Abstract: Aluminium bronze alloys are well known for their superior abrasion, tensile strength and non-magnetic properties, due to the co-presence of iron (Fe) and aluminium (Al) as alloying elements and have been commonly used in many industrial applications. However, continuous exposure to the marine environment will accelerate the risk of a tendency to Al bronze alloys parts failures. Although a higher level of corrosion resistance properties can be achieved by modifying its elemental composition, it will come at a price through the complex manufacturing process and increases the risk of reducing the ductility of Al bronze alloy. In this research, the use of ironmaking slag and waste plastic as the input source for surface modification of Al bronze alloy was implemented. Microstructural analysis conducted using polarised light microscopy and scanning electron microscopy (SEM) that is equipped with energy dispersive spectroscopy (EDS). An electrochemical corrosion test was carried out through Tafel polarisation method and calculation of protection efficiency against the base-material was determined. Results have indicated that uniform modified surface which is as the result of selective diffusion process, has enhanced corrosion resistance properties up to 12.67%. This approach has opened a new opportunity to access various industrial utilisations in commercial scale through minimising the dependency on natural resources by transforming waste sources into the protective coating in environmentally friendly and cost-effective ways.
Abstract: The effect of laser surface treatment parameters on the residual strength of titanium alloy has been investigated. The influence of the laser surface treatment on the bonding strength between the titanium and poly-ether-ketone-ketone (PEKK) surfaces was also evaluated and compared to those offered by titanium foils without surface treatment to optimize the laser parameters. Material characterization using an optical microscope was carried out to study the microstructure and to measure the mean roughness value of the titanium surface. The results showed that the surface roughness shows a significant dependency on the laser power parameters in which surface roughness increases with the laser power increment. Moreover, the results of the tensile tests have shown that there is no significant dropping in tensile strength for the treated samples comparing to the virgin ones. In order to optimize the laser parameter as well as the corresponding surface roughness, single-lap shear tests were conducted on pairs of the laser treated titanium stripes. The results showed that the bonding shear strength between titanium alloy and PEKK film increased with the surface roughness increment to a specific limit. After this point, it is interesting to note that there was no significant effect for the laser parameter on the bonding strength. This evidence suggests that it is not necessary to use very high power of laser to treat titanium surface to achieve a good bonding strength between titanium alloy and the PEKK film.
Abstract: Mesoporous materials are very commonly used as adsorbent materials for removing phenolic compounds. However, the adsorption mechanism of these compounds is still poorly controlled. However, understanding the interactions mesoporous materials/adsorbed molecules is very important in order to optimize the processes of liquid phase adsorption. The difficulty of synthesis is to keep an orderly and cubic pore structure and achieve a homogeneous surface modification. The grafting of Si(CH3)3 was chosen, to transform hydrophilic surfaces hydrophobic surfaces. The aim of this work is to study the kinetics and thermodynamics of two volatile organic compounds VOC phenol (PhOH) and P hydroxy benzoic acid (4AHB) on a mesoporous material of type MCM-48 grafted with an organosilane of the Trimethylchlorosilane (TMCS) type, the material thus grafted or functionalized (hereinafter referred to as MCM-48-G). In a first step, the kinetic and thermodynamic study of the adsorption isotherms of each of the VOCs in mono-solution was carried out. In a second step, a similar study was carried out on a mixture of these two compounds. Kinetic models (pseudo-first order, pseudo-second order) were used to determine kinetic adsorption parameters. The thermodynamic parameters of the adsorption isotherms were determined by the adsorption models (Langmuir, Freundlich). The comparative study of adsorption of PhOH and 4AHB proved that MCM-48-G had a high adsorption capacity for PhOH and 4AHB; this may be related to the hydrophobicity created by the organic function of TMCS in MCM-48-G. The adsorption results for the two compounds using the Freundlich and Langmuir models show that the adsorption of 4AHB was higher than PhOH. The values obtained by the adsorption thermodynamics show that the adsorption interactions for our sample with the phenol and 4AHB are of a physical nature. The adsorption of our VOCs on the MCM-48 (G) is a spontaneous and exothermic process.
