Abstract: In this study, ZnO nano rods and ZnO ultrafine particles were synthesized by Gel-casting method. The synthesized ZnO powder has a hexagonal zincite structure. The ZnO aggregates with rod-like morphology are typically 1.4 μm in length and 120 nm in diameter, which consist of many small nanocrystals with diameters of 10 nm. Longer wires connected by many hexahedral ZnO nanocrystals were obtained after calcinations at the temperature over 600° C.The crystalline structures and morphologies of the powder have been characterized by X-ray diffraction(XRD) and Scaning electron microscopy (SEM).The result shows that the different preparation conditions such as concentration H2O, calcinations time and calcinations temperature have a lot of influences upon the properties of nano ZnO powders, an increase in the temperature of the calcinations results in an increase of the grain size and also the increase of the calcinations time in high temperature makes the size of the grains bigger. The existences of extra watter prevent nano grains from improving like rod morphology. We have obtained the smallest grain size of ZnO powder by controlling the process conditions. Finally In a suitable condition, a novel nanostructure, namely bi-rod-like ZnO nano rods was found which is different from known ZnO nanostructures.
Abstract: A major challenge in biomaterials research is the
regulation of protein adsorption which is a key factor for controlling
the subsequent cell adhesion at implant surfaces. The aim of the
present study was to control the adsorption of fibronectin (FN) and
the attachment of MG-63 osteoblasts with an electronic
nanostructure. Shallow doping line lattices with a period of 260 nm
were produced for this purpose by implantation of phosphorous in
silicon wafers. Protein coverage was determined after incubating the
substrate with FN by means of an immunostaining procedure and the
measurement of the fluorescence intensity with a TECAN analyzer.
We observed an increased amount of adsorbed FN on the
nanostructure compared to control substrates. MG-63 osteoblasts
were cultivated for 24h on FN-incubated substrates and their
morphology was assessed by SEM. Preferred orientation and
elongation of the cells in direction of the doping lattice lines was
observed on FN-coated nanostructures.
Abstract: The present work is a numerical simulation of
nanofluids flow in a double pipe heat exchanger provided with
porous baffles. The hot nanofluid flows in the inner cylinder, whereas
the cold nanofluid circulates in the annular gap. The Darcy-
Brinkman-Forchheimer model is adopted to describe the flow in the
porous regions, and the governing equations with the appropriate
boundary conditions are solved by the finite volume method. The
results reveal that the addition of metallic nanoparticles enhances the
rate of heat transfer in comparison to conventional fluids but this
augmentation is accompanied by an increase in pressure drop. The
highest heat exchanger performances are obtained when
nanoparticles are added only to the cold fluid.
Abstract: The possibility of intrinsic electromagnetic fields
within living cells and their resonant self-interaction and interaction
with ambient electromagnetic fields is suggested on the basis of a
theoretical and experimental study. It is reported that intrinsic
electromagnetic fields are produced in the form of radio-frequency
and infra-red photons within atoms (which may be coupled or
uncoupled) in cellular structures, such as the cell cytoskeleton and
plasma membrane. A model is presented for the interaction of these
photons among themselves or with atoms under a dipole-dipole
coupling, induced by single-photon or two-photon processes. This
resonance is manifested by conspicuous field amplification and it is
argued that it is possible for these resonant photons to undergo
tunnelling in the form of evanescent waves to a short range (of a few
nanometers to micrometres). This effect, suggested as a resonant
photon tunnelling mechanism in this report, may enable these fields
to act as intracellular signal communication devices and as bridges
between macromolecules or cellular structures in the cell
cytoskeleton, organelles or membrane. A brief overview of an
experimental technique and a review of some preliminary results are
presented, in the detection of these fields produced in living cell
membranes under physiological conditions.
Abstract: Most of the drugs used for pharmaceutical purposes
are poorly water-soluble drugs. About 40% of all newly discovered
drugs are lipophilic and the numbers of lipophilic drugs seem to
increase more and more. Drug delivery systems such as
nanoparticles, micelles or liposomes are applied to improve their
solubility and thus their bioavailability. Besides various techniques of
solubilization, oil-in-water emulsions are often used to incorporate
lipophilic drugs into the oil phase. To stabilize emulsions surface
active substances (surfactants) are generally used. An alternative
method to avoid the application of surfactants was of great interest.
