Abstract: Cold press technique is a traditional method to obtain oil. The cold-pressing procedure involves neither heat nor chemical treatments; therefore, cold press technique has low oil yield. The cold pressed herbal material residue still contains some oil after cold press. In this study, the oil that is remained in the cold pressed aniseed was extracted with hexane; and it was analyzed to determine physicochemical properties and quality parameters. It was found that the aniseed after cold press process still contained 10% oil. The values of other analysis parameters were 2.1 mgKOH/g for free fatty acid (FFA) and 7.6 meq02/kg for peroxide. Cold pressed aniseed oil values were determined as 2.1 mgKOH/g for FFA and 4.5 meq02/kg for peroxide, respectively. In addition, fatty acid composition was analyzed, and it was found that both types of oil had same fatty acid compositions. The main fatty acids were oleic, linoleic and palmitic acids.
Abstract: Composite material based on Fe3Si micro-particles
and Mn-Zn nano-ferrite was prepared using powder metallurgy
technology. The sol-gel followed by autocombustion process was
used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically
milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano
powder system was homogenized by the Resonant Acoustic Mixing
using ResodynLabRAM Mixer. This non-invasive homogenization
technique was used to preserve spherical morphology of Fe3Si
powder particles. Uniaxial cold pressing in the closed die at pressure
600 MPa was applied to obtain a compact sample. Microwave
sintering of green compact was realized at 800°C, 20 minutes, in air.
Density of the powders and composite was measured by
Hepycnometry. Impulse excitation method was used to measure
elastic properties of sintered composite. Mechanical properties were
evaluated by measurement of transverse rupture strength (TRS) and
Vickers hardness (HV). Resistivity was measured by 4 point probe
method. Ferrite phase distribution in volume of the composite was
documented by metallographic analysis.
It has been found that nano-ferrite particle distributed among
micro- particles of Fe3Si powder alloy led to high relative density
(~93%) and suitable mechanical properties (TRS >100 MPa, HV
~1GPa, E-modulus ~140 GPa) of the composite. High electric
resistivity (R~6.7 ohm.cm) of prepared composite indicate their
potential application as soft magnetic material at medium and high
frequencies.
Abstract: After cold pressing of pumpkin oil, the defatted oil cake (PUOC) was utilised as raw material for processing of bio-functional hydrolysates. In this study, the in vitro bioactivity of an alcalase (AH) and a pepsin hydrolysate (PH) prepared from the major pumpkin 12S globulin (cucurbitin) are compared. The hydrolysates were produced at optimum reaction conditions (temperature, pH) for the enzymes, during 60min. The bioactivity testing included antioxidant and angiotensin I converting enzyme inhibitory activity assays. The hydrolysates showed high potential as natural antioxidants and possibly antihypertensive agents in functional food or nutraceuticals. Additionally, preliminary studies have shown that both hydrolysates could exhibit modest α-amylase inhibitory activity, which indicates on their hypoglycemic potential.
Abstract: This paper studied the synthesis of monoacylglycerol (monolaurin) by glycerolysis of coconut oil and crude glycerol, catalyzed by Carica papaya lipase. Coconut oil obtained from cold pressed extraction method and crude glycerol obtained from the biodiesel plant in Department of Chemistry, Uttaradit Rajabhat University, Thailand which used oils were used as raw materials for biodiesel production through transesterification process catalyzed by sodium hydroxide. The influences of the following variables were studied: (i) type of organic solvent, (ii) molar ratio of substrate, (iii) reaction temperature, (iv) reaction time, (v) lipase dosage, and (vi) initial water activity of enzyme. High yields in monoacylglycerol (58.35%) were obtained with molar ratio of glycerol to oil at 8:1 in ethanol, temperature was controlled at 45oC for 36 hours, the amount of enzyme used was 20 wt% of oil and initial water activity of enzyme at 0.53.
Abstract: In this study, the powders of Ni and Ti with 50.5 at.%
Ni for 12 h were blended and cold pressed at the different pressures
(50, 75 and100 MPa).The porous product obtained after Ni-Ti
compacts were synthesized by SHS (self-propagating hightemperature
synthesis) in the different preheating temperatures (200,
250 and 300oC) and heating rates (30, 60 and 90oC/min). The effects
of the pressure, preheating temperature and heating rate were
investigated on biocompatibility in vivo. The porosity in the
synthesized products was in the range of 50.7–59.7 vol. %. The
pressure, preheating temperature and heating rate were found to have
an important effect on the biocompatibility in-vivo of the synthesized
products. Max. fibrotic tissue within the porous implant was found in
vivo periods (6 months), in which compacting pressure 100MPa.