Abstract: The tribological behavior of commercially used Perspex was evaluated under dry and wet sliding condition using a pin-on-disc wear tester with different applied loads ranging from 2.5 to 20 N. Experiments were conducted with varying sliding distance from 0.2 km to 4.6 km, wherein the sliding velocity was kept constant, 0.64 ms-1. The results reveal that the weight loss increases with applied load and the sliding distance. The nature of the wear rate was very similar in both the sliding environments in which initially the wear rate increased very rapidly with increasing sliding distance and then progressed to a slower rate. Moreover, the wear rate in wet sliding environment was significantly lower than that under dry sliding condition. The worn surfaces were characterized by optical microscope and SEM. It is found that surface modification has significant effect on sliding wear performance of Perspex.
Abstract: Tissue engineering includes combination of materials and techniques used for the improvement, repair or replacement of the tissue. Scaffolds, permanent or temporally material, are used as support for the creation of the "new cell structures". For this important component (scaffold), a variety of materials can be used. The advantage of some polymeric materials is their cytocompatibility and possibility of biodegradation. Poly(L-lactic acid) (PLLA) is a biodegradable, semi-crystalline thermoplastic polymer. PLLA can be fully degraded into H2O and CO2. In this experiment, the effect of the surface modification of biodegradable polymer (performed by plasma treatment) on the various cell types was studied. The surface parameters and changes of the physicochemical properties of modified PLLA substrates were studied by different methods. Surface wettability was determined by goniometry, surface morphology and roughness study were performed with atomic force microscopy and chemical composition was determined using photoelectron spectroscopy. The physicochemical properties were studied in relation to cytocompatibility of human osteoblast (MG 63 cells), rat vascular smooth muscle cells (VSMC), and human stem cells (ASC) of the adipose tissue in vitro. A fluorescence microscopy was chosen to study and compare cell-material interaction. Important parameters of the cytocompatibility like adhesion, proliferation, viability, shape, spreading of the cells were evaluated. It was found that the modification leads to the change of the surface wettability depending on the time of modification. Short time of exposition (10-120 s) can reduce the wettability of the aged samples, exposition longer than 150 s causes to increase of contact angle of the aged PLLA. The surface morphology is significantly influenced by duration of modification, too. The plasma treatment involves the formation of the crystallites, whose number increases with increasing time of modification. On the basis of physicochemical properties evaluation, the cells were cultivated on the selected samples. Cell-material interactions are strongly affected by material chemical structure and surface morphology. It was proved that the plasma treatment of PLLA has a positive effect on the adhesion, spreading, homogeneity of distribution and viability of all cultivated cells. This effect was even more apparent for the VSMCs and ASCs which homogeneously covered almost the whole surface of the substrate after 7 days of cultivation. The viability of these cells was high (more than 98% for VSMCs, 89-96% for ASCs). This experiment is one part of the basic research, which aims to easily create scaffolds for tissue engineering with subsequent use of stem cells and their subsequent "reorientation" towards the bone cells or smooth muscle cells.
Abstract: Surface topography plays a significant role in the functional performance of engineered parts. It is important to have a control on the surface geometry and understanding on the surface details to get the desired performance. Hence, in the current research contribution, a non-contact micro-texturing technique has been explored and developed. The technique involves ultrasonic excitation of a tool as a prime source of surface texturing for aluminum alloy workpieces. The specimen surface is polished first and is then immersed in a liquid bath containing 10% weight concentration of Ti6Al4V grade 5 spherical powders. A submerged slurry jet is used to recirculate the spherical powders under the ultrasonic horn which is excited at an ultrasonic frequency and amplitude of 40 kHz and 70 µm respectively. The distance between the horn and workpiece surface was remained fixed at 200 µm using a precision control stage. Texturing effects were investigated for different process timings of 1, 3 and 5 s. Thereafter, the specimens were cleaned in an ultrasonic bath for 5 mins to remove loose debris on the surface. The developed surfaces are characterized by optical and contact surface profiler. The optical microscopic images show a texture of circular spots on the workpiece surface indented by titanium spherical balls. Waviness patterns obtained from contact surface profiler supports the texturing effect produced from the proposed technique. Furthermore, water droplet tests were performed to show the efficacy of the proposed technique to develop hydrophilic surfaces and to quantify the texturing effect produced.
