Abstract: Polymer nanocomposites represent a new class of materials in which nanomaterials act as the reinforcing material in composites, wherein small additions of nanomaterials lead to large enhancements in thermal, optical and mechanical properties. A boost in these properties is due to the large interfacial area per unit volume or weight of the nanoparticles and the interactions between the particle and the polymer. Micro sized particles used as reinforcing agents scatter light, thus reducing light transmittance and optical clarity. Efficient nanoparticle dispersion combined with good polymer–particle interfacial adhesion eliminates scattering and allows the exciting possibility of developing strong yet transparent films, coatings and membranes. This paper aims at synthesising zinc oxide nanoparticles which are reinforced in poly vinyl alcohol (PVA) polymer. The mechanical properties showed that the tensile strength of the PVA nanocomposites increases with the increase in the amount of nanoparticles.
Abstract: This study fabricates p-type Ni1−xO:Li/n-Si heterojunction solar cells (P+/n HJSCs) by using radio frequency (RF) magnetron sputtering and investigates the effect of substrate temperature on photovoltaic cell properties. Grazing incidence x-ray diffraction, four point probe, and ultraviolet-visible-near infrared discover the optoelectrical properties of p-Ni1-xO thin films. The results show that p-Ni1-xO thin films deposited at 300 oC has the highest grain size (22.4 nm), average visible transmittance (~42%), and electrical resistivity (2.7 Ωcm). However, the conversion efficiency of cell is shown only 2.33% which is lower than the cell (3.39%) fabricated at room temperature. This result can be mainly attributed to interfacial layer thickness (SiOx) reduces from 2.35 nm to 1.70 nm, as verified by high-resolution transmission electron microscopy.
Abstract: Optical properties of sputter-deposited ZnS thin films
were investigated as potential replacements for CBD(chemical bath
deposition) CdS buffer layers in the application of CIGS solar cells.
ZnS thin films were fabricated on glass substrates at RT, 150oC, 200oC,
and 250oC with 50 sccm Ar gas using an RF magnetron sputtering
system. The crystal structure of the thin film is found to be zinc blende
(cubic) structure. Lattice parameter of ZnS is slightly larger than CdS
on the plane and thus better matched with that of CIGS. Within a
400-800 nm wavelength region, the average transmittance was larger
than 75%. When the deposition temperature of the thin film was
increased, the blue shift phenomenon was enhanced. Band gap energy
of the ZnS thin film tended to increase as the deposition temperature
increased. ZnS thin film is a promising material system for the CIGS
buffer layer, in terms of ease of processing, low cost, environmental
friendliness, higher transparency, and electrical properties
Abstract: The use of solar control film on windows as one of
solar passive strategies for building have becoming important and is
gaining recognition. Malaysia located close to equator is having
warm humid climate with long sunshine hours and abundant solar
radiation throughout the year. Hence, befitting solar control on
windows is absolutely necessary to capture the daylight whilst
moderating thermal impact and eliminating glare problems. This is
one of the energy efficient strategies to achieve thermal and visual
comfort in buildings. Therefore, this study was carried out to
investigate the effect of window solar controls on thermal and visual
performance of naturally ventilated buildings. This was conducted via
field data monitoring using a test building facility. Four types of
window glazing systems were used with three types of solar control
films. Data were analysed for thermal and visual impact with
reference to thermal and optical characteristics of the films. Results
show that for each glazing system, the surface temperature of
windows are influenced by the Solar Energy Absorption property, the
indoor air temperature are influenced by the Solar Energy
Transmittance and Solar Energy Reflectance, and the daylighting by
Visible Light Transmission and Shading Coefficient. Further
investigations are underway to determine the mathematical relation
between thermal energy and visual performance with the thermal and
optical characteristics of solar control films.
Abstract: We derive simple sets of equations to describe the microwave response of a thin film of magnetized hydrogen plasma in the presence of carbon nanotubes, which were grown by ironcatalyzed high-pressure disproportionation (HiPco). By considering the interference effects due to multiple reflections between thin plasma film interfaces, we present the effects of the continuously changing external magnetic field and plasma parameters on the reflected power, absorbed power, and transmitted power in the system. The simulation results show that the interference effects play an important role in the reflectance, transmittance and absorptance of microwave radiation at the magnetized plasma slab. As a consequence, the interference effects lead to a sinusoidal variation of the reflected intensity and can greatly reduce the amount of reflection power, but the absorption power increases.
