Abstract: Low density polyethylene (LDPE) nanocomposites
with 3, 5 and 7 wt. % cobalt ferrite (CoFe2O4) nanopowder fabricated
with extrusion mixing and followed up by hot press to reach compact
samples. The transmission/reflection measurements were carried out
with a network analyzer in the frequency range of 8-12 GHz. By
increasing the percent of CoFe2O4 nanopowder, reflection loss (S11)
increases, while transferring loss (S21) decreases. Reflectivity (R)
calculations made using S11 and S21. Increase in percent of CoFe2O4
nanopowder up to 7 wt. % in composite leaded to higher reflectivity
amount, and revealed that increasing the percent of CoFe2O4
nanopowder up to 7 wt. % leads to further microwave absorption in
8-12 GHz range.
Abstract: At the present work, highly transparent strip type
quasi-solid state dye-sensitized solar cells (DSSCs) were fabricated
through inkjet printing using nanocomposite TiO2 inks as raw
materials and tested under outdoor illumination conditions. The cells,
which can be considered as the structural units of large area modules,
were fully characterized electrically and electrochemically and after
the evaluation of the received results a large area DSSC module was
manufactured. The module design was a sandwich Z-interconnection
where the working electrode is deposited on one conductive glass and
the counter electrode on a second glass. Silver current collective
fingers were printed on the conductive glasses to make the internal
electrical connections and the adjacent cells were connected in series
and finally insulated using a UV curing resin to protect them from the
corrosive (I-/I3-) redox couple of the electrolyte. Finally, outdoor tests
were carried out to the fabricated dye-sensitized solar module and its
performance data were collected and assessed.
Abstract: In the present study we have investigated axial
buckling characteristics of nanocomposite beams reinforced by
single-walled carbon nanotubes (SWCNTs). Various types of beam
theories including Euler-Bernoulli beam theory, Timoshenko beam
theory and Reddy beam theory were used to analyze the buckling
behavior of carbon nanotube-reinforced composite beams.
Generalized differential quadrature (GDQ) method was utilized to
discretize the governing differential equations along with four
commonly used boundary conditions. The material properties of the
nanocomposite beams were obtained using molecular dynamic (MD)
simulation corresponding to both short-(10,10) SWCNT and long-
(10,10) SWCNT composites which were embedded by amorphous
polyethylene matrix. Then the results obtained directly from MD
simulations were matched with those calculated by the mixture rule
to extract appropriate values of carbon nanotube efficiency
parameters accounting for the scale-dependent material properties.
The selected numerical results were presented to indicate the
influences of nanotube volume fractions and end supports on the
critical axial buckling loads of nanocomposite beams relevant to
long- and short-nanotube composites.
Abstract: Carbon nanotubes (CNTs) are known for having high elastic properties with high surface area that promote them as good candidates for reinforcing polymeric matrices. In composite materials, CNTs lack chemical bonding with the surrounding matrix which decreases the possibility of better stress transfer between the components. In this work, a chemical treatment for activating the surface of the multi-wall carbon nanotubes (MWCNT) was applied and the effect of this functionalization on the elastic properties of the epoxy nanocomposites was studied. Functional amino-groups were added to the surface of the CNTs and it was evaluated to be about 34% of the total weight of the CNTs. Elastic modulus was found to increase by about 40% of the neat epoxy resin at CNTs’ weight fraction of 0.5%. The elastic modulus was found to decrease after reaching a certain concentration of CNTs which was found to be 1% wt. The scanning electron microscopic pictures showed the effect of the CNTs on the crack propagation through the sample by forming stress concentrated spots at the nanocomposite samples.
Abstract: The effect of carbon nanofibers (CNFs) on the
electrical properties of Poly(vinylidene fluoride-hexafluoropropylene)
(P(VdF-HFP)) based gel polymer electrolytes has been investigated
in the present work. The length and diameter ranges of CNFs used in
the present work are 5-50 μm and 200-600 nm respectively. The
nanocomposite gel polymer electrolytes have been synthesized by
solution casting technique with varying CNFs content in terms of
weight percentage. Electrochemical impedance analysis demonstrates
that the reinforcement of carbon nanofibers significantly enhances the
ionic conductivity of the polymer electrolyte. The decrease of
crystallinity of P(VdF-HFP) due the addition of CNFs has been
confirmed by X-ray diffraction (XRD). The interaction of CNFs with
various constituents of nanocomposite gel polymer electrolytes has
been assessed by Fourier Transform Infrared (FTIR) spectroscopy.
