Abstract: PVC foam-fly ash composites (PVC-FA) are
characterized for their structural, morphological, mechanical and
thermal properties. The tensile strength of the composites increased
modestly with higher fly ash loading, while there was a significant
increase in the elastic modulus for the same composites. On the other
hand, a decrease in elongation at UTS was observed upon increasing
fly ash content due to increased rigidity of the composites. Similarly,
the flexural modulus increased as the fly ash loading increased,
where the composites containing 25 phr fly ash showed the highest
flexural strength. Thermal properties of PVC-fly ash composites were
determined by Thermo Gravimetric Analysis (TGA). The
microstructural properties were studied by Scanning Electron
Microscopy (SEM). SEM results confirm that fly ash particles were
mechanically interlocked in PVC matrix with good interfacial
interaction with the matrix. Particle agglomeration and debonding
was observed in samples containing higher amounts of fly ash.
Abstract: Two types of glass fibers having different lengths
(1/16" and 1/32") were added into rigid PVC foams to enhance the
dimensional stability of extruded rigid Polyvinyl Chloride (PVC)
foam at different concentrations (0-20 phr) using a single screw
profile extruder. PVC foam-glass fiber composites (PVC-GF) were
characterized for their dimensional stability, structural, thermal, and
mechanical properties. Experimental results show that the
dimensional stability, heat resistance, and storage modulus were
enhanced without compromising the tensile and flexural strengths of
the composites. Overall, foam composites which were prepared with
longer glass fibers exhibit better mechanical and thermal properties
than those prepared with shorter glass fibers due to higher
interlocking between the fibers and the foam cells, which result in
better load distribution in the matrix.
Abstract: Particles are the most common and cheapest
reinforcement producing discontinuous reinforced composites with
isotropic properties. Conventional fabrication methods can be used to
produce a wide range of product forms, making them relatively
inexpensive. Optimising composite development must include
consideration of all the fundamental aspect of particles including
their size, shape, volume fraction, distribution and mechanical
properties. Research has shown that the challenges of low fracture
toughness, poor crack growth resistance and low thermal stability can
be overcome by reinforcement with particles. The unique properties
exhibited by micro particles reinforced ceramic composites have
made them to be highly attractive in a vast array of applications.
Abstract: This paper illustrates the effect of nano Magnesium
Hydroxide (MH) loading on the thermal properties of Low Density
Polyethylene (LDPE)/Poly (ethylene-co vinyl acetate) (EVA) nano
composite. Thermal studies were conducted, as it understanding is
vital for preliminary development of new polymeric systems.
Thermal analysis of nanocomposite was conducted using thermo
gravimetric analysis (TGA), and differential scanning calorimetry
(DSC). Major finding of TGA indicated two main stages of
degradation process found at (350 ± 25oC) and (480 ± 25oC)
respectively. Nano metal filler expressed better fire resistance as it
stand over high degree of temperature. Furthermore, DSC analysis
provided a stable glass temperature around 51 (±1oC) and captured
double melting point at 84 (±2oC) and 108 (±2oC). This binary
melting point reflects the modification of nano filler to the polymer
matrix forming melting crystals of folded and extended chain. The
percent crystallinity of the samples grew vividly with increasing filler
content. Overall, increasing the filler loading improved the
degradation temperature and weight loss evidently and a better
process and phase stability was captured in DSC.
Abstract: Dissimilar joining of Titanium and Aluminum thin
sheets has potential applications in aerospace and automobile
industry which can reduce weight and cost and improve strength,
corrosion resistance and high temperature properties. However
successful welding of Titanium/Aluminium sheets is of challenge due
to differences in physical, chemical and metallurgical properties
between the two. This paper describes research results of Laser Beam
Welding (LBW) of Ti/Al thin sheets in which many researchers have
recently performed and critically reviewed from different
perspectives. Also some of notable works in the field of laser welding
with changes in mechanical properties, crack propagation, diffusion
behavior, chemical potential, interfacial reaction and the
microstructure are reported.
Abstract: Laser beam welding is an important joining technique
for Titanium/Aluminum thin sheet alloys with their increasing
applications in aerospace, aircraft, automotive, electronics and other
industries. In this paper the research and progress in laser welding of
Ti/Al thin sheets are critically reviewed from different perspectives.
Some important aspects such as microstructure, metallurgical defects
and mechanical properties in weldments are discussed. Also the
recent progress in laser welding of Ti/Al dissimilar thin sheets to
provide a basis for further research work is reported.
Abstract: To elucidate the material characteristics of single
crystals of pure aluminum and copper, the respective relations between
crystallographic orientations and microstructures were examined,
along with bending and mechanical properties. The texture
distribution was also analysed. Bending tests were performed in a
SEM apparatus while its behaviors were observed. Some analytical
results related to crystal direction maps, inverse pole figures, and
textures were obtained from electron backscatter diffraction (EBSD)
analyses.
