount of TiO2 affected the efficiency of the photocatalytic activity, this work was mainly concentrated on the effort to embed the high amount of TiO2 in the Polyethylene matrix. The developed photocatalyst was characterized by XRD, UV-Vis spectrophotometer and SEM. The SEM images revealed the high homogeneity of the deposition of TiO2 on the polyethylene matrix. The XRD patterns interpreted that TiO2 embedded in the PE matrix exhibited mainly in anatase form. In addition, the photocatalytic results show that the toluene removal efficiencies of 30±5%, 49±4%, 68±5%, 42±6% and 33±5% were obtained when using the catalyst loading at 0%, 10%, 15%, 25% and 50% (wt. cat./wt. film), respectively.
Abstract: A study concerning the photocatalytic decolourization
of Congo red (CR) dye, over artificial UV irradiation is presented.
Photocatalysts based on a commercial titanium dioxide (TiO2)
modified with transition metals (Ni, Cu and Zn) were used. The
dopage method used was wet impregnation. A TiO2 sample without
salt was subjected to the same hydrothermal treatment to be used as
reference. Congo red solutions to several pH conditions (natural and
basic) were used to evaluate photocatalytic performance of each
doped catalysts. Photodecolourization percentage was measured
spectrofotrometically after 3 h of treatment to 499 nm as response
variable. Kinetics investigations of photodegradation indicated that
reactions obey to Langmuir-Hinshelwood model and pseudo–first
order law. The rate constant studies of photocatalytic decolourization
reactions for Zn–TiO2 and Cu–TiO2 photocatalysts indicated that in
all cases the rate constant of the reaction was higher than that of TiO2
undoped. These results show that nature of the metal modifying the
TiO2 influence on the efficiency of the photocatalyst evaluated in
process. Ni does not present an additional effect compared with TiO2,
while Zn enhances the photoactivity due to its electronic properties.