Moreover CNFs added gel polymer electrolytes offer superior
thermal stability as compared to that of CNFs free electrolytes as
confirmed by Thermogravimetric analysis (TGA).
Abstract: In the present study, the properties of Al-Al2O3
nanocomposite hollow sphere structures were investigated. For this
reason, the Al-based nanocomposite hollow spheres with different
amounts of nano-alumina reinforcement (0-10wt %) and different
ratio of thickness to diameter (t/D: 0.06-0.3) were prepared via a
powder metallurgy method. Then, the effect of mentioned parameters
was studied on physical and quasi static mechanical properties of
their related prepared structures (open/closed cell) such as density,
hardness, strength, and energy absorption. It was found that, as the
t/D ratio increases the relative density, compressive strength and
energy absorption increase. The highest values of strength and energy
absorption were obtained from the specimen with 5 wt. % of
nanoparticle reinforcement, t/D of 0.3 (t=1 mm, D=400μm) as 22.88
MPa and 13.24 MJ/m3, respectively. The moderate specific strength
of prepared composites in the present study showed the good
consistency with the properties of others low carbon steel composite
with similar structure.
Abstract: Polyaniline is an indispensible component in lightemitting
devices (LEDs), televisions, cellular telephones, automotive,
corrosion-resistant coatings, actuators etc. The electrical conductivity
properties was found be increased by introduction of metal nano
particles. In the present study, an attempt has been made to utilize
platinum nano particles to achieve the improved electrical properties.
Polyaniline and Pt-polyaniline composite are synthesized by
electrochemical routes. X-ray diffractometer confirms the amorphous
nature of polyaniline. The Bragg’s diffraction peaks correspond to
platinum nanoparticles in Pt-polyaniline composite and
thermogravimetric analyzer indicates its decomposition at certain
temperature. The Scanning Electron Micrographs of colloidal
platinum nanoparticles were spherical, uniform shape in the
composite. The current-voltage (I-V) characteristics of the PANI and
composites were also studied which indicate a significant decreasing
resistivity than PANI-Platinum after introduction of pt nanoparticles
in the matrix of polyaniline (PANI).
Abstract: Typical load-bearing biological materials like bone,
mineralized tendon and shell, are biocomposites made from both
organic (collagen) and inorganic (biomineral) materials. This
amazing class of materials with intrinsic internally designed
hierarchical structures show superior mechanical properties with
regard to their weak components from which they are formed.
Extensive investigations concentrating on static loading conditions
have been done to study the biological materials failure. However,
most of the damage and failure mechanisms in load-bearing
biological materials will occur whenever their structures are exposed
to dynamic loading conditions. The main question needed to be
answered here is: What is the relation between the layout and
architecture of the load-bearing biological materials and their
dynamic behavior? In this work, a staggered model has been
developed based on the structure of natural materials at nanoscale and
Finite Element Analysis (FEA) has been used to study the dynamic
behavior of the structure of load-bearing biological materials to
answer why the staggered arrangement has been selected by nature to
make the nanocomposite structure of most of the biological materials.
The results showed that the staggered structures will efficiently
attenuate the stress wave rather than the layered structure.
Furthermore, such staggered architecture is effectively in charge of
utilizing the capacity of the biostructure to resist both normal and
shear loads. In this work, the geometrical parameters of the model
like the thickness and aspect ratio of the mineral inclusions selected
from the typical range of the experimentally observed feature sizes
and layout dimensions of the biological materials such as bone and
mineralized tendon. Furthermore, the numerical results validated with
existing theoretical solutions. Findings of the present work emphasize
on the significant effects of dynamic behavior on the natural
evolution of load-bearing biological materials and can help scientists
to design bioinspired materials in the laboratories.
Abstract: Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.
