Abstract: This work describes an investigation on the effect of filler metals diameter to weld joint, and low alloy carbon steel A516 Grade 70 is the base metal. Commercially SA516 Grade70 is frequently used for the manufacturing of pressure vessels, boilers and storage tank, etc. In fabrication industry, the hardness of the weld joint is between the important parameters to check, after heat treatment of the weld. Submerged arc welding (SAW) is used with two filler metal diameters, and this solid wire electrode is used for SAW non-alloy and for fine grain steels (SFA 5.17). The different diameters were selected (Ø = 2.4 mm and Ø = 4 mm) to weld two specimens. Both specimens were subjected to the same preparation conditions, heat treatment, macrograph, metallurgy micrograph, and micro-hardness test. Samples show almost similar structure with highest hardness. It is important to indicate that the thickness used in the base metal is 22 mm, and all specifications, preparation and controls were according to the ASME section IX. It was observed that two different filler metal diameters performed on two similar specimens demonstrated that the mechanical property (hardness) increases with decreasing diameter. It means that even the heat treatment has the same effect with the same conditions, the filler metal diameter insures a depth weld penetration and better homogenization. Hence, the SAW welding technique mentioned in the present study is favorable to implicate for the industry using the small filler metal diameter.
Abstract: Submerged arc welding is a very complex process. It
is a very efficient and high performance welding process. In this
present study an attempt have been done to reduce the welding
distortion by increased amount of oxide flux through TiO2 in
submerged arc welding process. Care has been taken to avoid the
excessiveness of the adding agent for attainment of significant
results. Data Envelopment Analysis (DEA) based BAT algorithm is
used for the parametric optimization purpose in which DEA is used
to convert multi response parameters into a single response
parameter. The present study also helps to know the effectiveness of
the addition of TiO2 in active flux during submerged arc welding
process.