Abstract: Huntite and hydromagnesite minerals have been used as additive materials to achieve incombustible material due to their inflammability property. Those fire retardants materials can help to extinguish in the early stages of fire. Thus dispersion of the flame can be prevented even if the fire started. Huntite and hydromagnesite minerals are known to impart fire-proofing of the polymer composites. However, the additives used in the applications led to deterioration in the mechanical properties due to the usage of high amount of the powders in the composites. In this study, by enriching huntite and hydromagnesite, it was aimed to use purer minerals to reinforce the polymer composites. Thus, predictably, using purer mineral will lead to use lower amount of mineral powders. By this manner, the minerals free from impurities by various processes were added to the polymer matrix with different loading level and grades. Different types of samples were manufactured, and subsequently characterized by XRD, SEM-EDS, XRF and flame-retardant tests. Tensile strength and elongation at break values were determined according to loading levels and grades. Besides, a comparison on the properties of the polymer composites produced by using of minerals with and without impurities was performed. As a result of the work, it was concluded that it is required to use beneficiated minerals to provide better fire-proofing behaviors in the polymer composites.
Abstract: A number of studies have been conducted recently to
investigate the influence of randomly oriented fibers on some
engineering properties of cohesive and cohesionless soils. However,
few studies have been carried out on freezing-thawing behavior of
fine-grained soils modified with discrete fiber inclusions and additive
materials. This experimental study was performed to investigate the
effect of randomly distributed polypropylene fibers (PP) and some
additive materials [e.g.., borogypsum (BG), fly ash (FA) and cement
(C)] on freezing-thawing durability (mass losses) of a fine-grained
soil for 6, 12, and 18 cycles. The Taguchi method was applied to the
experiments and a standard L9 orthogonal array (OA) with four
factors and three levels were chosen. A series of freezing-thawing
tests were conducted on each specimen. 0-20% BG, 0-20% FA, 0-
0.25% PP and 0-3% of C by total dry weight of mixture were used in
the preparation of specimens. Experimental results showed that the
most effective materials for the freezing-thawing durability (mass
losses) of the samples were borogypsum and fly ash. The values of
mass losses for 6, 12 and 18 cycles in optimum conditions were
16.1%, 5.1% and 3.6%, respectively.
Abstract: Boron-gypsum is a waste which occurs in the boric
acid production process. In this study, the boron content of this waste
is evaluated for the use in synthesis of magnesium borates and such
evaluation of this kind of waste is useful more than storage or
disposal. Magnesium borates, which are a sub-class of boron
minerals, are useful additive materials for the industries due to their
remarkable thermal and mechanical properties. Magnesium borates
were obtained hydrothermally at different temperatures. Novelty of
this study is the search of the solution density effects to magnesium
borate synthesis process for the increasing the possibility of borongypsum
usage as a raw material. After the synthesis process, products
are subjected to XRD and FT-IR to identify and characterize their
crystal structure, respectively.
Abstract: Dehydration behavior gives a hint about thermal properties of materials. It is important for the usage areas and transportation of minerals. Magnesium borates can be used as additive materials in areas such as in the production of superconducting materials, in the composition of detergents, due to the content of boron in the friction-reducing additives in oils and insulating coating compositions due to their good mechanic and thermal properties.
In this study, thermal dehydration behavior of admontite (MgO(B2O3)3.7(H2O)), which is a kind of magnesium borate mineral, is experimented by microwave energy at 360W. Structure of admontite is suitable for the investigation of dehydration behavior by microwave because of its seven moles of crystal water. It is seen that admontite lost its 28.7% of weight at the end of the 120 minutes heating in microwave furnace.