Abstract: This paper presents the effect of corrugation profile
geometry on the crushing behavior, energy absorption, failure
mechanism, and failure mode of woven roving glass fibre/epoxy
laminated composite tube. Experimental investigations were carried
out on composite tubes with three different profile shapes: sinusoidal,
triangular and trapezoidal. The tubes were subjected to lateral
compressive loading. On the addition to a radial corrugated
composite tube, cylindrical composite tube, were fabricated and
tested under the same condition in order to know the effect of
corrugation geometry. Typical histories of their deformation are
presented. Behavior of tubes as regards the peak crushing load,
energy absorbed and mode of crushing has been discussed. The
results show that the behavior of the tube under lateral compression
load is influenced by the geometry of the tube itself.
Abstract: F-actin fibrils are the cytoskeleton of osteocytes. They react in a dynamic manner to mechanical loading, and strength and
reposition their efforts to reinforce the cells structure. We hypothesize that f-actin is temporarly disrupted after loading and repolymerizes
in a new orientation to oppose the applied load. In vitro studies are conducted to determine f-actin disruption after varying mechanical stimulus parameters that are known to affect bone
formation. Results indicate that the f-actin cytoskeleton is disrupted in vitro as a function of applied mechanical stimulus parameters and
that the f-actin bundles reassemble after loading induced disruption
within 3 minutes after cessation of loading. The disruption of the factin
cytoskeleton depends on the magnitude of stretch, the numbers
of loading cycles, frequency, the insertion of rest between loading
cycles and extracellular calcium. In vivo studies also demonstrate
disruption of the f-actin cytoskeleton in cells embedded in the bone
matrix immediately after mechanical loading. These studies suggest
that adaptation of the f-actin fiber bundles of the cytoskeleton in
response to applied loads occurs by disruption and subsequent repolymerization.
Abstract: The development of shape and size of a crack in a
pressure vessel under uniaxial and biaxial loadings is important in
fitness-for-service evaluations such as leak-before-break. In this
work finite element modelling was used to evaluate the mean stress
and the J-integral around a front of a surface-breaking crack. A
procedure on the basis of ductile tearing resistance curves of high and
low constrained fracture mechanics geometries was developed to
estimate the amount of ductile crack extension for surface-breaking
cracks and to show the evolution of the initial crack shape. The
results showed non-uniform constraint levels and crack driving forces
around the crack front at large deformation levels. It was also shown
that initially semi-elliptical surface cracks under biaxial load
developed higher constraint levels around the crack front than in
uniaxial tension. However similar crack shapes were observed with
more extensions associated with cracks under biaxial loading.
Abstract: Evaluation of contact pressure, surface and
subsurface contact stresses are essential to know the functional
response of surface coatings and the contact behavior mainly depends
on surface roughness, material property, thickness of layer and the
manner of loading. Contact parameter evaluation of real rough
surface contacts mostly relies on statistical single asperity contact
approaches. In this work, a three dimensional layered solid rough
surface in contact with a rigid flat is modeled and analyzed using
finite element method. The rough surface of layered solid is
generated by FFT approach. The generated rough surface is exported
to a finite element method based ANSYS package through which the
bottom up solid modeling is employed to create a deformable solid
model with a layered solid rough surface on top. The discretization
and contact analysis are carried by using the same ANSYS package.
The elastic, elastoplastic and plastic deformations are continuous in
the present finite element method unlike many other contact models.
The Young-s modulus to yield strength ratio of layer is varied in the
present work to observe the contact parameters effect while keeping
the surface roughness and substrate material properties as constant.
The contacting asperities attain elastic, elastoplastic and plastic states
with their continuity and asperity interaction phenomena is inherently
included. The resultant contact parameters show that neighboring
asperity interaction and the Young-s modulus to yield strength ratio
of layer influence the bulk deformation consequently affect the
interface strength.
Abstract: Added stresses due to adjacent structure should be
considered in foundation design and stress control in soil under the structure. This case is considered less than other cases in design and
calculation whereas stresses in implementation are greater than analytical stress.
Structure load are transmitted to earth by foundation and role of foundation is propagation of load on the continuous and half extreme
soil. This act cause that, present stresses lessen to allowable strength
of soil. Some researchers such as Boussinesq and westergaurd by
using of some assumption studied on this issue, theorically. Target of
this paper is study and evaluation of added stresses under structure
due to adjacent structure. For this purpose, by using of assumption, theoric relation and numeral methods, effects of adjacent structure
with 4 to 10 storeys on the main structure with 4 storeys are studied
and effect of parameters and sensitivity of them are evaluated.
