Abstract: This work describes an investigation on the effect of filler metals diameter to weld joint, and low alloy carbon steel A516 Grade 70 is the base metal. Commercially SA516 Grade70 is frequently used for the manufacturing of pressure vessels, boilers and storage tank, etc. In fabrication industry, the hardness of the weld joint is between the important parameters to check, after heat treatment of the weld. Submerged arc welding (SAW) is used with two filler metal diameters, and this solid wire electrode is used for SAW non-alloy and for fine grain steels (SFA 5.17). The different diameters were selected (Ø = 2.4 mm and Ø = 4 mm) to weld two specimens. Both specimens were subjected to the same preparation conditions, heat treatment, macrograph, metallurgy micrograph, and micro-hardness test. Samples show almost similar structure with highest hardness. It is important to indicate that the thickness used in the base metal is 22 mm, and all specifications, preparation and controls were according to the ASME section IX. It was observed that two different filler metal diameters performed on two similar specimens demonstrated that the mechanical property (hardness) increases with decreasing diameter. It means that even the heat treatment has the same effect with the same conditions, the filler metal diameter insures a depth weld penetration and better homogenization. Hence, the SAW welding technique mentioned in the present study is favorable to implicate for the industry using the small filler metal diameter.
Abstract: The heat flow in weldment changes its nature from 2D to 3D with the increase in plate thickness. For welding of thicker plates the heat loss in thickness direction increases the cooling rate of plate. Since the cooling rate changes, the various bead parameters like bead penetration, bead height and bead width also got affected by it. The present study incorporates the effect of variable plate thickness on penetration and bead width. The penetration reduces with increase in plate thickness due to heat loss in thickness direction for same heat input, while bead width increases for thicker plate due to faster cooling.
Abstract: Commercially SA 516 Grade 70 is frequently used for the manufacturing of pressure vessels, boilers and storage tanks etc. in fabrication industry. Heat input is the major parameter during welding that may bring significant changes in the microstructure as well as the mechanical properties. Different welding technique has different heat input rate per unit surface area. Materials with large thickness are dealt with different combination of welding techniques to achieve required mechanical properties. In the present research two schemes: Scheme 1: SMAW (Shielded Metal Arc Welding) & GTAW (Gas Tungsten Arc Welding) and Scheme 2: SMAW & SAW (Submerged Arc Welding) of hybrid welding techniques have been studied. The purpose of these schemes was to study hybrid welding effect on the microstructure and mechanical properties of the weldment, heat affected zone and base metal area. It is significant to note that the thickness of base plate was 12 mm, also welding conditions and parameters were set according to ASME Section IX. It was observed that two different hybrid welding techniques performed on two different plates demonstrated that the mechanical properties of both schemes are more or less similar. It means that the heat input, welding techniques and varying welding operating conditions & temperatures did not make any detrimental effect on the mechanical properties. Hence, the hybrid welding techniques mentioned in the present study are favorable to implicate for the industry using the plate thickness around 12 mm thick.
Abstract: Proper selection of welding parameters for getting
excellent weld is a challenge. HAZ simulation helps in identifying
suitable welding parameters like heating rate, cooling rate, peak
temperature, and energy input. In this study, the influence of weld
thermal cycle of heat affected zone (HAZ) is simulated for
Submerged Arc Welding (SAW) using Gleeble ® 3800 thermomechanical
simulator. A (Micro-alloyed) MA steel plate of thickness
18 mm having yield strength 450MPa is used for making test
specimens. Determination of the mechanical properties of weld
simulated specimens including Charpy V-notch toughness and
hardness is performed. Peak temperatures of 1300°C, 1150°C,
1000°C, 900°C, 800°C, heat energy input of 22KJ/cm and preheat
temperatures of 30°C have been used with Rykalin-3D simulation
model. It is found that the impact toughness (75J) is the best for the
simulated HAZ specimen at the peak temperature 900ºC. For parent
steel, impact toughness value is 26.8J at -50°C in transverse
direction.
Abstract: Submerged arc welding is a very complex process. It
is a very efficient and high performance welding process. In this
present study an attempt have been done to reduce the welding
distortion by increased amount of oxide flux through TiO2 in
submerged arc welding process. Care has been taken to avoid the
excessiveness of the adding agent for attainment of significant
results. Data Envelopment Analysis (DEA) based BAT algorithm is
used for the parametric optimization purpose in which DEA is used
to convert multi response parameters into a single response
parameter. The present study also helps to know the effectiveness of
the addition of TiO2 in active flux during submerged arc welding
process.