Abstract: Cotton dyeing using reactive dyes is one of the major water polluter; this is due to large amount of dye and salt remaining in effluent. Recent adverse climate change and its associated effect to human life have lead to search for more sustainable industrial production. Cationization of cotton to improve its affinity for reactive dye has been earmarked as a major solution for dyeing of cotton with no or less salt. Synthetic cationizing agents of ammonium salt have already been commercialized. However, in nature there are proteinous products which are rich in amino and ammonium salts which can be carefully harnessed to be used as cationizing agent for cotton. The hoofs and horns have successfully been used to cationize cotton so as to improve cotton affinity to the dye. The cationization action of the hoof and horn extract on cotton was confirmed by dyeing the pretreated fabric without salt and comparing it with conventionally dyed and untreated salt free dyed fabric. UV-VIS absorption results showed better dye absorption (62.5% and 50% dye bath exhaustion percentage for cationized and untreated respectively) while K/S values of treated samples were similar to conventional sample.
Abstract: Chromium in the environment is considered as one of the most toxic elements probably next only to mercury and arsenic. It is acutely toxic, mutagenic and carcinogenic in the environment. Chromium contamination of soil and underground water due to industrial activities is a very serious problem in several parts of India covering Karnataka, Tamil Nadu, Andhra Pradesh etc. Functionally modified Activated Carbon Fabrics (ACF) offer targeted chromium removal from drinking water and industrial effluents. Activated carbon fabric is a light weight adsorbing material with high surface area and low resistance to fluid flow. We have investigated surface modification of ACF using various acids in the laboratory through batch as well as through continuous flow column experiments with a view to develop the optimum conditions for chromium removal. Among the various acids investigated, phosphoric acid modified ACF gave best results with a removal efficiency of 95% under optimum conditions. Optimum pH was around 2 – 4 with 2 hours contact time. Continuous column experiments with an effective bed contact time (EBCT) of 5 minutes indicated that breakthrough occurred after 300 bed volumes. Adsorption data followed a Freundlich isotherm pattern. Nickel adsorbs preferentially and sulphate reduces chromium adsorption by 50%. The ACF could be regenerated up to 52.3% using 3 M NaOH under optimal conditions. The process is simple, economical, energy efficient and applicable to industrial effluents and drinking water.
Abstract: Electrospun microtube array membranes (MTAMs) made of PLLA (poly-L-lactic acid) have wide potential applications in tissue engineering. However, their surface hydrophobicity and poor biocompatability have limited their further usage. In this study, the surface of PLLA MTAMs were made hydrophilic by introducing extra functional groups, such as peroxide, via an acetic acid plasma (AAP). UV-graft polymerization of acrylic acid (G-AAc) was then used to produce carboxyl group on MTAMs surface, which bonded covalently with chitosan through EDC / NHS crosslinking agents. To evaluate the effects of the surface modification on PLLA MTAMs, water contact angle (WCA) measurement and cell compatibility tests were carried out. We found that AAP treated electrospun PLLA MTAMs grafted with AAc and, finally, with chitosan immobilized via crosslinking agent, exhibited improved hydrophilic and cell compatibility.