Abstract: The dilute acid pretreatment and enzymatic
saccharification of lignocellulosic substrate, cogon grass (Imperata
cylindrical, L.) was optimized prior ethanol fermentation using
simultaneous saccharification and fermentation (SSF) method. The
optimum pretreatment conditions, temperature, sulfuric acid
concentration, and reaction time were evaluated by determining the
maximum sugar yield at constant enzyme loading. Cogon grass, at
10% w/v substrate loading, has optimum pretreatment conditions of
126°C, 0.6% v/v H2SO4, and 20min reaction time. These
pretreatment conditions were used to optimize enzymatic
saccharification using different enzyme combinations. The maximum
saccharification yield of 36.68mg/mL (71.29% reducing sugar) was
obtained using 25FPU/g-cellulose cellulase complex combined with
1.1% w/w of cellobiase, ß-glucosidase, and 0.225% w/w of
hemicellulase complex, after 96 hours of saccharification. Using the
optimum pretreatment and saccharification conditions, SSF of treated
substrates was done at 37°C for 120 hours using industrial yeast
strain HBY3, Saccharomyces cerevisiae. The ethanol yield for cogon
grass at 4% w/w loading was 9.11g/L with 5.74mg/mL total residual
sugar.
Abstract: This paper studies, maps and explains the interactions between downloaders and uploaders pertaining to the Internet film piracy. This study also covers several motivational factors that influence users to upload or download movies, and thus to engage in film piracy over the Internet. The essay also proposes a model that describes user behavior including their relationships and influences. Moreover, proposed theoretical interactions and motivational factors are applied to the real world scenario, using examples of a data storage webpage server Ulozto.net and webpage Piratebay.org gathering information about downloadable BitTorrents. Moreover, the theory is further supported by description of behavior of real Internet uploaders.
Abstract: Two-dimensional finite element model was created in this work to investigate the stresses distribution within rock-like samples with offset open non-persistent joints under biaxial loading. The results of this study have explained the fracture mechanisms observed in tests on rock-like material with open non-persistent offset joints [1]. Finite element code SAP2000 was used to study the stresses distribution within the specimens. Four-nodded isoperimetric plain strain element with two degree of freedom per node, and the three-nodded constant strain triangular element with two degree of freedom per node were used in the present study.The results of the present study explained the formation of wing cracks at the tip of the joints for low confining stress as well as the formation of wing cracks at the middle of the joint for the higher confining stress. High shear stresses found in the numerical study at the tip of the joints explained the formation of secondary cracks at the tip of the joints in the experimental study. The study results coincide with the experimental observations which showed that for bridge inclination of 0o, the coalescence occurred due to shear failure and for bridge inclination of 90o the coalescence occurred due to tensile failure while for the other bridge inclinations coalescence occurred due to mixed tensile and shear failure.
Abstract: The pavement constructions on soft and expansive soils are not durable and unable to sustain heavy traffic loading. As a result, pavement failures and settlement problems will occur very often even under light traffic loading due to cyclic and rolling effects. Geotechnical engineers have dwelled deeply into this matter, and adopt various methods to improve the engineering characteristics of soft fine-grained soils and expansive soils. The problematic soils are either replaced by good and better quality material or treated by using chemical stabilization with various binding materials. Increased the strength and durability are also the part of the sustainability drive to reduce the environment footprint of the built environment by the efficient use of resources and waste recycle materials. This paper presents a series of laboratory tests and evaluates the effect of cement and fly ash on the strength and drainage characteristics of soil in Miri. The tests were performed at different percentages of cement and fly ash by dry weight of soil. Additional tests were also performed on soils treated with the combinations of fly ash with cement and lime. The results of this study indicate an increase in unconfined compression strength and a decrease in hydraulic conductivity of the treated soil.
Abstract: In many buildings we rely on large footings to offer
structural stability. Designers often compensate for the lack of
knowledge available with regard to foundation-soil interaction by
furnishing structures with overly large footings. This may lead to a
significant increase in building expenditures if many large
foundations are present. This paper describes the interface material
law that governs the behavior along the contact surface of adjacent
materials, and the behavior of a large foundation under ultimate limit
loading. A case study is chosen that represents a common
foundation-soil system frequently used in general practice and
therefore relevant to other structures. Investigations include
compressing versus uplifting wind forces, alterations to the
foundation size and subgrade compositions, the role of the slab
stiffness and presence and the effect of commonly used structural
joints and connections. These investigations aim to provide the
reader with an objective design approach, efficiently preventing
structural instability.
