Abstract: NiTi alloys possess magnificent superelastic, shape memory, high strength and biocompatible properties. For improving mechanical properties, foremost, superelasticity behavior, heat treatment process is carried out. In this paper, two different heat treatment methods were undertaken: (1) solid solution, and (2) aging. The effect of each treatment in a constant time is investigated. Five samples were prepared to study the structure and optimize mechanical properties under different time and temperature. For measuring the upper plateau stress, lower plateau stress and residual strain, tensile test is carried out. The samples were aged at two different temperatures to see difference between aging temperatures. The sample aged at 500 °C has a bigger crystallite size and lower amount of Ni which causes the mentioned sample to possess poor pseudo elasticity behaviour than the other aged sample. The sample aged at 460 °C has shown remarkable superelastic properties. The mentioned sample’s higher plateau is 580 MPa with the lowest residual strain (0.17%) while other samples have possessed higher residual strains. X-ray diffraction was used to investigate the produced phases.
Abstract: Multi-point forming (MPF) and asymmetric incremental forming (ISF) are two flexible processes for sheet metal manufacturing. To take advantages of these two techniques, a hybrid process has been developed: The Multipoint Incremental Forming (MPIF). This process accumulates at once the advantages of each of these last mentioned forming techniques, which makes it a very interesting and particularly an efficient process for single, small, and medium series production. In this paper, an experimental and a numerical investigation of this technique are presented. To highlight the flexibility of this process and its capacity to manufacture standard and complex shapes, several pieces were produced by using MPIF. The forming experiments are performed on a 3-axis CNC machine. Moreover, a numerical model of the MPIF process has been implemented in ABAQUS and the analysis showed a good agreement with experimental results in terms of deformed shape. Furthermore, the use of an elastomeric interpolator allows avoiding classical local defaults like dimples, which are generally caused by the asymmetric contact and also improves the distribution of residual strain. Future works will apply this approach to other alloys used in aeronautic or automotive applications.
Abstract: In this study, a general approach to the reliability
based limit analysis of laterally loaded piles is presented. In
engineering practice the uncertainties play a very important role. The
aim of this study is to evaluate the lateral load capacity of free-head
and fixed-head long pile when plastic limit analysis is considered. In
addition to the plastic limit analysis to control the plastic behaviour
of the structure, uncertain bound on the complementary strain energy
of the residual forces is also applied. This bound has significant effect
for the load parameter. The solution to reliability-based problems is
obtained by a computer program which is governed by the reliability
index calculation.
Abstract: Through a proper analysis of residual strain and stress
distributions obtained at the surface of high speed milled specimens
of AA 6082–T6 aluminium alloy, the performance of an improved
indentation method is evaluated. This method integrates a special
device of indentation to a universal measuring machine. The
mentioned device allows introducing elongated indents allowing to
diminish the absolute error of measurement. It must be noted that the
present method offers the great advantage of avoiding both the
specific equipment and highly qualified personnel, and their inherent
high costs. In this work, the cutting tool geometry and high speed
parameters are selected to introduce reduced plastic damage.
Through the variation of the depth of cut, the stability of the shapes
adopted by the residual strain and stress distributions is evaluated.
The results show that the strain and stress distributions remain
unchanged, compressive and small. Moreover, these distributions
reveal a similar asymmetry when the gradients corresponding to
conventional and climb cutting zones are compared.
Abstract: In this article, using finite element analysis (FEA)
and an X-ray diffractometer (XRD), cold-sprayed titanium particles
on a steel substrate is investigated in term of cooling time and the
development of residual strains. Three cooling-down models of
sprayed particles after deposition stage are simulated and discussed:
the first model (m1) considers conduction effect to the substrate only,
the second model (m2) considers both conduction as well as
convection effect to the environment, and the third model (m3) which
is the same as the second model but with the substrate heated to a
near particle temperature before spraying. Thereafter, residual strains
developed in the third model is compared with the experimental
measurement of residual strains, which involved a Bruker D8
Advance Diffractometer using CuKa radiation (40kV, 40mA)
monochromatised with a graphite sample monochromator. For
deposition conditions of this study, a good correlation was found to
exist between the FEA results and XRD measurements of residual
strains.
Abstract: Group-III nitride material as particularly AlxGa1-xN is
one of promising optoelectronic materials to require for shortwavelength
devices. To achieve the high-quality AlxGa1-xN films for
a high performance of such devices, AlN-nucleation layers are the
important factor. To improve the AlN-nucleation layers with a
variation of Ga-addition, XRD measurements were conducted to
analyze the crystalline quality of the subsequent Al0.1Ga0.9N with the
minimum ω-FWHMs of (0002) and (10-10) reflections of 425 arcsec
and 750 arcsec, respectively. SEM and AFM measurements were
performed to observe the surface morphology and TEM
measurements to identify the microstructures and orientations.
Results showed that the optimized Ga-atoms in the Al(Ga)Nnucleation
layers improved the surface diffusion to form moreuniform
crystallites in structure and size, better alignment of each
crystallite, and better homogeneity of island distribution. This, hence,
improves the orientation of epilayers on the Si-surface and finally
improves the crystalline quality and reduces the residual strain of
subsequent Al0.1Ga0.9N layers.