One possibility is to develop O/W-emulsion without any addition of
surface active agents or the so called “surfactant-free emulsion or
SFE”. The aim of this study was to develop and characterize SFE as a
drug carrier by varying the production conditions. Lidocaine base
was used as a model drug. The injection method was developed.
Effects of ultrasound as well as of temperature on the properties of
the emulsion were studied. Particle sizes and release were
determined. The long-term stability up to 30 days was performed.
The results showed that the surfactant-free O/W emulsions with
pharmaceutical oil as drug carrier can be produced.
Abstract: Selective oxidation of H2S to elemental sulfur in a
fixed bed reactor over newly synthesized alumina nanocatalysts was
physio-chemically investigated and results compared with a
commercial Claus catalyst. Amongst these new materials, Al2O3-
supported sodium oxide prepared with wet chemical technique and
Al2O3 nanocatalyst prepared with spray pyrolysis method were the
most active catalysts for selective oxidation of H2S to elemental
sulfur. Other prepared nanocatalysts were quickly deactivated,
mainly due to the interaction with H2S and conversion into sulfides.
Abstract: Water 2H NMR signal on the surface of nano-silica material, MCM-41, consists of two overlapping resonances. The 2H water spectrum shows a superposition of a Lorentzian line shape and the familiar NMR powder pattern line shape, indicating the existence of two spin components. Chemical exchange occurs between these two groups. Decomposition of the two signals is a crucial starting point for study the exchange process. In this article we have determined these spin component populations along with other important parameters for the 2H water NMR signal over a temperature range between 223 K and 343 K.
Abstract: The carbon based coils with the nanometer scale have
the 3 dimension helix geometry. We synthesized the carbon nano-coils
by the use of chemical vapor deposition technique with iron and tin as
the catalysts. The fabricated coils have the external diameter of
ranging few hundred nm to few thousand nm. The Scanning
Electro-Microscope (SEM) and Tunneling Electro-Microscope has
shown detail images of the coil-s structure. The fabrication of the
carbon nano-coils can be grown on the metal and non-metal substrates,
such as the stainless steel and silicon substrates. Besides growth on the
flat substrate; they also can be grown on the stainless steel wires. After
the synthesis of the coils, the mechanical and electro-mechanical
property is measured. The experimental results were reported.
Abstract: Three dimensional nanostructure materials have attracted the attention of many researches because the possibility to apply them for near future devices in sensors, catalysis and energy related. Tin dioxide is the most used material for gas sensing because its three-dimensional nanostructures and properties are related to the large surface exposed to gas adsorption. We propose the use of branch SnO2 nanowhiskers in interaction with ethanol. All Sn atoms are symmetric. The total energy, potential energy and Kinetic energy calculated for interaction between SnO2 and ethanol in different distances and temperatures. The calculations achieved by methods of Langevin Dynamic and Mont Carlo simulation. The total energy increased with addition ethanol molecules and temperature so interactions between them are endothermic.
Abstract: Minimum Quantity Lubrication (MQL) technique
obtained a significant attention in machining processes to reduce
environmental loads caused by usage of conventional cutting fluids.
Recently nanofluids are finding an extensive application in the field
of mechanical engineering because of their superior lubrication and
heat dissipation characteristics. This paper investigates the use of a
nanofluid under MQL mode to improve grinding characteristics of
Ti-6Al-4V alloy. Taguchi-s experimental design technique has been
used in the present investigation and a second order model has been
established to predict grinding forces and surface roughness.
Different concentrations of water based Al2O3 nanofluids were
applied in the grinding operation through MQL setup developed in
house and the results have been compared with those of conventional
coolant and pure water. Experimental results showed that grinding
forces reduced significantly when nano cutting fluid was used even at
low concentration of the nano particles and surface finish has been
found to improve with higher concentration of the nano particles.