Abstract: The term hybrid composite refers to the composite
containing more than one type of fiber material as reinforcing fillers.
It has become attractive structural material due to the ability of
providing better combination of properties with respect to single fiber
containing composite. The eco-friendly nature as well as processing
advantage, light weight and low cost have enhanced the attraction
and interest of natural fiber reinforced composite. The objective of
present research is to study the mechanical properties of jute-coir
fiber reinforced hybrid polypropylene (PP) composite according to
filler loading variation. In the present work composites were
manufactured by using hot press machine at four levels of fiber
loading (5, 10, 15 and 20 wt %). Jute and coir fibers were utilized at a
ratio of (1:1) during composite manufacturing. Tensile, flexural,
impact and hardness tests were conducted for mechanical
characterization. Tensile test of composite showed a decreasing trend
of tensile strength and increasing trend of the Young-s modulus with
increasing fiber content. During flexural, impact and hardness tests,
the flexural strength, flexural modulus, impact strength and hardness
were found to be increased with increasing fiber loading. Based on
the fiber loading used in this study, 20% fiber reinforced composite
resulted the best set of mechanical properties.
Abstract: The distributions of stresses and deflection in
rectangular isotropic and orthotropic plates with central
circular hole under transverse static loading have been studied
using finite element method. The aim of author is to analyze
the effect of D/A ratio (where D is hole diameter and A is plate
width) upon stress concentration factor (SCF) and deflection
in isotropic and orthotropic plates under transverse static
loading. The D/A ratio is varied from 0.01 to 0.9. The analysis
is done for plates of isotropic and two different orthotropic
materials. The results are obtained for three different boundary
conditions. The variations of SCF and deflection with respect
to D/A ratio are presented in graphical form and discussed.
The finite element formulation is carried out in the analysis
section of the ANSYS package.
Abstract: A research program is conducted to evaluate the
mechanical properties of Ultra High Performance Concrete, target
compressive strength at the age of 28 days being more than 150 MPa.
The methodology to develop such mix has been explained. The
material properties, mix design and curing regime are determined.
The material attributes are understood by studying the stress strain
behaviour of UHPC cylinders under uniaxial compressive loading.
The load –crack mouth opening displacement (cmod) of UHPC
beams, flexural strength and fracture energy was evaluated using
third point loading test. Compressive strength and Split tensile
strength results are determined to find out the compressive and tensile
behaviour. Residual strength parameters are presented vividly
explaining the flexural performance, toughness of concrete.Durability
studies were also done to compare the effect of fibre to that of a
control mix For all the studies the Mechanical properties were
evaluated by varying the percentage and aspect ratio of steel fibres
The results reflected that higher aspect ratio and fibre volume
produced drastic changes in the cube strength, cylinder strength, post
peak response, load-cmod, fracture energy flexural strength, split
tensile strength, residual strength and durability. In regards to null
application of UHPC in India, an initiative is undertaken to
comprehend the mechanical behaviour of UHPC, which will be vital
for longer run in commercialization for structural applications.
Abstract: The present study deals with the analysis of the cylindrical part of a CNG storage vessel, combining a plastic liner and an over wrapped filament wound composite. Three kind of polymer are used in the present analysis: High density Polyethylene HDPE, Light low density Polyethylene LLDPE and finally blend of LLDPE/HDPE. The effect of the mechanical properties on the behavior of type IV vessel may be then investigated. In the present paper, the effect of the order of the circumferential winding on the stacking sequence may be then investigated. Based on mechanical considerations, the present model provides an exact solution for stresses and deformations on the cylindrical section of the vessel under thermo-mechanical static loading. The result show a good behavior of HDPE liner compared to the other plastic materials. The presence of circumferential winding angle in the stacking improves the rigidity of vessel by improving the burst pressure.
Abstract: In this study, optimization is carried out to find the optimized design of a foam-filled column for the best Specific Energy Absorption (SEA) and Crush Force Efficiency (CFE). In order to maximize SEA, the optimization gives the value of 2.3 for column thickness and 151.7 for foam length. On the other hand to maximize CFE, the optimization gives the value of 1.1 for column thickness and 200 for foam length. Finite Element simulation is run by using this value and the SEA and CFE obtained 1237.76 J/kg and 0.92.