Abstract: Ultra-high-performance fiber reinforced concrete (UHPFRC) is a specially formulated cement-based composite characterized with an ultra-high compressive strength (fc’ = 240 MPa) and a low water-cement ratio (W/B= 0.2). With such material characteristics, UHPFRC is favored for the design and constructions of structures required high structural performance and slender geometries. Unlike conventional concrete, the structural performance of members manufactured with UHPFRC has not yet been fully studied, particularly, for UHPFRC columns with high slenderness. In this study, the behaviors of slender UHPFRC columns under concentric or eccentric load will be investigated both experimentally and numerically. Four slender UHPFRC columns were tested under eccentric loads with eccentricities, of 0 mm, 35 mm, 50 mm, and 85 mm, respectively, and one UHPFRC beam was tested under four-point bending. Finite element (FE) analysis was conducted with concrete damage plasticity (CDP) modulus to simulating the load-middle height or middle span deflection relationships and damage patterns of all UHPFRC members. Simulated results were compared against the experimental results and observation to gain the confidence of FE model, and this model was further extended to conduct parametric studies, which aim to investigate the effects of slenderness regarding failure modes and load-moment interaction relationships. Experimental results showed that the load bearing capacities of the slender columns reduced with an increase in eccentricity. Comparisons between load-middle height and middle span deflection relationships as well as damage patterns of all UHPFRC members obtained both experimentally and numerically demonstrated high accuracy of the FE simulations. Based on the available FE model, the following parametric study indicated that a further increase in the slenderness of column resulted in significant decreases in the load-bearing capacities, ductility index, and flexural bending capacities.
Abstract: This is report on experiment out to compare the sulphate resistance of sand mortar made with five different pozzolanic cement. The pozzolanic cement were prepared by blending powered burnt bricks from the Adamawa, Makurdi, Kano, Kaduna and Niger bricks factories with ordinary Portland cement in the ratio 1:4. Sand –pozzolanic cement mortars of mix ratio 1:6 and 1:3 with water-cement ratio of 0.65 and 0.40 respectively were used to prepare cubes and bars specimens. 150 mortar cubes of size 70mm x 70mm x 70mm and 35 mortar bars of 15mm x 15mm x 100mm dimensions were cast and cured for 28 days. The cured specimens then immersed in the solutions of K2SO4, (NH4)2SO4 and water for 28 days and then tested. The compressive strengths of cubes in water increased by 34% while those in the sulphate solutions decreased. Strength decreases of the cubes, cracking and warping of bars immersed in K2SO4 were less than those in (NH4)2SO4. Specimens made with Niger and Makurdi pulverized burnt bricks experienced less effect of the sulphates and can therefore be used as pozzolan in mortar and concrete to resist sulphate.
Abstract: The present study aims to assess the performance of vermiculite concrete containing poly-lactic acid beads as an eco-friendly aggregate. Vermiculite aggregate was replaced by poly-lactic acid in percentages of 0%, 20%, 40%, 60% and 80%. Mechanical and thermal properties of concrete were investigated. Test results indicated that the inclusion of poly-lactic acid decreased the PH value of concrete and all the poly-lactic acid particles were dissolved due to the formation of sodium lactide and lactide oligomers when subjected to the high alkaline environment of concrete. In addition, an increase in thermal conductivity value of concrete was observed as the ratio of poly-lactic acid increased. Moreover, a set of equations was proposed to estimate the water-cement ratio, cement content and water absorption ratio of concrete.
Abstract: Lightweight concrete is being used in the construction industry as a building material in its own right. Ultra-lightweight concrete can be applied as a filler and support material for the manufacturing of composite building materials. This paper is about the development of a stable and reproducible ultra-lightweight concrete with the inclusion of poly-lactic acid (PLA) beads and assessing the feasibility of PLA as a lightweight aggregate that will deliver advantages such as a more eco-friendly concrete and a non-petroleum polymer aggregate. In total, sixty-three samples were prepared and the effectiveness of mineral admixture, curing conditions, water-cement ratio, PLA ratio, EPS ratio and perlite ratio on compressive strength of perlite concrete are studied. The results show that PLA particles are sensitive to alkali environment of cement paste and considerably shrank and lost their strength. A higher compressive strength and a lower density was observed when expanded polystyrene (EPS) particles replaced PLA beads. In addition, a set of equations is proposed to estimate the water-cement ratio, cement content and compressive strength of perlite concrete.
Abstract: This paper aimed to introduce the solution of concrete
slump recovery using chemical admixture type-F (superplasticizer,
naphthalene base) to the practice in order to solve unusable concrete
problem due to concrete loss its slump, especially for those tropical
countries that have faster slump loss rate. In the other hand, randomly
adding superplasticizer into concrete can cause concrete to segregate.
Therefore, this paper also develops the estimation model used to
calculate amount of second dose of superplasticizer need for concrete
slump recovery. Fresh properties of ordinary Portland cement
concrete with volumetric ratio of paste to void between aggregate
(paste content) of 1.1-1.3 with water-cement ratio zone of 0.30 to
0.67 and initial superplasticizer (naphthalene base) of 0.25%-1.6%
were tested for initial slump and slump loss for every 30 minutes for
one and half hour by slump cone test. Those concretes with slump
loss range from 10% to 90% were re-dosed and successfully
recovered back to its initial slump. Slump after re-dosed was tested
by slump cone test. From the result, it has been concluded that, slump
loss was slower for those mix with high initial dose of
superplasticizer due to addition of superplasticizer will disturb
cement hydration. The required second dose of superplasticizer was
affected by two major parameters, which were water-cement ratio
and paste content, where lower water-cement ratio and paste content
cause an increase in require second dose of superplasticizer. The
amount of second dose of superplasticizer is higher as the solid
content within the system is increase, solid can be either from cement
particles or aggregate. The data was analyzed to form an equation use
to estimate the amount of second dosage requirement of
superplasticizer to recovery slump to its original.
Abstract: The topic of the article focuses on the evaluation of selected technological factors and their influence on resulting elasticity modulus of concrete. A series of various factors enter into the manufacturing process which, more or less, influences the elasticity modulus. This paper presents the results of concrete in which the influence of water coefficient and the size of maximum fraction of the aggregate on the static elasticity modulus were monitored. Part of selected results of the long-term programme was discussed in which a wide scope of various variants of proposals for the composition of concretes was evaluated.
Abstract: Nowadays, the performance required for concrete
structures is more complicated and diversified. Self-compacting
concrete is a fluid mixture suitable for placing in structures with
congested reinforcement without vibration. Self-compacting concrete
development must ensure a good balance between deformability and
stability. Also, compatibility is affected by the characteristics of
materials and the mix proportions; it becomes necessary to evolve a
procedure for mix design of SCC.
This paper presents an experimental procedure for the design of
self-compacting concrete mixes with different water-cement ratios
(w/c) and other constant ratios by local materials. The test results for
acceptance characteristics of self-compacting concrete such as slump
flow, V-funnel and L-Box are presented. Further, compressive
strength, tensile strength and modulus of elasticity of specimens were
also determined and results are included here