Abstract: ZnO-SnO2 i.e. Zinc-Tin-Oxide (ZTO) thin films were
deposited on glass substrate with varying concentrations (ZnO:SnO2
- 100:0, 90:10, 70:30 and 50:50 wt.%) at room temperature by flash
evaporation technique. These deposited ZTO film were annealed at
450 0C in vacuum. These films were characterized to study the effect
of annealing on the structural, electrical, and optical properties.
Atomic force microscopy (AFM) and Scanning electron microscopy
(SEM) images manifest the surface morphology of these ZTO thin
films. The apparent growth of surface features revealed the formation
of nanostructure ZTO thin films. The small value of surface
roughness (root mean square RRMS) ensures the usefulness in
optical coatings. The sheet resistance was also found to be decreased
for both types of films with increasing concentration of SnO2. The
optical transmittance found to be decreased however blue shift has
been observed after annealing.
Abstract: In this investigation, anatase TiO2 thin films were
grown by radio frequency magnetron sputtering on glass substrates at
a high sputtering pressure and room temperature. The anatase films
were then annealed at 300-600 °C in air for a period of 1 hour. To
examine the structure and morphology of the films, X-ray diffraction
(XRD) and atomic force microscopy (AFM) methods were used
respectively. From X-ray diffraction patterns of the TiO2 films, it was
found that the as-deposited film showed some differences compared
with the annealed films and the intensities of the peaks of the
crystalline phase increased with the increase of annealing
temperature. From AFM images, the distinct variations in the
morphology of the thin films were also observed. The optical
constants were characterized using the transmission spectra of the
films obtained by UV-VIS-IR spectrophotometer. Besides, optical
thickness of the film deposited at room temperature was calculated
and cross-checked by taking a cross-sectional image through SEM.
The optical band gaps were evaluated through Tauc model. It was
observed that TiO2 films produced at room temperatures exhibited
high visible transmittance and transmittance decreased slightly with
the increase of annealing temperatures. The films were found to be
crystalline having anatase phase. The refractive index of the films
was found from 2.31-2.35 in the visible range. The extinction
coefficient was nearly zero in the visible range and was found to
increase with annealing temperature. The allowed indirect optical
band gap of the films was estimated to be in the range from 3.39 to
3.42 eV which showed a small variation. The allowed direct band
gap was found to increase from 3.67 to 3.72 eV. The porosity was
also found to decrease at a higher annealing temperature making the
film compact and dense.
Abstract: In this paper, we proposed the effects of Mo thickness
on the properties of AZO/Mo/AZO multilayer thin films for
opto-electronics applications. The structural, optical and electrical
properties of AZO/Mo/AZO thin films were investigated.
Optimization of the thin films coatings resulted with low resistivity of
9.98 × 10-5 )-cm, mobility of 12.75 cm2/V-s, carrier concentration of
1.05 × 1022 cm-3, maximum transmittance of 79.13% over visible
spectrum of 380 – 780 nm and Haacke figure of merit (FOM) are 5.95
× 10-2 )-1 under Mo layer thickness of 15 nm. These results indicate an
alternative candidate for use as a transparent electrode in solar cells
and various displays applications.
Abstract: ZnO+Ga2O3 functionally graded thin films (FGTFs)
were examined for their potential use as Solar cell and organic light
emitting diodes (OLEDs). FGTF transparent conducting oxides (TCO)
were fabricated by combinatorial RF magnetron sputtering. The
composition gradient was controlled up to 10% by changing the
plasma power of the two sputter guns. A Ga2O3+ZnO graded region
was placed on the top layer of ZnO. The FGTFs showed up to 80%
transmittance. Their surface resistances were reduced to < 10% by
increasing the Ga2O3: pure ZnO ratio in the TCO. The FGTFs- work
functions could be controlled within a range of 0.18 eV. The
controlled work function is a very promising technology because it
reduces the contact resistance between the anode and Hall transport
layers of OLED and solar cell devices.
Abstract: Semiconductor materials with coatings have a wide range of applications in MEMS and NEMS. This work uses transfermatrix method for calculating the radiative properties. Dopped silicon is used and the coherent formulation is applied. The Drude model for the optical constants of doped silicon is employed. Results showed that for the visible wavelengths, more emittance occurs in greater concentrations and the reflectance decreases as the concentration increases. In these wavelengths, transmittance is negligible. Donars and acceptors act similar in visible wavelengths. The effect of wave interference can be understood by plotting the spectral properties such as reflectance or transmittance of a thin dielectric film versus the film thickness and analyzing the oscillations of properties due to constructive and destructive interferences. But this effect has not been shown at visible wavelengths. At room temperature, the scattering process is dominated by lattice scattering for lightly doped silicon, and the impurity scattering becomes important for heavily doped silicon when the dopant concentration exceeds1018cm-3 .