Abstract: In recent years a new method of combination
treatment for cancer has been developed and studied that has led to
significant advancements in the field of cancer therapy. Hyperthermia
is a traditional therapy that, along with a creation of a medically
approved level of heat with the help of an alternating magnetic AC
current, results in the destruction of cancer cells by heat. This paper
gives details regarding the production of the spherical nanocomposite
PVA/γ-Fe2O3 in order to be used for medical purposes such as tumor
treatment by hyperthermia. To reach a suitable and evenly distributed
temperature, the nanocomposite with core-shell morphology and
spherical form within a 100 to 200 nanometer size was created using
phase separation emulsion, in which the magnetic nano-particles γ-
Fe2O3 with an average particle size of 20 nano-meters and with
different percentages of 0.2, 0.4, 0.5 and 0.6 were covered by
polyvinyl alcohol. The main concern in hyperthermia and heat
treatment is achieving desirable specific absorption rate (SAR) and
one of the most critical factors in SAR is particle size. In this project
all attempts has been done to reach minimal size and consequently
maximum SAR. The morphological analysis of the spherical
structure of the nanocomposite PVA/γ-Fe2O3 was achieved by SEM
analyses and the study of the chemical bonds created was made
possible by FTIR analysis. To investigate the manner of magnetic
nanocomposite particle size distribution a DLS experiment was
conducted. Moreover, to determine the magnetic behavior of the γ-
Fe2O3 particle and the nanocomposite PVA/γ-Fe2O3 in different
concentrations a VSM test was conducted. To sum up, creating
magnetic nanocomposites with a spherical morphology that would be
employed for drug loading opens doors to new approaches in
developing nanocomposites that provide efficient heat and a
controlled release of drug simultaneously inside the magnetic field,
which are among their positive characteristics that could significantly
improve the recovery process in patients.
Abstract: In contrast with literal meaning of nano, researchers
have been achieved mega adventures in this area and every day more
nanomaterials are being introduced to the market. After long time
application of fossil-based plastics, nowadays accumulation of their
waste seems to be a big problem to the environment. On the other
hand, mankind has more attention to safety and living environment.
Replacing common plastic packaging materials with degradable ones
that degrade faster and convert to non-dangerous components like
water and carbon dioxide have more attractions; these new materials
are based on renewable and inexpensive sources of starch and
cellulose. However, the functional properties of them do not suitable
for packaging. At this point, nanotechnology has an important role.
Utilizing of nanomaterials in polymer structure will improve
mechanical and physical properties of them; nanocrystalline cellulose
(NCC) has this ability. This work has employed a chemical method to
produce NCC and starch bio nanocomposite containing NCC. X-Ray
Diffraction technique has characterized the obtained materials.
Results showed that applied method is a suitable one as well as
applicable one to NCC production.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: In this work, we report, a systematic study on the
structural and optical properties of Pr-doped ZnO nanostructures and
PVA:Zn98Pr2O polymer matrix nanocomposites free standing films.
These particles are synthesized through simple wet chemical route
and solution casting technique at room temperature, respectively.
Structural studies carried out by X-ray diffraction method confirm
that the prepared pure ZnO and Pr doped ZnO nanostructures are in
hexagonal wurtzite structure and the microstrain is increased upon
doping. TEM analysis reveals that the prepared materials are in sheet
like nature. Absorption spectra show free excitonic absorption band
at 370 nm and red shift for the Pr doped ZnO nanostructures. The
PVA:Zn98Pr2O composite film exhibits both free excitonic and PVA
absorption bands at 282 nm. Fourier transform infrared spectral
studies confirm the presence of A1 (TO) and E1 (TO) modes of Zn-O
bond vibration and the formation of polymer composite materials.
Abstract: Polysulfone (PSU) is a specialty engineering polymer
having various industrial applications. PSU is especially used in
waste water treatment membranes due to its good mechanical
properties, structural and chemical stability. But it is a hydrophobic
material and therefore its surface aim to pollute easily. In order to
resolve this problem and extend the properties of membrane, PSU
surface is rendered hydrophilic by addition of the sepiolite
nanofibers. Sepiolite is one of the natural clays, which is a hydrate
magnesium silicate fiber, also one of the well known layered clays of
the montmorillonites where has several unique channels and pores
within. It has also moisture durability, strength and low price.
Sepiolite channels give great capacity of absorption and good surface
properties. In this study, nanocomposites of commercial PSU and
Sepiolite were prepared by solvent mixing method. Different organic
solvents and their mixtures were used. Rheological characteristics of
PSU-Sepiolite solvent mixtures were analyzed, the solubility of
nanocomposite content in those mixtures were studied.
Abstract: Water contamination by toxic compound is one of the serious environmental problems today. These toxic compounds mostly originated from industrial effluents, agriculture, natural sources and human waste. These studies focus on modification of multiwalled carbon nanotube (MWCNTs) with nanoparticle of calixarene and explore the possibility of using this modification for the remediation of cadmium in water. The nanocomposites were prepared by dissolving calixarene in chloroform solution as solvent, followed by additional multiwalled carbon nanotube (MWCNTs) then sonication process for 3 hour and fabricated the nanocomposites on substrate by spin coating method. Finally, the nanocomposites were tested on cadmium ion (10 mg/ml). The morphology of nanocomposites was investigated by FESEM showing the formation of calixarene on the outer walls of carbon nanotube and cadmium ion also clearly seen from the micrograph. This formation was supported by using energy dispersive x-ray (EDX). The presence of cadmium ions in the films, leads to some changes in the surface potential and Fourier Transform Infrared spectroscopy (FTIR).The nanocomposites MWCNTs-calixarene have potential for development of sensor for pollutant monitoring and nanoelectronics devices applications.