Abstract: Aluminum hybrid reinforcement technology is a
response to the dynamic ever increasing service requirements of such
industries as transportation, aerospace, automobile, marine, etc. It is
unique in that it offers a platform of almost unending combinations of
materials to produce various hybrid composites. This article reviews
the studies carried out on various combinations of aluminum hybrid
composite and the effects on mechanical, physical and chemical
properties. It is observed that the extent of enhancement of these
properties of hybrid composites is strongly dependent on the nature
of the reinforcement, its hardness, particle size, volume fraction,
uniformity of dispersion within the matrix and the method of hybrid
production.
Abstract: This work presents the result of investigations aimed
at determining the hardness of the welded Chromoly (A 4130) steel
plate of 2” thickness. Multi pass welding for the thick sections was
carried out and analyzed for the Chromoly alloy steel plates. The
study of hardness at the weld metal reveals that there is the presence
of different micro structure products which yields diverse properties.
The welding carried out using GMAW with ER70s-2 electrode.
Single V groove design was selected for the butt joint configuration.
The presence of hydrogen has been suppressed by selecting low
hydrogen electrode. Preheating of the plate prior to welding reduces
the cooling rate which also affects the weld metal microstructure. The
shielding gas composition used in this analysis is 80% Ar-20% CO2.
The experimental analysis gives the detailed study of the hardness of
the material.
Abstract: Calcium phosphate cement (CPC) is one of the most
attractive bioceramics due to its moldable and shape ability to fill
complicated bony cavities or small dental defect positions. In this
study, CPC was produced by using mixture of tetracalcium phosphate
(TTCP, Ca4O(PO4)2) and dicalcium phosphate anhydrous (DCPA,
CaHPO4) in equimolar ratio (1/1) with aqueous solutions of acetic
acid (C2H4O2) and disodium hydrogen phosphate dehydrate
(Na2HPO4.2H2O) in combination with sodium alginate in order to
improve theirs moldable characteristic. The concentration of the
aqueous solutions and sodium alginate were varied to investigate the
effect of different aqueous solutions and alginate on properties of the
cements. The cement paste was prepared by mixing cement powder
(P) with aqueous solution (L) in a P/L ratio of 1.0g/0.35ml. X-ray
diffraction (XRD) was used to analyses phase formation of the
cements. Setting time and compressive strength of the set CPCs were
measured using the Gilmore apparatus and Universal testing
machine, respectively.
The results showed that CPCs could be produced by using both
basic (Na2HPO4.2H2O) and acidic (C2H4O2) solutions. XRD results
show the precipitation of hydroxyapatite in all cement samples. No
change in phase formation among cements using difference
concentrations of Na2HPO4.2H2O solutions. With increasing
concentration of acidic solutions, samples obtained less
hydroxyapatite with a high dicalcium phosphate dehydrate leaded to
a shorter setting time. Samples with sodium alginate exhibited higher
crystallization of hydroxyapatite than that of without alginate as a
result of shorten setting time in a basic solution but a longer setting
time in an acidic solution. The stronger cement was attained from
samples using the acidic solution with sodium alginate; however the
strength was lower than that of using the basic solution.
Abstract: Hydrogenated amorphous carbon (a-C:H) films have
been synthesized by a radio frequency plasma enhanced chemical
vapor deposition (rf-PECVD) technique with different bias voltage
from 0.0 to -0.5 kV. The Raman spectra displayed the polymer-like
hydrogenated amorphous carbon (PLCH) film with 0.0 to -0.1 and
a-C:H films with -0.2 to -0.5 kV of bias voltages. The surface chemical
information of all films were studied by X-ray photoelectron
spectroscopy (XPS) technique, presented to C-C (sp2 and sp3) and C-O
bonds, and relative carbon (C) and oxygen (O) atomics contents. The
O contamination had affected on structure and optical properties. The
true density of PLCH and a-C:H films were characterized by X-ray
refractivity (XRR) method, showed the result as in the range of
1.16-1.73 g/cm3 that depending on an increasing of bias voltage. The
hardness was proportional to the true density of films. In addition, the
optical properties i.e. refractive index (n) and extinction coefficient (k)
of these films were determined by a spectroscopic ellipsometry (SE)
method that give formation to in 1.62-2.10 (n) and 0.04-0.15 (k)
respectively. These results indicated that the optical properties
confirmed the Raman results as presenting the structure changed with
applied bias voltage increased.
Abstract: The aim of this paper is to introduce the notions of
intuitionistic T-S fuzzy subalgebras and intuitionistic T-S fuzzy ideals
in BCI-algebras, and then to investigate their basic properties.
Abstract: Ficus deltoidea from the Moraceae family is a popular
medicinal herb in Malaysia. It possesses strong antioxidant and antiinflammatory
properties. In the present study, the anti-inflammatory
effects of F. deltoidea extract on UVB-irradiated HaCaT
Keratinocytes were investigated. HaCaT Keratinocytes were UVBirradiated
(12.5 mJ/cm3) and were treated with 0.05, 0.08 or 0.1% of
F. deltoidea extract. Cell viability following UVB irradiation was
significantly higher in the groups treated with the F. deltoidea extract
at doses of 0.05, 0.08 or 0.1% than in control group with UVB
irradiation only. Tumor necrosis factor-α (TNF-α), interleukin-1α
(IL-1α), interleukin-6 (IL-6) and cyclooxygenase (COX-2) play
primary roles in the inflammation process upon UV irradiation and
are known to be stimulated by UVB irradiation. Treatment with the
F. deltoidea extract dramatically inhibited the UV-induced TNF-α,
IL-1α, IL-6, and COX-2 expression. These results suggest that the F.
deltoidea extract inhibits the production of pro-inflammatory
cytokines and may be an effective protective agent for the treatment
of skin diseases.