Abstract: Nylon 6-clay hybrid/neat nylon 6, sheath/core
bicomponent nanocomposite fibers containing 4 wt% of clay in
sheath section were melt spun at different take-up speeds. Their
orientation and crystalline structure were compared to those of neat
nylon 6 fibers. Birefringence measurements showed that the
orientation development in sheath and core parts of bicomponent
fibers was different. Crystallinity results showed that clay did not act
as a nucleating agent for bicomponent fibers. The neat nylon 6 fiber
had a smooth surface while striped pattern was appeared on the
surface of bicomponent fiber containing clay due to thermal
shrinkage of the core part.
Abstract: This paper presents a vertical silicon nanowire n- MOSFET integrated with a CMOS-compatible fully-silicided (FUSI) NiSi2 gate. Devices with nanowire diameter of 50nm show good electrical performance (SS < 70mV/dec, DIBL < 30mV/V, Ion/Ioff > 107). Most significantly, threshold voltage tunability of about 0.2V is shown. Although threshold voltage remains low for the 50nm diameter device, it is expected to become more positive as nanowire diameter reduces.
Abstract: When the characteristic length of an elastic solid is
down to the nanometer level, its deformation behavior becomes size
dependent. Surface energy /surface stress have recently been applied
to explain such dependency. In this paper, the effect of
strain-independent surface stress on the deformation of an isotropic
elastic solid containing a nanosized elliptical hole is studied by the
finite element method. Two loading cases are considered, in the first
case, hoop stress along the rim of the elliptical hole induced by pure
surface stress is studied, in the second case, hoop stress around the
elliptical opening under combined remote tension and surface stress is
investigated. It has been shown that positive surface stress induces
compressive hoop stress along the hole, and negative surface stress has
opposite effect, maximum hoop stress occurs near the major semi-axes
of the ellipse. Under combined loading of remote tension and surface
stress, stress concentration around the hole can be either intensified or
weakened depending on the sign of the surface stress.
Abstract: Magnetic carbon nanotubes composites were obtained
by filling carbon nanotubes with paramagnetic iron oxide particles.
Detailed investigation of magnetic behaviour of resulting composites
was done at different temperatures. Measurements indicate that these
functionalized nanotubes are superparamagnetic at room temperature;
however, no superparamagnetism was observed at 125 K and 80 K.
The blocking temperature TB was estimated at 145 K. These magnetic
carbon nanotubes have the potential of being used in a wide range of
applications, in particular, the production of nanofluids, which can be
controlled and steered by appropriate magnetic fields.
Abstract: We integrate TiN/Ni/HfO2/Si RRAM cell with a
vertical gate-all-around (GAA) nanowire transistor to achieve
compact 4F2 footprint in a 1T1R configuration. The tip of the Si
nanowire (source of the transistor) serves as bottom electrode of the
memory cell. Fabricated devices with nanowire diameter ~ 50nm
demonstrate ultra-low current/power switching; unipolar switching
with 10μA/30μW SET and 20μA/30μW RESET and bipolar switching
with 20nA/85nW SET and 0.2nA/0.7nW RESET. Further, the
switching current is found to scale with nanowire diameter making the
architecture promising for future scaling.
Abstract: We investigated a modified thermal evaporation
method in the growth process of ZnO nanowires. ZnO nanowires
were fabricated on p-type silicon substrates without using a metal
catalyst. A simple horizontal double-tube system along with
chemical vapor diffusion of the precursor was used to grow the ZnO
nanowires. The substrates were placed in different temperature
zones, and ZnO nanowires with different diameters were obtained for
the different substrate temperatures. In addition to the nanowires,
ZnO microdiscs with different diameters were obtained on another
substrate, which was placed at a lower temperature than the other
substrates. The optical properties and crystalline quality of the ZnO
nanowires and microdiscs were characterized by room temperature
photoluminescence (PL) and Raman spectrometers. The PL and
Raman studies demonstrated that the ZnO nanowires and microdiscs
grown using such set-up had good crystallinity with excellent optical
properties. Rectifying behavior of ZnO/Si heterostructures was
characterized by a simple DC circuit.
