Abstract: Climate change, namely precipitation patterns alteration, has led to extreme conditions such as floods and droughts. In turn, excessive construction has led to the waterproofing of the soil, increasing the surface runoff and decreasing the groundwater recharge capacity. The permeable pavements used in areas with low traffic lead to a decrease in the probability of floods peaks occurrence and the sediments reduction and pollutants transport, ensuring rainwater quality improvement. This study aims to evaluate the porous asphalt performance, developed in the laboratory, with addition of cellulosic fibres. One of the main objectives of cellulosic fibres use is to stop binder drainage, preventing its loss during storage and transport. Comparing to the conventional porous asphalt the cellulosic fibres addition improved the porous asphalt performance. The cellulosic fibres allowed the bitumen content increase, enabling retention and better aggregates coating and, consequently, a greater mixture durability. With this solution, it is intended to develop better practices of resilience and adaptation to the extreme climate changes and respond to the sustainability current demands, through the eco-friendly materials use. The mix design was performed for different size aggregates (with fine aggregates – PA1 and with coarse aggregates – PA2). The percentage influence of the fibres to be used was studied. It was observed that overall, the binder drainage decreases as the cellulose fibres percentage increases. It was found that the PA2 mixture obtained most binder drainage relative to PA1 mixture, irrespective of the fibres percentage used. Subsequently, the performance was evaluated through laboratory tests of indirect tensile stiffness modulus, water sensitivity, permeability and permanent deformation. The stiffness modulus for the two mixtures groups (with and without cellulosic fibres) presented very similar values between them. For the water sensitivity test it was observed that porous asphalt containing more fine aggregates are more susceptible to the water presence than mixtures with coarse aggregates. The porous asphalt with coarse aggregates have more air voids which allow water to pass easily leading to ITSR higher values. In the permeability test was observed that asphalt porous without cellulosic fibres presented had lower permeability than asphalt porous with cellulosic fibres. The resistance to permanent deformation results indicates better behaviour of porous asphalt with cellulosic fibres, verifying a bigger rut depth in porous asphalt without cellulosic fibres. In this study, it was observed that porous asphalt with bitumen higher percentages improve the performance to permanent deformation. This fact was only possible due to the bitumen retention by the cellulosic fibres.
Abstract: Cold bitumen emulsion mixture (CBEM) offers a series benefits as compared with hot mix asphalt (HMA); these include environmental factors, energy saving, the resolution of logistical challenges that can characterise hot mix, and the potential to reserve funds. However, this mixture has some problems similar to any bituminous mixtures as it has low early strength, long curing time that needed to obtain the maximum performance, high air voids and considered inferior to HMA. Thus, CBEM has been used in limited applications such as lightly trafficked roads, footways and reinstatements. This laboratory study describes the development of CBEM using ordinary Portland cement (OPC) instead of the traditional mineral filler. Stiffness modulus, moisture damage and temperature sensitivity tests were used to evaluate the mechanical properties of the produced mixtures. The study concluded that there is a substantial improvement in the mechanical properties and moisture damage resistance of CBEMs containing OPC. Also, the produced cement modified CBEM shows a considerable lower thermal sensitivity than the conventional CBEM.
Abstract: This study aims at developing a novel cold asphalt
concrete binder course mixture by using Ordinary Portland Cement
(OPC) as a replacement for conventional mineral filler (0%-100%)
with new by-product material (LJMU-A2) used as a supplementary
cementitious material. With this purpose, cold asphalt concrete binder
course mixtures with cationic emulsions were studied by means of
stiffness modulus whereas water sensitivity was assessed by
measuring the stiffness modulus ratio before and after sample
conditioning.
The results indicate that a substantial enhancement in the stiffness
modulus and a considerable improvement of water sensitivity
resistance is achieved by adding LJMU-A2 to the cold asphalt
mixtures as a supplementary cementitious material. Moreover, the
addition of LJMU-A2 to those mixtures leads to a stiffness modulus
after 2-day curing compared to that obtained with Portland cement,
which occurs after 7-day curing.
Abstract: Utilization of waste material in asphalt pavement
would be beneficial in order to find an alternative solution to increase
service life of asphalt pavement and reduce environmental pollution
as well. One of these waste materials is Polyethylene Terephthalate
(PET) which is a type of polyester material and is produced in a large
extent. This research program is investigating the effects of adding
waste PET particles into the asphalt mixture with a maximum size of
2.36 mm. Different percentages of PET were added into the mixture
during dry process. Gap-graded mixture (SMA 14) and PG 80-100
asphalt binder have been used for this study. To evaluate PET
reinforced asphalt mixture different laboratory investigations have
been conducted on specimens. Marshall Stability test was carried
out. Besides, stiffness modulus test and indirect tensile fatigue test
were conducted on specimens at optimum asphalt content. It was
observed that in many cases PET reinforced SMA mixture had better
mechanical properties in comparison with control mixture.