Abstract: The use of permanent magnets (PM) is increasing in
permanent magnet synchronous machines (PMSM) to fulfill the
requirements of high efficiency machines in modern industry. PMSM
are widely used in industrial applications, wind power plants and the
automotive industry. Since PMSM are used in different
environmental conditions, the long-term effect of NdFeB-based
magnets at high temperatures and their corrosion behavior have to be
studied due to the irreversible loss of magnetic properties.
In this paper, the effect of magnetic properties due to corrosion
and increasing temperature in a climatic chamber has been presented.
The magnetic moment and magnetic field of the magnets were
studied experimentally.
Abstract: Boron-gypsum is a waste which occurs in the boric
acid production process. In this study, the boron content of this waste
is evaluated for the use in synthesis of magnesium borates and such
evaluation of this kind of waste is useful more than storage or
disposal. Magnesium borates, which are a sub-class of boron
minerals, are useful additive materials for the industries due to their
remarkable thermal and mechanical properties. Magnesium borates
were obtained hydrothermally at different temperatures. Novelty of
this study is the search of the solution density effects to magnesium
borate synthesis process for the increasing the possibility of borongypsum
usage as a raw material. After the synthesis process, products
are subjected to XRD and FT-IR to identify and characterize their
crystal structure, respectively.
Abstract: Multipotent mesenchymal stromal cells (MSCs)
possess immunomodulatory properties. The effect of MSCs on the
crucial cellular immunity compartment – T-cells is of a special
interest. It is known that MSC tissue niche and expected milieu of
their interaction with T- cells are characterized by low oxygen
concentration, whereas the in vitro experiments usually are carried
out at a much higher ambient oxygen (20%). We firstly evaluated
immunomodulatory effects of MSCs on T-cells at tissue-related
oxygen (5%) after interaction implied cell-to-cell contacts and
paracrine factors only. It turned out that MSCs under reduced oxygen
can effectively suppress the activation and proliferation of PHAstimulated
T-cells and can provoke decrease in the production of
proinflammatory and increase in anti-inflammatory cytokines. In
hypoxia some effects were amplified (inhibition of proliferation, antiinflammatory
cytokine profile shift). This impact was more evident
after direct cell-to-cell interaction; lack of intercellular contacts could
revoke the potentiating effect of hypoxia.
Abstract: High temperature deformation behavior of cast
Fe-20Cr-5Al alloy has been investigated in this study by performing
tensile and compression tests at temperatures from 1100 to 1200oC.
Rectangular ingots of which the dimensions were 300×300×100 in
millimeter were cast using vacuum induction melting. Phase
equilibrium was calculated using the FactSage®, thermodynamic
software and database. Tensile strength of cast Fe-20Cr-5Al alloy was
4 MPa at 1200oC. With temperature decreased, tensile strength
increased rapidly and reached up to 13 MPa at 1100oC. Elongation
also increased from 18 to 80% with temperature decreased from
1200oC to 1100oC. Microstructure observation revealed that M23C6
carbide was precipitated along the grain boundary and within the
matrix.
Abstract: Paper deals with analysis of strategic management
methods in non-profit making organization in the Czech Republic.
Strategic management represents an aggregate of methods and
approaches that can be applied for managing organizations - in this
article the organizations which associate owners and keepers of nonstate
forest properties. Authors use these methods of strategic
management: analysis of stakeholders, SWOT analysis and
questionnaire inquiries. The questionnaire was distributed
electronically via e-mail. In October 2013 we obtained data from a
total of 84 questionnaires. Based on the results the authors
recommend the using of confrontation strategy which improves the
competitiveness of non-profit making organizations.
Abstract: This paper conducts a comparison study using KES-FB and PhabrOmeter to measure 58 selected warp knitted fabric hand properties. Fabric samples were selected and measured by both KES-FB and PhabrOmeter. Results show differences between these two measurement methods. Smoothness and stiffness values obtained by KES-FB were found significant correlated (p value = 0.003 and 0.022) to the PhabrOmeter results while softness values between two measurement methods did not show significant correlation (p value = 0.828). Disagreements among these two measurement methods imply limitations on different mechanism principles when facing warp knitted fabrics. Subjective measurement methods and further studies are suggested in order to ascertain deeper investigation on the mechanisms of fabric hand perceptions.
Abstract: In this article the problem of distributional moments estimation is considered. The new approach of moments estimation based on usage of the characteristic function is proposed. By statistical simulation technique author shows that new approach has some robust properties. For calculation of the derivatives of characteristic function there is used numerical differentiation. Obtained results confirmed that author’s idea has a certain working efficiency and it can be recommended for any statistical applications.