Abstract: Replacement of plastics used in the food industry
seems to be a serious issue to overcome mainly the environmental
problems in recent years. This study investigates the hydrophilicity
and permeability properties of starch biopolymer which ethylene
vinyl alcohol (EVOH) (0-10%) and nanocrystalline cellulose (NCC)
(1-15%) were used to enhance its properties. Starch -EVOH
nanocomposites were prepared by casting method in different
formulations. NCC production by acid hydrolysis was confirmed by
scanning electron microscopy. Solubility, water vapor permeability,
water vapor transmission rate and moisture absorbance were
measured on each of the nanocomposites. The results were analyzed
by SAS software. The lowest moisture absorbance was measured in
pure starch nanocomposite containing 8% NCC. The lowest
permeability to water vapor belongs to starch nanocomposite
containing 8% NCC and the sample containing 7.8% EVOH and 13%
NCC. Also the lowest solubility was observed in the composite
contains the highest amount of EVOH. Applied Process resulted in
production of bio films which have good resistance to water vapor
permeability and solubility in water. The use of NCC and EVOH
leads to reduced moisture absorbance property of the biofilms.
Abstract: In situ modified cyclohexanone-formaldehyde resins
were prepared by addition of alendronic acid during resin
preparation. Clay nanocomposites in ketonic resins were achieved by
adding clay into the flask at the beginning of the resin preparation.
The prepared resins were used for the synthesis of fire resistant
polyurethanes foam. Both phosphorous containing modifier
compound alendronic acid and nanoclay increases fire resistance of
the cyclohexanone-formaldehyde resin thus polyurethane produced
from these resins. The effect of the concentrations of alendronic acid
and clay on the fire resistance and physical properties of
polyurethanes was studied.
Abstract: The paper involves a chain of activities from
synthesis, establishment of the methodology for characterization and
testing of novel protective materials through the pilot production and
application on model supports.
It summarizes the results regarding the development of the pilot
production protocol for newly developed self-cleaning materials. The
optimization of the production parameters was completed in order to
improve the most important functional properties (mineralogy
characteristics, particle size, self-cleaning properties and
photocatalytic activity) of the newly designed nanocomposite
material.
Abstract: This paper illustrates the effect of nano Magnesium
Hydroxide (MH) loading on the thermal properties of Low Density
Polyethylene (LDPE)/Poly (ethylene-co vinyl acetate) (EVA) nano
composite. Thermal studies were conducted, as it understanding is
vital for preliminary development of new polymeric systems.
Thermal analysis of nanocomposite was conducted using thermo
gravimetric analysis (TGA), and differential scanning calorimetry
(DSC). Major finding of TGA indicated two main stages of
degradation process found at (350 ± 25oC) and (480 ± 25oC)
respectively. Nano metal filler expressed better fire resistance as it
stand over high degree of temperature. Furthermore, DSC analysis
provided a stable glass temperature around 51 (±1oC) and captured
double melting point at 84 (±2oC) and 108 (±2oC). This binary
melting point reflects the modification of nano filler to the polymer
matrix forming melting crystals of folded and extended chain. The
percent crystallinity of the samples grew vividly with increasing filler
content. Overall, increasing the filler loading improved the
degradation temperature and weight loss evidently and a better
process and phase stability was captured in DSC.
Abstract: The influence of three different types of halloysite
nanotubes (HNTs) with different dimensions, namely as camel lake
(CLA), Jarrahdale (JA) and Matauri Bay (MB), on their reinforcing
ability of ethylene propylene dine monomer (EPDM) were
investigated by varying the HNTs loading (from 0-15 phr).
Mechanical properties of the nanocomposites improved with addition
of all three HNTs, but CLA based nanocomposites exhibited a
significant enhancement compared to the other HNTs. For instance,
tensile properties of EPDM nanocomposites increased by 120%,
256% and 340% for MB, JA and CLA, respectively, with addition of
15 phr of HNTs. This could be due to the higher aspect ratio and
higher surface area of CLA compared to others. Scanning electron
microscopy (SEM) of nanocomposites at 15 phr of HNT loadings
showed low amounts of pulled-out nanotubes which confirmed the
presence of more embedded nanotubes inside the EPDM matrix, as
well as aggregates within the fracture surface of EPDM/HNT
nanocomposites