Abstract: Titanium and its alloys have been used extensively over the past 25 years as biomedical materials in orthopedic and dental applications because of their good mechanical properties, corrosion resistance, and biocompatibility. It is known that the surface properties of titanium implants can enhance the cellular response and play an important role in Osseo integration. The rate and quality of Osseo integration in titanium implants are related to their surface properties. The purpose of this investigation was to evaluate the effect of sandblasting and acid etching on surface morphology, roughness, the wettability of titanium. The surface properties will be characterized by scanning electron microscopy and contact angle and roughness measurements. The results show that surface morphology, roughness, and wettability were changed and enhanced by these treatments.
Abstract: Artificial joint replacements such as total knee and total hip prosthesis have been applied to the patients who affected by osteoarthritis. Although different material combinations are used for these joints, biopolymers are most commonly preferred materials especially for acetabular cup and tibial component of hip and knee joints respectively. The main limitation that shortens the service life of these prostheses is wear. Wear is complicated phenomena and it must be considered with friction and lubrication. In this study, micro wave (MW) induced argon+oxygen plasma surface modification were applied on ultra-high molecular weight polyethylene (UHMWPE) and vitamin E blended UHMWPE (VE-UHMWPE) biopolymer surfaces to improve surface wettability and wear resistance of the surfaces. Contact angel measurement method was used for determination of wettability. Ball-on-disc wear test was applied under 25% bovine serum lubrication conditions. The results show that surface wettability and wear resistance of both material samples were increased by plasma surface modification.
Abstract: Surface characteristics of Bacillus megaterium strain
were investigated; zeta potential, FTIR and contact angle were
measured. Surface energy components including Lifshitz-van der
Waals, Hamaker constant, and acid/base components (Lewis
acid/Lewis base) were calculated from the contact angle data. The
results showed that the microbial cells were negatively charged over
all pH regions with high values at alkaline region. A hydrophilic
nature for the strain was confirmed by contact angle and free energy
of adhesion between microbial cells. Adsorption affinity of the strain
toward dolomite was studied at different pH values. The results
showed that the cells had a high affinity to dolomite at acid pH
comparing to neutral and alkaline pH. Extended DLVO theory was
applied to calculate interaction energy between B. megaterium cells
and dolomite particles. The adsorption results were in agreement with
the results of Extended DLVO approach. Surface changes occurred
on dolomite surface after the bio-treatment were monitored; contact
angle decreased from 69° to 38° and the mineral’s floatability
decreased from 95% to 25% after the treatment.
Abstract: Lightweight and efficient structures have the aim to
enhance the efficiency of the components in various industries.
Toward this end, composites are one of the most widely used
materials because of durability, high strength and modulus, and low
weight. One type of the advanced composites is grid-stiffened
composite (GSC) structures, which have been extensively considered
in aerospace, automotive, and aircraft industries. They are one of the
top candidates for replacing some of the traditional components,
which are used here. Although there are a good number of published
surveys on the design aspects and fabrication of GSC structures, little
systematic work has been reported on their material modification to
improve their properties, to our knowledge. Matrix modification
using nanoparticles is an effective method to enhance the flexural
properties of the fibrous composites. In the present study, a silanecoupling
agent (3-glycidoxypropyltrimethoxysilane/3-GPTS) was
introduced onto the silica (SiO2) nanoparticle surface and its effects
on the three-point flexural response of isogrid E-glass/epoxy
composites were assessed. Based on the Fourier Transform Infrared
Spectrometer (FTIR) spectra, it was inferred that the 3-GPTS
coupling agent was successfully grafted onto the surface of SiO2
nanoparticles after modification. Flexural test revealed an
improvement of 16%, 14%, and 36% in stiffness, maximum load and
energy absorption of the isogrid specimen filled with 3 wt.% 3-
GPTS/SiO2 compared to the neat one. It would be worth mentioning
that in these structures, considerable energy absorption was observed
after the primary failure related to the load peak. In addition, 3-
GPTMS functionalization had a positive effect on the flexural
behavior of the multiscale isogrid composites. In conclusion, this
study suggests that the addition of modified silica nanoparticles is a
promising method to improve the flexural properties of the gridstiffened
fibrous composite structures.
