Abstract: Around the globe, there is demand for the development of bio-based lubricant which will be biodegradable, non -toxic and environmental friendly. This paper outlines the friction and wear characteristics of Pongamia oil (PO) contaminated bio-lubricant by using pin-on-disc tribometer. To formulate the bio-lubricants, PO was blended in the ratios 15, 30 and 50% by volume with the base lubricant SAE 20 W 40. Tribological characteristics of these blends were carried out at 3.8 m/s sliding velocity and loads applied were 50, 100, 150 N. Experimental results showed that the lubrication regime that occurred during the test was boundary lubrication while the main wear mechanisms were abrasive and the adhesive wear. During testing, the lowest wear was found with the addition of 15% PO, and above this contamination, the wear rate was increased considerably. With increase in load, viscosity of all the bio-lubricants increases and meets the ISO VG 100 requirement at 40 oC except PB 50. The addition of PO in the base lubricant acted as a very good lubricant additive which reduced the friction and wear scar diameter during the test. It has been concluded that the PB 15 can act as an alternative lubricant to increase the mechanical efficiency at 3.8 m/s sliding velocity and contribute in reduction of dependence on the petroleum based products.
Abstract: Vancron 40, a nitrided powder metallurgical tool
Steel, is used in cold work applications where the predominant failure
mechanisms are adhesive wear or galling. Typical applications of
Vancron 40 are among others fine blanking, cold extrusion, deep
drawing and cold work rolls for cluster mills. Vancron 40 positive
results for cold work rolls for cluster mills and as a tool for some
severe metal forming process makes it competitive compared to other
type of work rolls that require higher precision, among others in cold
rolling of thin stainless steel, which required high surface finish
quality. In this project, three roll materials for cold rolling of stainless
steel strip was examined, Vancron 40, Narva 12B (a high-carbon,
high-chromium tool steel alloyed with tungsten) and Supra 3 (a
Chromium-molybdenum tungsten-vanadium alloyed high speed
steel). The purpose of this project was to study the depth profiles of
the ironed stainless steel strips, emergence of galling and to study the
lubrication performance used by steel industries. Laboratory
experiments were conducted to examine scratch of the strip, galling
and surface roughness of the roll materials under severe tribological
conditions. The critical sliding length for onset of galling was
estimated for stainless steel with four different lubricants. Laboratory
experiments result of performance evaluation of resistance capability
of rolls toward adhesive wear under severe conditions for low and
high reductions. Vancron 40 in combination with cold rolling
lubricant gave good surface quality, prevents galling of
metal surfaces and good bearing capacity.