Abstract: In this study, structural, mechanical, thermal and
electrical properties of poly (lactic acid) (PLA) nanocomposites with
low-loaded (0-1.5 wt%) untreated, heat and nitric acid treated multiwalled
carbon nanotubes (MWCNTs) were studied. Among the
composites, untreated 0.5 wt % MWCNTs and acid-treated 1.0 wt%
MWCNTs reinforced PLA show the tensile strength and modulus
values higher than the others. These two samples along with pure
PLA exhibit the stable orthorhombic α-form, whilst other samples
reveal the less stable orthorhombic β-form, as demonstrated by X-ray
diffraction study. Differential scanning calorimetry reveals the
evolution of the mentioned different phases by controlled cooling and
discloses an enhancement of PLA crystallization by nanotubes
incorporation. Thermogravimetric analysis shows that the MWCNTs
loaded sample degraded faster than PLA. Surface resistivity of the
nanocomposites is found to be dropped drastically by a factor of 1013
with a low loading of MWCNTs (1.5 wt%).
Abstract: The nanotechnology based on epitaxial systems
includes single or arranged misfit dislocations. In general, whatever
is the type of dislocation or the geometry of the array formed by the
dislocations; it is important for experimental studies to know exactly
the stress distribution for which there is no analytical expression [1,
2]. This work, using a numerical analysis, deals with relaxation of
epitaxial layers having at their interface a periodic network of edge
misfit dislocations. The stress distribution is estimated by using
isotropic elasticity. The results show that the thickness of the two
sheets is a crucial parameter in the stress distributions and then in the
profile of the two sheets.
A comparative study between the case of single dislocation and
the case of parallel network shows that the layers relaxed better when
the interface is covered by a parallel arrangement of misfit.
Consequently, a single dislocation at the interface produces an
important stress field which can be reduced by inserting a parallel
network of dislocations with suitable periodicity.
Abstract: Polarization-interferometric nonlinear confocal
microscopy is proposed for measuring a nano-sized particle with
optical anisotropy. The anisotropy in the particle was
spectroscopically imaged through a three-dimensional distribution of
third-order nonlinear dielectric polarization photoinduced.
Abstract: Nowadays due to globalization of economy and
competition environment, innovation and technology plays key role
at creation of wealth and economic growth of countries. In fact
prompt growth of practical and technologic knowledge may results in
social benefits for countries when changes into effective innovation.
Considering the importance of innovation for the development of
countries, this study addresses the radical technological innovation
introduced by nanopapers at different stages of producing paper
including stock preparation, using authorized additives, fillers and
pigments, using retention, calender, stages of producing conductive
paper, porous nanopaper and Layer by layer self-assembly. Research
results show that in coming years the jungle related products will lose
considerable portion of their market share, unless embracing radical
innovation. Although incremental innovations can make this industry
still competitive in mid-term, but to have economic growth and
competitive advantage in long term, radical innovations are
necessary. Radical innovations can lead to new products and
materials which their applications in packaging industry can produce
value added. However application of nanotechnology in this industry
can be costly, it can be done in cooperation with other industries to
make the maximum use of nanotechnology possible. Therefore this
technology can be used in all the production process resulting in the
mass production of simple and flexible papers with low cost and
special properties such as facility at shape, form, easy transportation,
light weight, recovery and recycle marketing abilities, and sealing.
Improving the resistance of the packaging materials without reducing
the performance of packaging materials enhances the quality and the
value added of packaging. Improving the cellulose at nano scale can
have considerable electron optical and magnetic effects leading to
improvement in packaging and value added. Comparing to the
specifications of thermoplastic products and ordinary papers,
nanopapers show much better performance in terms of effective
mechanical indexes such as the modulus of elasticity, tensile strength,
and strain-stress. In densities lower than 640 kgm -3, due to the
network structure of nanofibers and the balanced and randomized
distribution of NFC in flat space, these specifications will even
improve more. For nanopapers, strains are 1,4Gpa, 84Mpa and 17%,
13,3 Gpa, 214Mpa and 10% respectively. In layer by layer self
assembly method (LbL) the tensile strength of nanopaper with Tio3
particles and Sio2 and halloysite clay nanotube are 30,4 ±7.6Nm/g
and 13,6 ±0.8Nm/g and 14±0.3,3Nm/g respectively that fall within
acceptable range of similar samples with virgin fiber. The usage of
improved brightness and porosity index in nanopapers can create
more competitive advantages at packaging industry.