Abstract: This study evaluated to facilitate separation of ABS
plastics from other waste plastics by froth flotation after surface
hydrophilization of ABS with heat treatment. The mild heat treatment
at 100oC for 60s could selectively increase the hydrophilicity of the
ABS plastics surface (i.e., ABS contact angle decreased from 79o to
65.8o) among other plastics mixture. The SEM and XPS results of
plastic samples sufficiently supported the increase in hydrophilic
functional groups and decrease contact angle on ABS surface, after
heat treatment. As a result of the froth flotation (at mixing speed 150
rpm and airflow rate 0.3 L/min) after heat treatment, about 85% of
ABS was selectively separated from other heavy plastics with 100%
of purity. The effect of optimum treatment condition and detailed
mechanism onto separation efficiency in the froth floatation was also
investigated. This research is successful in giving a simple, effective,
and inexpensive method for ABS separation from waste plastics.
Abstract: Surface modification and functionalization has been
an important tool for scientists in order to open new frontiers in
nanoscience and nanotechnology. Desired surface characteristics for
the intended applications can be achieved with surface
functionalization.
In this work, the effect of water soluble ligands on the adsorption
capabilities of silver nanoparticles onto AC which was synthesized
from German beech wood was investigated. Sodium borohydride
(NaBH4) and polyvinyl alcohol (PVA) were used as the ligands.
Silver nanoparticles with different surface coatings have average
sizes range from 10 to 13 nm. They were synthesized in aqueous
media by reducing Ag (I) ion in the presence of ligands. These
particles displayed adsorption tendencies towards AC when they
were mixed together and shaken in distilled water.
Silver nanoparticles (NaBH4-AgNPs) reduced and stabilized by
NaBH4 adsorbed onto AC with a homogenous dispersion of
aggregates with sizes in the range of 100-400 nm. Beside, silver
nanoparticles, which were prepared in the presence of both NaBH4
and PVA (NaBH4/PVA-Ag NPs), demonstrated that NaBH4/PVA-Ag
NPs adsorbed and dispersed homogenously but, they aggregated with
larger sizes on the AC surface (range from 300 to 600 nm). In
addition, desorption resistance of Ag nanoparticles were investigated
in distilled water. According to the results AgNPs were not desorbed
on the AC surface in distilled water.
Abstract: In the scope of application of technical textiles, Non-
Crimp Fabrics are increasingly used. In general, NCF exhibit
excellent load bearing properties, but caused by the manufacturing
process, there are some remaining disadvantages which have to be
reduced. Regarding to this, a novel technique of processing NCF was
developed substituting the binding-thread by an adhesive. This stitchfree
method requires new manufacturing concept as well as new basic
methods to prove adhesion of glue at fibres and textiles. To improve
adhesion properties and the wettability of carbon-fibres by the
adhesive, oxy-fluorination was used. The modification of carbonfibres
by oxy-fluorination was investigated via scanning electron
microscope, X-ray photoelectron spectroscopy and single fibre
tensiometry. Special tensile tests were developed to determine the
maximum force required for detachment.
Abstract: The surface properties of many materials can be readily and predictably modified by the controlled deposition of thin layers containing appropriate functional groups and this research area is now a subject of widespread interest. The layer-by-layer (lbl) method involves depositing oppositely charged layers of polyelectrolytes onto the substrate material which are stabilized due to strong electrostatic forces between adjacent layers. This type of modification affords products that combine the properties of the original material with the superficial parameters of the new external layers. Through an appropriate selection of the deposited layers, the surface properties can be precisely controlled and readily adjusted in order to meet the requirements of the intended application. In the presented paper a variety of anionic (poly(acrylic acid)) and cationic (linear poly(ethylene imine), polymers were successfully deposited onto the polypropylene nonwoven using the lbl technique. The chemical structure of the surface before and after modification was confirmed by reflectance FTIR spectroscopy, volumetric analysis and selective dyeing tests. As a direct result of this work, new materials with greatly improved properties have been produced. For example, following a modification process significant changes in the electrostatic activity of a range of novel nanocomposite materials were observed. The deposition of polyelectrolyte nanolayers was found to strongly accelerate the loss of electrostatically generated charges and to increase considerably the thermal resistance properties of the modified fabric (the difference in T50% is over 20oC). From our results, a clear relationship between the type of polyelectrolyte layer deposited onto the flat fabric surface and the properties of the modified fabric was identified.
Abstract: This paper investigates the influence of various
parameters on the behaviour of water droplets on polymeric surfaces
under high electric fields. An inclined plane test was carried out to
understand the droplet behaviour in strong electric field. Parameters
such as water droplet conductivity, droplet volume, polymeric
surface roughness and droplet positioning with respect to the
electrodes were studied. The flashover voltage is affected by all
aforementioned parameters. The droplet positioning is in some cases
more vital than the droplet volume. Surface damages were analysed
using Scanning Electron Microscopy (SEM) studies and by Energy
dispersive X-ray Analysis (EDAX). It is observes that magnitude of
discharge have direct influence on amount of surface da
Abstract: We demonstrate a nonfaradaic electrochemical impedance spectroscopy measurement of biochemically modified gold plated electrodes using a two-electrode system. The absence of any redox indicator in the impedance measurements provide more precise and accurate characterization of the measured bioanalyte at molecular resolution. An equivalent electrical circuit of the electrodeelectrolyte interface was deduced from the observed impedance data of saline solution at low and high concentrations. The detection of biomolecular interactions was fundamentally correlated to electrical double-layer variation at modified interface. The investigations were done using 20mer deoxyribonucleic acid (DNA) strands without any label. Surface modification was performed by creating mixed monolayer of the thiol-modified single-stranded DNA and a spacer thiol (mercaptohexanol) by a two-step self-assembly method. The results clearly distinguish between the noncomplementary and complementary hybridization of DNA, at low frequency region below several hundreds Hertz.
Abstract: A new strategy for oriented immobilization of proteins was proposed. The strategy contains two steps. The first step is to search for a docking site away from the active site on the protein surface. The second step is trying to find a ligand that is able to grasp the targeted site of the protein. To avoid ligand binding to the active site of protein, the targeted docking site is selected to own opposite charges to those near the active site. To enhance the ligand-protein binding, both hydrophobic and electrostatic interactions need to be included. The targeted docking site should therefore contain hydrophobic amino acids. The ligand is then selected through the help of molecular docking simulations. The enzyme α-amylase derived from Aspergillus oryzae (TAKA) was taken as an example for oriented immobilization. The active site of TAKA is surrounded by negatively charged amino acids. All the possible hydrophobic sites on the surface of TAKA were evaluated by the free energy estimation through benzene docking. A hydrophobic site on the opposite side of TAKA-s active site was found to be positive in net charges. A possible ligand, 3,3-,4,4- – Biphenyltetra- carboxylic acid (BPTA), was found to catch TAKA by the designated docking site. Then, the BPTA molecules were grafted onto silica gels and measured the affinity of TAKA adsorption and the specific activity of thereby immobilized enzymes. It was found that TAKA had a dissociation constant as low as 7.0×10-6 M toward the ligand BPTA on silica gel. The increase in ionic strength has little effect on the adsorption of TAKA, which indicated the existence of hydrophobic interaction between ligands and proteins. The specific activity of the immobilized TAKA was compared with the randomly adsorbed TAKA on primary amine containing silica gel. It was found that the orderly immobilized TAKA owns a specific activity twice as high as the one randomly adsorbed by ionic interaction.